THE MATERIALS ATLAS.
DISCOVER IT.

About the atlas

Crevice Corrosion in a Subsea System — Aspect Before Analysis

296 images

TryStructureML00128corrosionBoilerML00040brittle fractureDamageductile behaviorSoundfatigueFerrous AlloyshydrogenLow Alloy Steelfractureembrittlementstress corrosion
Microstructure: Ferritic pearlitic Standard: A clear all
M

Material

79 classified

Browse all Material →
P

Product

96 classified

Browse all Product →
Ap

Application

37 classified

Browse all Application →
C

Condition

84 classified

Browse all Condition →
Cm

Capture method

52 classified

Browse all Capture method →
Df

Detail focus

208 classified

Browse all Detail focus →

Sharpest next filters

The Materials
Image Database

296 images
Macrography of the longitudinally seam weld of the 24" diameter tube, showing that it was welded from both sides and there is a segregation line in the center of the tube thickness.
737
VIEW
ML00177 / Dec.2021
Cr-Mo Seam Welded Tube
M - CrMo SteelP - Longitudinally Seam WeldedAp - Fired HeaterCd - Not according to spec
Cm - NItal Etched MacroDf - Seam
Gas piping. Aspect of a branching line 2" ND, lateral to a horizontal main pipe ND 8", welded using a weldolet. The cracking started at the margin of the weld in the upper part of the pipe, where the weld crossed the longitudinal direction of the pipe, perpendicular to the branch.
932
VIEW
ML00149 / Dec.2018
Vibration Induced Fatigue in a Gas Piping
M - Low Carbon SteelP - Piping spoolAp - FPSOCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - Cracking
Red painted device where the 50 mm x 50 mm carbon steel plate was positioned (in the circle). The image presents the target, positioned 100 meters far from the gun, after the shot and the projectile perforated the plate, as will be presented in the other figures.
602
VIEW
ML00143 / Aug.2018
Impact of a .308 Winchester on A36 Plate
M - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Cm - Aspect Before AnalysisDf - General View
Fractured position of the casting cylinder of 10.5 mm thickness (minimum measured thickness) showing a brittle behavior (lack of plastic deformation), typical of overloading a material with 1% ductility (measured in the tensile test). This is the view of the internal surface of the cylinder, presenting regions of localized thinning in this surface that was in contact with (treated) cooling water. The external side of the cylinder was painted.
918
VIEW
ML00141 / Jul.2018
Brittle Fracture of a Corroded Gray Cast Iron
M - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Cm - Fracture Surface AspectDf - General View
Micrographic detail of a transverse section of the tubing, in the center of the thickness. Ferritic-pearlitic structure. Pearlite colonies in bands.
401
VIEW
ML00116 / Jan.2018
CMn Steel Structural Tubing 6 mm thick
M - CMn SteelP - Seamless Round ShapeAp - StructureCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Micrographic detail of a transverse section of the 5 mm thick tubing, in the center of the thickness. Ferritic-pearlitic structure, with the pearlite presenting a coalesced aspect. The tubing was in service at ambient temperature, painted, and the coalesced aspect was generated before service, perhaps during the tubing manufacturing.
393
VIEW
ML00115 / Jan.2018
CMn Steel Structural Tubing 5 mm thick
M - CMn SteelP - Seamless Round ShapeAp - StructureCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Micrographic detail of a transverse section of the tubing, in the center of the thickness. Ferritic-pearlitic structure. Pearlite colonies in bands.
346
VIEW
ML00114 / Jan.2018
CMn Steel Structural Tubing 8 mm thick
M - CMn SteelP - Seamless Round ShapeAp - StructureCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Micrography of a transverse section of the pipe, external diameter 33.4 mm schedule XXS, in the center of the 9.1 mm thickness. The structure is predominantly ferritic. Small amount of pearlite.
553
VIEW
ML00112 / Dec.2017
1" XXS Pipe Not Qualified For Low Temp
M - Low Carbon SteelP - Seamless PipeAp - RefineryCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Predominantly Ferritic

More from these cases

ML00177 — Cr-Mo Seam Welded TubeM - CrMo SteelP - Longitudinally Seam WeldedAp - Fired HeaterCd - Not according to spec
Identification of the regions of metallographies of the base metal, heat affected zone (HAZ) and weld metal. Locations in the root, in the center of the thickness and close to the tube OD (external surface).
118
VIEW
ML00177 / Dec.2021
Cr-Mo Seam Welded Tube
M - CrMo SteelP - Longitudinally Seam WeldedAp - Fired HeaterCd - Not according to spec
Cm - NItal Etched MacroDf - Welded Joint
BASE METAL SURFACE - Ferritic structure, grain refined.
90
VIEW
ML00177 / Dec.2021
Cr-Mo Seam Welded Tube
M - CrMo SteelP - Longitudinally Seam WeldedAp - Fired HeaterCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Base Metal
BASE METAL SURFACE - The micrography (transverse to the tube) presents the ferritic/pearlitic/bainitic structure.
75
VIEW
ML00177 / Dec.2021
Cr-Mo Seam Welded Tube
M - CrMo SteelP - Longitudinally Seam WeldedAp - Fired HeaterCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Granular structure
BASE METAL SURFACE - The microstructure of the base metal is ferritic/pearlitic/bainitic.
74
VIEW
ML00177 / Dec.2021
Cr-Mo Seam Welded Tube
M - CrMo SteelP - Longitudinally Seam WeldedAp - Fired HeaterCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Grain refined structure
HAZ SURFACE
72
VIEW
ML00177 / Dec.2021
Cr-Mo Seam Welded Tube
M - CrMo SteelP - Longitudinally Seam WeldedAp - Fired HeaterCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Last Bead HAZ

+20 more from this case →

ML00149 — Vibration Induced Fatigue in a Gas PipingM - Low Carbon SteelP - Piping spoolAp - FPSOCd - Vibration Induced Fatigue
Gas piping. Aspect of a branching line 2" ND with a flange, lateral to a main pipe ND 8", welded using a weldolet. The cracking is at the margin of the weld.
115
VIEW
ML00149 / Dec.2018
Vibration Induced Fatigue in a Gas Piping
M - Low Carbon SteelP - Piping spoolAp - FPSOCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - General View
Micrography of a transverse section of the seamless pipe, presenting a ferritic-pearlitic structure.
84
VIEW
ML00149 / Dec.2018
Vibration Induced Fatigue in a Gas Piping
M - Low Carbon SteelP - Piping spoolAp - FPSOCd - Vibration Induced Fatigue
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Micrography of a transverse section of the seamless pipe, presenting a ferritic-pearlitic structure.
70
VIEW
ML00149 / Dec.2018
Vibration Induced Fatigue in a Gas Piping
M - Low Carbon SteelP - Piping spoolAp - FPSOCd - Vibration Induced Fatigue
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Gas piping. Aspect of a branching line 2" ND, lateral to a horizontal main pipe ND 8", welded using a weldolet. In the lower part of the branch there are no cracks.
61
VIEW
ML00149 / Dec.2018
Vibration Induced Fatigue in a Gas Piping
M - Low Carbon SteelP - Piping spoolAp - FPSOCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - Welded Joint
Aspect of the brach line viewed from the internal side of the main pipe, after cuting. It is possible to see that the pipe was perforated by a thermal cutting (looking the finishing aspect of the edge of the hole). The weldolet was welded only from the external side of the pipe.
62
VIEW
ML00149 / Dec.2018
Vibration Induced Fatigue in a Gas Piping
M - Low Carbon SteelP - Piping spoolAp - FPSOCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - Internal Surface

+13 more from this case →

ML00143 — Impact of a .308 Winchester on A36 PlateM - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Aspect of a typical .308 Winchester projectile, similar to the one adopted to shot the plate, cut in a longitudinal section. It is a Cu alloy case filled with Pb-Sb.
92
VIEW
ML00143 / Aug.2018
Impact of a .308 Winchester on A36 Plate
M - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Cm - Longitudinal Section AspectDf - Longitudinal Section
Aspect of the 3/8" thickness plate, 50 mm x 50 mm, of the low carbon steel steel, in the face of impact with the projectile. The plate was perforated by the bullet.
88
VIEW
ML00143 / Aug.2018
Impact of a .308 Winchester on A36 Plate
M - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Cm - Aspect Before AnalysisDf - General View
Micrography of the plate in a section, showing a ferritic-pearlitic microstructure in the middle of the thickness.
84
VIEW
ML00143 / Aug.2018
Impact of a .308 Winchester on A36 Plate
M - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Micrography of the plate in a section, showing a ferritic-pearlitic microstructure in the middle of the thickness, in a position where the plate was not affected by the shot.
65
VIEW
ML00143 / Aug.2018
Impact of a .308 Winchester on A36 Plate
M - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Micrographic detail of the plate in a section, showing a ferritic-pearlitic microstructure in the middle of the thickness.
66
VIEW
ML00143 / Aug.2018
Impact of a .308 Winchester on A36 Plate
M - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite

+51 more from this case →

ML00141 — Brittle Fracture of a Corroded Gray Cast IronM - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Fracture aspect of the casting cylinder at the 10.5 mm thickness, showing a brittle behavior (lack of plastic deformation). The internal side of the cylinder is to the top of the figure, and the painted surface is to the bottom of the figure.
129
VIEW
ML00141 / Jul.2018
Brittle Fracture of a Corroded Gray Cast Iron
M - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Cm - Fracture Surface AspectDf - Brittle Fracture
Detailed aspect of the cylinder fracture, the internal surface to the top of the figure and the painted external surface to the bottom of the figure.
103
VIEW
ML00141 / Jul.2018
Brittle Fracture of a Corroded Gray Cast Iron
M - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Cm - Fracture Surface AspectDf - Brittle Fracture
Macrographic aspect of a section of the cast cylinder, transverse to the fracture (top). The internal diameter of the cylinder (exposed to treated water) is to the left side and the external diameter of the cylinder (painted) is to the right side.
96
VIEW
ML00141 / Jul.2018
Brittle Fracture of a Corroded Gray Cast Iron
M - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Cm - NItal Etched MacroDf - Brittle Fracture
Micrographic aspect, as polished, of the cast cylinder section at the fracture position (top of the figure), close to the internal surface (left side). It is possible to see large graphite flakes.
98
VIEW
ML00141 / Jul.2018
Brittle Fracture of a Corroded Gray Cast Iron
M - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Cm - As polished micrographyDf - Close to the Internal Surface
Micrographic aspect, as polished, of the cast cylinder section at the fracture position (top of the figure), in the center of the thickness. It is possible to see a mixture of large graphite flakes and rosette grouping flakes.
80
VIEW
ML00141 / Jul.2018
Brittle Fracture of a Corroded Gray Cast Iron
M - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Cm - As polished micrographyDf - In the Center of the Thickness

+30 more from this case →

ML00116 — CMn Steel Structural Tubing 6 mm thickM - CMn SteelP - Seamless Round ShapeAp - StructureCd - Removed From Service
Low magnification micrography of a transverse section of the tubing, in the center of the thickness. Ferritic-pearlitic banded structure.
30
VIEW
ML00116 / Jan.2018
CMn Steel Structural Tubing 6 mm thick
M - CMn SteelP - Seamless Round ShapeAp - StructureCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Banded Structure
Micrography of a transverse section of the tubing, in the center of the thickness. Ferritic-pearlitic structure. Bands of pearlite colonies. Refined grains.
26
VIEW
ML00116 / Jan.2018
CMn Steel Structural Tubing 6 mm thick
M - CMn SteelP - Seamless Round ShapeAp - StructureCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - In the Center of the Thickness
Micrography of a transverse section of the tubing in the center of the thickness. Ferritic-pearlitic structure. The structure is fully ferritic in a small extension at the surface, due to a decarburization effect during manufacturing.
26
VIEW
ML00116 / Jan.2018
CMn Steel Structural Tubing 6 mm thick
M - CMn SteelP - Seamless Round ShapeAp - StructureCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Close to the External Surface
Micrographic detail of a transverse section of the tubing, close to the internal surface. Ferritic-pearlitic structure, refined.
20
VIEW
ML00116 / Jan.2018
CMn Steel Structural Tubing 6 mm thick
M - CMn SteelP - Seamless Round ShapeAp - StructureCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Close to the Internal Surface
ML00115 — CMn Steel Structural Tubing 5 mm thickM - CMn SteelP - Seamless Round ShapeAp - StructureCd - Removed From Service
Low magnification micrography of a transverse section of the tubing, in the center of the thickness. Banded structure, ferritic-pearlitic.
16
VIEW
ML00115 / Jan.2018
CMn Steel Structural Tubing 5 mm thick
M - CMn SteelP - Seamless Round ShapeAp - StructureCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Banded Structure
Micrography of a transverse section of the tubing, in the center of the thickness. Ferritic-pearlitic structure. The pearlite is banded and presented a coalesced aspect.
12
VIEW
ML00115 / Jan.2018
CMn Steel Structural Tubing 5 mm thick
M - CMn SteelP - Seamless Round ShapeAp - StructureCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - In the Center of the Thickness
Micrographic detail of a transverse section of the tubing, at the external surface. Ferritic-pearlitic structure. The roughness of the surface is high because the structure was painted and a blasting treatment was probably applied to the surface to improve adherence.
15
VIEW
ML00115 / Jan.2018
CMn Steel Structural Tubing 5 mm thick
M - CMn SteelP - Seamless Round ShapeAp - StructureCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Close to the External Surface
Micrographic detail of a transverse section of the tubing, close to the internal surface. Ferritic-pearlitic structure. Very close to the surface the amount of ferrite is higher than in the center and the grain is coarser, due to a decarburization effect probably occurred when the surface was exposed to high temperature during manufacturing.
13
VIEW
ML00115 / Jan.2018
CMn Steel Structural Tubing 5 mm thick
M - CMn SteelP - Seamless Round ShapeAp - StructureCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Close to the Internal Surface
ML00114 — CMn Steel Structural Tubing 8 mm thickM - CMn SteelP - Seamless Round ShapeAp - StructureCd - Removed From Service
Low magnification micrography of a transverse section of the tubing, in the center of the thickness. Ferritic-pearlitic banded structure.
29
VIEW
ML00114 / Jan.2018
CMn Steel Structural Tubing 8 mm thick
M - CMn SteelP - Seamless Round ShapeAp - StructureCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Banded Structure
Micrography of a transverse section of the tubing, in the center of the thickness. Ferritic-pearlitic structure. Bands of pearlite colonies. Refined grains.
29
VIEW
ML00114 / Jan.2018
CMn Steel Structural Tubing 8 mm thick
M - CMn SteelP - Seamless Round ShapeAp - StructureCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - In the Center of the Thickness
Micrography of a transverse section of the tubing, at the external surface. Ferritic-pearlitic structure. The roughness of the surface is high because the structure was painted and a blasting treatment was probably applied to the surface to improve adherence.
20
VIEW
ML00114 / Jan.2018
CMn Steel Structural Tubing 8 mm thick
M - CMn SteelP - Seamless Round ShapeAp - StructureCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Close to the External Surface
Micrography of a transverse section of the tubing, close to the internal surface. Ferritic-pearlitic structure, refined.
16
VIEW
ML00114 / Jan.2018
CMn Steel Structural Tubing 8 mm thick
M - CMn SteelP - Seamless Round ShapeAp - StructureCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Close to the Internal Surface
ML00112 — 1" XXS Pipe Not Qualified For Low TempM - Low Carbon SteelP - Seamless PipeAp - RefineryCd - Not according to spec
Micrography of a transverse section of the pipe, close to the external surface (OD). The pipe presented a predominatly ferritic structure.
43
VIEW
ML00112 / Dec.2017
1" XXS Pipe Not Qualified For Low Temp
M - Low Carbon SteelP - Seamless PipeAp - RefineryCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Close to the External Surface
Micrography of a transverse section of the pipe, close to the external surface (OD). The pipe presented a 0.2 mm decarburized layer, fully ferritic.
35
VIEW
ML00112 / Dec.2017
1" XXS Pipe Not Qualified For Low Temp
M - Low Carbon SteelP - Seamless PipeAp - RefineryCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Close to the External Surface
Micrography of a transverse section of the pipe, close to the external surface (OD). The pipe presented a predominatly ferritic structure.
31
VIEW
ML00112 / Dec.2017
1" XXS Pipe Not Qualified For Low Temp
M - Low Carbon SteelP - Seamless PipeAp - RefineryCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Predominantly Ferritic
Micrography of a transverse section of the pipe, close to the internal surface (ID). The pipe presented a predominatly ferritic structure.
29
VIEW
ML00112 / Dec.2017
1" XXS Pipe Not Qualified For Low Temp
M - Low Carbon SteelP - Seamless PipeAp - RefineryCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Close to the Internal Surface
Micrography of a transverse section of the pipe, close to the internal surface (ID). The pipe presented a predominatly ferritic structure.
22
VIEW
ML00112 / Dec.2017
1" XXS Pipe Not Qualified For Low Temp
M - Low Carbon SteelP - Seamless PipeAp - RefineryCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Close to the Internal Surface

+2 more from this case →

View all 296 images in the Atlas →

most recent

The location of the threaded fitting started leaking after less than five years in service. Although the corrosion rate was not high, the localized material loss in the threaded surface of the carbon steel flange allowed the connection leakage.
769
VIEW
ML00184 / Apr.2023
Dissimilar Steels in a Threaded Connection
M - Low Carbon SteelP - ForgingAp - OffshoreCd - Localized Dissolution
Cm - Aspect Before AnalysisDf - General View
Front wheel 17 x 7J of a passenger vehicle (identified as WHEEL 1) that broke during a car accident on a road.
1644
VIEW
ML00183 / Dec.2022
Ductile Behavior of an Aluminum Wheel
M - Aluminum Silicon MagnesiumP - CastingAp - AutomotiveCd - Ductile Behavior
Cm - Aspect Before AnalysisDf - General View
Tool fixture 5" long, nominal diameter 2", presenting a recess 1/2" deep from two sides. The rupture occurred about 2" from the end of the rod. Scale in milimeters.
523
VIEW
ML00182 / Jul.2022
Brittle Fracture of a LAS Fixing Rod
M - Low Alloy Medium Carbon QTP - StemAp - Mechanical IndustryCd - Brittle Fracture
Cm - Aspect Before AnalysisDf - General View
Pinion of hypoid gearbox, assembled in a 1560-mm long shaft that operated during more than 60,000 hours, and removed from service due to unacceptable wear damage.
1028
VIEW
ML00181 / Apr.2022
Wear of a Carburized Hypoid Gear
M - Low Alloy for Thermochemical TreatmentP - Pinion-crown assemblyAp - ShipCd - Wear
Cm - Aspect Before AnalysisDf - General View
Aspect of the 3 1/2" diameter tube after the water leakage in high temperature.
962
VIEW
ML00180 / Mar.2022
Local Melting of Copper Cooling Tubes
M - Pure CopperP - Cooling TubeAp - SiderurgyCd - Overheating
Cm - Aspect Before AnalysisDf - General View
2" drain line from the main 10" line. The leakage occurred at the margin of the weld, a short time after the introduction of the reinforced ribs to reduce vibration.
641
VIEW
ML00179 / Feb.2022
Hydrides in Titanium Weld
M - Unalloyed TitaniumP - In Field WeldAp - Chemical IndustryCd - Hydride Formation
Cm - Field photoDf - General View
The drilling connector, 21" diameter, presented a crack at the margin of the weld in the forging side (left side of the weld in the figure).
744
VIEW
ML00178 / Jan.2022
Cold cracks in Cr-Mo Welded Forging
M - CrMo SteelP - ForgingAp - O&G Well DrillingCd - Welding Defect
Cm - Aspect Before AnalysisDf - General View
Macrography of the longitudinally seam weld of the 24" diameter tube, showing that it was welded from both sides and there is a segregation line in the center of the tube thickness.
737
VIEW
ML00177 / Dec.2021
Cr-Mo Seam Welded Tube
M - CrMo SteelP - Longitudinally Seam WeldedAp - Fired HeaterCd - Not according to spec
Cm - NItal Etched MacroDf - Seam
The titanium rotor blade of a flowmeter broke after two years in service in an acid environment, containing H2S.
339
VIEW
ML00176 / Nov.2021
Hydride Formation in a Titanium Blade
M - Unalloyed TitaniumP - BladeAp - Oil and GasCd - Hydride Formation
Cm - Aspect Before AnalysisDf - General View
Aspect of the wire rope, 1 1/2" diameter, presenting regions of flattened areas at the surface of the outer wires. It is a 6 x 19 Seale construction, right regular lay.
552
VIEW
ML00175 / Aug.2021
Localized External Wear of a Wire Rope
M - High Carbon SteelP - Wire RopeAp - Oil and GasCd - Wear
Cm - Aspect Before AnalysisDf - General View
The carcass was manufactured using niobium stabilized plates, grade AISI 347, with circumferential welds, where the through wall cracks were detected.
300
VIEW
ML00174 / Jul.2021
Carburization of a 347 SS Welded Joint
M - Austenitic Stainless SteelP - Fabrication WeldAp - EnergyCd - Carburization
Cm - Field photoDf - General View
Aged microstructure of the HP stainless steel, modified with 1%Nb, cast fitting, tubular, operating for 6 years in a furnace which design temperature is 1100°C. The material presented a network of primary carbides, white and grey, and an austenitic matrix with coalescing secondary precipitation. Some voids. The Vickers identation indicates a hardness value about 260HV 100g in the aged austenitic matrix.
491
VIEW
ML00173 / May.2021
Welding Cracks in an Aged HP Cast Fitting
M - Heat Resistant SteelP - Cast FtittingAp - PetrochemicalCd - Welding
Cm - Kalling Etched Micrography by OMDf - Microhardness identations

Partners

Companies involved

TECMETAL