Fatigue Fracture

10 cases · 17 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Results

SortNewestOldestTitle A-ZTitle Z-A
Microscopic aspect of the fracture, propagating by contact fatigue.
43
VIEW
ML00181 / Apr.2022
Wear of a Carburized Hypoid Gear
M - Low Alloy for Thermochemical TreatmentP - Pinion-crown assemblyAp - ShipCd - Wear
Cm - Fractography by SEMDf - Fatigue Fracture
Pipe fracture, flat, at the region of subcritical crack growth.
68
VIEW
ML00169 / Nov.2020
Drill Pipe Fracture in the Pipe Body
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - Fatigue Fracture
Flat aspect of the fracture. The striation micromechanism is revealed.
50
VIEW
ML00167 / Aug.2020
Fatigue of a Flared Tubing Connection
M - Austenitic Stainless SteelP - TubingAp - EngineCd - Mechanical Fatigue
Cm - Fractography by SEMDf - Fatigue Fracture
Fracture apperance by scanning electron microscopy of the region where the fatigue crack started, from the piping outside . The fracture is flat, presents some smashed regions close to the surface (to the right side) and there are some thin secondary cracks.
140
VIEW
ML00150 / Dec.2018
Vibration Induced Fatigue in a SS Oil Piping
M - Duplex Stainless SteelP - PipingAp - FPSOCd - Vibration Induced Fatigue
Cm - Fractography by SEMDf - Fatigue Fracture
Aspect of the bolt fracture surface by scanning electron microscopy, (SEM) presenting striations that indicate a FATIGUE micromechanism. The bolt is of a medium strength (class 8.8) low alloy steel, medium carbon, quenched and tempered.
1123
VIEW
ML00130 / Jun.2018
Fatigue Fracture of Overloaded Bolts
M - Low Alloy Medium Carbon QTP - FastenerAp - O&G Well DrillingCd - Mechanical Fatigue
Cm - Fractography by SEMDf - Fatigue Fracture
Micrographic detail of a secondary cracking close to the fracture position. The crack presents no plastic deformation, is slightly branched and filled with products.
52
VIEW
ML00085 / Nov.2017
Corrosion Fatigue of a Martensitic SS Pin
M - Martensitic Stainless SteelP - Forged PinAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Kalling Etched Micrography by OMDf - Fatigue Fracture
Detail of the fracture surface presenting a fatigue propagation from the outside of the tool.
69
VIEW
ML00082 / Dec.2017
Corrosion Fatigue of a Drilling Tool
M - Low Alloy Medium Carbon QTP - Tubular ForgingAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - Fatigue Fracture
The aspect of the pin fracture surface shows that a fatigue crack propagated from the pin surface at the edge of a lubrication hole in the chromium plated pin.
83
VIEW
ML00081 / Aug.2017
Hydrogen Cracking of a Chromium Plated Carburized Pin
M - Low Alloy for Thermochemical TreatmentP - Chromium PlatedAp - AutomotiveCd - Hydrogen Embrittlement
Cm - Aspect Before AnalysisDf - Fatigue Fracture

More from these cases

ML00167 — Fatigue of a Flared Tubing ConnectionM - Austenitic Stainless SteelP - TubingAp - EngineCd - Mechanical Fatigue
When the fracture propagates, the striation becomes wider and with transgranular irregular steps.
47
VIEW
ML00167 / Aug.2020
Fatigue of a Flared Tubing Connection
M - Austenitic Stainless SteelP - TubingAp - EngineCd - Mechanical Fatigue
Cm - Fractography by SEMDf - Fatigue Fracture
ML00150 — Vibration Induced Fatigue in a SS Oil PipingM - Duplex Stainless SteelP - PipingAp - FPSOCd - Vibration Induced Fatigue
Fracture apperance by scanning electron microscopy in the center of the thickness where the crack propagated through wall. The fracture is flat and the striation is not so clear at this magnification.
133
VIEW
ML00150 / Dec.2018
Vibration Induced Fatigue in a SS Oil Piping
M - Duplex Stainless SteelP - PipingAp - FPSOCd - Vibration Induced Fatigue
Cm - Fractography by SEMDf - Fatigue Fracture
ML00130 — Fatigue Fracture of Overloaded BoltsM - Low Alloy Medium Carbon QTP - FastenerAp - O&G Well DrillingCd - Mechanical Fatigue
Aspect of the fracture surface by scanning electron microscopy, presenting fatigue striations micromechanism. The bolt is a medium strength low alloy steel, medium carbon, quenched and tempered.
153
VIEW
ML00130 / Jun.2018
Fatigue Fracture of Overloaded Bolts
M - Low Alloy Medium Carbon QTP - FastenerAp - O&G Well DrillingCd - Mechanical Fatigue
Cm - Fractography by SEMDf - Fatigue Fracture
Detailed fractographic aspect of the flat part of the bolt fracture, presenting fatigue striations. The bolt is a medium strength low alloy steel, medium carbon, quenched and tempered.
141
VIEW
ML00130 / Jun.2018
Fatigue Fracture of Overloaded Bolts
M - Low Alloy Medium Carbon QTP - FastenerAp - O&G Well DrillingCd - Mechanical Fatigue
Cm - Fractography by SEMDf - Fatigue Fracture