Creep

3 cases · 32 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Results

SortNewestOldestTitle A-ZTitle Z-A
Aspect of the cracking after Dye Check Test (Liquid Penetrant) in the external side of the line that operates at 800°C, insulated, and presented the leakage associated to the longitudinal seam weld of the fitting. The circumferential butt weld of the fitting to a pipe did not fail. See the schematic drawing in the next figure
371
VIEW
ML00061 / Apr.2017
Creep in a Seam Weld of a 304H SS Fitting
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Creep
Cm - Aspect by NDTDf - Through Wall Cracking
Micrography of the transverse section of the NEW TUBE, in the center of the thickness, showing the austenitic structure with primary carbides network.
410
VIEW
ML00038 / Apr.2017
Cast SS Tube for High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - Creep
Cm - Glyceregia Etched Micrography by OMDf - Austenitic with Primary Carbides
Micrography of a longitudinal section of the bolt at the fracture surface. The material showed several creep voids and interconnected cracks. The broken bolt remained in service during some time and the fracture surface presented a thick oxide layer(grey). As polished.
529
VIEW
ML00004 / Jun.2018
Creep in High Temperature Bolts
M - CrMo SteelP - FastenerAp - Gas TurbineCd - Creep
Cm - Micrography by OMDf - Oxide Layer

More from these cases

ML00061 — Creep in a Seam Weld of a 304H SS FittingM - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Creep
Schematic drawing presenting the aspect of the cracking after Dye Check Test (Liquid Penetrant) in the external side of the line that operates at 800°C, insulated, and presented the leakage associated to the longitudinal seam weld of the fitting. The circumferential butt weld of the fitting to a pipe did not fail.
62
VIEW
ML00061 / Apr.2017
Creep in a Seam Weld of a 304H SS Fitting
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Creep
Cm - Identification drawingDf - Through Wall Cracking
Aspect of the internal side of the fitting, at the longitudinal seam weld, and macrography of a transverse section showing the through wall cracks.
62
VIEW
ML00061 / Apr.2017
Creep in a Seam Weld of a 304H SS Fitting
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Creep
Cm - Macro Oxalic Acid Electrolytic EtchedDf - Transverse Section
Through wall cracking in the longitudinal seam weld of the fitting. Several cracks, longitudinal to the weld, were created by the connection of voids in the weld metal, associated to a strong microstructural evolution.
191
VIEW
ML00061 / Apr.2017
Creep in a Seam Weld of a 304H SS Fitting
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Creep
Cm - Micrography by OM using A262 Method ADf - Cracks
Micrography of a longitudinal section of the fitting, at the base metal, presenting an austenitic structure with intergranular and transgranular precipitation as a result of microstructural evolution.
44
VIEW
ML00061 / Apr.2017
Creep in a Seam Weld of a 304H SS Fitting
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Creep
Cm - Micrography by OM using A262 Method ADf - Base Metal
Micrographic detail of the fitting base metal, presenting an austenitic structure with intergranular and transgranular precipitation as a result of microstructural evolution.
40
VIEW
ML00061 / Apr.2017
Creep in a Seam Weld of a 304H SS Fitting
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Creep
Cm - Micrography by OM using A262 Method ADf - Base Metal

+10 more from this case →

ML00038 — Cast SS Tube for High Temperature ServiceM - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - Creep
Micrography of the transverse section of the NEW TUBE, close to the external surface, showing the austenitic structure with primary carbides network.
59
VIEW
ML00038 / Apr.2017
Cast SS Tube for High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - Creep
Cm - Glyceregia Etched Micrography by OMDf - Close to the External Surface
Macrography of the NEW TUBE, centrifugally cast, in the transverse section, presenting columnar grains close to the external surface.
50
VIEW
ML00038 / Apr.2017
Cast SS Tube for High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - Creep
Cm - Kalling Etched MacroDf - Transverse Section
The micrography in the as polished condition of the NEW TUBE shows that there are no casting defects close to the external surface.
49
VIEW
ML00038 / Apr.2017
Cast SS Tube for High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - Creep
Cm - Micrography by OMDf - Close to the External Surface
The micrography in the as polished condition of the NEW TUBE shows that there are no casting defects in the center of the thickness.
47
VIEW
ML00038 / Apr.2017
Cast SS Tube for High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - Creep
Cm - Micrography by OMDf - Transverse Section
Micrography of the transverse section of the TUBE REMOVED FROM SERVICE, in the center of the thickness, showing the austenitic structure with primary carbides network and secondary precipitation.
59
VIEW
ML00038 / Apr.2017
Cast SS Tube for High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - Creep
Cm - Glyceregia Etched Micrography by OMDf - Intragranular Secondary Precipitation

+4 more from this case →

ML00004 — Creep in High Temperature BoltsM - CrMo SteelP - FastenerAp - Gas TurbineCd - Creep
Micrographic detail of the creep voids and interconnected cracks. The broken bolt remained in service during some time and the fracture surface presented a thick oxide layer(grey). As polished.
121
VIEW
ML00004 / Jun.2018
Creep in High Temperature Bolts
M - CrMo SteelP - FastenerAp - Gas TurbineCd - Creep
Cm - Micrography by OMDf - Interconnected Cracks
Micrographic detail of the creep voids and interconnected cracks. The broken bolt remained in service during some time and the fracture surface presented a thick oxide layer(grey). As polished.
101
VIEW
ML00004 / Jun.2018
Creep in High Temperature Bolts
M - CrMo SteelP - FastenerAp - Gas TurbineCd - Creep
Cm - Micrography by OMDf - Voids
Micrography of a longitudinal section of a CrMov steel bolt that broke in service by a creep mechanism in a gas turbine. Tempered structure. Interconnected cracks paralled to the fracture surface.
95
VIEW
ML00004 / Jun.2018
Creep in High Temperature Bolts
M - CrMo SteelP - FastenerAp - Gas TurbineCd - Creep
Cm - Nital Etched Micrography by OMDf - Crack
Micrographic detail of a longitudinal section of the bolt far from the fracture, presenting a tempered structure.
82
VIEW
ML00004 / Jun.2018
Creep in High Temperature Bolts
M - CrMo SteelP - FastenerAp - Gas TurbineCd - Creep
Cm - Nital Etched Micrography by OMDf - Tempered Structure
Micrographic detail of a longitudinal section of the bolt close to the fracture, presenting an overtempered structure.
76
VIEW
ML00004 / Jun.2018
Creep in High Temperature Bolts
M - CrMo SteelP - FastenerAp - Gas TurbineCd - Creep
Cm - Nital Etched Micrography by OMDf - Overtempered Structure