Optical Microscope

7 cases · 17 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Detail focus: Fusion Line clear all

Optical Microscope — sub-branches

Kalling Etched Micrography by OM 5Micrography by OM using A262 Method A 2NaOH Electrolytic Etched Micro 2Nital Etched Micrography by OM 8

Results

SortNewestOldestTitle A-ZTitle Z-A
Fusion line between the aged base metal (in the top) and the weld metal (in the bottom). The adopted filler metal is similar to the base metal.
27
VIEW
ML00173 / May.2021
Welding Cracks in an Aged HP Cast Fitting
M - Heat Resistant SteelP - Cast FtittingAp - PetrochemicalCd - Welding
Cm - Kalling Etched Micrography by OMDf - Fusion Line
Micrography of the weld repair at the fusion line. Weld metal to the right and heat affected zone to the left.
37
VIEW
ML00162 / Apr.2020
Valve Body Crack Growth from Weld Defects
M - Low Alloy Medium Carbon QTP - Valve BodyAp - O&G Well DrillingCd - Fatigue Induced by a Defect
Cm - Nital Etched Micrography by OMDf - Fusion Line
Micrography of the longitudinal section of the line at the fusion line of the fitting, close to OD. It is possible to see that the base metal is austenitic and the weld metal is austeno-ferritic. In the center of the thickness the average hardness of the fitting is 250HV1 and the average hardness of the weld metal is 180HV1.
48
VIEW
ML00095 / Sep.2017
MIC of a Riser Control Line
M - Austenitic Stainless SteelP - Fabrication WeldAp - Oil and GasCd - Brittle Behavior
Cm - Micrography by OM using A262 Method ADf - Fusion Line
Micrography of the low alloy steel tube at the fusion line, presenting a martensitic structure at the HAZ and acicular ferrite in the weld metal.
41
VIEW
ML00052 / Apr.2017
Cold Cracks in API 5CT L80 Tube Welded to a Structural Part
M - Low Alloy SteelP - Seamless tubeAp - OffshoreCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Fusion Line
Micrographic detail of the fusion line of the second pass (not reheated). The HAZ is bainitic and the weld metal microstructure is predominantly formed by acicular ferrite.
51
VIEW
ML00053 / Mar.2017
SAW Longitudinal Seam of X70 Pipe
M - Microalloyed SteelP - Longitudinal Seam Welded PipeAp - SubseaCd - Welding
Cm - Nital Etched Micrography by OMDf - Fusion Line
Micrography of the fusion line of the weld in the pipe side.
44
VIEW
ML00049 / Apr.2017
Pipe to Flange Welded Joint in a 14" ND Superduplex Spool
M - Super Duplex Stainless SteelP - Piping spoolAp - Oil and GasCd - Removed From Service
Cm - NaOH Electrolytic Etched MicroDf - Fusion Line
Micrography of the transverse section of the tube presenting the autogenous weld at the fusion line.
40
VIEW
ML00026 / Feb.2017
Autogenous Seam Welded Tube in Ferritic SS
M - Ferritic Stainless SteelP - Fabrication WeldAp - AutomotiveCd - Typical manufacturing
Cm - Kalling Etched Micrography by OMDf - Fusion Line

More from these cases

ML00173 — Welding Cracks in an Aged HP Cast FittingM - Heat Resistant SteelP - Cast FtittingAp - PetrochemicalCd - Welding
Fusion line between the aged base metal (in the top) and the weld metal (in the bottom). There is a region where the primary carbides melted (partially melted zone), that appears dark, and a region of high dilution cloe to the fusion line.
26
VIEW
ML00173 / May.2021
Welding Cracks in an Aged HP Cast Fitting
M - Heat Resistant SteelP - Cast FtittingAp - PetrochemicalCd - Welding
Cm - Kalling Etched Micrography by OMDf - Fusion Line
Same region as the previous figure, showing the structure of the base metal and weld metal, at the cracked area. In the base metal, the cracks are associated to the primary carbides network and in the weld metal it is associated to the solidification columnar grains.
110
VIEW
ML00173 / May.2021
Welding Cracks in an Aged HP Cast Fitting
M - Heat Resistant SteelP - Cast FtittingAp - PetrochemicalCd - Welding
Cm - Kalling Etched Micrography by OMDf - Fusion Line
ML00162 — Valve Body Crack Growth from Weld DefectsM - Low Alloy Medium Carbon QTP - Valve BodyAp - O&G Well DrillingCd - Fatigue Induced by a Defect
Micrographic detail of the fusion line.
33
VIEW
ML00162 / Apr.2020
Valve Body Crack Growth from Weld Defects
M - Low Alloy Medium Carbon QTP - Valve BodyAp - O&G Well DrillingCd - Fatigue Induced by a Defect
Cm - Nital Etched Micrography by OMDf - Fusion Line
ML00095 — MIC of a Riser Control LineM - Austenitic Stainless SteelP - Fabrication WeldAp - Oil and GasCd - Brittle Behavior
Micrographic detail of the fusion line of the fitting, close to OD. Austenitic base metal and austeno-ferritic weld metal.
50
VIEW
ML00095 / Sep.2017
MIC of a Riser Control Line
M - Austenitic Stainless SteelP - Fabrication WeldAp - Oil and GasCd - Brittle Behavior
Cm - Micrography by OM using A262 Method ADf - Fusion Line
ML00053 — SAW Longitudinal Seam of X70 PipeM - Microalloyed SteelP - Longitudinal Seam Welded PipeAp - SubseaCd - Welding
Fusion line of the first pass (reheated in high temperature). The HAZ is bainitic and the weld metal microstructure is predominantly formed by acicular ferrite.
43
VIEW
ML00053 / Mar.2017
SAW Longitudinal Seam of X70 Pipe
M - Microalloyed SteelP - Longitudinal Seam Welded PipeAp - SubseaCd - Welding
Cm - Nital Etched Micrography by OMDf - Fusion Line
Micrographic detail of the fusion line of the first pass (reheated in high temperature). The HAZ is bainitic and the weld metal microstructure is predominantly formed by acicular ferrite.
37
VIEW
ML00053 / Mar.2017
SAW Longitudinal Seam of X70 Pipe
M - Microalloyed SteelP - Longitudinal Seam Welded PipeAp - SubseaCd - Welding
Cm - Nital Etched Micrography by OMDf - Fusion Line
Micrographic detail of the fusion line of the first pass (reheated in high temperature). The HAZ is bainitic and the weld metal microstructure is predominantly formed by acicular ferrite.
38
VIEW
ML00053 / Mar.2017
SAW Longitudinal Seam of X70 Pipe
M - Microalloyed SteelP - Longitudinal Seam Welded PipeAp - SubseaCd - Welding
Cm - Nital Etched Micrography by OMDf - Fusion Line
Micrographic detail of the fusion line of the second pass (not reheated). Bainitic HAZ and acicular ferrite in the weld metal.
45
VIEW
ML00053 / Mar.2017
SAW Longitudinal Seam of X70 Pipe
M - Microalloyed SteelP - Longitudinal Seam Welded PipeAp - SubseaCd - Welding
Cm - Nital Etched Micrography by OMDf - Fusion Line
ML00049 — Pipe to Flange Welded Joint in a 14" ND Superduplex SpoolM - Super Duplex Stainless SteelP - Piping spoolAp - Oil and GasCd - Removed From Service
Micrography of the fusion line of the weld in the flange side.
36
VIEW
ML00049 / Apr.2017
Pipe to Flange Welded Joint in a 14" ND Superduplex Spool
M - Super Duplex Stainless SteelP - Piping spoolAp - Oil and GasCd - Removed From Service
Cm - NaOH Electrolytic Etched MicroDf - Fusion Line
ML00026 — Autogenous Seam Welded Tube in Ferritic SSM - Ferritic Stainless SteelP - Fabrication WeldAp - AutomotiveCd - Typical manufacturing
Micrography of the transverse section of the tube presenting the autogenous weld at the fusion line.
27
VIEW
ML00026 / Feb.2017
Autogenous Seam Welded Tube in Ferritic SS
M - Ferritic Stainless SteelP - Fabrication WeldAp - AutomotiveCd - Typical manufacturing
Cm - Kalling Etched Micrography by OMDf - Fusion Line