Forged Pin

4 cases · 44 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Results

SortNewestOldestTitle A-ZTitle Z-A
Longitudinal cracks in the surface of the pin, detected by dye check, after high pressure hydrostatic test.
657
VIEW
ML00110 / Jan.2018
Non Conformance in Spray and Fuse Pin
M - Low Alloy Medium Carbon QTP - Tubular ForgingAp - O&G Well DrillingCd - Heat Treatment Defect
Cm - Aspect by NDTDf - General View
Micrography, as polished, of the transverse section of the forged pin with the layer applied by a (thermal) spray and fuse process. The structure of the layer that is 0.7 mm thick, presented entrapped pores and globular oxides. The layer was melted after application by thermal spray (in this case using a flame) and the pin was quenched and tempered after the full application and melting of the layer.
360
VIEW
ML00109 / Jan.2018
Thermal Spray and Fuse Layer in Forged Pin
M - Low Alloy Medium Carbon QTP - Tubular ForgingAp - O&G Well DrillingCd - Thermal spray
Cm - As polished micrographyDf - Transverse Section
Microscopic detail of the cracks at the surface of the pin, close to the fracture. It is possible to see that the cracks are not associated to plastic deformation at the surface. Instead they are brittle and associated to regions where the material lost the passivation (dark grey stains at the surface). Some cracks that already opened (a little) showed deformation at the tips.
1024
VIEW
ML00085 / Nov.2017
Corrosion Fatigue of a Martensitic SS Pin
M - Martensitic Stainless SteelP - Forged PinAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Surface Aspect by SEMDf - Multiple cracks
Pin A micrography presenting a ferritic-perlitic structure.
462
VIEW
ML00048 / Apr.2017
Medium Carbon Steel Pins of Electrical Insulators
M - Medium Carbon SteelP - Forged PinAp - EnergyCd - Typical manufacturing
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite

More from these cases

ML00110 — Non Conformance in Spray and Fuse PinM - Low Alloy Medium Carbon QTP - Tubular ForgingAp - O&G Well DrillingCd - Heat Treatment Defect
Micrography, as polished, of the transverse section of the forged pin with the layer applied by a (thermal) spray and fuse process. The layer presented entrapped pores and globular oxides. It was melted after application by thermal spray (in this case using a flame) but the pin was not heat treated after the full application and melting of the layer and the base metal is ferritc-pearlitic.
50
VIEW
ML00110 / Jan.2018
Non Conformance in Spray and Fuse Pin
M - Low Alloy Medium Carbon QTP - Tubular ForgingAp - O&G Well DrillingCd - Heat Treatment Defect
Cm - As polished micrographyDf - Transverse Section
Micrography, as polished, of the transverse section of the forged pin with the layer applied by a (thermal) spray and fuse process. The layer was melted after thermal spray application and the layer presents a continuous matrix, but there are globular oxides and pores entrapped.
36
VIEW
ML00110 / Jan.2018
Non Conformance in Spray and Fuse Pin
M - Low Alloy Medium Carbon QTP - Tubular ForgingAp - O&G Well DrillingCd - Heat Treatment Defect
Cm - As polished micrographyDf - Surface Layer
Micrographic detail, as polished, of the transverse section of the forged pin at the interface between the pin and the spray and fuse layer. The interface presents globular oxides and small pores, entrapped.
35
VIEW
ML00110 / Jan.2018
Non Conformance in Spray and Fuse Pin
M - Low Alloy Medium Carbon QTP - Tubular ForgingAp - O&G Well DrillingCd - Heat Treatment Defect
Cm - As polished micrographyDf - Surface Layer
Low magnification micrography of the interface between the pin and the spray and fuse layer. Close to the surface, under the layer, the pin presents a ferritic perlitic structure, non conform with the high strenght requirement. Transverse section.
37
VIEW
ML00110 / Jan.2018
Non Conformance in Spray and Fuse Pin
M - Low Alloy Medium Carbon QTP - Tubular ForgingAp - O&G Well DrillingCd - Heat Treatment Defect
Cm - As polished micrographyDf - Low Mag
Micrography of the pin close to the interface with the spray and fuse layer. Transverse section. The fuse was conducted in high temperature and the pin was cooled very slowly, forming a ferritic-perlitic structure even for this high hardenability base metal.
35
VIEW
ML00110 / Jan.2018
Non Conformance in Spray and Fuse Pin
M - Low Alloy Medium Carbon QTP - Tubular ForgingAp - O&G Well DrillingCd - Heat Treatment Defect
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite

+6 more from this case →

ML00109 — Thermal Spray and Fuse Layer in Forged PinM - Low Alloy Medium Carbon QTP - Tubular ForgingAp - O&G Well DrillingCd - Thermal spray
Micrography, as polished, of the transverse section of the forged pin with the layer applied by a (thermal) spray and fuse process. The layer was melted after thermal spray application and the layer presents a continuous matrix, but there are globular oxides and pores entrapped.
28
VIEW
ML00109 / Jan.2018
Thermal Spray and Fuse Layer in Forged Pin
M - Low Alloy Medium Carbon QTP - Tubular ForgingAp - O&G Well DrillingCd - Thermal spray
Cm - As polished micrographyDf - Surface Layer
Micrographic detail, as polished, of the transverse section of the forged pin at the interface between the pin and the spray and fuse layer. The pin was heat treated after the thermal spray, and fuse treatment. The interface presents a higher concentration of globular oxides and pores, entrapped.
23
VIEW
ML00109 / Jan.2018
Thermal Spray and Fuse Layer in Forged Pin
M - Low Alloy Medium Carbon QTP - Tubular ForgingAp - O&G Well DrillingCd - Thermal spray
Cm - As polished micrographyDf - Surface Layer
Low magnification micrography of the interface between the pin and the spray and fuse layer. Close to the surface, under the layer, the pin presents a quenched and tempered structure, compatible with a high strenght requirement. Transverse section.
20
VIEW
ML00109 / Jan.2018
Thermal Spray and Fuse Layer in Forged Pin
M - Low Alloy Medium Carbon QTP - Tubular ForgingAp - O&G Well DrillingCd - Thermal spray
Cm - Nital Etched Micrography by OMDf - Surface Layer
Micrography of the pin close to the interface with the spray and fuse layer. Transverse section. The fuse is conducted in high temperature and the pin was quenched and tempered after the thermal spray deposition and fuse by flame (in this case the melting of the applied layer was conducted by a oxifuel flame.
21
VIEW
ML00109 / Jan.2018
Thermal Spray and Fuse Layer in Forged Pin
M - Low Alloy Medium Carbon QTP - Tubular ForgingAp - O&G Well DrillingCd - Thermal spray
Cm - Nital Etched Micrography by OMDf - Martensite
Micrographic detail of the tempered martensite structure close to the interface with the spray and fuse layer. Transverse section. The fuse is conducted in high temperature and the pin was heat treated after the thermal spray deposition and fuse.
15
VIEW
ML00109 / Jan.2018
Thermal Spray and Fuse Layer in Forged Pin
M - Low Alloy Medium Carbon QTP - Tubular ForgingAp - O&G Well DrillingCd - Thermal spray
Cm - Nital Etched Micrography by OMDf - Martensite

+3 more from this case →

ML00085 — Corrosion Fatigue of a Martensitic SS PinM - Martensitic Stainless SteelP - Forged PinAp - O&G Well DrillingCd - Corrosion Fatigue
Low magnification microscopy (stereoscope) detail of the multiple cracks at the pin surface.
146
VIEW
ML00085 / Nov.2017
Corrosion Fatigue of a Martensitic SS Pin
M - Martensitic Stainless SteelP - Forged PinAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Surface AspectDf - Multiple cracks
Aspect of the pin surface, presenting multiple cracks, paralel to the fracture position.
122
VIEW
ML00085 / Nov.2017
Corrosion Fatigue of a Martensitic SS Pin
M - Martensitic Stainless SteelP - Forged PinAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - Multiple cracks
Aspect of the 5/8" diameter pin, that was 3" long and broke close to the center.
104
VIEW
ML00085 / Nov.2017
Corrosion Fatigue of a Martensitic SS Pin
M - Martensitic Stainless SteelP - Forged PinAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - General View
Typical fatigue fracture, reversed bending.
74
VIEW
ML00085 / Nov.2017
Corrosion Fatigue of a Martensitic SS Pin
M - Martensitic Stainless SteelP - Forged PinAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - Fracture
The fractographic analysis of the pin showed fatigue striation at the subcritical propagation region.
75
VIEW
ML00085 / Nov.2017
Corrosion Fatigue of a Martensitic SS Pin
M - Martensitic Stainless SteelP - Forged PinAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Fractography by SEMDf - Fatigue Striation

+13 more from this case →

ML00048 — Medium Carbon Steel Pins of Electrical InsulatorsM - Medium Carbon SteelP - Forged PinAp - EnergyCd - Typical manufacturing
Detail of Pin A microstructure. Ferritic-perlitic.
138
VIEW
ML00048 / Apr.2017
Medium Carbon Steel Pins of Electrical Insulators
M - Medium Carbon SteelP - Forged PinAp - EnergyCd - Typical manufacturing
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Pin B micrography presenting a ferritic-bainitic structure.
97
VIEW
ML00048 / Apr.2017
Medium Carbon Steel Pins of Electrical Insulators
M - Medium Carbon SteelP - Forged PinAp - EnergyCd - Typical manufacturing
Cm - Nital Etched Micrography by OMDf - Ferrite and Bainite
Detail of Pin B microstructure. Ferritic-bainitic.
87
VIEW
ML00048 / Apr.2017
Medium Carbon Steel Pins of Electrical Insulators
M - Medium Carbon SteelP - Forged PinAp - EnergyCd - Typical manufacturing
Cm - Nital Etched Micrography by OMDf - Ferrite and Bainite