Refinery

5 cases · 63 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Results

SortNewestOldestTitle A-ZTitle Z-A
Macrography of the longitudinally seam weld of the 24" diameter tube, showing that it was welded from both sides and there is a segregation line in the center of the tube thickness.
737
VIEW
ML00177 / Dec.2021
Cr-Mo Seam Welded Tube
M - CrMo SteelP - Longitudinally Seam WeldedAp - Fired HeaterCd - Not according to spec
Cm - NItal Etched MacroDf - Seam
Micrography of a transverse section of the pipe, external diameter 33.4 mm schedule XXS, in the center of the 9.1 mm thickness. The structure is predominantly ferritic. Small amount of pearlite.
553
VIEW
ML00112 / Dec.2017
1" XXS Pipe Not Qualified For Low Temp
M - Low Carbon SteelP - Seamless PipeAp - RefineryCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Predominantly Ferritic
Micrography of a transverse section of the pipe, external diameter 26.7 mm, in the center of the 7.85mm thickness. Refined structure but not uniform. Ferrite and pearlite.
512
VIEW
ML00111 / Dec.2017
3/4" XXS Pipe Not Qualified for Low Temp
M - Low Carbon SteelP - Seamless PipeAp - RefineryCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
The micrography of the transverse section of the plate, as polished, close to the surface. The material presents intergranular corrosion and some grains were lost.
1184
VIEW
ML00015 / Oct.2017
Intergranular Corrosion of 304SS Plate
M - Austenitic Stainless SteelP - Rolled PlateAp - RefineryCd - Intergranular Corrosion
Cm - Micrography by OMDf - Intergranular Corrosion
The main pipe, ND 18", has suffered a pipe through wall cracking at the margin of the 1 1/2" branch socket weld.
664
VIEW
ML00006 / Apr.2017
Vibration Induced Fatigue in 304SS
M - Austenitic Stainless SteelP - Longitudinal Seam Welded PipeAp - PipingCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - Crack

More from these cases

ML00177 — Cr-Mo Seam Welded TubeM - CrMo SteelP - Longitudinally Seam WeldedAp - Fired HeaterCd - Not according to spec
Identification of the regions of metallographies of the base metal, heat affected zone (HAZ) and weld metal. Locations in the root, in the center of the thickness and close to the tube OD (external surface).
118
VIEW
ML00177 / Dec.2021
Cr-Mo Seam Welded Tube
M - CrMo SteelP - Longitudinally Seam WeldedAp - Fired HeaterCd - Not according to spec
Cm - NItal Etched MacroDf - Welded Joint
BASE METAL SURFACE - Ferritic structure, grain refined.
90
VIEW
ML00177 / Dec.2021
Cr-Mo Seam Welded Tube
M - CrMo SteelP - Longitudinally Seam WeldedAp - Fired HeaterCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Base Metal
BASE METAL SURFACE - The micrography (transverse to the tube) presents the ferritic/pearlitic/bainitic structure.
75
VIEW
ML00177 / Dec.2021
Cr-Mo Seam Welded Tube
M - CrMo SteelP - Longitudinally Seam WeldedAp - Fired HeaterCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Granular structure
BASE METAL SURFACE - The microstructure of the base metal is ferritic/pearlitic/bainitic.
74
VIEW
ML00177 / Dec.2021
Cr-Mo Seam Welded Tube
M - CrMo SteelP - Longitudinally Seam WeldedAp - Fired HeaterCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Grain refined structure
HAZ SURFACE
72
VIEW
ML00177 / Dec.2021
Cr-Mo Seam Welded Tube
M - CrMo SteelP - Longitudinally Seam WeldedAp - Fired HeaterCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Last Bead HAZ

+20 more from this case →

ML00112 — 1" XXS Pipe Not Qualified For Low TempM - Low Carbon SteelP - Seamless PipeAp - RefineryCd - Not according to spec
Micrography of a transverse section of the pipe, close to the external surface (OD). The pipe presented a predominatly ferritic structure.
43
VIEW
ML00112 / Dec.2017
1" XXS Pipe Not Qualified For Low Temp
M - Low Carbon SteelP - Seamless PipeAp - RefineryCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Close to the External Surface
Micrography of a transverse section of the pipe, close to the external surface (OD). The pipe presented a 0.2 mm decarburized layer, fully ferritic.
35
VIEW
ML00112 / Dec.2017
1" XXS Pipe Not Qualified For Low Temp
M - Low Carbon SteelP - Seamless PipeAp - RefineryCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Close to the External Surface
Micrography of a transverse section of the pipe, close to the external surface (OD). The pipe presented a predominatly ferritic structure.
31
VIEW
ML00112 / Dec.2017
1" XXS Pipe Not Qualified For Low Temp
M - Low Carbon SteelP - Seamless PipeAp - RefineryCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Predominantly Ferritic
Micrography of a transverse section of the pipe, close to the internal surface (ID). The pipe presented a predominatly ferritic structure.
29
VIEW
ML00112 / Dec.2017
1" XXS Pipe Not Qualified For Low Temp
M - Low Carbon SteelP - Seamless PipeAp - RefineryCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Close to the Internal Surface
Micrography of a transverse section of the pipe, close to the internal surface (ID). The pipe presented a predominatly ferritic structure.
22
VIEW
ML00112 / Dec.2017
1" XXS Pipe Not Qualified For Low Temp
M - Low Carbon SteelP - Seamless PipeAp - RefineryCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Close to the Internal Surface

+2 more from this case →

ML00111 — 3/4" XXS Pipe Not Qualified for Low TempM - Low Carbon SteelP - Seamless PipeAp - RefineryCd - Not according to spec
Micrography of a transverse section of the pipe, close to the internal surface (ID). Refined structure. Ferrite and pearlite.
64
VIEW
ML00111 / Dec.2017
3/4" XXS Pipe Not Qualified for Low Temp
M - Low Carbon SteelP - Seamless PipeAp - RefineryCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Close to the Internal Surface
Micrography of a transverse section of the pipe, close to the internal surface (ID). Refined structure, but not uniform. Ferrite and pearlite. The pearlite colonies appear in a network.
45
VIEW
ML00111 / Dec.2017
3/4" XXS Pipe Not Qualified for Low Temp
M - Low Carbon SteelP - Seamless PipeAp - RefineryCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Close to the Internal Surface
Micrography of a transverse section of the pipe, close to the internal surface (ID). Refined structure. Ferrite and pearlite. The structure is not uniform. There is a large variation in the ferritic grain size and the pearlite colonies appear forming a network.
39
VIEW
ML00111 / Dec.2017
3/4" XXS Pipe Not Qualified for Low Temp
M - Low Carbon SteelP - Seamless PipeAp - RefineryCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Micrography of a transverse section of the pipe, close to the external surface (OD). Refined structure. Ferrite and pearlite.
33
VIEW
ML00111 / Dec.2017
3/4" XXS Pipe Not Qualified for Low Temp
M - Low Carbon SteelP - Seamless PipeAp - RefineryCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Close to the External Surface
Micrography of a transverse section of the pipe, close to the external surface (OD). Refined structure. Ferrite and pearlite.
34
VIEW
ML00111 / Dec.2017
3/4" XXS Pipe Not Qualified for Low Temp
M - Low Carbon SteelP - Seamless PipeAp - RefineryCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Close to the External Surface

+2 more from this case →

ML00015 — Intergranular Corrosion of 304SS PlateM - Austenitic Stainless SteelP - Rolled PlateAp - RefineryCd - Intergranular Corrosion
Microstructure of the plate in the center of the ¼” thickness. Equiaxed austenitic grains with delta ferrite stringers and grain boundary carbide precipitation (sensitization).
303
VIEW
ML00015 / Oct.2017
Intergranular Corrosion of 304SS Plate
M - Austenitic Stainless SteelP - Rolled PlateAp - RefineryCd - Intergranular Corrosion
Cm - Micrography by OM using A262 Method ADf - Intergranular Precipitation
Microstructure of the plate in the center of the ¼” thickness. Equiaxed austenitic grains with delta ferrite stringers and grain boundary carbide precipitation (sensitization).
201
VIEW
ML00015 / Oct.2017
Intergranular Corrosion of 304SS Plate
M - Austenitic Stainless SteelP - Rolled PlateAp - RefineryCd - Intergranular Corrosion
Cm - Micrography by OM using A262 Method ADf - Intergranular Precipitation
Micrographic aspect of a longitudinal section of the plate, close to the surface, in a region where it was detected intergranular corrosion up to 0,5 mm depth. As polished.
188
VIEW
ML00015 / Oct.2017
Intergranular Corrosion of 304SS Plate
M - Austenitic Stainless SteelP - Rolled PlateAp - RefineryCd - Intergranular Corrosion
Cm - Micrography by OMDf - Intergranular Corrosion
Micrographic detail of intergranular corrosion, up to 0,5 mm depth. As polished.
171
VIEW
ML00015 / Oct.2017
Intergranular Corrosion of 304SS Plate
M - Austenitic Stainless SteelP - Rolled PlateAp - RefineryCd - Intergranular Corrosion
Cm - Micrography by OMDf - Intergranular Corrosion
Micrographic aspect of a longitudinal section of the plate, close to the surface, in a region with intergranular corrosion. Several loose grains were removed, indicating that the structure was embrittled by the intergranular corrosion.
171
VIEW
ML00015 / Oct.2017
Intergranular Corrosion of 304SS Plate
M - Austenitic Stainless SteelP - Rolled PlateAp - RefineryCd - Intergranular Corrosion
Cm - Micrography by OM using A262 Method ADf - Intergranular Corrosion

+5 more from this case →

ML00006 — Vibration Induced Fatigue in 304SSM - Austenitic Stainless SteelP - Longitudinal Seam Welded PipeAp - PipingCd - Vibration Induced Fatigue
The macro section transverse to the welded region, show that the through wall cracking occurred in the pipe base metal, from the margin of the weld.
191
VIEW
ML00006 / Apr.2017
Vibration Induced Fatigue in 304SS
M - Austenitic Stainless SteelP - Longitudinal Seam Welded PipeAp - PipingCd - Vibration Induced Fatigue
Cm - Macro Oxalic Acid Electrolytic EtchedDf - Through Wall Cracking
Macro transverse to the weld showing that the fracture occurred in the main pipe, at the margin of the weld.
163
VIEW
ML00006 / Apr.2017
Vibration Induced Fatigue in 304SS
M - Austenitic Stainless SteelP - Longitudinal Seam Welded PipeAp - PipingCd - Vibration Induced Fatigue
Cm - Macro Oxalic Acid Electrolytic EtchedDf - Fracture
The fracture surface of the main pipe is presented in low magnification (external pipe surface in the top) showing a flat propagation starting from the contour of the weld margin.
173
VIEW
ML00006 / Apr.2017
Vibration Induced Fatigue in 304SS
M - Austenitic Stainless SteelP - Longitudinal Seam Welded PipeAp - PipingCd - Vibration Induced Fatigue
Cm - Fractography by SEMDf - Margin of the Weld Crack
Fracture surface micromechanism by striation, evidence of FATIGUE.
158
VIEW
ML00006 / Apr.2017
Vibration Induced Fatigue in 304SS
M - Austenitic Stainless SteelP - Longitudinal Seam Welded PipeAp - PipingCd - Vibration Induced Fatigue
Cm - Fractography by SEMDf - Fatigue Striation
Fracture surface micromechanism by striation, evidence of FATIGUE.
147
VIEW
ML00006 / Apr.2017
Vibration Induced Fatigue in 304SS
M - Austenitic Stainless SteelP - Longitudinal Seam Welded PipeAp - PipingCd - Vibration Induced Fatigue
Cm - Fractography by SEMDf - Fatigue Striation

+4 more from this case →