Optical Microscope

183 cases · 1637 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Optical Microscope — sub-branches

As polished micrography 128Chromic Acid Electrolytic Etched 7Eletrolytically Etched Micrography by OM 11FeCl3+HCl+Ethanol Etched Micro 15FeCl3+HCl+H2O Etched Micro 28Glyceregia Etched Micrography by OM 7H2SO4+HNO3+H3PO4 Etched Micro 4Kalling Etched Micrography by OM 202Keller Etched Micrography by OM 58Kroll Etched Micrography by OM 15Micro by OM, HCl + Ethanol + Picric Acid 12Micro by OM, picric acid+FeCl3+H2O etch 4Micrography by OM 73Micrography by OM using A262 Method A 80Micrography by OM, HF + HNO3 + H2O etch 8NH4OH+H2O+H2O2 Etched Micro 8NaOH Electrolytic Etched Micro 108Nital Etched Micrography by OM 801Oxalic Acid Electrolytic Etch 68

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrographic aspect of the corrosion damage in a section transverse to the pitting.
167
VIEW
ML00054 / Dec.2018
Cutlery Corrosion
M - Martensitic Stainless SteelP - Foodstuff ArticleAp - KitchenCd - Pitting Corrosion
Cm - Kalling Etched Micrography by OMDf - Pitting
The micrography of the pipe in the longitudinal section shows an aligned structure.
60
VIEW
ML00053 / Mar.2017
SAW Longitudinal Seam of X70 Pipe
M - Microalloyed SteelP - Longitudinal Seam Welded PipeAp - SubseaCd - Welding
Cm - Nital Etched Micrography by OMDf - Base Metal
Micrographic detail of the fatigue cracking at the margin of the flange to shell fillet weld.
484
VIEW
ML00050 / Nov.2017
Fatigue Failure of a 316SS Pressure Stabilizer
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Mechanical Fatigue
Cm - Micrography by OM using A262 Method ADf - Fatigue Crack
Micrography of the shell plate in the longitudinal section. Ferritic-perlitic microstructure.
96
VIEW
ML00019 / Apr.2017
Transgranular SCC in Boiler Steam Drum
M - CMn SteelP - Rolled PlateAp - BoilerCd - Stress Corrosion
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Micrography of the pipe base metal presenting a refined duplex ferritic austenitc structure, banded.
47
VIEW
ML00049 / Apr.2017
Pipe to Flange Welded Joint in a 14" ND Superduplex Spool
M - Super Duplex Stainless SteelP - Piping spoolAp - Oil and GasCd - Removed From Service
Cm - NaOH Electrolytic Etched MicroDf - Duplex structure
Typical branched stress corrosion cracks in a low carbon steel, ferritic-pertlitic structure. The cracks are filled with corrosion products.
771
VIEW
ML00018 / Apr.2017
SCC in Boiler Steam Drum
M - Low Carbon SteelP - Rolled PlateAp - BoilerCd - Stress Corrosion
Cm - Nital Etched Micrography by OMDf - Branched Cracks
Pin A micrography presenting a ferritic-perlitic structure.
463
VIEW
ML00048 / Apr.2017
Medium Carbon Steel Pins of Electrical Insulators
M - Medium Carbon SteelP - Forged PinAp - EnergyCd - Typical manufacturing
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Micrography of CAP A, showing graphite in imperfect nodules and ferritic matrix.
481
VIEW
ML00047 / Mar.2017
Ductile Cast Iron Caps of Electrical Insulators
M - Ductile Cast IronP - Cast iron capAp - EnergyCd - Typical manufacturing
Cm - Nital Etched Micrography by OMDf - Graphite in Imperfect Nodules

More from these cases

ML00053 — SAW Longitudinal Seam of X70 PipeM - Microalloyed SteelP - Longitudinal Seam Welded PipeAp - SubseaCd - Welding
Detail of the microstructure in the center of the plate, in the longitudinal section. The structure is refined and presents different ferritic grain sizes.
49
VIEW
ML00053 / Mar.2017
SAW Longitudinal Seam of X70 Pipe
M - Microalloyed SteelP - Longitudinal Seam Welded PipeAp - SubseaCd - Welding
Cm - Nital Etched Micrography by OMDf - Base Metal
Detail of the microstructure in the center of the plate, in the longitudinal section. The ferritic structure is refined and presents different grain sizes. Carbides are presented in different morphologies (perlite, precipitated) and there are probably microphases (aligned in a central segregation line).
55
VIEW
ML00053 / Mar.2017
SAW Longitudinal Seam of X70 Pipe
M - Microalloyed SteelP - Longitudinal Seam Welded PipeAp - SubseaCd - Welding
Cm - Nital Etched Micrography by OMDf - Base Metal
Micrographic detail of the fusion line of the second pass (not reheated). The HAZ is bainitic and the weld metal microstructure is predominantly formed by acicular ferrite.
51
VIEW
ML00053 / Mar.2017
SAW Longitudinal Seam of X70 Pipe
M - Microalloyed SteelP - Longitudinal Seam Welded PipeAp - SubseaCd - Welding
Cm - Nital Etched Micrography by OMDf - Fusion Line
Center of the weld in the second pass. Columnar grains of the previous austenite.
45
VIEW
ML00053 / Mar.2017
SAW Longitudinal Seam of X70 Pipe
M - Microalloyed SteelP - Longitudinal Seam Welded PipeAp - SubseaCd - Welding
Cm - Nital Etched Micrography by OMDf - Weld Metal
Fusion line of the first pass (reheated in high temperature). The HAZ is bainitic and the weld metal microstructure is predominantly formed by acicular ferrite.
43
VIEW
ML00053 / Mar.2017
SAW Longitudinal Seam of X70 Pipe
M - Microalloyed SteelP - Longitudinal Seam Welded PipeAp - SubseaCd - Welding
Cm - Nital Etched Micrography by OMDf - Fusion Line

+6 more from this case →

ML00050 — Fatigue Failure of a 316SS Pressure StabilizerM - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Mechanical Fatigue
The shell plate micrography showed an austenitic structure.
101
VIEW
ML00050 / Nov.2017
Fatigue Failure of a 316SS Pressure Stabilizer
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Mechanical Fatigue
Cm - Micrography by OM using A262 Method ADf - Austenite
The micrography of the welded joint between the flange and the shell, in a region that was through wall cracked, the fracture propagating in the shell plate base metal.
74
VIEW
ML00050 / Nov.2017
Fatigue Failure of a 316SS Pressure Stabilizer
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Mechanical Fatigue
Cm - Micrography by OM using A262 Method ADf - Welded Joint
The micrography of the welded joint between the flange and the shell, in a region that was not yet macroscopically cracked, presented a fatigue crack from the margin of the fillet weld.
71
VIEW
ML00050 / Nov.2017
Fatigue Failure of a 316SS Pressure Stabilizer
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Mechanical Fatigue
Cm - Micrography by OM using A262 Method ADf - Welded Joint
ML00019 — Transgranular SCC in Boiler Steam DrumM - CMn SteelP - Rolled PlateAp - BoilerCd - Stress Corrosion
Micrographic detail of the shell plate in the longitudinal section. Ferritic-perlitic microstructure.
89
VIEW
ML00019 / Apr.2017
Transgranular SCC in Boiler Steam Drum
M - CMn SteelP - Rolled PlateAp - BoilerCd - Stress Corrosion
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Micrography of the cracking showing the branched nature, typical of a stress corrosion cracking. The cracks started from the internal surface of the steam drum.
94
VIEW
ML00019 / Apr.2017
Transgranular SCC in Boiler Steam Drum
M - CMn SteelP - Rolled PlateAp - BoilerCd - Stress Corrosion
Cm - Nital Etched Micrography by OMDf - Branched Cracks
Micrographic detail of the cracking showing the branched nature, typical of a stress corrosion cracking. The cracks presented a transgranular morphology
86
VIEW
ML00019 / Apr.2017
Transgranular SCC in Boiler Steam Drum
M - CMn SteelP - Rolled PlateAp - BoilerCd - Stress Corrosion
Cm - Nital Etched Micrography by OMDf - Transgranular Crack
Micrographic detail of the transgranular stress corrosion cracking.
80
VIEW
ML00019 / Apr.2017
Transgranular SCC in Boiler Steam Drum
M - CMn SteelP - Rolled PlateAp - BoilerCd - Stress Corrosion
Cm - Nital Etched Micrography by OMDf - Transgranular Crack
Micrographic detail of the transgranular stress corrosion cracking.
157
VIEW
ML00019 / Apr.2017
Transgranular SCC in Boiler Steam Drum
M - CMn SteelP - Rolled PlateAp - BoilerCd - Stress Corrosion
Cm - Nital Etched Micrography by OMDf - Transgranular Crack
ML00049 — Pipe to Flange Welded Joint in a 14" ND Superduplex SpoolM - Super Duplex Stainless SteelP - Piping spoolAp - Oil and GasCd - Removed From Service
Micrographic detail of the pipe base metal presenting a refined duplex ferritic austenitc structure, banded.
55
VIEW
ML00049 / Apr.2017
Pipe to Flange Welded Joint in a 14" ND Superduplex Spool
M - Super Duplex Stainless SteelP - Piping spoolAp - Oil and GasCd - Removed From Service
Cm - NaOH Electrolytic Etched MicroDf - Base Metal
Micrographic detail of the pipe base metal presenting a refined duplex ferritic austenitc structure, banded.
56
VIEW
ML00049 / Apr.2017
Pipe to Flange Welded Joint in a 14" ND Superduplex Spool
M - Super Duplex Stainless SteelP - Piping spoolAp - Oil and GasCd - Removed From Service
Cm - NaOH Electrolytic Etched MicroDf - Duplex structure
Micrography of the flange base metal presenting a coarse duplex ferritic austenitc structure.
88
VIEW
ML00049 / Apr.2017
Pipe to Flange Welded Joint in a 14" ND Superduplex Spool
M - Super Duplex Stainless SteelP - Piping spoolAp - Oil and GasCd - Removed From Service
Cm - NaOH Electrolytic Etched MicroDf - Duplex structure
Micrographic detail of the flange base metal presenting a coarse duplex ferritic austenitc structure. Detrimental phases associated to the ferritic structure.
62
VIEW
ML00049 / Apr.2017
Pipe to Flange Welded Joint in a 14" ND Superduplex Spool
M - Super Duplex Stainless SteelP - Piping spoolAp - Oil and GasCd - Removed From Service
Cm - NaOH Electrolytic Etched MicroDf - Duplex structure
Micrography of the pipe heat affected zone. In the left the pipe base metal, with banded duplex structure; and in the right the weld metal, with Widmanstatten morphology of the structure.
43
VIEW
ML00049 / Apr.2017
Pipe to Flange Welded Joint in a 14" ND Superduplex Spool
M - Super Duplex Stainless SteelP - Piping spoolAp - Oil and GasCd - Removed From Service
Cm - NaOH Electrolytic Etched MicroDf - Heat Affected Zone

+11 more from this case →

ML00018 — SCC in Boiler Steam DrumM - Low Carbon SteelP - Rolled PlateAp - BoilerCd - Stress Corrosion
Ferritic perlitic structure of the shell plate.
207
VIEW
ML00018 / Apr.2017
SCC in Boiler Steam Drum
M - Low Carbon SteelP - Rolled PlateAp - BoilerCd - Stress Corrosion
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Micrography of the crack at the internal surface of the steam drum. The shell plate presents a ferritic perlitic structure.
162
VIEW
ML00018 / Apr.2017
SCC in Boiler Steam Drum
M - Low Carbon SteelP - Rolled PlateAp - BoilerCd - Stress Corrosion
Cm - Nital Etched Micrography by OMDf - Branched Cracks
Micrography of a crack, in a sample as polished, presenting the opened crack.
144
VIEW
ML00018 / Apr.2017
SCC in Boiler Steam Drum
M - Low Carbon SteelP - Rolled PlateAp - BoilerCd - Stress Corrosion
Cm - Micrography by OMDf - Branched Cracks
Stress corrosion cracks propagating in the ferritic-perlitic structure.
120
VIEW
ML00018 / Apr.2017
SCC in Boiler Steam Drum
M - Low Carbon SteelP - Rolled PlateAp - BoilerCd - Stress Corrosion
Cm - Nital Etched Micrography by OMDf - Branched Cracks
Micrography of a crack, as polished, presenting the cracks filled with corrosion products.
100
VIEW
ML00018 / Apr.2017
SCC in Boiler Steam Drum
M - Low Carbon SteelP - Rolled PlateAp - BoilerCd - Stress Corrosion
Cm - Micrography by OMDf - Branched Cracks

+2 more from this case →

ML00048 — Medium Carbon Steel Pins of Electrical InsulatorsM - Medium Carbon SteelP - Forged PinAp - EnergyCd - Typical manufacturing
Detail of Pin A microstructure. Ferritic-perlitic.
138
VIEW
ML00048 / Apr.2017
Medium Carbon Steel Pins of Electrical Insulators
M - Medium Carbon SteelP - Forged PinAp - EnergyCd - Typical manufacturing
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Pin B micrography presenting a ferritic-bainitic structure.
97
VIEW
ML00048 / Apr.2017
Medium Carbon Steel Pins of Electrical Insulators
M - Medium Carbon SteelP - Forged PinAp - EnergyCd - Typical manufacturing
Cm - Nital Etched Micrography by OMDf - Ferrite and Bainite
Detail of Pin B microstructure. Ferritic-bainitic.
87
VIEW
ML00048 / Apr.2017
Medium Carbon Steel Pins of Electrical Insulators
M - Medium Carbon SteelP - Forged PinAp - EnergyCd - Typical manufacturing
Cm - Nital Etched Micrography by OMDf - Ferrite and Bainite
ML00047 — Ductile Cast Iron Caps of Electrical InsulatorsM - Ductile Cast IronP - Cast iron capAp - EnergyCd - Typical manufacturing
Detail of CAP A microstructure. Graphite in imperfect nodules and ferritic matrix. Grey sulphide inclusions.
90
VIEW
ML00047 / Mar.2017
Ductile Cast Iron Caps of Electrical Insulators
M - Ductile Cast IronP - Cast iron capAp - EnergyCd - Typical manufacturing
Cm - Nital Etched Micrography by OMDf - Predominantly Ferritic
Micrography of CAP B, showing graphite in nodules and ferritic matrix.
67
VIEW
ML00047 / Mar.2017
Ductile Cast Iron Caps of Electrical Insulators
M - Ductile Cast IronP - Cast iron capAp - EnergyCd - Typical manufacturing
Cm - Nital Etched Micrography by OMDf - Graphite in Nodules
Detail of CAP B microstructure. Graphite in nodules and ferritic matrix. Small sulphide inclusions (grey).
60
VIEW
ML00047 / Mar.2017
Ductile Cast Iron Caps of Electrical Insulators
M - Ductile Cast IronP - Cast iron capAp - EnergyCd - Typical manufacturing
Cm - Nital Etched Micrography by OMDf - Predominantly Ferritic
Micrography of CAP C, showing graphite in nodules and ferritic-perlitic matrix.
52
VIEW
ML00047 / Mar.2017
Ductile Cast Iron Caps of Electrical Insulators
M - Ductile Cast IronP - Cast iron capAp - EnergyCd - Typical manufacturing
Cm - Nital Etched Micrography by OMDf - Graphite in Nodules
Detail of CAP C microstructure. Graphite in nodules and ferritic-perlitic matrix.
56
VIEW
ML00047 / Mar.2017
Ductile Cast Iron Caps of Electrical Insulators
M - Ductile Cast IronP - Cast iron capAp - EnergyCd - Typical manufacturing
Cm - Nital Etched Micrography by OMDf - Predominantly Ferritic