Crevice Corrosion in a Subsea System — Aspect Before Analysis

170 images

TryRefineryML00081corrosionEnergyML00116brittle fractureFerritic pearliticductile behaviorFerritic BainiticfatigueRaw MaterialhydrogenFinished Productfractureembrittlementstress corrosion
Condition: Fabrication Defect Standard: A clear all
M

Material

79 classified

Browse all Material →
P

Product

96 classified

Browse all Product →
Ap

Application

37 classified

Browse all Application →
C

Condition

84 classified

Browse all Condition →
Cm

Capture method

52 classified

Browse all Capture method →
Df

Detail focus

208 classified

Browse all Detail focus →

Sharpest next filters

Browse by category (1)
Microstructure17
+9 more

The Materials
Image Database

170 images
The drilling connector, 21" diameter, presented a crack at the margin of the weld in the forging side (left side of the weld in the figure).
745
VIEW
ML00178 / Jan.2022
Cold cracks in Cr-Mo Welded Forging
M - CrMo SteelP - ForgingAp - O&G Well DrillingCd - Welding Defect
Cm - Aspect Before AnalysisDf - General View
Macrography of the longitudinally seam weld of the 24" diameter tube, showing that it was welded from both sides and there is a segregation line in the center of the tube thickness.
737
VIEW
ML00177 / Dec.2021
Cr-Mo Seam Welded Tube
M - CrMo SteelP - Longitudinally Seam WeldedAp - Fired HeaterCd - Not according to spec
Cm - NItal Etched MacroDf - Seam
Aspect of the barrel nut that is broken in a brittle way (without plastic deformation). The Nut diameter is 1", the nut length is 2" and the bolt thread is 1/2" (nominal diameter).
753
VIEW
ML00148 / Sep.2018
Brittle Fracture of a 420 SS Barrel Nut
M - Martensitic Stainless SteelP - Barrel NutAp - LiftingCd - Heat Treatment Defect
Cm - Aspect Before AnalysisDf - General View
Fractographic detail of the longitudinal Charpy V testpiece, broken at -46°C and presenting energy of 64J (the average energy of three tespieces was 70J). The Charpy V testpiece was removed from the center of the bar. The micromechanism is quasicleavage and the test in this direction presented energy values superior than the minimum requirement of 45J.
944
VIEW
ML00123 / Feb.2018
Non Qualified Superduplex for Subsea
M - Super Duplex Stainless SteelP - BarAp - Oil and GasCd - Not according to spec
Cm - Fractography by SEMDf - Broken Testpiece
Micrography of a transverse section of the pipe, external diameter 33.4 mm schedule XXS, in the center of the 9.1 mm thickness. The structure is predominantly ferritic. Small amount of pearlite.
553
VIEW
ML00112 / Dec.2017
1" XXS Pipe Not Qualified For Low Temp
M - Low Carbon SteelP - Seamless PipeAp - RefineryCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Predominantly Ferritic
Micrography of a transverse section of the pipe, external diameter 26.7 mm, in the center of the 7.85mm thickness. Refined structure but not uniform. Ferrite and pearlite.
512
VIEW
ML00111 / Dec.2017
3/4" XXS Pipe Not Qualified for Low Temp
M - Low Carbon SteelP - Seamless PipeAp - RefineryCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Micrographic detail of the forging lap defect that appears at the nut surface like a crack, filled with oxides. The nut presented a martensitic structure in the center of the nut, but in the regions adjacent to the defect the structure is ferritic-bainitic due to decarburization. There are several globular oxides (grey spots) that became entrapped during the forging.
654
VIEW
ML00099 / Jan.2018
Forging Defect in a Cadmium Plated Nut
M - Medium Carbon SteelP - NutAp - PipingCd - Fabrication Defect
Cm - Nital Etched Micrography by OMDf - Crack
Macrography showing the different regions of a pipe-to-plate fillet weld. See the schematic drawing in the next image
954
VIEW
ML00052 / Apr.2017
Cold Cracks in API 5CT L80 Tube Welded to a Structural Part
M - Low Alloy SteelP - Seamless tubeAp - OffshoreCd - Welding Defect
Cm - NItal Etched MacroDf - Fracture

More from these cases

ML00178 — Cold cracks in Cr-Mo Welded ForgingM - CrMo SteelP - ForgingAp - O&G Well DrillingCd - Welding Defect
Circumferential weld aspect. Two passes in the cap. This forging to pipe welded joint, 22 mm thick, was welded by an automatic process in a narrow gap. The pipe is to the top of the image and the forging is to the bottom of the image.
165
VIEW
ML00178 / Jan.2022
Cold cracks in Cr-Mo Welded Forging
M - CrMo SteelP - ForgingAp - O&G Well DrillingCd - Welding Defect
Cm - Aspect Before AnalysisDf - External Surface
The dye check image shows the detected crack, 50 mm long, at the margin of the weld in the forging side.
137
VIEW
ML00178 / Jan.2022
Cold cracks in Cr-Mo Welded Forging
M - CrMo SteelP - ForgingAp - O&G Well DrillingCd - Welding Defect
Cm - Aspect by NDTDf - Cracking
Macrography of the welded joint between the forging and the pipe, showing it was welded in a narrow gap, indicating by the arrow the location of the crack at the margin of the weld, in the forging side.
129
VIEW
ML00178 / Jan.2022
Cold cracks in Cr-Mo Welded Forging
M - CrMo SteelP - ForgingAp - O&G Well DrillingCd - Welding Defect
Cm - NItal Etched MacroDf - Welded Joint
Quenched and tempered structure of the F22 steel forging, presenting about 230HV10 average hardness.
133
VIEW
ML00178 / Jan.2022
Cold cracks in Cr-Mo Welded Forging
M - CrMo SteelP - ForgingAp - O&G Well DrillingCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Base Metal
Tempered martensitic structure for the F22 forging base metal.
129
VIEW
ML00178 / Jan.2022
Cold cracks in Cr-Mo Welded Forging
M - CrMo SteelP - ForgingAp - O&G Well DrillingCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Tempered Martensite

+14 more from this case →

ML00177 — Cr-Mo Seam Welded TubeM - CrMo SteelP - Longitudinally Seam WeldedAp - Fired HeaterCd - Not according to spec
Identification of the regions of metallographies of the base metal, heat affected zone (HAZ) and weld metal. Locations in the root, in the center of the thickness and close to the tube OD (external surface).
118
VIEW
ML00177 / Dec.2021
Cr-Mo Seam Welded Tube
M - CrMo SteelP - Longitudinally Seam WeldedAp - Fired HeaterCd - Not according to spec
Cm - NItal Etched MacroDf - Welded Joint
BASE METAL SURFACE - Ferritic structure, grain refined.
90
VIEW
ML00177 / Dec.2021
Cr-Mo Seam Welded Tube
M - CrMo SteelP - Longitudinally Seam WeldedAp - Fired HeaterCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Base Metal
BASE METAL SURFACE - The micrography (transverse to the tube) presents the ferritic/pearlitic/bainitic structure.
75
VIEW
ML00177 / Dec.2021
Cr-Mo Seam Welded Tube
M - CrMo SteelP - Longitudinally Seam WeldedAp - Fired HeaterCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Granular structure
BASE METAL SURFACE - The microstructure of the base metal is ferritic/pearlitic/bainitic.
74
VIEW
ML00177 / Dec.2021
Cr-Mo Seam Welded Tube
M - CrMo SteelP - Longitudinally Seam WeldedAp - Fired HeaterCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Grain refined structure
HAZ SURFACE
72
VIEW
ML00177 / Dec.2021
Cr-Mo Seam Welded Tube
M - CrMo SteelP - Longitudinally Seam WeldedAp - Fired HeaterCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Last Bead HAZ

+20 more from this case →

ML00148 — Brittle Fracture of a 420 SS Barrel NutM - Martensitic Stainless SteelP - Barrel NutAp - LiftingCd - Heat Treatment Defect
Visual aspect of both sides of the fractures. They present a macroscopically brittle aspect, with chevron marks indicating the starting point at the thinner edge of the thread.
81
VIEW
ML00148 / Sep.2018
Brittle Fracture of a 420 SS Barrel Nut
M - Martensitic Stainless SteelP - Barrel NutAp - LiftingCd - Heat Treatment Defect
Cm - Aspect Before AnalysisDf - Fracture
The fracture is flat, in the region of the lower resistant section, presenting no macroscopic evidences of plastic deformation. The starting point of the fracture is indicated by the chevron marks.
62
VIEW
ML00148 / Sep.2018
Brittle Fracture of a 420 SS Barrel Nut
M - Martensitic Stainless SteelP - Barrel NutAp - LiftingCd - Heat Treatment Defect
Cm - Fracture Surface AspectDf - Chevron Marks
Low magnification micrography of the nut in the longitudinal section, presenting the machined internal thread and a banded microstructure.
55
VIEW
ML00148 / Sep.2018
Brittle Fracture of a 420 SS Barrel Nut
M - Martensitic Stainless SteelP - Barrel NutAp - LiftingCd - Heat Treatment Defect
Cm - Kalling Etched Micrography by OMDf - Banded Structure
Microstructural aspect of a longitudinal section of the nut, in the middle of the thickness. Martensitic structure, banded.
46
VIEW
ML00148 / Sep.2018
Brittle Fracture of a 420 SS Barrel Nut
M - Martensitic Stainless SteelP - Barrel NutAp - LiftingCd - Heat Treatment Defect
Cm - Kalling Etched Micrography by OMDf - Banded Structure
Microstructural detail of the banded structure. The rough aspect of the band is created by the carbides (better seen in the higher magnification image) in the segregation band.
38
VIEW
ML00148 / Sep.2018
Brittle Fracture of a 420 SS Barrel Nut
M - Martensitic Stainless SteelP - Barrel NutAp - LiftingCd - Heat Treatment Defect
Cm - Kalling Etched Micrography by OMDf - Banded Structure

+15 more from this case →

ML00123 — Non Qualified Superduplex for SubseaM - Super Duplex Stainless SteelP - BarAp - Oil and GasCd - Not according to spec
Fractography of the broken Charpy V testpiece, longitudinal, broken at -46°C and presenting energy of 64J (the average of three values was 70J). In this direction the material presented an energy value higher than the minimum requirement of 45J.
109
VIEW
ML00123 / Feb.2018
Non Qualified Superduplex for Subsea
M - Super Duplex Stainless SteelP - BarAp - Oil and GasCd - Not according to spec
Cm - Fractography by SEMDf - Broken Testpiece
Fractography of the Charpy V testpiece, transverse section, broken at -46°C and presenting energy of 20J (the average of three results was 33J). The coarse structure and the alignement created a condition for low energy results in this specific direction, and the material did not present the minimum requirement of 45J.
103
VIEW
ML00123 / Feb.2018
Non Qualified Superduplex for Subsea
M - Super Duplex Stainless SteelP - BarAp - Oil and GasCd - Not according to spec
Cm - Fractography by SEMDf - Broken Testpiece
Micrography of a transverse section of the forged bar in the center of the thickness. Ferrite and austenite. Coarse structure.
74
VIEW
ML00123 / Feb.2018
Non Qualified Superduplex for Subsea
M - Super Duplex Stainless SteelP - BarAp - Oil and GasCd - Not according to spec
Cm - NaOH Electrolytic Etched MicroDf - Transverse Section
Micrography of a longitudinal section of the forged bar in the center of the thickness. Ferrite and austenite. Coarse structure.
61
VIEW
ML00123 / Feb.2018
Non Qualified Superduplex for Subsea
M - Super Duplex Stainless SteelP - BarAp - Oil and GasCd - Not according to spec
Cm - NaOH Electrolytic Etched MicroDf - Longitudinal Section
Micrography of a transverse section of the forged bar in the center of the thickness. Ferrite and austenite. The ferrite amount, measured by metallographic method, manual counting, is 59%.
53
VIEW
ML00123 / Feb.2018
Non Qualified Superduplex for Subsea
M - Super Duplex Stainless SteelP - BarAp - Oil and GasCd - Not according to spec
Cm - NaOH Electrolytic Etched MicroDf - Transverse Section

+3 more from this case →

ML00112 — 1" XXS Pipe Not Qualified For Low TempM - Low Carbon SteelP - Seamless PipeAp - RefineryCd - Not according to spec
Micrography of a transverse section of the pipe, close to the external surface (OD). The pipe presented a predominatly ferritic structure.
43
VIEW
ML00112 / Dec.2017
1" XXS Pipe Not Qualified For Low Temp
M - Low Carbon SteelP - Seamless PipeAp - RefineryCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Close to the External Surface
Micrography of a transverse section of the pipe, close to the external surface (OD). The pipe presented a 0.2 mm decarburized layer, fully ferritic.
35
VIEW
ML00112 / Dec.2017
1" XXS Pipe Not Qualified For Low Temp
M - Low Carbon SteelP - Seamless PipeAp - RefineryCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Close to the External Surface
Micrography of a transverse section of the pipe, close to the external surface (OD). The pipe presented a predominatly ferritic structure.
31
VIEW
ML00112 / Dec.2017
1" XXS Pipe Not Qualified For Low Temp
M - Low Carbon SteelP - Seamless PipeAp - RefineryCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Predominantly Ferritic
Micrography of a transverse section of the pipe, close to the internal surface (ID). The pipe presented a predominatly ferritic structure.
29
VIEW
ML00112 / Dec.2017
1" XXS Pipe Not Qualified For Low Temp
M - Low Carbon SteelP - Seamless PipeAp - RefineryCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Close to the Internal Surface
Micrography of a transverse section of the pipe, close to the internal surface (ID). The pipe presented a predominatly ferritic structure.
22
VIEW
ML00112 / Dec.2017
1" XXS Pipe Not Qualified For Low Temp
M - Low Carbon SteelP - Seamless PipeAp - RefineryCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Close to the Internal Surface

+2 more from this case →

ML00111 — 3/4" XXS Pipe Not Qualified for Low TempM - Low Carbon SteelP - Seamless PipeAp - RefineryCd - Not according to spec
Micrography of a transverse section of the pipe, close to the internal surface (ID). Refined structure. Ferrite and pearlite.
64
VIEW
ML00111 / Dec.2017
3/4" XXS Pipe Not Qualified for Low Temp
M - Low Carbon SteelP - Seamless PipeAp - RefineryCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Close to the Internal Surface
Micrography of a transverse section of the pipe, close to the internal surface (ID). Refined structure, but not uniform. Ferrite and pearlite. The pearlite colonies appear in a network.
45
VIEW
ML00111 / Dec.2017
3/4" XXS Pipe Not Qualified for Low Temp
M - Low Carbon SteelP - Seamless PipeAp - RefineryCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Close to the Internal Surface
Micrography of a transverse section of the pipe, close to the internal surface (ID). Refined structure. Ferrite and pearlite. The structure is not uniform. There is a large variation in the ferritic grain size and the pearlite colonies appear forming a network.
39
VIEW
ML00111 / Dec.2017
3/4" XXS Pipe Not Qualified for Low Temp
M - Low Carbon SteelP - Seamless PipeAp - RefineryCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Micrography of a transverse section of the pipe, close to the external surface (OD). Refined structure. Ferrite and pearlite.
33
VIEW
ML00111 / Dec.2017
3/4" XXS Pipe Not Qualified for Low Temp
M - Low Carbon SteelP - Seamless PipeAp - RefineryCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Close to the External Surface
Micrography of a transverse section of the pipe, close to the external surface (OD). Refined structure. Ferrite and pearlite.
34
VIEW
ML00111 / Dec.2017
3/4" XXS Pipe Not Qualified for Low Temp
M - Low Carbon SteelP - Seamless PipeAp - RefineryCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Close to the External Surface

+2 more from this case →

ML00099 — Forging Defect in a Cadmium Plated NutM - Medium Carbon SteelP - NutAp - PipingCd - Fabrication Defect
Micrography of the nut in a section transverse to the surface indication. There are several microcracks (parallel and perpendicular to the nut surface) filled with oxides. The nut presented a martensitic microstructure in the center of the thickness and a ferritic-bainitic microstructure at surface and adjacent to the defect, due to decarburization occurred during high temperature forging.
130
VIEW
ML00099 / Jan.2018
Forging Defect in a Cadmium Plated Nut
M - Medium Carbon SteelP - NutAp - PipingCd - Fabrication Defect
Cm - Nital Etched Micrography by OMDf - Crack
The general aspect of the 1 1/8" 2H nut, presenting rejectable indications that appear like cracks, located in the face and in the lateral side of the nut.
46
VIEW
ML00099 / Jan.2018
Forging Defect in a Cadmium Plated Nut
M - Medium Carbon SteelP - NutAp - PipingCd - Fabrication Defect
Cm - Aspect Before AnalysisDf - General View
Aspect in detail of the 1 1/8" 2H nut face, presenting rejectable indications that appear like cracks.
49
VIEW
ML00099 / Jan.2018
Forging Defect in a Cadmium Plated Nut
M - Medium Carbon SteelP - NutAp - PipingCd - Fabrication Defect
Cm - Aspect Before AnalysisDf - Lap
The general aspect of the lateral side of the 1 1/8" 2H nut, presenting a rejectable indication that looks like a straight crack.
48
VIEW
ML00099 / Jan.2018
Forging Defect in a Cadmium Plated Nut
M - Medium Carbon SteelP - NutAp - PipingCd - Fabrication Defect
Cm - Aspect Before AnalysisDf - Lap
Micrographic detail of the lap at the nut surface, as polished. The 20 microns cadmium layer is evident, penetrating in the lap.
46
VIEW
ML00099 / Jan.2018
Forging Defect in a Cadmium Plated Nut
M - Medium Carbon SteelP - NutAp - PipingCd - Fabrication Defect
Cm - As polished micrographyDf - Lap

+2 more from this case →

ML00052 — Cold Cracks in API 5CT L80 Tube Welded to a Structural PartM - Low Alloy SteelP - Seamless tubeAp - OffshoreCd - Welding Defect
Schematic drawing presenting the different regions of a pipe-to-plate fillet weld.
71
VIEW
ML00052 / Apr.2017
Cold Cracks in API 5CT L80 Tube Welded to a Structural Part
M - Low Alloy SteelP - Seamless tubeAp - OffshoreCd - Welding Defect
Cm - Identification drawingDf - Fracture
Macrography of the fillet welded joint between the 3" ND tube and the 3/4" thick plate. See the schematic drawing in the next figure
56
VIEW
ML00052 / Apr.2017
Cold Cracks in API 5CT L80 Tube Welded to a Structural Part
M - Low Alloy SteelP - Seamless tubeAp - OffshoreCd - Welding Defect
Cm - NItal Etched MacroDf - Welded Joint
Schematic drawing presenting the position of the cracking, at the margin of the weld in the tube and underbead.
47
VIEW
ML00052 / Apr.2017
Cold Cracks in API 5CT L80 Tube Welded to a Structural Part
M - Low Alloy SteelP - Seamless tubeAp - OffshoreCd - Welding Defect
Cm - Identification drawingDf - Welded Joint
The micrography shows the region underbead, of the tube HAZ, responsible for the hydrogen cracking (fracture in the right side of the photo - black). The hardness of the HAZ is about 600 HV.
55
VIEW
ML00052 / Apr.2017
Cold Cracks in API 5CT L80 Tube Welded to a Structural Part
M - Low Alloy SteelP - Seamless tubeAp - OffshoreCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Cracking
Low carbon plate base metal presenting the ferritic perlitic structure.
55
VIEW
ML00052 / Apr.2017
Cold Cracks in API 5CT L80 Tube Welded to a Structural Part
M - Low Alloy SteelP - Seamless tubeAp - OffshoreCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Base Metal

+13 more from this case →

View all 170 images in the Atlas →

most recent

The location of the threaded fitting started leaking after less than five years in service. Although the corrosion rate was not high, the localized material loss in the threaded surface of the carbon steel flange allowed the connection leakage.
769
VIEW
ML00184 / Apr.2023
Dissimilar Steels in a Threaded Connection
M - Low Carbon SteelP - ForgingAp - OffshoreCd - Localized Dissolution
Cm - Aspect Before AnalysisDf - General View
Front wheel 17 x 7J of a passenger vehicle (identified as WHEEL 1) that broke during a car accident on a road.
1644
VIEW
ML00183 / Dec.2022
Ductile Behavior of an Aluminum Wheel
M - Aluminum Silicon MagnesiumP - CastingAp - AutomotiveCd - Ductile Behavior
Cm - Aspect Before AnalysisDf - General View
Tool fixture 5" long, nominal diameter 2", presenting a recess 1/2" deep from two sides. The rupture occurred about 2" from the end of the rod. Scale in milimeters.
523
VIEW
ML00182 / Jul.2022
Brittle Fracture of a LAS Fixing Rod
M - Low Alloy Medium Carbon QTP - StemAp - Mechanical IndustryCd - Brittle Fracture
Cm - Aspect Before AnalysisDf - General View
Pinion of hypoid gearbox, assembled in a 1560-mm long shaft that operated during more than 60,000 hours, and removed from service due to unacceptable wear damage.
1028
VIEW
ML00181 / Apr.2022
Wear of a Carburized Hypoid Gear
M - Low Alloy for Thermochemical TreatmentP - Pinion-crown assemblyAp - ShipCd - Wear
Cm - Aspect Before AnalysisDf - General View
Aspect of the 3 1/2" diameter tube after the water leakage in high temperature.
962
VIEW
ML00180 / Mar.2022
Local Melting of Copper Cooling Tubes
M - Pure CopperP - Cooling TubeAp - SiderurgyCd - Overheating
Cm - Aspect Before AnalysisDf - General View
2" drain line from the main 10" line. The leakage occurred at the margin of the weld, a short time after the introduction of the reinforced ribs to reduce vibration.
641
VIEW
ML00179 / Feb.2022
Hydrides in Titanium Weld
M - Unalloyed TitaniumP - In Field WeldAp - Chemical IndustryCd - Hydride Formation
Cm - Field photoDf - General View
The drilling connector, 21" diameter, presented a crack at the margin of the weld in the forging side (left side of the weld in the figure).
745
VIEW
ML00178 / Jan.2022
Cold cracks in Cr-Mo Welded Forging
M - CrMo SteelP - ForgingAp - O&G Well DrillingCd - Welding Defect
Cm - Aspect Before AnalysisDf - General View
Macrography of the longitudinally seam weld of the 24" diameter tube, showing that it was welded from both sides and there is a segregation line in the center of the tube thickness.
737
VIEW
ML00177 / Dec.2021
Cr-Mo Seam Welded Tube
M - CrMo SteelP - Longitudinally Seam WeldedAp - Fired HeaterCd - Not according to spec
Cm - NItal Etched MacroDf - Seam
The titanium rotor blade of a flowmeter broke after two years in service in an acid environment, containing H2S.
339
VIEW
ML00176 / Nov.2021
Hydride Formation in a Titanium Blade
M - Unalloyed TitaniumP - BladeAp - Oil and GasCd - Hydride Formation
Cm - Aspect Before AnalysisDf - General View
Aspect of the wire rope, 1 1/2" diameter, presenting regions of flattened areas at the surface of the outer wires. It is a 6 x 19 Seale construction, right regular lay.
552
VIEW
ML00175 / Aug.2021
Localized External Wear of a Wire Rope
M - High Carbon SteelP - Wire RopeAp - Oil and GasCd - Wear
Cm - Aspect Before AnalysisDf - General View
The carcass was manufactured using niobium stabilized plates, grade AISI 347, with circumferential welds, where the through wall cracks were detected.
300
VIEW
ML00174 / Jul.2021
Carburization of a 347 SS Welded Joint
M - Austenitic Stainless SteelP - Fabrication WeldAp - EnergyCd - Carburization
Cm - Field photoDf - General View
Aged microstructure of the HP stainless steel, modified with 1%Nb, cast fitting, tubular, operating for 6 years in a furnace which design temperature is 1100°C. The material presented a network of primary carbides, white and grey, and an austenitic matrix with coalescing secondary precipitation. Some voids. The Vickers identation indicates a hardness value about 260HV 100g in the aged austenitic matrix.
491
VIEW
ML00173 / May.2021
Welding Cracks in an Aged HP Cast Fitting
M - Heat Resistant SteelP - Cast FtittingAp - PetrochemicalCd - Welding
Cm - Kalling Etched Micrography by OMDf - Microhardness identations