NaOH Electrolytic Etched Macro

6 cases · 13 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Results

SortNewestOldestTitle A-ZTitle Z-A
Macrography of the section transverse to the ND 14" main pipe (that is only 5mm thick) and to the ND 2" branch that is a weldolet fitting welded to the main pipe and flange. This image is interesting because it shows clearly how thin is the pipe compared with the fitting thickness and the large amount of welding required to assure a full penetration weld in the weldolet.
220
VIEW
ML00150 / Dec.2018
Vibration Induced Fatigue in a SS Oil Piping
M - Duplex Stainless SteelP - PipingAp - FPSOCd - Vibration Induced Fatigue
Cm - NaOH Electrolytic Etched MacroDf - Transverse Section
Macrographic aspect of the sleeve longitudinal section where the coating was applied in the external side (top of the figure). It is possible to see that the sleeve was manufactured by centrifugal casting, with elongated grains from the external side, and equiaxial grains close to the internal side (bottom of the figure). There is a weaved interface between the sleeve and the first layer of thermal spray coating, 1 mm thick; and a second layer of thermal spray coating, 0.2mm thick (almost imperceptible at this low magnification).
49
VIEW
ML00147 / Aug.2018
WC Layer Detached from a Cast Lean Duplex
M - Lean Duplex Stainless SteelP - Centrifugal CastingAp - ShipCd - Lack of Sealing
Cm - NaOH Electrolytic Etched MacroDf - Coating Layer
Aspect of the valve body after cutting a slice containg the crack and the welded joint of the body to the insert (fillet weld). The cracking was arrested at the position of this welded joint.
56
VIEW
ML00134 / Aug.2020
Brittle Fracture of a Superduplex Valve Body
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Cm - NaOH Electrolytic Etched MacroDf - Welded Joint
Macrography of the welded joint between a forging connector (right side) and a seamless tubing (left side). It was welded in two passes by GTAW process.
168
VIEW
ML00100 / Nov.2017
Superduplex Tubing to Forging Welded Joint
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Welding
Cm - NaOH Electrolytic Etched MacroDf - Welded Joint
Macrography of the pipe to flange weld. Transverse section identifying the regions of the base materials, heat affected zones and weld metal, which microstructures are presented in this ML.
527
VIEW
ML00049 / Apr.2017
Pipe to Flange Welded Joint in a 14" ND Superduplex Spool
M - Super Duplex Stainless SteelP - Piping spoolAp - Oil and GasCd - Removed From Service
Cm - NaOH Electrolytic Etched MacroDf - Welded Joint
Macrography of a longitudinal section of the flange to pipe weld, cracked in the flange. Pipe thickness, measured, is 5 mm. Flange thickness at the welded region is 7.5 mm. The macro was etched using NaOH solution, electrolytic.
181
VIEW
ML00002 / Jan.2018
Preferential Dissolution and Cracks in SDSS
M - Super Duplex Stainless SteelP - Fabrication WeldAp - PipingCd - Preferential Dissolution
Cm - NaOH Electrolytic Etched MacroDf - Longitudinal Section

More from these cases

ML00150 — Vibration Induced Fatigue in a SS Oil PipingM - Duplex Stainless SteelP - PipingAp - FPSOCd - Vibration Induced Fatigue
Macrographic detail of the pipe to weldolet weld, and the through wall cracking in the pipe from the margin of the weld. The pipe thickness is only 5 mm (SCH 10S) but the large thickness of the fitting required several weld passes to create a full penetration weld.
84
VIEW
ML00150 / Dec.2018
Vibration Induced Fatigue in a SS Oil Piping
M - Duplex Stainless SteelP - PipingAp - FPSOCd - Vibration Induced Fatigue
Cm - NaOH Electrolytic Etched MacroDf - Welded Joint
Macrography of a transverse section of the welded joint, at the fatigue crack position in the pipe. It is very interesting to observe that the crack propagated from the margin of the weld, independently of the defects in the weld (porosity and lack of fusion), and without relationship with the unbalanced structure at the cap (with a large amount of ferrite). These characteristics are detailed in the next figures.
89
VIEW
ML00150 / Dec.2018
Vibration Induced Fatigue in a SS Oil Piping
M - Duplex Stainless SteelP - PipingAp - FPSOCd - Vibration Induced Fatigue
Cm - NaOH Electrolytic Etched MacroDf - Welded Joint
ML00147 — WC Layer Detached from a Cast Lean DuplexM - Lean Duplex Stainless SteelP - Centrifugal CastingAp - ShipCd - Lack of Sealing
Macrography of a longitudinal section showing the region where the surface layer was detached (top of the figure), creating a lack of sealing condition.
23
VIEW
ML00147 / Aug.2018
WC Layer Detached from a Cast Lean Duplex
M - Lean Duplex Stainless SteelP - Centrifugal CastingAp - ShipCd - Lack of Sealing
Cm - NaOH Electrolytic Etched MacroDf - Thermal Spray Layer
ML00134 — Brittle Fracture of a Superduplex Valve BodyM - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Macrographic detail of the valve at the welded joint of the SDSS body (left side of the figure) to the Alloy 625 insert (right side of the figure), by a fillet weld. The cracking was arrested at the position of this welded joint.
48
VIEW
ML00134 / Aug.2020
Brittle Fracture of a Superduplex Valve Body
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Cm - NaOH Electrolytic Etched MacroDf - Welded Joint
ML00049 — Pipe to Flange Welded Joint in a 14" ND Superduplex SpoolM - Super Duplex Stainless SteelP - Piping spoolAp - Oil and GasCd - Removed From Service
Macrography of the pipe heat affected zone.
55
VIEW
ML00049 / Apr.2017
Pipe to Flange Welded Joint in a 14" ND Superduplex Spool
M - Super Duplex Stainless SteelP - Piping spoolAp - Oil and GasCd - Removed From Service
Cm - NaOH Electrolytic Etched MacroDf - Heat Affected Zone
Macrography of the flange HAZ. The macroscopic aspect shows a remarkable modified region.
56
VIEW
ML00049 / Apr.2017
Pipe to Flange Welded Joint in a 14" ND Superduplex Spool
M - Super Duplex Stainless SteelP - Piping spoolAp - Oil and GasCd - Removed From Service
Cm - NaOH Electrolytic Etched MacroDf - Heat Affected Zone
Micrographic detail of the center of the weld metal (fill pass). Duplex ferritic austenitic structure.
26
VIEW
ML00049 / Apr.2017
Pipe to Flange Welded Joint in a 14" ND Superduplex Spool
M - Super Duplex Stainless SteelP - Piping spoolAp - Oil and GasCd - Removed From Service
Cm - NaOH Electrolytic Etched MacroDf - Weld Metal in the Center