Carbon Steel

3 cases · 32 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Application: Automotive clear all

Carbon Steel — sub-branches

Low Carbon Steel 3

Results

SortNewestOldestTitle A-ZTitle Z-A
Detailed aspect of the eye bolt fracture position, with strong plastic deformation indicating ductile overloading. The red marks in the thread surface of the bolt (in the left side of the image) correspond to the position where the nut was tight. Thread fillets adjacent to the fracture presented secondary cracks.
1125
VIEW
ML00120 / Jun.2018
Ductile Rupture of a Carbon Steel Eye Bolt
M - Low Carbon SteelP - FastenerAp - AutomotiveCd - Overload
Cm - Aspect Before AnalysisDf - Ductile Fracture
Fracture occurred during fabrication of a low carbon steel automotive part, welded by SAW process in one fillet, between a superior plate (8mm thick) and an inferior plate (12 mm thick). See the schematic drawing in the next figure.
290
VIEW
ML00069 / May.2017
Liquation Cracks in SAW of Low Carbon Steel
M - Low Carbon SteelP - Fabrication WeldAp - AutomotiveCd - Welding Defect
Cm - Aspect Before AnalysisDf - Fracture
Detail of the longitudinal section of the ring, showing a fully ferritic structure.
619
VIEW
ML00057 / Apr.2017
Low Carbon Steel of Segment Ring
M - Low Carbon SteelP - Machined PartAp - AutomotiveCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Longitudinal Section

More from these cases

ML00120 — Ductile Rupture of a Carbon Steel Eye BoltM - Low Carbon SteelP - FastenerAp - AutomotiveCd - Overload
Macrography of a longitudinal section of the eye bolt, presenting the fracture in the top of the figure and the threads in the left side of the figure. Details of the fracture of the first thread fillet below the fracture are presented in the next figures.
225
VIEW
ML00120 / Jun.2018
Ductile Rupture of a Carbon Steel Eye Bolt
M - Low Carbon SteelP - FastenerAp - AutomotiveCd - Overload
Cm - NItal Etched MacroDf - Longitudinal Section
Micrography as polished of the longitudinal section of the bolt at the fracture position. The fracture (top of the figure) is rough, characteristic of a ductile fracture.
196
VIEW
ML00120 / Jun.2018
Ductile Rupture of a Carbon Steel Eye Bolt
M - Low Carbon SteelP - FastenerAp - AutomotiveCd - Overload
Cm - As polished micrographyDf - Fracture
Micrography as polished of the longitudinal section of the bolt at the first thread fillet below the fracture, presenting a cracking at the bottom of the fillet.
194
VIEW
ML00120 / Jun.2018
Ductile Rupture of a Carbon Steel Eye Bolt
M - Low Carbon SteelP - FastenerAp - AutomotiveCd - Overload
Cm - NItal Etched MacroDf - Crack
Apect of the 1/2" ND bumper eye bolt that was fractured (in the left side of the figure) in the position where the nut was tight.
192
VIEW
ML00120 / Jun.2018
Ductile Rupture of a Carbon Steel Eye Bolt
M - Low Carbon SteelP - FastenerAp - AutomotiveCd - Overload
Cm - Aspect Before AnalysisDf - General View
Micrography of a longitudinal section of the bolt in the center of the thickness, presenting a ferritic pearlitic structure with elongated grains due to the forming process, without later heat treatment.
173
VIEW
ML00120 / Jun.2018
Ductile Rupture of a Carbon Steel Eye Bolt
M - Low Carbon SteelP - FastenerAp - AutomotiveCd - Overload
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite

+5 more from this case →

ML00069 — Liquation Cracks in SAW of Low Carbon SteelM - Low Carbon SteelP - Fabrication WeldAp - AutomotiveCd - Welding Defect
Schematic drawing presenting the fracture occured during fabrication of a low carbon steel automotive part.
82
VIEW
ML00069 / May.2017
Liquation Cracks in SAW of Low Carbon Steel
M - Low Carbon SteelP - Fabrication WeldAp - AutomotiveCd - Welding Defect
Cm - Identification drawingDf - Fracture
Macrography of the typical welded joint between the superior plate (8mm) and the inferior plate (12 mm) using one SAW fillet. The superior plate is welded in the thickness and the inferior plate is welded at the surface in this overlap joint. See the schematic drawing in the next figure
95
VIEW
ML00069 / May.2017
Liquation Cracks in SAW of Low Carbon Steel
M - Low Carbon SteelP - Fabrication WeldAp - AutomotiveCd - Welding Defect
Cm - NItal Etched MacroDf - Welded Joint
Schematic drawing presenting the different zones at the welded joint.
88
VIEW
ML00069 / May.2017
Liquation Cracks in SAW of Low Carbon Steel
M - Low Carbon SteelP - Fabrication WeldAp - AutomotiveCd - Welding Defect
Cm - Identification drawingDf - Welded Joint
Micrography of the ferritic low carbon steel plate (8 mm superior plate).
80
VIEW
ML00069 / May.2017
Liquation Cracks in SAW of Low Carbon Steel
M - Low Carbon SteelP - Fabrication WeldAp - AutomotiveCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Base Metal
Micrographic detail of the ferritic low carbon steel plate (8 mm superior plate).
80
VIEW
ML00069 / May.2017
Liquation Cracks in SAW of Low Carbon Steel
M - Low Carbon SteelP - Fabrication WeldAp - AutomotiveCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Base Metal

+10 more from this case →

ML00057 — Low Carbon Steel of Segment RingM - Low Carbon SteelP - Machined PartAp - AutomotiveCd - Removed From Service
Longitudinal section of the ring, showing a fully ferritic structure.
128
VIEW
ML00057 / Apr.2017
Low Carbon Steel of Segment Ring
M - Low Carbon SteelP - Machined PartAp - AutomotiveCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Longitudinal Section
The longitudinal section of the ring reveals a very fine ferritic structure.
115
VIEW
ML00057 / Apr.2017
Low Carbon Steel of Segment Ring
M - Low Carbon SteelP - Machined PartAp - AutomotiveCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Longitudinal Section
Transverse section of the ring presenting a fully ferritic structure, that presents a hardness level a little higher probably due to a cold forming effect.
93
VIEW
ML00057 / Apr.2017
Low Carbon Steel of Segment Ring
M - Low Carbon SteelP - Machined PartAp - AutomotiveCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Transverse Section
Transverse section of the ring presenting a fully ferritic structure, that presents a hardness level a little higher probably due to a cold forming effect.
54
VIEW
ML00057 / Apr.2017
Low Carbon Steel of Segment Ring
M - Low Carbon SteelP - Machined PartAp - AutomotiveCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Transverse Section