NH4OH+H2O+H2O2 Etched Micro

2 cases · 8 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Results

SortNewestOldestTitle A-ZTitle Z-A
Low magnification metallography of the coaster after etching, revealing a casting structure of alpha plus beta phases. Beta is the dark brown matrix phase and alpha is the dendritic yellow phase.
45
VIEW
ML00156 / Jan.2020
Antique Silver Plated Decorative Piece
M - BrassP - Decorative PieceAp - OrnamentalCd - Non Destructive Examination
Cm - NH4OH+H2O+H2O2 Etched MicroDf - Alpha and Beta
The micrography of the transverse section shows coarse grains and biphasic structure. Alpha grains and a lamellar eutectoid structure can be observed in the material.
464
VIEW
ML00044 / Feb.2017
Centrifugally Cast CuAl Bushing
M - Aluminum BronzeP - Cast BushingAp - EngineCd - Removed From Service
Cm - NH4OH+H2O+H2O2 Etched MicroDf - Close to the External Surface

More from these cases

ML00156 — Antique Silver Plated Decorative PieceM - BrassP - Decorative PieceAp - OrnamentalCd - Non Destructive Examination
Metallography of the coaster after etching, revealing a casting structure of alpha plus beta phases. Beta is the dark brown matrix phase and alpha is the dendritic yellow phase.
48
VIEW
ML00156 / Jan.2020
Antique Silver Plated Decorative Piece
M - BrassP - Decorative PieceAp - OrnamentalCd - Non Destructive Examination
Cm - NH4OH+H2O+H2O2 Etched MicroDf - Alpha and Beta
High magnification metallography of the coaster after etching, revealing a casting structure of alpha plus beta phases. Beta is the dark brown matrix phase and alpha is the dendritic yellow phase. The non destructive preparation created a metallographic surface not well polished (full of grinding scratches).
48
VIEW
ML00156 / Jan.2020
Antique Silver Plated Decorative Piece
M - BrassP - Decorative PieceAp - OrnamentalCd - Non Destructive Examination
Cm - NH4OH+H2O+H2O2 Etched MicroDf - Alpha and Beta
ML00044 — Centrifugally Cast CuAl BushingM - Aluminum BronzeP - Cast BushingAp - EngineCd - Removed From Service
Micrographic detail of the structure at the external surface.
58
VIEW
ML00044 / Feb.2017
Centrifugally Cast CuAl Bushing
M - Aluminum BronzeP - Cast BushingAp - EngineCd - Removed From Service
Cm - NH4OH+H2O+H2O2 Etched MicroDf - Close to the External Surface
The micrography of the transverse section shows coarse grains and biphasic structure. No diferentes close to the internal surface. Alpha grains and a lamellar eutectoid structure can be observed in the material.
46
VIEW
ML00044 / Feb.2017
Centrifugally Cast CuAl Bushing
M - Aluminum BronzeP - Cast BushingAp - EngineCd - Removed From Service
Cm - NH4OH+H2O+H2O2 Etched MicroDf - Close to the Internal Surface
Micrographic detail of the structure at the internal surface.
38
VIEW
ML00044 / Feb.2017
Centrifugally Cast CuAl Bushing
M - Aluminum BronzeP - Cast BushingAp - EngineCd - Removed From Service
Cm - NH4OH+H2O+H2O2 Etched MicroDf - Close to the Internal Surface
Detail of the structure in the center of the thickness. Alpha grains and lamellar eutectoid structure.
28
VIEW
ML00044 / Feb.2017
Centrifugally Cast CuAl Bushing
M - Aluminum BronzeP - Cast BushingAp - EngineCd - Removed From Service
Cm - NH4OH+H2O+H2O2 Etched MicroDf - In the Center of the Thickness