Micrography of a transverse section of the pipe, external diameter 33.4 mm schedule XXS, in the center of the 9.1 mm thickness. The structure is predominantly ferritic. Small amount of pearlite.
553
VIEW
ML00112 / Dec.2017
1" XXS Pipe Not Qualified For Low Temp
M - Low Carbon SteelP - Seamless PipeAp - RefineryCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Predominantly Ferritic
Micrography of a transverse section of the pipe, external diameter 26.7 mm, in the center of the 7.85mm thickness. Refined structure but not uniform. Ferrite and pearlite.
512
VIEW
ML00111 / Dec.2017
3/4" XXS Pipe Not Qualified for Low Temp
M - Low Carbon SteelP - Seamless PipeAp - RefineryCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
The main pipe, ND 18", has suffered a pipe through wall cracking at the margin of the 1 1/2" branch socket weld.
664
VIEW
ML00006 / Apr.2017
Vibration Induced Fatigue in 304SS
M - Austenitic Stainless SteelP - Longitudinal Seam Welded PipeAp - PipingCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - Crack

More from these cases

ML00112 — 1" XXS Pipe Not Qualified For Low TempM - Low Carbon SteelP - Seamless PipeAp - RefineryCd - Not according to spec
Micrography of a transverse section of the pipe, close to the external surface (OD). The pipe presented a predominatly ferritic structure.
43
VIEW
ML00112 / Dec.2017
1" XXS Pipe Not Qualified For Low Temp
M - Low Carbon SteelP - Seamless PipeAp - RefineryCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Close to the External Surface
Micrography of a transverse section of the pipe, close to the external surface (OD). The pipe presented a 0.2 mm decarburized layer, fully ferritic.
35
VIEW
ML00112 / Dec.2017
1" XXS Pipe Not Qualified For Low Temp
M - Low Carbon SteelP - Seamless PipeAp - RefineryCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Close to the External Surface
Micrography of a transverse section of the pipe, close to the external surface (OD). The pipe presented a predominatly ferritic structure.
31
VIEW
ML00112 / Dec.2017
1" XXS Pipe Not Qualified For Low Temp
M - Low Carbon SteelP - Seamless PipeAp - RefineryCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Predominantly Ferritic
Micrography of a transverse section of the pipe, close to the internal surface (ID). The pipe presented a predominatly ferritic structure.
29
VIEW
ML00112 / Dec.2017
1" XXS Pipe Not Qualified For Low Temp
M - Low Carbon SteelP - Seamless PipeAp - RefineryCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Close to the Internal Surface
Micrography of a transverse section of the pipe, close to the internal surface (ID). The pipe presented a predominatly ferritic structure.
22
VIEW
ML00112 / Dec.2017
1" XXS Pipe Not Qualified For Low Temp
M - Low Carbon SteelP - Seamless PipeAp - RefineryCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Close to the Internal Surface

+2 more from this case →

ML00111 — 3/4" XXS Pipe Not Qualified for Low TempM - Low Carbon SteelP - Seamless PipeAp - RefineryCd - Not according to spec
Micrography of a transverse section of the pipe, close to the internal surface (ID). Refined structure. Ferrite and pearlite.
64
VIEW
ML00111 / Dec.2017
3/4" XXS Pipe Not Qualified for Low Temp
M - Low Carbon SteelP - Seamless PipeAp - RefineryCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Close to the Internal Surface
Micrography of a transverse section of the pipe, close to the internal surface (ID). Refined structure, but not uniform. Ferrite and pearlite. The pearlite colonies appear in a network.
45
VIEW
ML00111 / Dec.2017
3/4" XXS Pipe Not Qualified for Low Temp
M - Low Carbon SteelP - Seamless PipeAp - RefineryCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Close to the Internal Surface
Micrography of a transverse section of the pipe, close to the internal surface (ID). Refined structure. Ferrite and pearlite. The structure is not uniform. There is a large variation in the ferritic grain size and the pearlite colonies appear forming a network.
39
VIEW
ML00111 / Dec.2017
3/4" XXS Pipe Not Qualified for Low Temp
M - Low Carbon SteelP - Seamless PipeAp - RefineryCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Micrography of a transverse section of the pipe, close to the external surface (OD). Refined structure. Ferrite and pearlite.
33
VIEW
ML00111 / Dec.2017
3/4" XXS Pipe Not Qualified for Low Temp
M - Low Carbon SteelP - Seamless PipeAp - RefineryCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Close to the External Surface
Micrography of a transverse section of the pipe, close to the external surface (OD). Refined structure. Ferrite and pearlite.
34
VIEW
ML00111 / Dec.2017
3/4" XXS Pipe Not Qualified for Low Temp
M - Low Carbon SteelP - Seamless PipeAp - RefineryCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Close to the External Surface

+2 more from this case →

ML00006 — Vibration Induced Fatigue in 304SSM - Austenitic Stainless SteelP - Longitudinal Seam Welded PipeAp - PipingCd - Vibration Induced Fatigue
The macro section transverse to the welded region, show that the through wall cracking occurred in the pipe base metal, from the margin of the weld.
191
VIEW
ML00006 / Apr.2017
Vibration Induced Fatigue in 304SS
M - Austenitic Stainless SteelP - Longitudinal Seam Welded PipeAp - PipingCd - Vibration Induced Fatigue
Cm - Macro Oxalic Acid Electrolytic EtchedDf - Through Wall Cracking
Macro transverse to the weld showing that the fracture occurred in the main pipe, at the margin of the weld.
163
VIEW
ML00006 / Apr.2017
Vibration Induced Fatigue in 304SS
M - Austenitic Stainless SteelP - Longitudinal Seam Welded PipeAp - PipingCd - Vibration Induced Fatigue
Cm - Macro Oxalic Acid Electrolytic EtchedDf - Fracture
The fracture surface of the main pipe is presented in low magnification (external pipe surface in the top) showing a flat propagation starting from the contour of the weld margin.
173
VIEW
ML00006 / Apr.2017
Vibration Induced Fatigue in 304SS
M - Austenitic Stainless SteelP - Longitudinal Seam Welded PipeAp - PipingCd - Vibration Induced Fatigue
Cm - Fractography by SEMDf - Margin of the Weld Crack
Fracture surface micromechanism by striation, evidence of FATIGUE.
158
VIEW
ML00006 / Apr.2017
Vibration Induced Fatigue in 304SS
M - Austenitic Stainless SteelP - Longitudinal Seam Welded PipeAp - PipingCd - Vibration Induced Fatigue
Cm - Fractography by SEMDf - Fatigue Striation
Fracture surface micromechanism by striation, evidence of FATIGUE.
147
VIEW
ML00006 / Apr.2017
Vibration Induced Fatigue in 304SS
M - Austenitic Stainless SteelP - Longitudinal Seam Welded PipeAp - PipingCd - Vibration Induced Fatigue
Cm - Fractography by SEMDf - Fatigue Striation

+4 more from this case →