Crevice Corrosion in a Subsea System — Aspect Before Analysis

Detail focus: Crack clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Detail of the fusion line region of the repair weld. Cracks filled with oxides indicating that the material was already corroded when the bead was deposited.
105
VIEW
ML00015 / Oct.2017
Intergranular Corrosion of 304SS Plate
M - Austenitic Stainless SteelP - Rolled PlateAp - RefineryCd - Intergranular Corrosion
Cm - Micrography by OM using A262 Method ADf - Crack
The main pipe, ND 18", has suffered a pipe through wall cracking at the margin of the 1 1/2" branch socket weld.
664
VIEW
ML00006 / Apr.2017
Vibration Induced Fatigue in 304SS
M - Austenitic Stainless SteelP - Longitudinal Seam Welded PipeAp - PipingCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - Crack