Internal Surface

17 cases · 33 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Results

SortNewestOldestTitle A-ZTitle Z-A
View of the iinternal side of the tube (water side), deformed in the overheated area. There are several leaking points.
115
VIEW
ML00180 / Mar.2022
Local Melting of Copper Cooling Tubes
M - Pure CopperP - Cooling TubeAp - SiderurgyCd - Overheating
Cm - Aspect Before AnalysisDf - Internal Surface
Visual aspect of the internal side of the tube, after longitudinal cut, presenting regions where the internal layer is fully stained.
55
VIEW
ML00170 / Sep.2020
MIC in Aluminum Brass Tubes
M - Aluminum BrassP - Seamless tubeAp - MaritimeCd - Preferential Dissolution
Cm - Aspect Before AnalysisDf - Internal Surface
Region where the internal coating was detached. The fracture at this position is flat.
28
VIEW
ML00169 / Nov.2020
Drill Pipe Fracture in the Pipe Body
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - Internal Surface
Aspect of the internal tube surface after a longitudinal cut, without cleaning. It is possible to see a clean surface inside the tube.
104
VIEW
ML00165 / Jul.2020
SCC of Aluminum Bronze Heating Coil
M - Aluminum BronzeP - Seamless tubeAp - Oil and GasCd - Stress Corrosion
Cm - Surface AspectDf - Internal Surface
Aspect of the tube internal surface after removal from the boiler, presenting multiple longitudinal cracks.
295
VIEW
ML00163 / Jun.2020
Corrosion Fatigue of a Boiler Waterwall Tube
M - Low Carbon SteelP - Seamless tubeAp - BoilerCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - Internal Surface
Micrographic aspect of the rim microstructure at the surface (internal to the wheel), not the heat treated one. The pearlitic structure is not so coarse than in the center of the thickness.
38
VIEW
ML00158 / Feb.2020
Surface Hardened Carbon Steel Wheel
M - High Carbon SteelP - WheelAp - TransportationCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Internal Surface
dfjg\flafhvm,b\,d
4
VIEW
ML00155 / Jan.2020
Failure of a Prestressed Concrete Steel Strand
M - High Carbon SteelP - Wire RopeAp - StructureCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - Internal Surface
Aspect of the brach line viewed from the internal side of the main pipe, after cuting. It is possible to see that the pipe was perforated by a thermal cutting (looking the finishing aspect of the edge of the hole). The weldolet was welded only from the external side of the pipe.
62
VIEW
ML00149 / Dec.2018
Vibration Induced Fatigue in a Gas Piping
M - Low Carbon SteelP - Piping spoolAp - FPSOCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - Internal Surface

More from these cases

ML00180 — Local Melting of Copper Cooling TubesM - Pure CopperP - Cooling TubeAp - SiderurgyCd - Overheating
Macroscopic aspect after cutting longitudinally in two halfs, at the damaged area. The tube internal surface showed a red copper colour at the overheated region and the perforation is associated to longitudinal cracks.
104
VIEW
ML00180 / Mar.2022
Local Melting of Copper Cooling Tubes
M - Pure CopperP - Cooling TubeAp - SiderurgyCd - Overheating
Cm - Longitudinal Section AspectDf - Internal Surface
ML00170 — MIC in Aluminum Brass TubesM - Aluminum BrassP - Seamless tubeAp - MaritimeCd - Preferential Dissolution
Detailed aspect, by a low magnification microscope, of the internal side of the tube with deposits.
36
VIEW
ML00170 / Sep.2020
MIC in Aluminum Brass Tubes
M - Aluminum BrassP - Seamless tubeAp - MaritimeCd - Preferential Dissolution
Cm - Surface AspectDf - Internal Surface
Scanning electron microscopy of the internal surface of the tube, showing that under the deposits there are regions of localized corrosion.
30
VIEW
ML00170 / Sep.2020
MIC in Aluminum Brass Tubes
M - Aluminum BrassP - Seamless tubeAp - MaritimeCd - Preferential Dissolution
Cm - Surface Aspect by SEMDf - Internal Surface
Micrography of a transverse section of the tube at the localized reduced thickness point. Close to the internal surface.
28
VIEW
ML00170 / Sep.2020
MIC in Aluminum Brass Tubes
M - Aluminum BrassP - Seamless tubeAp - MaritimeCd - Preferential Dissolution
Cm - FeCl3+HCl+Ethanol Etched MicroDf - Internal Surface
Micrographic detail of a transverse section of the tube at the localized reduced thickness point. Close to the internal surface.
26
VIEW
ML00170 / Sep.2020
MIC in Aluminum Brass Tubes
M - Aluminum BrassP - Seamless tubeAp - MaritimeCd - Preferential Dissolution
Cm - FeCl3+HCl+Ethanol Etched MicroDf - Internal Surface
ML00169 — Drill Pipe Fracture in the Pipe BodyM - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Corrosion Fatigue
Micrographic detail of the strain hardening effect, probably generated by blasting before applying the coating. The microstructure is tempered martensite and the surface it is slightly decarburized.
23
VIEW
ML00169 / Nov.2020
Drill Pipe Fracture in the Pipe Body
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Nital Etched Micrography by OMDf - Internal Surface
Drill Pipe Fracture in the Pipe Body
2
VIEW
ML00169 / Nov.2020
Drill Pipe Fracture in the Pipe Body
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - As polished micrographyDf - Internal Surface
Drill Pipe Fracture in the Pipe Body
3
VIEW
ML00169 / Nov.2020
Drill Pipe Fracture in the Pipe Body
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - As polished micrographyDf - Internal Surface
ML00165 — SCC of Aluminum Bronze Heating CoilM - Aluminum BronzeP - Seamless tubeAp - Oil and GasCd - Stress Corrosion
SCC of Aluminum Bronze Heating Coil
2
VIEW
ML00165 / Jul.2020
SCC of Aluminum Bronze Heating Coil
M - Aluminum BronzeP - Seamless tubeAp - Oil and GasCd - Stress Corrosion
Cm - Aspect Before AnalysisDf - Internal Surface