Cupronickel

1 case · 4 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Results

SortNewestOldestTitle A-ZTitle Z-A
The micrography of the tube shows a granular structure and light deformation lines. No evidences of corrosion from the external surface (upper side of the figure) or internal surface (lower side of the figure).
440
VIEW
ML00043 / Apr.2017
CuNi Condenser Tube
M - CupronickelP - Seamless tubeAp - Heat ExchangerCd - Removed From Service
Cm - FeCl3+HCl+H2O Etched MicroDf - Longitudinal Section

More from these cases

ML00043 — CuNi Condenser TubeM - CupronickelP - Seamless tubeAp - Heat ExchangerCd - Removed From Service
The material structure is monophasic.
110
VIEW
ML00043 / Apr.2017
CuNi Condenser Tube
M - CupronickelP - Seamless tubeAp - Heat ExchangerCd - Removed From Service
Cm - FeCl3+HCl+H2O Etched MicroDf - Single phase
The material structure is similar all through the thickness and there are no evidencies of corrosion at the surfaces.
89
VIEW
ML00043 / Apr.2017
CuNi Condenser Tube
M - CupronickelP - Seamless tubeAp - Heat ExchangerCd - Removed From Service
Cm - FeCl3+HCl+H2O solution Etched MacroDf - At the Surface
Detail of the structure at the surface.
79
VIEW
ML00043 / Apr.2017
CuNi Condenser Tube
M - CupronickelP - Seamless tubeAp - Heat ExchangerCd - Removed From Service
Cm - FeCl3+HCl+H2O Etched MicroDf - At the Surface