Crevice Corrosion in a Subsea System — Aspect Before Analysis

Carbon Steel — sub-branches

High Carbon Steel 4Low Carbon Steel 21Medium Carbon Steel 6

Results

SortNewestOldestTitle A-ZTitle Z-A
The location of the threaded fitting started leaking after less than five years in service. Although the corrosion rate was not high, the localized material loss in the threaded surface of the carbon steel flange allowed the connection leakage.
769
VIEW
ML00184 / Apr.2023
Dissimilar Steels in a Threaded Connection
M - Low Carbon SteelP - ForgingAp - OffshoreCd - Localized Dissolution
Cm - Aspect Before AnalysisDf - General View
Aspect of the wire rope, 1 1/2" diameter, presenting regions of flattened areas at the surface of the outer wires. It is a 6 x 19 Seale construction, right regular lay.
552
VIEW
ML00175 / Aug.2021
Localized External Wear of a Wire Rope
M - High Carbon SteelP - Wire RopeAp - Oil and GasCd - Wear
Cm - Aspect Before AnalysisDf - General View
Aspect before cleaning of the heavy U bolt pipe clamp, 38 mm diameter wire, at the fractured position. It is possible to see that it broke in a region where the clamp was no longer coated and there is no insert in the groove (at the internal clamp diameter). The fracture is transverse to the clamp axis.
522
VIEW
ML00171 / Feb.2021
Corrosion Fatigue of U Bolt Pipe Clamp
M - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - General View
Aspect of the waterwall during removal of the leaking tube. The leakage was detected, by visual inspection, from the outside of the boiler.
1675
VIEW
ML00163 / Jun.2020
Corrosion Fatigue of a Boiler Waterwall Tube
M - Low Carbon SteelP - Seamless tubeAp - BoilerCd - Corrosion Fatigue
Cm - Field photoDf - General View
Macrography of a wheel section close to the tread, where the material receives a localized surface hardening by quenching and tempering. The average hardness at the surface is 346HB and in the center is 196HB. The wheel was in operation for a long time and the analyzed part is at the wheel tread.
902
VIEW
ML00158 / Feb.2020
Surface Hardened Carbon Steel Wheel
M - High Carbon SteelP - WheelAp - TransportationCd - Removed From Service
Cm - NItal Etched MacroDf - Transverse Section
Concrete steel strand general view, presenting fracture of several wires and a corroded aspect. The full part is composed by 19 strands, each strand using 7 wires, and each wire about 5 mm diameter.
834
VIEW
ML00155 / Jan.2020
Failure of a Prestressed Concrete Steel Strand
M - High Carbon SteelP - Wire RopeAp - StructureCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - General View
Gas piping. Aspect of a branching line 2" ND, lateral to a horizontal main pipe ND 8", welded using a weldolet. The cracking started at the margin of the weld in the upper part of the pipe, where the weld crossed the longitudinal direction of the pipe, perpendicular to the branch.
932
VIEW
ML00149 / Dec.2018
Vibration Induced Fatigue in a Gas Piping
M - Low Carbon SteelP - Piping spoolAp - FPSOCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - Cracking
Red painted device where the 50 mm x 50 mm carbon steel plate was positioned (in the circle). The image presents the target, positioned 100 meters far from the gun, after the shot and the projectile perforated the plate, as will be presented in the other figures.
601
VIEW
ML00143 / Aug.2018
Impact of a .308 Winchester on A36 Plate
M - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Cm - Aspect Before AnalysisDf - General View

More from these cases

ML00184 — Dissimilar Steels in a Threaded ConnectionM - Low Carbon SteelP - ForgingAp - OffshoreCd - Localized Dissolution
The painting of the valve body was detaching at the vent location where the fitting was installed, not fully tighted. Three threaded fillets were outside of the body.
190
VIEW
ML00184 / Apr.2023
Dissimilar Steels in a Threaded Connection
M - Low Carbon SteelP - ForgingAp - OffshoreCd - Localized Dissolution
Cm - Aspect After CleaningDf - Painting Detachment
The austenitic stainless steel fitting was removed from the valve body and presented the sdhesion of oily deposits.
150
VIEW
ML00184 / Apr.2023
Dissimilar Steels in a Threaded Connection
M - Low Carbon SteelP - ForgingAp - OffshoreCd - Localized Dissolution
Cm - Aspect Before AnalysisDf - Surface Deposits
The cleaned fitting is sound. No corrosion, only surface stains.
121
VIEW
ML00184 / Apr.2023
Dissimilar Steels in a Threaded Connection
M - Low Carbon SteelP - ForgingAp - OffshoreCd - Localized Dissolution
Cm - Aspect After CleaningDf - General View
The threads of the carbon steel valve body is corroded. The offshore ambient is wet and chloride rich, creating an aggressive environment for the carbon steel threads.
99
VIEW
ML00184 / Apr.2023
Dissimilar Steels in a Threaded Connection
M - Low Carbon SteelP - ForgingAp - OffshoreCd - Localized Dissolution
Cm - Surface AspectDf - Corrosion
Not only the threads were corroded but all regions under the painting that was detached from the surface.
86
VIEW
ML00184 / Apr.2023
Dissimilar Steels in a Threaded Connection
M - Low Carbon SteelP - ForgingAp - OffshoreCd - Localized Dissolution
Cm - Surface AspectDf - Corrosion

+8 more from this case →

ML00175 — Localized External Wear of a Wire RopeM - High Carbon SteelP - Wire RopeAp - Oil and GasCd - Wear
Macrosection of the wire rope, transverse, showing 6 strands and an independent wire rope core (IWRC). Each strand presents three layers in a SEALE construction.
92
VIEW
ML00175 / Aug.2021
Localized External Wear of a Wire Rope
M - High Carbon SteelP - Wire RopeAp - Oil and GasCd - Wear
Cm - Transverse Section AspectDf - Plastic Deformation
Low magnification micrography of a strain hardened pearlitic structure, in a longitudinal section, of one 3.2mm round wire of one strand.
62
VIEW
ML00175 / Aug.2021
Localized External Wear of a Wire Rope
M - High Carbon SteelP - Wire RopeAp - Oil and GasCd - Wear
Cm - Nital Etched Micrography by OMDf - Longitudinal Section
Highly strain hardened pearlitic structure of one external wire, 3.2mm diameter, of one strand.
55
VIEW
ML00175 / Aug.2021
Localized External Wear of a Wire Rope
M - High Carbon SteelP - Wire RopeAp - Oil and GasCd - Wear
Cm - Nital Etched Micrography by OMDf - Pearlite
Micrographic detail of the strain hardened pearlitic structure, in a longitudinal section, of a 3.2mm external round wire of one strand. This structure presented a hardness level about 500 HV (1kg), measured in the center of the thickness in the metallographic section.
47
VIEW
ML00175 / Aug.2021
Localized External Wear of a Wire Rope
M - High Carbon SteelP - Wire RopeAp - Oil and GasCd - Wear
Cm - Nital Etched Micrography by OMDf - Strain Hardened
Metallographic aspect of the wire surface in one strand external wire, showing the presence of oxides.
41
VIEW
ML00175 / Aug.2021
Localized External Wear of a Wire Rope
M - High Carbon SteelP - Wire RopeAp - Oil and GasCd - Wear
Cm - Nital Etched Micrography by OMDf - At the Surface

+11 more from this case →

ML00171 — Corrosion Fatigue of U Bolt Pipe ClampM - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Aspect of the U bolt clamp with partial detachment of the coating (white brown) in a region where the polimeric insert (dirty white) is still in the wire groove at the internal clamp diameter (ID).
91
VIEW
ML00171 / Feb.2021
Corrosion Fatigue of U Bolt Pipe Clamp
M - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - General View
Detailed aspect of the fractured position, in a region where the clamp was no longer coated and there is no insert in the groove (at the internal clamp diameter). The fracture is transverse to the clamp axis.
86
VIEW
ML00171 / Feb.2021
Corrosion Fatigue of U Bolt Pipe Clamp
M - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - Fracture
Same aspect of the previous image after cleaning, showing a subcritical propagation aspect (fatigue), starting at the groove (ID) and also at the clamp surface in the OD.
75
VIEW
ML00171 / Feb.2021
Corrosion Fatigue of U Bolt Pipe Clamp
M - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - Fracture
In the region where the polimeric insert was loose, the protective coating of the clamp has suffered detachment.
69
VIEW
ML00171 / Feb.2021
Corrosion Fatigue of U Bolt Pipe Clamp
M - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - Layer Detachment
Close to the ID of the clamp, at the groove position, there are cracks in the coating (white brown) and also at the substrate.
63
VIEW
ML00171 / Feb.2021
Corrosion Fatigue of U Bolt Pipe Clamp
M - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - Cracks

+22 more from this case →

ML00163 — Corrosion Fatigue of a Boiler Waterwall TubeM - Low Carbon SteelP - Seamless tubeAp - BoilerCd - Corrosion Fatigue
Aspect of the sample removed from the waterwall, where the tube has leaked, presenting the crack in the membrane.
361
VIEW
ML00163 / Jun.2020
Corrosion Fatigue of a Boiler Waterwall Tube
M - Low Carbon SteelP - Seamless tubeAp - BoilerCd - Corrosion Fatigue
Cm - Field photoDf - Through Wall Cracking
Aspect of the tube internal surface after removal from the boiler, presenting multiple longitudinal cracks.
295
VIEW
ML00163 / Jun.2020
Corrosion Fatigue of a Boiler Waterwall Tube
M - Low Carbon SteelP - Seamless tubeAp - BoilerCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - Internal Surface
Aspect of the external surface of the leaking tube, after removal of the membrane.
262
VIEW
ML00163 / Jun.2020
Corrosion Fatigue of a Boiler Waterwall Tube
M - Low Carbon SteelP - Seamless tubeAp - BoilerCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - External Surface
Throught wall cracking of the waterwall tube at the leakage position, thick edged, The external surface of the tube was grounded to remove the membrane and the cracking is associated to the tube attachement.
242
VIEW
ML00163 / Jun.2020
Corrosion Fatigue of a Boiler Waterwall Tube
M - Low Carbon SteelP - Seamless tubeAp - BoilerCd - Corrosion Fatigue
Cm - Transverse Section AspectDf - Thick-edged rupture
Macrography of the transverse section of the tube, in a position where the cracking was not yet through wall. The internal tube surface shows multiple corrosion fatigue cracks, parallel, under the weld of the membrane, probably related to the cold side of the tube (the cracks opened to the boiler outside). The external side of the tube presenting a small crack at the margem of the weld, suggesting also the action of thermal stresses.
214
VIEW
ML00163 / Jun.2020
Corrosion Fatigue of a Boiler Waterwall Tube
M - Low Carbon SteelP - Seamless tubeAp - BoilerCd - Corrosion Fatigue
Cm - NItal Etched MacroDf - Multiple cracks

+18 more from this case →

ML00158 — Surface Hardened Carbon Steel WheelM - High Carbon SteelP - WheelAp - TransportationCd - Removed From Service
Micrography of the wheel in the center of the thickness. The material presents a coarse structure.
88
VIEW
ML00158 / Feb.2020
Surface Hardened Carbon Steel Wheel
M - High Carbon SteelP - WheelAp - TransportationCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - In the Center of the Thickness
Micrography of the wheel in the center of the thickness, presenting a predominantly pearlitic structure and average hardness abot 196HB.
74
VIEW
ML00158 / Feb.2020
Surface Hardened Carbon Steel Wheel
M - High Carbon SteelP - WheelAp - TransportationCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Coarse Structure
Micrographic detail of the coarse pearlitic structure in the center of the wheel thickness. The part presents a wrought structure.
73
VIEW
ML00158 / Feb.2020
Surface Hardened Carbon Steel Wheel
M - High Carbon SteelP - WheelAp - TransportationCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Pearlite
Micrography of the wheel at the surface that was quenched and tempered. The material presents a tempered martensitic structure, with hardness that varied from 327HB to 363HB.
55
VIEW
ML00158 / Feb.2020
Surface Hardened Carbon Steel Wheel
M - High Carbon SteelP - WheelAp - TransportationCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - At the Surface
Micrography of the wheel at the hardened surface, presenting a refined martensitic structure, tempered for average hardness of 346 HB.
50
VIEW
ML00158 / Feb.2020
Surface Hardened Carbon Steel Wheel
M - High Carbon SteelP - WheelAp - TransportationCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - At the Surface

+5 more from this case →

ML00155 — Failure of a Prestressed Concrete Steel StrandM - High Carbon SteelP - Wire RopeAp - StructureCd - Corrosion Fatigue
General aspect of the degradated wires of the strand, most part presenting rust and rupture.
107
VIEW
ML00155 / Jan.2020
Failure of a Prestressed Concrete Steel Strand
M - High Carbon SteelP - Wire RopeAp - StructureCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - General View
General aspect of the degradated wires of the strand, most part presenting rust and rupture. There are two mais aspects of the degradation: wire thickness reduction by corrosion and cracks creating a longitudinal fracture of several wires.
96
VIEW
ML00155 / Jan.2020
Failure of a Prestressed Concrete Steel Strand
M - High Carbon SteelP - Wire RopeAp - StructureCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - Fracture
Micrography of a wire in a longitudinal section, presenting a predominantly oearlitic structure, highly strained. The wires did not present any coating.
104
VIEW
ML00155 / Jan.2020
Failure of a Prestressed Concrete Steel Strand
M - High Carbon SteelP - Wire RopeAp - StructureCd - Corrosion Fatigue
Cm - Nital Etched Micrography by OMDf - Longitudinal Section
Higher magnification detail of the predominantly pearlitic microstructure of the wire.
88
VIEW
ML00155 / Jan.2020
Failure of a Prestressed Concrete Steel Strand
M - High Carbon SteelP - Wire RopeAp - StructureCd - Corrosion Fatigue
Cm - Nital Etched Micrography by OMDf - Predominantly Pearlitic
Macrography of a typical corroded wire in a longitudinal section, showing loss of thickness by corrosion.
75
VIEW
ML00155 / Jan.2020
Failure of a Prestressed Concrete Steel Strand
M - High Carbon SteelP - Wire RopeAp - StructureCd - Corrosion Fatigue
Cm - NItal Etched MacroDf - Corrosion

+36 more from this case →

ML00149 — Vibration Induced Fatigue in a Gas PipingM - Low Carbon SteelP - Piping spoolAp - FPSOCd - Vibration Induced Fatigue
Gas piping. Aspect of a branching line 2" ND with a flange, lateral to a main pipe ND 8", welded using a weldolet. The cracking is at the margin of the weld.
115
VIEW
ML00149 / Dec.2018
Vibration Induced Fatigue in a Gas Piping
M - Low Carbon SteelP - Piping spoolAp - FPSOCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - General View
Micrography of a transverse section of the seamless pipe, presenting a ferritic-pearlitic structure.
84
VIEW
ML00149 / Dec.2018
Vibration Induced Fatigue in a Gas Piping
M - Low Carbon SteelP - Piping spoolAp - FPSOCd - Vibration Induced Fatigue
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Micrography of a transverse section of the seamless pipe, presenting a ferritic-pearlitic structure.
70
VIEW
ML00149 / Dec.2018
Vibration Induced Fatigue in a Gas Piping
M - Low Carbon SteelP - Piping spoolAp - FPSOCd - Vibration Induced Fatigue
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Gas piping. Aspect of a branching line 2" ND, lateral to a horizontal main pipe ND 8", welded using a weldolet. In the lower part of the branch there are no cracks.
61
VIEW
ML00149 / Dec.2018
Vibration Induced Fatigue in a Gas Piping
M - Low Carbon SteelP - Piping spoolAp - FPSOCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - Welded Joint
Aspect of the brach line viewed from the internal side of the main pipe, after cuting. It is possible to see that the pipe was perforated by a thermal cutting (looking the finishing aspect of the edge of the hole). The weldolet was welded only from the external side of the pipe.
62
VIEW
ML00149 / Dec.2018
Vibration Induced Fatigue in a Gas Piping
M - Low Carbon SteelP - Piping spoolAp - FPSOCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - Internal Surface

+13 more from this case →

ML00143 — Impact of a .308 Winchester on A36 PlateM - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Aspect of a typical .308 Winchester projectile, similar to the one adopted to shot the plate, cut in a longitudinal section. It is a Cu alloy case filled with Pb-Sb.
91
VIEW
ML00143 / Aug.2018
Impact of a .308 Winchester on A36 Plate
M - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Cm - Longitudinal Section AspectDf - Longitudinal Section
Aspect of the 3/8" thickness plate, 50 mm x 50 mm, of the low carbon steel steel, in the face of impact with the projectile. The plate was perforated by the bullet.
88
VIEW
ML00143 / Aug.2018
Impact of a .308 Winchester on A36 Plate
M - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Cm - Aspect Before AnalysisDf - General View
Micrography of the plate in a section, showing a ferritic-pearlitic microstructure in the middle of the thickness.
84
VIEW
ML00143 / Aug.2018
Impact of a .308 Winchester on A36 Plate
M - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Micrography of the plate in a section, showing a ferritic-pearlitic microstructure in the middle of the thickness, in a position where the plate was not affected by the shot.
65
VIEW
ML00143 / Aug.2018
Impact of a .308 Winchester on A36 Plate
M - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Micrographic detail of the plate in a section, showing a ferritic-pearlitic microstructure in the middle of the thickness.
66
VIEW
ML00143 / Aug.2018
Impact of a .308 Winchester on A36 Plate
M - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite

+51 more from this case →