Vibration Induced Fatigue

5 cases · 96 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Results

SortNewestOldestTitle A-ZTitle Z-A
Vertical piping in a corrosive oil producing system of a FPSO. The line is a nominal diameter 14" sch 10S (pipe thickness about 5 mm) and the flanged branch line is a 2" nominal diameter welded to the main pipe using a weldolet (forged fitting). The fatigue induced cracking occurred longitudinal to the main pipe, originated at the margem of the weld interface with the pipe.
1480
VIEW
ML00150 / Dec.2018
Vibration Induced Fatigue in a SS Oil Piping
M - Duplex Stainless SteelP - PipingAp - FPSOCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - General View
Gas piping. Aspect of a branching line 2" ND, lateral to a horizontal main pipe ND 8", welded using a weldolet. The cracking started at the margin of the weld in the upper part of the pipe, where the weld crossed the longitudinal direction of the pipe, perpendicular to the branch.
932
VIEW
ML00149 / Dec.2018
Vibration Induced Fatigue in a Gas Piping
M - Low Carbon SteelP - Piping spoolAp - FPSOCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - Cracking
General view of the 2" branch line that was supporting an instrument in a 12" gas piping of an offshore unity. The branch line is composed by a seamless pipe welded to a weldolet (left side of the figure) and to a flange (right side of the figure). The leakage is associated to a through wall cracking in the middle of the pipe length. The cracking is not evidenced in the figure, since it is too thin. See the schematic drawing in the next figure
494
VIEW
ML00012 / Aug.2017
Vibration Induced Fatigue in a 316/316L SS
M - Austenitic Stainless SteelP - Seamless PipeAp - OffshoreCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - General View
Macroscopic aspect of the 1" shaft fracture surface, revealing beach marks at the surface typical of fatigue, initiated from the surface of the spline shaft at the gear position.
498
VIEW
ML00041 / Jun.2017
Fatigue Fracture of Inconel 718 Spline Shaft
M - NiCrFe AlloyP - ShaftAp - Oil and GasCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - Fatigue Fracture
The main pipe, ND 18", has suffered a pipe through wall cracking at the margin of the 1 1/2" branch socket weld.
664
VIEW
ML00006 / Apr.2017
Vibration Induced Fatigue in 304SS
M - Austenitic Stainless SteelP - Longitudinal Seam Welded PipeAp - PipingCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - Crack

More from these cases

ML00150 — Vibration Induced Fatigue in a SS Oil PipingM - Duplex Stainless SteelP - PipingAp - FPSOCd - Vibration Induced Fatigue
Macrography of the section transverse to the ND 14" main pipe (that is only 5mm thick) and to the ND 2" branch that is a weldolet fitting welded to the main pipe and flange. This image is interesting because it shows clearly how thin is the pipe compared with the fitting thickness and the large amount of welding required to assure a full penetration weld in the weldolet.
220
VIEW
ML00150 / Dec.2018
Vibration Induced Fatigue in a SS Oil Piping
M - Duplex Stainless SteelP - PipingAp - FPSOCd - Vibration Induced Fatigue
Cm - NaOH Electrolytic Etched MacroDf - Transverse Section
Transverse section of the 14" pipe in the center of the 2" branch using a weldolet fitting welded to the main pipe. The internal side of the pipe is to the top of the figure and the through wall fatigue cracking is located at the margem of the weld. It is possible to see that it is a full penetration weld and the fitting thickness is several times larger than the pipe thickness.
174
VIEW
ML00150 / Dec.2018
Vibration Induced Fatigue in a SS Oil Piping
M - Duplex Stainless SteelP - PipingAp - FPSOCd - Vibration Induced Fatigue
Cm - Electrolytically Etched MacroDf - Crack
Detail of the fatigue cracking, staring from the margin of the weld. The crack propagated though wall of the pipe (5 mm). The larger thickness of the weldolet requires a large amount of deposited weld metal, about 20 mm that is 4 times the pipe thickness. It is an interesting aspect to be considered by designers.
176
VIEW
ML00150 / Dec.2018
Vibration Induced Fatigue in a SS Oil Piping
M - Duplex Stainless SteelP - PipingAp - FPSOCd - Vibration Induced Fatigue
Cm - Electrolytically Etched MacroDf - Fatigue Crack
After cutting the pipe and opening the crack, the fracture appearance shows a clean fracture, flat, starting from the margem of the weld of the pipe (right side of the figure), and propagating through wall into the pipe (aproximately 5 mm thickness). The external side of the pipe is to the right side of the figure (presenting the weld finishing) and the internal side of the pipe is to the left side of the figure.
176
VIEW
ML00150 / Dec.2018
Vibration Induced Fatigue in a SS Oil Piping
M - Duplex Stainless SteelP - PipingAp - FPSOCd - Vibration Induced Fatigue
Cm - Fracture Surface AspectDf - Fracture
The same fracture appearance of the previous figure, looking at a higher magnification by scanning electron microscopy. The fracture is clean, flat, starting in the right side of the figure, at the margem of the weld and propagating into the pipe thickness. The external side of the pipe is to the right side of the figure and the internal side of the pipe is to the left side of the figure.
154
VIEW
ML00150 / Dec.2018
Vibration Induced Fatigue in a SS Oil Piping
M - Duplex Stainless SteelP - PipingAp - FPSOCd - Vibration Induced Fatigue
Cm - Fractography by SEMDf - Fracture

+29 more from this case →

ML00149 — Vibration Induced Fatigue in a Gas PipingM - Low Carbon SteelP - Piping spoolAp - FPSOCd - Vibration Induced Fatigue
Gas piping. Aspect of a branching line 2" ND with a flange, lateral to a main pipe ND 8", welded using a weldolet. The cracking is at the margin of the weld.
115
VIEW
ML00149 / Dec.2018
Vibration Induced Fatigue in a Gas Piping
M - Low Carbon SteelP - Piping spoolAp - FPSOCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - General View
Micrography of a transverse section of the seamless pipe, presenting a ferritic-pearlitic structure.
84
VIEW
ML00149 / Dec.2018
Vibration Induced Fatigue in a Gas Piping
M - Low Carbon SteelP - Piping spoolAp - FPSOCd - Vibration Induced Fatigue
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Micrography of a transverse section of the seamless pipe, presenting a ferritic-pearlitic structure.
70
VIEW
ML00149 / Dec.2018
Vibration Induced Fatigue in a Gas Piping
M - Low Carbon SteelP - Piping spoolAp - FPSOCd - Vibration Induced Fatigue
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Gas piping. Aspect of a branching line 2" ND, lateral to a horizontal main pipe ND 8", welded using a weldolet. In the lower part of the branch there are no cracks.
61
VIEW
ML00149 / Dec.2018
Vibration Induced Fatigue in a Gas Piping
M - Low Carbon SteelP - Piping spoolAp - FPSOCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - Welded Joint
Aspect of the brach line viewed from the internal side of the main pipe, after cuting. It is possible to see that the pipe was perforated by a thermal cutting (looking the finishing aspect of the edge of the hole). The weldolet was welded only from the external side of the pipe.
62
VIEW
ML00149 / Dec.2018
Vibration Induced Fatigue in a Gas Piping
M - Low Carbon SteelP - Piping spoolAp - FPSOCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - Internal Surface

+13 more from this case →

ML00012 — Vibration Induced Fatigue in a 316/316L SSM - Austenitic Stainless SteelP - Seamless PipeAp - OffshoreCd - Vibration Induced Fatigue
Schematic drawing presenting the general view of the 2" branch line that was supporting an instrument in a 12" gas piping of an offshore unity.
94
VIEW
ML00012 / Aug.2017
Vibration Induced Fatigue in a 316/316L SS
M - Austenitic Stainless SteelP - Seamless PipeAp - OffshoreCd - Vibration Induced Fatigue
Cm - Identification drawingDf - General View
Aspect of the internal surface of the pipe after longitudinal cutting, presenting a straight cracking, circumferential. The weldolet is to the left side and the flange is to the right side. See the schematic drawing in the next figure.
89
VIEW
ML00012 / Aug.2017
Vibration Induced Fatigue in a 316/316L SS
M - Austenitic Stainless SteelP - Seamless PipeAp - OffshoreCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - Internal Surface
Schematic drawing presenting the cracking surface aspect.
71
VIEW
ML00012 / Aug.2017
Vibration Induced Fatigue in a 316/316L SS
M - Austenitic Stainless SteelP - Seamless PipeAp - OffshoreCd - Vibration Induced Fatigue
Cm - Identification drawingDf - Internal Surface
Aspect of the internal surface of the 2" nominal diameter pipe, SCH 40, presenting a circumferential through wall cracking in the pipe, not associated to any of the welded joints. It is possible to see the cracking parallel to the two welded joints: the pipe to weldolet (left side of the figure); and the pipe to flange (right side of the figure).
64
VIEW
ML00012 / Aug.2017
Vibration Induced Fatigue in a 316/316L SS
M - Austenitic Stainless SteelP - Seamless PipeAp - OffshoreCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - Through Wall Cracking
Aspect of the internal surface of the 2" nominal diameter pipe, SCH 40, presenting a circumferential through wall cracking in the pipe, not associated to any of the welded joints. It is possible to see the cracking parallel to the two welded joints: the pipe to weldolet (left side of the figure); and the pipe to flange (right side of the figure).
57
VIEW
ML00012 / Aug.2017
Vibration Induced Fatigue in a 316/316L SS
M - Austenitic Stainless SteelP - Seamless PipeAp - OffshoreCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - Through Wall Cracking

+13 more from this case →

ML00041 — Fatigue Fracture of Inconel 718 Spline ShaftM - NiCrFe AlloyP - ShaftAp - Oil and GasCd - Vibration Induced Fatigue
xx
117
VIEW
ML00041 / Jun.2017
Fatigue Fracture of Inconel 718 Spline Shaft
M - NiCrFe AlloyP - ShaftAp - Oil and GasCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - At the Surface
Macroscopic aspect of the 1" shaft fracture surface, revealing beach marks at the surface typical of fatigue, initiated from the surface of the spline shaft at the gear position.
120
VIEW
ML00041 / Jun.2017
Fatigue Fracture of Inconel 718 Spline Shaft
M - NiCrFe AlloyP - ShaftAp - Oil and GasCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - Fatigue Fracture
SEM fractograph at 1200x magnification showing an intergranular fracture surface with angular, faceted grains and fine feather-like markings.
86
VIEW
ML00041 / Jun.2017
Fatigue Fracture of Inconel 718 Spline Shaft
M - NiCrFe AlloyP - ShaftAp - Oil and GasCd - Vibration Induced Fatigue
Cm - Fractography by SEMDf - Fatigue Fracture
Microscopic detail of the transgranular striation in the fracture surface.
77
VIEW
ML00041 / Jun.2017
Fatigue Fracture of Inconel 718 Spline Shaft
M - NiCrFe AlloyP - ShaftAp - Oil and GasCd - Vibration Induced Fatigue
Cm - Fractography by SEMDf - Fatigue Fracture
The micrography of a transverse section of the shaft shows the granular austenitic structure close to the surface of the shaft.
67
VIEW
ML00041 / Jun.2017
Fatigue Fracture of Inconel 718 Spline Shaft
M - NiCrFe AlloyP - ShaftAp - Oil and GasCd - Vibration Induced Fatigue
Cm - Kalling Etched Micrography by OMDf - At the Surface

+7 more from this case →

ML00006 — Vibration Induced Fatigue in 304SSM - Austenitic Stainless SteelP - Longitudinal Seam Welded PipeAp - PipingCd - Vibration Induced Fatigue
The macro section transverse to the welded region, show that the through wall cracking occurred in the pipe base metal, from the margin of the weld.
191
VIEW
ML00006 / Apr.2017
Vibration Induced Fatigue in 304SS
M - Austenitic Stainless SteelP - Longitudinal Seam Welded PipeAp - PipingCd - Vibration Induced Fatigue
Cm - Macro Oxalic Acid Electrolytic EtchedDf - Through Wall Cracking
Macro transverse to the weld showing that the fracture occurred in the main pipe, at the margin of the weld.
163
VIEW
ML00006 / Apr.2017
Vibration Induced Fatigue in 304SS
M - Austenitic Stainless SteelP - Longitudinal Seam Welded PipeAp - PipingCd - Vibration Induced Fatigue
Cm - Macro Oxalic Acid Electrolytic EtchedDf - Fracture
The fracture surface of the main pipe is presented in low magnification (external pipe surface in the top) showing a flat propagation starting from the contour of the weld margin.
173
VIEW
ML00006 / Apr.2017
Vibration Induced Fatigue in 304SS
M - Austenitic Stainless SteelP - Longitudinal Seam Welded PipeAp - PipingCd - Vibration Induced Fatigue
Cm - Fractography by SEMDf - Margin of the Weld Crack
Fracture surface micromechanism by striation, evidence of FATIGUE.
158
VIEW
ML00006 / Apr.2017
Vibration Induced Fatigue in 304SS
M - Austenitic Stainless SteelP - Longitudinal Seam Welded PipeAp - PipingCd - Vibration Induced Fatigue
Cm - Fractography by SEMDf - Fatigue Striation
Fracture surface micromechanism by striation, evidence of FATIGUE.
147
VIEW
ML00006 / Apr.2017
Vibration Induced Fatigue in 304SS
M - Austenitic Stainless SteelP - Longitudinal Seam Welded PipeAp - PipingCd - Vibration Induced Fatigue
Cm - Fractography by SEMDf - Fatigue Striation

+4 more from this case →