Crevice Corrosion in a Subsea System — Aspect Before Analysis

Results

SortNewestOldestTitle A-ZTitle Z-A
The titanium rotor blade of a flowmeter broke after two years in service in an acid environment, containing H2S.
339
VIEW
ML00176 / Nov.2021
Hydride Formation in a Titanium Blade
M - Unalloyed TitaniumP - BladeAp - Oil and GasCd - Hydride Formation
Cm - Aspect Before AnalysisDf - General View
Image of the surface of the blade, after preparation and Kalling etch, revealing the welded joint between the original casting and the insert casting adopted in the remanufacture. See the schematic drawing in the next figure
341
VIEW
ML00055 / Apr.2017
CA6NM Blade Remanufactured by Welding
M - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Cm - Surface AspectDf - Welded Joint
Transverse section of the blade showing large grains of this poliycristaline cast material.
421
VIEW
ML00042 / Apr.2017
Gas Turbine Blade IN 939, Coated
M - NiCrCo AlloyP - CastAp - Gas TurbineCd - Intergranular Cracking
Cm - H2SO4+HNO3+H3PO4 Etched MicroDf - Coarse Structure

More from these cases

ML00176 — Hydride Formation in a Titanium BladeM - Unalloyed TitaniumP - BladeAp - Oil and GasCd - Hydride Formation
The rotor blade failed without deformation. At the rotor surface it is possible to see different colours of deposits.
53
VIEW
ML00176 / Nov.2021
Hydride Formation in a Titanium Blade
M - Unalloyed TitaniumP - BladeAp - Oil and GasCd - Hydride Formation
Cm - Aspect Before AnalysisDf - Fracture
Detail of the fracture surface, dark in the root of the blade, presenting a brittle aspect and indication that it started from this position.
39
VIEW
ML00176 / Nov.2021
Hydride Formation in a Titanium Blade
M - Unalloyed TitaniumP - BladeAp - Oil and GasCd - Hydride Formation
Cm - Aspect Before AnalysisDf - Fracture
Macroscopic aspect of the fracture surface.
37
VIEW
ML00176 / Nov.2021
Hydride Formation in a Titanium Blade
M - Unalloyed TitaniumP - BladeAp - Oil and GasCd - Hydride Formation
Cm - Fracture Surface AspectDf - Fracture
Low magnification image by scanning electron microscopy. In the bottom of the image the fracture appearance is brittle and presenting several secondary cracks. In the top of the image the fracture is fully flat, also without macroscopic plastic deformation.
33
VIEW
ML00176 / Nov.2021
Hydride Formation in a Titanium Blade
M - Unalloyed TitaniumP - BladeAp - Oil and GasCd - Hydride Formation
Cm - Fractography by SEMDf - Fracture
The position of the fracture at the starting point of the failure is brittle, transgranular, with a cleavage/quase-cleavage morphology.
24
VIEW
ML00176 / Nov.2021
Hydride Formation in a Titanium Blade
M - Unalloyed TitaniumP - BladeAp - Oil and GasCd - Hydride Formation
Cm - Fractography by SEMDf - Cleavage Facets

+10 more from this case →

ML00055 — CA6NM Blade Remanufactured by WeldingM - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Schematic drawing presenting the surface of the blade
40
VIEW
ML00055 / Apr.2017
CA6NM Blade Remanufactured by Welding
M - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Cm - Identification drawingDf - Welded Joint
Original casting base metal presenting a coarse martensitic structure with a small amount of delta ferrite.
50
VIEW
ML00055 / Apr.2017
CA6NM Blade Remanufactured by Welding
M - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Cm - Kalling Etched Micrography by OMDf - Base Metal Left Side
Micrographic detail of the original casting blade structure. The tempered martensite is more clearly revealed by the scanning electron microscopy. The average hardness level measured in this side is 270 HV.
70
VIEW
ML00055 / Apr.2017
CA6NM Blade Remanufactured by Welding
M - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Cm - Kalling Etched Micrography by SEMDf - Base Metal Left Side
Higher magnification of the martensitic structure of the original casting blade structure, hardness level of 270HV10.
26
VIEW
ML00055 / Apr.2017
CA6NM Blade Remanufactured by Welding
M - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Cm - Kalling Etched Micrography by SEMDf - Base Metal Left Side
Inserted casting base metal presenting a coarse martensitic structure with a small amount of delta ferrite.
24
VIEW
ML00055 / Apr.2017
CA6NM Blade Remanufactured by Welding
M - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Cm - Kalling Etched Micrography by OMDf - Base Metal Right Side

+19 more from this case →

ML00042 — Gas Turbine Blade IN 939, CoatedM - NiCrCo AlloyP - CastAp - Gas TurbineCd - Intergranular Cracking
Micrography of the blade, view inside the grain. The intragranular precipitation presents one unique size of precipitation, not yet coalesced, although the blade was in high temperature service for 50.000 hours. Etched by H2SO4 + HNO3 + H3PO4 reagent.
66
VIEW
ML00042 / Apr.2017
Gas Turbine Blade IN 939, Coated
M - NiCrCo AlloyP - CastAp - Gas TurbineCd - Intergranular Cracking
Cm - Micrography by SEMDf - Intragranular Secondary Precipitation
Micrography close to the surface of the blade, showing the diffusion coating (aluminum base alloy) that is still sound. No strong oxidation or erosion was detected.
53
VIEW
ML00042 / Apr.2017
Gas Turbine Blade IN 939, Coated
M - NiCrCo AlloyP - CastAp - Gas TurbineCd - Intergranular Cracking
Cm - H2SO4+HNO3+H3PO4 Etched MicroDf - Coating
Micrographic detail of the diffusion coating. H2SO4 + HNO3 + H3PO4 etched.
47
VIEW
ML00042 / Apr.2017
Gas Turbine Blade IN 939, Coated
M - NiCrCo AlloyP - CastAp - Gas TurbineCd - Intergranular Cracking
Cm - Micrography by SEMDf - Coating
Micrography as polished of the region where there was a refrigeration hole, presenting a cracking.
35
VIEW
ML00042 / Apr.2017
Gas Turbine Blade IN 939, Coated
M - NiCrCo AlloyP - CastAp - Gas TurbineCd - Intergranular Cracking
Cm - Micrography by OMDf - Cracking
The cracking from the refrigeration hole presents an intergranular morphology, as shown in the micrography of a transverse section of the blade.
35
VIEW
ML00042 / Apr.2017
Gas Turbine Blade IN 939, Coated
M - NiCrCo AlloyP - CastAp - Gas TurbineCd - Intergranular Cracking
Cm - H2SO4+HNO3+H3PO4 Etched MicroDf - Intergranular Cracking