Crevice Corrosion in a Subsea System — Aspect Before Analysis

17 images

TryML00003corrosionML00056brittle fractureductile behaviorfatiguehydrogenfractureembrittlementstress corrosion
Capture method: Micrography by OM Detail focus: Microstructure clear all
M

Material

79 classified

Browse all Material →
P

Product

96 classified

Browse all Product →
Ap

Application

37 classified

Browse all Application →
C

Condition

84 classified

Browse all Condition →
Cm

Capture method

52 classified

Browse all Capture method →
Df

Detail focus

208 classified

Browse all Detail focus →
Browse by category (2)
Microstructure73
+65 more

and 25 more not shown here — refine in the Atlas

Standard298
+290 more

and 250 more not shown here — refine in the Atlas

The Materials
Image Database

17 images
Micrography of the plate in the middle of the thickness, showing the aligned structure tyical of a rolling process. The sample was mechanically-electrolitically polished and etched with HF (10%) + HNO3 (5%) +H2O (85%) solution.
28
VIEW
ML00144 / Aug.2018
Impact of a .380 Winchester on Ti64 Plate
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Micrography by OMDf - Alpha and Beta
Micrographic detail of the zinc at the fracture surface.
57
VIEW
ML00138 / Jun.2018
Liquid Metal Embrittlement of a HSLA Steel
M - High Strength Low AlloyP - Coated ProductAp - Mechanical IndustryCd - Liquid Metal Embrittlement
Cm - Micrography by OMDf - Zn Layer
The as polished micrography of a longitudinal section of the pin, showing several microcracks associated to the chromium layer.
56
VIEW
ML00081 / Aug.2017
Hydrogen Cracking of a Chromium Plated Carburized Pin
M - Low Alloy for Thermochemical TreatmentP - Chromium PlatedAp - AutomotiveCd - Hydrogen Embrittlement
Cm - Micrography by OMDf - Hard Chromium Layer
Low magnification micrography presenting the grapjite morphology.
137
VIEW
ML00032 / Jan.2017
Cast Iron Case of Drilling Equipment
M - Gray Cast ironP - CastAp - O&G Well DrillingCd - Typical manufacturing
Cm - Micrography by OMDf - Graphite Type A (ASTM A247)
Micrographic detail non metalic inclusions in the region where there are casting defects. As polished.
47
VIEW
ML00017 / Apr.2017
Casting Defect in CA6NM
M - Martensitic Stainless SteelP - Machined PartAp - EnergyCd - Casting Defect
Cm - Micrography by OMDf - Non Metallic Inclusions
The intake valve seat cylinder, manufactured in a high alloy white cast iron, presents a network of primary carbides, not degradated even after high temperature exposition during all lifetime.
632
VIEW
ML00003 / Apr.2017
Cast iron Engine Valve Seats
M - White Cast IronP - Valve SeatAp - MaritimeCd - Microstructural Evolution
Cm - Micrography by OMDf - Network of Primary Carbides

More from these cases

ML00144 — Impact of a .380 Winchester on Ti64 PlateM - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Micrography showing the alpha plus beta microstructure in the middle of the thickness. The sample was mechanically-electrolitically polished and etched with HF (10%) + HNO3 (5%) +H2O (85%) solution.
32
VIEW
ML00144 / Aug.2018
Impact of a .380 Winchester on Ti64 Plate
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Micrography by OMDf - Alpha and Beta
Micrographic detail of the plate, showing the alpha (light grains as a matrix) plus beta (dark phase) microstructure. Etched with HF (10%) + HNO3 (5%) +H2O (85%) solution.
28
VIEW
ML00144 / Aug.2018
Impact of a .380 Winchester on Ti64 Plate
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Micrography by OMDf - Alpha and Beta
Micrographic detail of the plate, showing the aligned beta phase (dark) in the alpha grains (light) microstructure. Etched with HF (10%) + HNO3 (5%) +H2O (85%) solution.
24
VIEW
ML00144 / Aug.2018
Impact of a .380 Winchester on Ti64 Plate
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Micrography by OMDf - Alpha and Beta
Micrographic detail of the plate, showing the aligned beta (dark phase) in alpha microstructure. Etched with HF+ HNO3+H2O solution.
26
VIEW
ML00144 / Aug.2018
Impact of a .380 Winchester on Ti64 Plate
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Micrography by OMDf - Alpha and Beta
Micrography by SEM of the plate in the middle of the thickness, showing the alpha microstructure (dark grains) and the beta phase (light). Etched with HF+HNO3+H2O.
35
VIEW
ML00144 / Aug.2018
Impact of a .380 Winchester on Ti64 Plate
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Micrography by OMDf - Alpha and Beta
ML00081 — Hydrogen Cracking of a Chromium Plated Carburized PinM - Low Alloy for Thermochemical TreatmentP - Chromium PlatedAp - AutomotiveCd - Hydrogen Embrittlement
The as polished micrography of a longitudinal section of the pin, showing that under the white layer of hard chromium (about 10 microns thick), there are already intergranular microcracks.
52
VIEW
ML00081 / Aug.2017
Hydrogen Cracking of a Chromium Plated Carburized Pin
M - Low Alloy for Thermochemical TreatmentP - Chromium PlatedAp - AutomotiveCd - Hydrogen Embrittlement
Cm - Micrography by OMDf - Hard Chromium Layer
ML00032 — Cast Iron Case of Drilling EquipmentM - Gray Cast ironP - CastAp - O&G Well DrillingCd - Typical manufacturing
Grey cast iron structure. As polished.
109
VIEW
ML00032 / Jan.2017
Cast Iron Case of Drilling Equipment
M - Gray Cast ironP - CastAp - O&G Well DrillingCd - Typical manufacturing
Cm - Micrography by OMDf - Graphite in Flakes
Grey cast iron with graphite in flakes.
97
VIEW
ML00032 / Jan.2017
Cast Iron Case of Drilling Equipment
M - Gray Cast ironP - CastAp - O&G Well DrillingCd - Typical manufacturing
Cm - Micrography by OMDf - Graphite in Flakes
ML00003 — Cast iron Engine Valve SeatsM - White Cast IronP - Valve SeatAp - MaritimeCd - Microstructural Evolution
The intake valve seat cylinder, manufactured in a high alloy white cast iron, presents a network of primary carbides, not degradated even after high temperature exposition during all lifetime.
206
VIEW
ML00003 / Apr.2017
Cast iron Engine Valve Seats
M - White Cast IronP - Valve SeatAp - MaritimeCd - Microstructural Evolution
Cm - Micrography by OMDf - Network of Primary Carbides
The exhaust valve seat cylinder, manufactured in a high alloy white cast iron, presents a coalesced structure, degradated by high temperature exposition during the lifetime.
182
VIEW
ML00003 / Apr.2017
Cast iron Engine Valve Seats
M - White Cast IronP - Valve SeatAp - MaritimeCd - Microstructural Evolution
Cm - Micrography by OMDf - Coalesced structure
The exhaust valve seat cylinder, manufactured in a high alloy white cast iron, presents a coalesced structure, degradated by high temperature exposition during the lifetime.
137
VIEW
ML00003 / Apr.2017
Cast iron Engine Valve Seats
M - White Cast IronP - Valve SeatAp - MaritimeCd - Microstructural Evolution
Cm - Micrography by OMDf - Coalesced structure

View all 17 images in the Atlas →

most recent

The location of the threaded fitting started leaking after less than five years in service. Although the corrosion rate was not high, the localized material loss in the threaded surface of the carbon steel flange allowed the connection leakage.
769
VIEW
ML00184 / Apr.2023
Dissimilar Steels in a Threaded Connection
M - Low Carbon SteelP - ForgingAp - OffshoreCd - Localized Dissolution
Cm - Aspect Before AnalysisDf - General View
Front wheel 17 x 7J of a passenger vehicle (identified as WHEEL 1) that broke during a car accident on a road.
1644
VIEW
ML00183 / Dec.2022
Ductile Behavior of an Aluminum Wheel
M - Aluminum Silicon MagnesiumP - CastingAp - AutomotiveCd - Ductile Behavior
Cm - Aspect Before AnalysisDf - General View
Tool fixture 5" long, nominal diameter 2", presenting a recess 1/2" deep from two sides. The rupture occurred about 2" from the end of the rod. Scale in milimeters.
523
VIEW
ML00182 / Jul.2022
Brittle Fracture of a LAS Fixing Rod
M - Low Alloy Medium Carbon QTP - StemAp - Mechanical IndustryCd - Brittle Fracture
Cm - Aspect Before AnalysisDf - General View
Pinion of hypoid gearbox, assembled in a 1560-mm long shaft that operated during more than 60,000 hours, and removed from service due to unacceptable wear damage.
1028
VIEW
ML00181 / Apr.2022
Wear of a Carburized Hypoid Gear
M - Low Alloy for Thermochemical TreatmentP - Pinion-crown assemblyAp - ShipCd - Wear
Cm - Aspect Before AnalysisDf - General View
Aspect of the 3 1/2" diameter tube after the water leakage in high temperature.
962
VIEW
ML00180 / Mar.2022
Local Melting of Copper Cooling Tubes
M - Pure CopperP - Cooling TubeAp - SiderurgyCd - Overheating
Cm - Aspect Before AnalysisDf - General View
2" drain line from the main 10" line. The leakage occurred at the margin of the weld, a short time after the introduction of the reinforced ribs to reduce vibration.
641
VIEW
ML00179 / Feb.2022
Hydrides in Titanium Weld
M - Unalloyed TitaniumP - In Field WeldAp - Chemical IndustryCd - Hydride Formation
Cm - Field photoDf - General View
The drilling connector, 21" diameter, presented a crack at the margin of the weld in the forging side (left side of the weld in the figure).
744
VIEW
ML00178 / Jan.2022
Cold cracks in Cr-Mo Welded Forging
M - CrMo SteelP - ForgingAp - O&G Well DrillingCd - Welding Defect
Cm - Aspect Before AnalysisDf - General View
Macrography of the longitudinally seam weld of the 24" diameter tube, showing that it was welded from both sides and there is a segregation line in the center of the tube thickness.
737
VIEW
ML00177 / Dec.2021
Cr-Mo Seam Welded Tube
M - CrMo SteelP - Longitudinally Seam WeldedAp - Fired HeaterCd - Not according to spec
Cm - NItal Etched MacroDf - Seam
The titanium rotor blade of a flowmeter broke after two years in service in an acid environment, containing H2S.
339
VIEW
ML00176 / Nov.2021
Hydride Formation in a Titanium Blade
M - Unalloyed TitaniumP - BladeAp - Oil and GasCd - Hydride Formation
Cm - Aspect Before AnalysisDf - General View
Aspect of the wire rope, 1 1/2" diameter, presenting regions of flattened areas at the surface of the outer wires. It is a 6 x 19 Seale construction, right regular lay.
552
VIEW
ML00175 / Aug.2021
Localized External Wear of a Wire Rope
M - High Carbon SteelP - Wire RopeAp - Oil and GasCd - Wear
Cm - Aspect Before AnalysisDf - General View
The carcass was manufactured using niobium stabilized plates, grade AISI 347, with circumferential welds, where the through wall cracks were detected.
300
VIEW
ML00174 / Jul.2021
Carburization of a 347 SS Welded Joint
M - Austenitic Stainless SteelP - Fabrication WeldAp - EnergyCd - Carburization
Cm - Field photoDf - General View
Aged microstructure of the HP stainless steel, modified with 1%Nb, cast fitting, tubular, operating for 6 years in a furnace which design temperature is 1100°C. The material presented a network of primary carbides, white and grey, and an austenitic matrix with coalescing secondary precipitation. Some voids. The Vickers identation indicates a hardness value about 260HV 100g in the aged austenitic matrix.
491
VIEW
ML00173 / May.2021
Welding Cracks in an Aged HP Cast Fitting
M - Heat Resistant SteelP - Cast FtittingAp - PetrochemicalCd - Welding
Cm - Kalling Etched Micrography by OMDf - Microhardness identations