In the Center of the Thickness

24 cases · 36 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrography of the tooth gear, in a transverse section of center region. Again, some segregation patterns are visible.
58
VIEW
ML00181 / Apr.2022
Wear of a Carburized Hypoid Gear
M - Low Alloy for Thermochemical TreatmentP - Pinion-crown assemblyAp - ShipCd - Wear
Cm - Nital Etched Micrography by OMDf - In the Center of the Thickness
Micrographic aspect of the tube out of the damaged region, in a longitudinal section, showing the grain refined copper structure.
96
VIEW
ML00180 / Mar.2022
Local Melting of Copper Cooling Tubes
M - Pure CopperP - Cooling TubeAp - SiderurgyCd - Overheating
Cm - FeCl3+HCl+H2O Etched MicroDf - In the Center of the Thickness
Micrography of the stub end in the middle of the thickness, outer diameter to the top of the image, presenting multiple branched cracks.
26
VIEW
ML00168 / Aug.2020
SCC of Austenitic SS Flange Stub End
M - Austenitic Stainless SteelP - Stub EndAp - Chemical IndustryCd - Stress Corrosion
Cm - Oxalic Acid Electrolytic EtchDf - In the Center of the Thickness
Micrography of a tube transverse section, at the through wall cracking position, showing intergranular morphology of the stress corrosion cracking. In the center of the thickness, far from the external surface corroded layer, the cracks are intergranular but did not present any dealloying evidence.
49
VIEW
ML00165 / Jul.2020
SCC of Aluminum Bronze Heating Coil
M - Aluminum BronzeP - Seamless tubeAp - Oil and GasCd - Stress Corrosion
Cm - FeCl3+HCl+H2O Etched MicroDf - In the Center of the Thickness
SAMPLE 1 AT 1 mm THICKNESS - Micrography in low magnification in the center of the thickness, as polished. There are no regions of internal damage (like internal voids or cracks), indicating that the mechanism is only related to surface effects.
42
VIEW
ML00160 / Apr.2020
High Temperature Degradation of 310SS
M - Austenitic Stainless SteelP - Rectangular TubeAp - Chemical IndustryCd - Scaling
Cm - As polished micrographyDf - In the Center of the Thickness
Micrography of the wheel in the center of the thickness. The material presents a coarse structure.
88
VIEW
ML00158 / Feb.2020
Surface Hardened Carbon Steel Wheel
M - High Carbon SteelP - WheelAp - TransportationCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - In the Center of the Thickness
Micrography of the crankshaft in the center of the thickness. The microstructure is nodules of graphite in a ferritic and pearlitic matrix, predominantly pearlitic.
34
VIEW
ML00154 / Jan.2019
High Strength Cast Iron Crankshaft
M - Nodular Cast IronP - CastingAp - EngineCd - Surface treatment
Cm - Nital Etched Micrography by OMDf - In the Center of the Thickness
Micrography of the longitudinal section of the cast sleeve in the middle of the thickness. The microstructure is coarse, austenitic ferritic.
34
VIEW
ML00147 / Aug.2018
WC Layer Detached from a Cast Lean Duplex
M - Lean Duplex Stainless SteelP - Centrifugal CastingAp - ShipCd - Lack of Sealing
Cm - NaOH Electrolytic Etched MicroDf - In the Center of the Thickness