Duplex Stainless Steel

1 case · 35 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Results

SortNewestOldestTitle A-ZTitle Z-A
Vertical piping in a corrosive oil producing system of a FPSO. The line is a nominal diameter 14" sch 10S (pipe thickness about 5 mm) and the flanged branch line is a 2" nominal diameter welded to the main pipe using a weldolet (forged fitting). The fatigue induced cracking occurred longitudinal to the main pipe, originated at the margem of the weld interface with the pipe.
1480
VIEW
ML00150 / Dec.2018
Vibration Induced Fatigue in a SS Oil Piping
M - Duplex Stainless SteelP - PipingAp - FPSOCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - General View

More from these cases

ML00150 — Vibration Induced Fatigue in a SS Oil PipingM - Duplex Stainless SteelP - PipingAp - FPSOCd - Vibration Induced Fatigue
Macrography of the section transverse to the ND 14" main pipe (that is only 5mm thick) and to the ND 2" branch that is a weldolet fitting welded to the main pipe and flange. This image is interesting because it shows clearly how thin is the pipe compared with the fitting thickness and the large amount of welding required to assure a full penetration weld in the weldolet.
220
VIEW
ML00150 / Dec.2018
Vibration Induced Fatigue in a SS Oil Piping
M - Duplex Stainless SteelP - PipingAp - FPSOCd - Vibration Induced Fatigue
Cm - NaOH Electrolytic Etched MacroDf - Transverse Section
Transverse section of the 14" pipe in the center of the 2" branch using a weldolet fitting welded to the main pipe. The internal side of the pipe is to the top of the figure and the through wall fatigue cracking is located at the margem of the weld. It is possible to see that it is a full penetration weld and the fitting thickness is several times larger than the pipe thickness.
174
VIEW
ML00150 / Dec.2018
Vibration Induced Fatigue in a SS Oil Piping
M - Duplex Stainless SteelP - PipingAp - FPSOCd - Vibration Induced Fatigue
Cm - Electrolytically Etched MacroDf - Crack
Detail of the fatigue cracking, staring from the margin of the weld. The crack propagated though wall of the pipe (5 mm). The larger thickness of the weldolet requires a large amount of deposited weld metal, about 20 mm that is 4 times the pipe thickness. It is an interesting aspect to be considered by designers.
176
VIEW
ML00150 / Dec.2018
Vibration Induced Fatigue in a SS Oil Piping
M - Duplex Stainless SteelP - PipingAp - FPSOCd - Vibration Induced Fatigue
Cm - Electrolytically Etched MacroDf - Fatigue Crack
After cutting the pipe and opening the crack, the fracture appearance shows a clean fracture, flat, starting from the margem of the weld of the pipe (right side of the figure), and propagating through wall into the pipe (aproximately 5 mm thickness). The external side of the pipe is to the right side of the figure (presenting the weld finishing) and the internal side of the pipe is to the left side of the figure.
176
VIEW
ML00150 / Dec.2018
Vibration Induced Fatigue in a SS Oil Piping
M - Duplex Stainless SteelP - PipingAp - FPSOCd - Vibration Induced Fatigue
Cm - Fracture Surface AspectDf - Fracture
The same fracture appearance of the previous figure, looking at a higher magnification by scanning electron microscopy. The fracture is clean, flat, starting in the right side of the figure, at the margem of the weld and propagating into the pipe thickness. The external side of the pipe is to the right side of the figure and the internal side of the pipe is to the left side of the figure.
154
VIEW
ML00150 / Dec.2018
Vibration Induced Fatigue in a SS Oil Piping
M - Duplex Stainless SteelP - PipingAp - FPSOCd - Vibration Induced Fatigue
Cm - Fractography by SEMDf - Fracture

+29 more from this case →