Crevice Corrosion in a Subsea System — Aspect Before Analysis

188 images

TryUNSML00136corrosionAISIML00132brittle fractureTempered Martensiteductile behaviorMartensitefatigueFinished ProducthydrogenRaw Materialfractureembrittlementstress corrosion
Application: O&G Well Drilling Capture method: Optical Microscope clear all
M

Material

79 classified

Browse all Material →
P

Product

96 classified

Browse all Product →
Ap

Application

37 classified

Browse all Application →
C

Condition

84 classified

Browse all Condition →
Cm

Capture method

52 classified

Browse all Capture method →
Df

Detail focus

208 classified

Browse all Detail focus →

Sharpest next filters

Browse by category (2)
Standard37
+29 more
Microstructure19
+11 more

The Materials
Image Database

188 images
Quenched and tempered structure of the F22 steel forging, presenting about 230HV10 average hardness.
133
VIEW
ML00178 / Jan.2022
Cold cracks in Cr-Mo Welded Forging
M - CrMo SteelP - ForgingAp - O&G Well DrillingCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Base Metal
Micrography presenting a uniform and refined tempered martensitic structure.
39
VIEW
ML00169 / Nov.2020
Drill Pipe Fracture in the Pipe Body
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Nital Etched Micrography by OMDf - Uniform Structure
Low magnification micrography of a longitudinal section of the valve body, in the center of the thickness. As expected for this high strength steel, the microstructure is martensitic, but with segregation bands.
48
VIEW
ML00162 / Apr.2020
Valve Body Crack Growth from Weld Defects
M - Low Alloy Medium Carbon QTP - Valve BodyAp - O&G Well DrillingCd - Fatigue Induced by a Defect
Cm - Nital Etched Micrography by OMDf - Banded Structure
Tempered martensite of the pipe body of this API 5D grade S135 drill pipe. The material presents, at this low magnification micrographic aspect, a slightly banded structure, usual for this type of drill pipe.
58
VIEW
ML00159 / Mar.2020
Collapse of a Drill Pipe
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Ductile Behavior
Cm - Nital Etched Micrography by OMDf - Banded Structure
Micrography of the longitudinal section, in the center of the thickness of the pin, presenting an aligned ferritic-austeinitic structure.
180
VIEW
ML00146 / Jul.2018
Plastic Deformation of a SDSS Riser Pin
M - Super Duplex Stainless SteelP - PinAp - O&G Well DrillingCd - Bending
Cm - NaOH Electrolytic Etched MicroDf - Ferrite and Austenite
Micrography of a longitudinal section, in the center, of the broken 5/8" bolt, presenting an aged martensitic structure. There are vertical "lines" that correspond to segregation bands due to the forming direction. These bands are evident only using low magnification microscopy.
168
VIEW
ML00139 / Jun.2018
Hydrogen Fracture of a 17-4 PH Allen Bolt
M - Precipitation Hardened Stainless SteelP - Allen BoltAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Longitudinal Section
Optical micrography of the transverse section of the drill collar, in the center of the thickness, presenting an uniform, granular, fully austenitic microstructure.
76
VIEW
ML00135 / May.2018
MIC of a Non Magnetic Drilling Tool
M - High Mn Austenitic SteelP - Tubular ForgingAp - O&G Well DrillingCd - Pitting Corrosion
Cm - Oxalic Acid Electrolytic EtchDf - Transverse Section
Micrographic aspect of the rolled thread that was heat treated later. Longitudinal section.
134
VIEW
ML00130 / Jun.2018
Fatigue Fracture of Overloaded Bolts
M - Low Alloy Medium Carbon QTP - FastenerAp - O&G Well DrillingCd - Mechanical Fatigue
Cm - Nital Etched Micrography by OMDf - At the Surface

More from these cases

ML00178 — Cold cracks in Cr-Mo Welded ForgingM - CrMo SteelP - ForgingAp - O&G Well DrillingCd - Welding Defect
Tempered martensitic structure for the F22 forging base metal.
129
VIEW
ML00178 / Jan.2022
Cold cracks in Cr-Mo Welded Forging
M - CrMo SteelP - ForgingAp - O&G Well DrillingCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Tempered Martensite
Fusion line of the forging side, in the cap, showing the weld metal (to the top of the image) and the base metal (to the bottom of the image). The heat affected zone hardness is about 270HV10.
108
VIEW
ML00178 / Jan.2022
Cold cracks in Cr-Mo Welded Forging
M - CrMo SteelP - ForgingAp - O&G Well DrillingCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Heat Affected Zone
Grain coarsened martensitic heat affected zone. The hardness values about 270HV10 indicates that the joint was post welding heat treated (PWHT).
97
VIEW
ML00178 / Jan.2022
Cold cracks in Cr-Mo Welded Forging
M - CrMo SteelP - ForgingAp - O&G Well DrillingCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Martensite
Detail of the quenched and tempered martensitic structure at the heat affected zone.
64
VIEW
ML00178 / Jan.2022
Cold cracks in Cr-Mo Welded Forging
M - CrMo SteelP - ForgingAp - O&G Well DrillingCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Tempered Martensite
The columnar grains of the weld metal in the cap presented a martensitic structure.
60
VIEW
ML00178 / Jan.2022
Cold cracks in Cr-Mo Welded Forging
M - CrMo SteelP - ForgingAp - O&G Well DrillingCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Weld Metal

+1 more from this case →

ML00169 — Drill Pipe Fracture in the Pipe BodyM - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Corrosion Fatigue
Micrography presenting a uniform and refined tempered martensitic structure.
39
VIEW
ML00169 / Nov.2020
Drill Pipe Fracture in the Pipe Body
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Nital Etched Micrography by OMDf - Martensite
Micrographic detail of the tempered martensite.
40
VIEW
ML00169 / Nov.2020
Drill Pipe Fracture in the Pipe Body
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Nital Etched Micrography by OMDf - Martensite
Micrography of a longitudinal section of the pipe, at the external pipe surface, where there is a corroded spot. The microstructure is tempered martensite and at the surface the pipe is slightly decarburized.
28
VIEW
ML00169 / Nov.2020
Drill Pipe Fracture in the Pipe Body
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Nital Etched Micrography by OMDf - External Surface
Micrography of a longitudinal section of the pipe, at the external pipe surface, where there is a crack propagating from the corroded spot. The microstructure is tempered martensite and at the surface the pipe is slightly decarburized.
26
VIEW
ML00169 / Nov.2020
Drill Pipe Fracture in the Pipe Body
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Nital Etched Micrography by OMDf - Crack
Micrographic detail of the crack from the corroded spot.
28
VIEW
ML00169 / Nov.2020
Drill Pipe Fracture in the Pipe Body
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Nital Etched Micrography by OMDf - Corrosion

+7 more from this case →

ML00162 — Valve Body Crack Growth from Weld DefectsM - Low Alloy Medium Carbon QTP - Valve BodyAp - O&G Well DrillingCd - Fatigue Induced by a Defect
Micrography of a longitudinal section of the valve body presenting a martensitic microstructure. The structure is banded and the darker regions show inclusions (grey sulfides).
50
VIEW
ML00162 / Apr.2020
Valve Body Crack Growth from Weld Defects
M - Low Alloy Medium Carbon QTP - Valve BodyAp - O&G Well DrillingCd - Fatigue Induced by a Defect
Cm - Nital Etched Micrography by OMDf - Martensite
Micrographic detail of the martensitic microstructure, in the longitudinal section. The hardness of the valve body is 34 HRc (Rockwell C) all through the thickness.
47
VIEW
ML00162 / Apr.2020
Valve Body Crack Growth from Weld Defects
M - Low Alloy Medium Carbon QTP - Valve BodyAp - O&G Well DrillingCd - Fatigue Induced by a Defect
Cm - Nital Etched Micrography by OMDf - Martensite
Macrography of the longitudinal section of the valve body, at the cracked position, a little far from the actuator hole. The valve body is 40 mm thick at this position and it is possible to see that at this position only one region is welded in repair, close to the outer surface (top), and there is a crack, transverse to the thickness, that is difficult to see with this magnification and that is clearly the propagation in fatigue.
47
VIEW
ML00162 / Apr.2020
Valve Body Crack Growth from Weld Defects
M - Low Alloy Medium Carbon QTP - Valve BodyAp - O&G Well DrillingCd - Fatigue Induced by a Defect
Cm - Nital Etched Micrography by OMDf - Fatigue Crack
Low magnification micrography at the weld repair close to the internal surface of the valve body, in a longitudinal section. Weld metal to the bottom and heat affected zone to the top.
42
VIEW
ML00162 / Apr.2020
Valve Body Crack Growth from Weld Defects
M - Low Alloy Medium Carbon QTP - Valve BodyAp - O&G Well DrillingCd - Fatigue Induced by a Defect
Cm - Nital Etched Micrography by OMDf - Weld Repair
Micrography of the weld repair at the fusion line. Weld metal to the right and heat affected zone to the left.
37
VIEW
ML00162 / Apr.2020
Valve Body Crack Growth from Weld Defects
M - Low Alloy Medium Carbon QTP - Valve BodyAp - O&G Well DrillingCd - Fatigue Induced by a Defect
Cm - Nital Etched Micrography by OMDf - Fusion Line

+18 more from this case →

ML00159 — Collapse of a Drill PipeM - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Ductile Behavior
Micrographic detail of the tempered martensite in the longitudinal section of the pipe body. Uniform structure.
44
VIEW
ML00159 / Mar.2020
Collapse of a Drill Pipe
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Ductile Behavior
Cm - Nital Etched Micrography by OMDf - Martensite
Micrographic detail of the tempered martensite in the longitudinal section of the pipe body.
39
VIEW
ML00159 / Mar.2020
Collapse of a Drill Pipe
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Ductile Behavior
Cm - Nital Etched Micrography by OMDf - Martensite
Micrography of the longitudinal section of the pipe, at the thicker part of the fracture, showing several secondary cracks opened to the external side of the pipe. There are no problems in the material structure and the cracks are associated to large plastic deformation.
36
VIEW
ML00159 / Mar.2020
Collapse of a Drill Pipe
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Ductile Behavior
Cm - Nital Etched Micrography by OMDf - Ductile Crack
Micrographic detail of the secondary cracks opened to the external side of the pipe. The cracks are associated to large plastic deformation.
30
VIEW
ML00159 / Mar.2020
Collapse of a Drill Pipe
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Ductile Behavior
Cm - Nital Etched Micrography by OMDf - Ductile Crack
Micrographic detail of the ductile secondary cracks in the pipe body, close to the fracture. The strong plastic deformation is associated to the compression stresses generated by the buckling.
27
VIEW
ML00159 / Mar.2020
Collapse of a Drill Pipe
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Ductile Behavior
Cm - Nital Etched Micrography by OMDf - Plastic Deformation

+3 more from this case →

ML00146 — Plastic Deformation of a SDSS Riser PinM - Super Duplex Stainless SteelP - PinAp - O&G Well DrillingCd - Bending
Micrography of a longitudinal section, at the surface of the pin, where the thermal spray layer is sound. The thickness of the layer is about 0.3 mm.
168
VIEW
ML00146 / Jul.2018
Plastic Deformation of a SDSS Riser Pin
M - Super Duplex Stainless SteelP - PinAp - O&G Well DrillingCd - Bending
Cm - NaOH Electrolytic Etched MicroDf - Coating Layer
Micrographic detail of a longitudinal section of the pin, at the surface, evidencing the thermal spray layer, about 0.3 mm. The layer presents typical characteristics of multiple layers, low amount of entrapped oxides and pores. The interface presents a high roughness level for a good adherence and some entrapped oxides. The structure of the SDSS substrate did not show thermal effects.
154
VIEW
ML00146 / Jul.2018
Plastic Deformation of a SDSS Riser Pin
M - Super Duplex Stainless SteelP - PinAp - O&G Well DrillingCd - Bending
Cm - NaOH Electrolytic Etched MicroDf - Coating Layer
Micrography of a longitudinal section, at the damage surface of the pin, where the thermal spray layer was partially detached and broken. The through layer breaking is ductile, typical of an overloading condition caused by the localized bending of the pin.
109
VIEW
ML00146 / Jul.2018
Plastic Deformation of a SDSS Riser Pin
M - Super Duplex Stainless SteelP - PinAp - O&G Well DrillingCd - Bending
Cm - NaOH Electrolytic Etched MicroDf - Layer Detachment
Micrographic detail of the damage surface layer, detached and broken. The substrate is not affected and the rupture of the layer is typically by overloading.
117
VIEW
ML00146 / Jul.2018
Plastic Deformation of a SDSS Riser Pin
M - Super Duplex Stainless SteelP - PinAp - O&G Well DrillingCd - Bending
Cm - NaOH Electrolytic Etched MicroDf - Layer Detachment
ML00139 — Hydrogen Fracture of a 17-4 PH Allen BoltM - Precipitation Hardened Stainless SteelP - Allen BoltAp - SubseaCd - Hydrogen Embrittlement
Micrography of a longitudinal section, in the center, of the broken 5/8" bolt, presenting an aged martensitic structure.
132
VIEW
ML00139 / Jun.2018
Hydrogen Fracture of a 17-4 PH Allen Bolt
M - Precipitation Hardened Stainless SteelP - Allen BoltAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Martensite
Micrographic detail of the aged martensitic structure. The bolt presented variations in the previous austenite grain boundaries from the center of the thickness to the surface. No delta ferrite or retained austenite islands are evidenced.
107
VIEW
ML00139 / Jun.2018
Hydrogen Fracture of a 17-4 PH Allen Bolt
M - Precipitation Hardened Stainless SteelP - Allen BoltAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Martensite
Micrography of a longitudinal section of the 5/8" bolt, at the bottom of the thread, presenting a refined structure compared to the center of the bolt and a mark at the thread flank that was probably created during tightening of the bolt.
95
VIEW
ML00139 / Jun.2018
Hydrogen Fracture of a 17-4 PH Allen Bolt
M - Precipitation Hardened Stainless SteelP - Allen BoltAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Longitudinal Section
Micrography of a longitudinal section of the 5/8" bolt, at the bottom of the thread, presenting a refined structure compared to the center of the bolt. The structure is aged martensite.
91
VIEW
ML00139 / Jun.2018
Hydrogen Fracture of a 17-4 PH Allen Bolt
M - Precipitation Hardened Stainless SteelP - Allen BoltAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Martensite
Micrographic detail of the aged martensite structure, refined when compared to the structure in the center of the bolt.
87
VIEW
ML00139 / Jun.2018
Hydrogen Fracture of a 17-4 PH Allen Bolt
M - Precipitation Hardened Stainless SteelP - Allen BoltAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Martensite

+19 more from this case →

ML00135 — MIC of a Non Magnetic Drilling ToolM - High Mn Austenitic SteelP - Tubular ForgingAp - O&G Well DrillingCd - Pitting Corrosion
Optical micrography of the transverse section of the drill collar, in the center of the thickness, presenting an uniform, granular, fully austenitic microstructure.
64
VIEW
ML00135 / May.2018
MIC of a Non Magnetic Drilling Tool
M - High Mn Austenitic SteelP - Tubular ForgingAp - O&G Well DrillingCd - Pitting Corrosion
Cm - Oxalic Acid Electrolytic EtchDf - Transverse Section
Micrographic detail of the transverse section of the drill collar, in the center of the thickness, presenting an uniform, granular, fully austenitic microstructure.
61
VIEW
ML00135 / May.2018
MIC of a Non Magnetic Drilling Tool
M - High Mn Austenitic SteelP - Tubular ForgingAp - O&G Well DrillingCd - Pitting Corrosion
Cm - Oxalic Acid Electrolytic EtchDf - Austenite
Optical micrography of the longitudinal section of the drill collar, in the center of the thickness, presenting slightly elongated grains of fully austenitic microstructure, cold worked. The material presented 38HRc hardness.
57
VIEW
ML00135 / May.2018
MIC of a Non Magnetic Drilling Tool
M - High Mn Austenitic SteelP - Tubular ForgingAp - O&G Well DrillingCd - Pitting Corrosion
Cm - Oxalic Acid Electrolytic EtchDf - Longitudinal Section
Optical micrography of the longitudinal section of the drill collar, in the center of the thickness, presenting slightly elongated grains of fully austenitic microstructure, cold worked.
62
VIEW
ML00135 / May.2018
MIC of a Non Magnetic Drilling Tool
M - High Mn Austenitic SteelP - Tubular ForgingAp - O&G Well DrillingCd - Pitting Corrosion
Cm - Oxalic Acid Electrolytic EtchDf - Longitudinal Section
Micrographic detail of the longitudinal section of the drill collar, in the center of the thickness, presenting slightly elongated grains of fully austenitic microstructure, cold worked.
59
VIEW
ML00135 / May.2018
MIC of a Non Magnetic Drilling Tool
M - High Mn Austenitic SteelP - Tubular ForgingAp - O&G Well DrillingCd - Pitting Corrosion
Cm - Oxalic Acid Electrolytic EtchDf - Austenite

+6 more from this case →

ML00130 — Fatigue Fracture of Overloaded BoltsM - Low Alloy Medium Carbon QTP - FastenerAp - O&G Well DrillingCd - Mechanical Fatigue
Micrographic aspect of the rolled thread that was heat treated later. Longitudinal section. The bolt was quenched and tempered to 30HRc and presented a martensitic structure.
124
VIEW
ML00130 / Jun.2018
Fatigue Fracture of Overloaded Bolts
M - Low Alloy Medium Carbon QTP - FastenerAp - O&G Well DrillingCd - Mechanical Fatigue
Cm - Nital Etched Micrography by OMDf - At the Surface
Micrographic detail of the rolled thread that was heat treated later. The bolt was quenched and tempered to 30 HRc and presented a martensitic structure.
110
VIEW
ML00130 / Jun.2018
Fatigue Fracture of Overloaded Bolts
M - Low Alloy Medium Carbon QTP - FastenerAp - O&G Well DrillingCd - Mechanical Fatigue
Cm - Nital Etched Micrography by OMDf - Martensite
The microstructure of the bolt is martensitic in the center of the thickness. Longitudinal section.
110
VIEW
ML00130 / Jun.2018
Fatigue Fracture of Overloaded Bolts
M - Low Alloy Medium Carbon QTP - FastenerAp - O&G Well DrillingCd - Mechanical Fatigue
Cm - Nital Etched Micrography by OMDf - In the Center of the Thickness
The microstructure of the bolt is martensitic in the center of the thickness. Longitudinal section.
103
VIEW
ML00130 / Jun.2018
Fatigue Fracture of Overloaded Bolts
M - Low Alloy Medium Carbon QTP - FastenerAp - O&G Well DrillingCd - Mechanical Fatigue
Cm - Nital Etched Micrography by OMDf - Martensite
Micrographic aspect of the rolled thread that was heat treated later. Longitudinal section.
115
VIEW
ML00130 / Jun.2018
Fatigue Fracture of Overloaded Bolts
M - Low Alloy Medium Carbon QTP - FastenerAp - O&G Well DrillingCd - Mechanical Fatigue
Cm - Nital Etched Micrography by OMDf - At the Surface

+3 more from this case →

View all 188 images in the Atlas →

most recent

The location of the threaded fitting started leaking after less than five years in service. Although the corrosion rate was not high, the localized material loss in the threaded surface of the carbon steel flange allowed the connection leakage.
769
VIEW
ML00184 / Apr.2023
Dissimilar Steels in a Threaded Connection
M - Low Carbon SteelP - ForgingAp - OffshoreCd - Localized Dissolution
Cm - Aspect Before AnalysisDf - General View
Front wheel 17 x 7J of a passenger vehicle (identified as WHEEL 1) that broke during a car accident on a road.
1644
VIEW
ML00183 / Dec.2022
Ductile Behavior of an Aluminum Wheel
M - Aluminum Silicon MagnesiumP - CastingAp - AutomotiveCd - Ductile Behavior
Cm - Aspect Before AnalysisDf - General View
Tool fixture 5" long, nominal diameter 2", presenting a recess 1/2" deep from two sides. The rupture occurred about 2" from the end of the rod. Scale in milimeters.
523
VIEW
ML00182 / Jul.2022
Brittle Fracture of a LAS Fixing Rod
M - Low Alloy Medium Carbon QTP - StemAp - Mechanical IndustryCd - Brittle Fracture
Cm - Aspect Before AnalysisDf - General View
Pinion of hypoid gearbox, assembled in a 1560-mm long shaft that operated during more than 60,000 hours, and removed from service due to unacceptable wear damage.
1028
VIEW
ML00181 / Apr.2022
Wear of a Carburized Hypoid Gear
M - Low Alloy for Thermochemical TreatmentP - Pinion-crown assemblyAp - ShipCd - Wear
Cm - Aspect Before AnalysisDf - General View
Aspect of the 3 1/2" diameter tube after the water leakage in high temperature.
962
VIEW
ML00180 / Mar.2022
Local Melting of Copper Cooling Tubes
M - Pure CopperP - Cooling TubeAp - SiderurgyCd - Overheating
Cm - Aspect Before AnalysisDf - General View
2" drain line from the main 10" line. The leakage occurred at the margin of the weld, a short time after the introduction of the reinforced ribs to reduce vibration.
641
VIEW
ML00179 / Feb.2022
Hydrides in Titanium Weld
M - Unalloyed TitaniumP - In Field WeldAp - Chemical IndustryCd - Hydride Formation
Cm - Field photoDf - General View
The drilling connector, 21" diameter, presented a crack at the margin of the weld in the forging side (left side of the weld in the figure).
744
VIEW
ML00178 / Jan.2022
Cold cracks in Cr-Mo Welded Forging
M - CrMo SteelP - ForgingAp - O&G Well DrillingCd - Welding Defect
Cm - Aspect Before AnalysisDf - General View
Macrography of the longitudinally seam weld of the 24" diameter tube, showing that it was welded from both sides and there is a segregation line in the center of the tube thickness.
737
VIEW
ML00177 / Dec.2021
Cr-Mo Seam Welded Tube
M - CrMo SteelP - Longitudinally Seam WeldedAp - Fired HeaterCd - Not according to spec
Cm - NItal Etched MacroDf - Seam
The titanium rotor blade of a flowmeter broke after two years in service in an acid environment, containing H2S.
339
VIEW
ML00176 / Nov.2021
Hydride Formation in a Titanium Blade
M - Unalloyed TitaniumP - BladeAp - Oil and GasCd - Hydride Formation
Cm - Aspect Before AnalysisDf - General View
Aspect of the wire rope, 1 1/2" diameter, presenting regions of flattened areas at the surface of the outer wires. It is a 6 x 19 Seale construction, right regular lay.
552
VIEW
ML00175 / Aug.2021
Localized External Wear of a Wire Rope
M - High Carbon SteelP - Wire RopeAp - Oil and GasCd - Wear
Cm - Aspect Before AnalysisDf - General View
The carcass was manufactured using niobium stabilized plates, grade AISI 347, with circumferential welds, where the through wall cracks were detected.
300
VIEW
ML00174 / Jul.2021
Carburization of a 347 SS Welded Joint
M - Austenitic Stainless SteelP - Fabrication WeldAp - EnergyCd - Carburization
Cm - Field photoDf - General View
Aged microstructure of the HP stainless steel, modified with 1%Nb, cast fitting, tubular, operating for 6 years in a furnace which design temperature is 1100°C. The material presented a network of primary carbides, white and grey, and an austenitic matrix with coalescing secondary precipitation. Some voids. The Vickers identation indicates a hardness value about 260HV 100g in the aged austenitic matrix.
491
VIEW
ML00173 / May.2021
Welding Cracks in an Aged HP Cast Fitting
M - Heat Resistant SteelP - Cast FtittingAp - PetrochemicalCd - Welding
Cm - Kalling Etched Micrography by OMDf - Microhardness identations

Partners

Companies involved

TECMETAL