Optical Microscope

9 cases · 56 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Application: Energy clear all

Optical Microscope — sub-branches

As polished micrography 3Kalling Etched Micrography by OM 23Keller Etched Micrography by OM 4Micrography by OM 2Nital Etched Micrography by OM 15Oxalic Acid Electrolytic Etch 9

Results

SortNewestOldestTitle A-ZTitle Z-A
Sample surface. Microstructure of the plate base metal, exposed to high temperature exhausting gases. Refined austenite and some cracks.
24
VIEW
ML00174 / Jul.2021
Carburization of a 347 SS Welded Joint
M - Austenitic Stainless SteelP - Fabrication WeldAp - EnergyCd - Carburization
Cm - Oxalic Acid Electrolytic EtchDf - Base Metal
Micrography of a transverse section of the ring presenting a uniform tempered martensite structure.
43
VIEW
ML00124 / Feb.2018
MIC of a Martensitic Valve Ring
M - Martensitic Stainless SteelP - ForgingAp - EnergyCd - Brittle Behavior
Cm - Kalling Etched Micrography by OMDf - Martensite
Micrography of a longitudinal section of the pin, presenting a tempered martensitic structure with aligned delta ferrite and carbide phases.
80
VIEW
ML00046 / Jan.2018
Brittle Fracture of SS Shear Pin
M - Martensitic Stainless SteelP - Machined PartAp - EnergyCd - Intergranular Cracking
Cm - Kalling Etched Micrography by OMDf - Martensite, delta ferrite & carbides
The micrographic aspect of the cracks in a section transverse to the weld (the removed sample), shows that there are cracks with different sizes, the larger are filled with products that indicate they were opened for longer times.
67
VIEW
ML00071 / Jan.2019
Reheating Cracking of a CrMo Vessel Weld
M - CrMo SteelP - In Field WeldAp - EnergyCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Intergranular Cracking
Micrography of the cast Aluminum alloy (AlSnCuNi) typically adopted for bearing applications.
419
VIEW
ML00058 / Apr.2017
High-Pressure Piston Seal in Casting Al Alloy
M - Aluminum TinP - CastingAp - EnergyCd - Removed From Service
Cm - Keller Etched Micrography by OMDf - Casting Structure
Original casting base metal presenting a coarse martensitic structure with a small amount of delta ferrite.
50
VIEW
ML00055 / Apr.2017
CA6NM Blade Remanufactured by Welding
M - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Cm - Kalling Etched Micrography by OMDf - Base Metal Left Side
Pin A micrography presenting a ferritic-perlitic structure.
463
VIEW
ML00048 / Apr.2017
Medium Carbon Steel Pins of Electrical Insulators
M - Medium Carbon SteelP - Forged PinAp - EnergyCd - Typical manufacturing
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Micrography of CAP A, showing graphite in imperfect nodules and ferritic matrix.
481
VIEW
ML00047 / Mar.2017
Ductile Cast Iron Caps of Electrical Insulators
M - Ductile Cast IronP - Cast iron capAp - EnergyCd - Typical manufacturing
Cm - Nital Etched Micrography by OMDf - Graphite in Imperfect Nodules

More from these cases

ML00174 — Carburization of a 347 SS Welded JointM - Austenitic Stainless SteelP - Fabrication WeldAp - EnergyCd - Carburization
Detailed microstructure of the plate base metal, exposed to high temperature exhausting gases. Refined austenite, precipitation of carbides in the grain boumdaries and some cracks.
23
VIEW
ML00174 / Jul.2021
Carburization of a 347 SS Welded Joint
M - Austenitic Stainless SteelP - Fabrication WeldAp - EnergyCd - Carburization
Cm - Oxalic Acid Electrolytic EtchDf - Austenite
Detailed microstructure of the plate base metal, exposed to high temperature exhausting gases. Refined austenite, precipitation of carbides in the grain boumdaries and some cracks.
24
VIEW
ML00174 / Jul.2021
Carburization of a 347 SS Welded Joint
M - Austenitic Stainless SteelP - Fabrication WeldAp - EnergyCd - Carburization
Cm - Oxalic Acid Electrolytic EtchDf - Crack
Sample surface. Microstructure of the weld metal, exposed to high temperature exhausting gases. Austeno-ferritic structure and some cracks.
20
VIEW
ML00174 / Jul.2021
Carburization of a 347 SS Welded Joint
M - Austenitic Stainless SteelP - Fabrication WeldAp - EnergyCd - Carburization
Cm - Oxalic Acid Electrolytic EtchDf - Weld Metal
Detailed microstructure of the weld metal, exposed to high temperature exhausting gases. Austeno-ferritic structure and some cracks.
21
VIEW
ML00174 / Jul.2021
Carburization of a 347 SS Welded Joint
M - Austenitic Stainless SteelP - Fabrication WeldAp - EnergyCd - Carburization
Cm - Oxalic Acid Electrolytic EtchDf - Ferrite and Austenite
Detailed microstructure of the weld metal, exposed to high temperature exhausting gases. Austeno-ferritic structure, strong carbide precipitation integranular and transgranular, and some cracks.
23
VIEW
ML00174 / Jul.2021
Carburization of a 347 SS Welded Joint
M - Austenitic Stainless SteelP - Fabrication WeldAp - EnergyCd - Carburization
Cm - Oxalic Acid Electrolytic EtchDf - Cracks

+3 more from this case →

ML00124 — MIC of a Martensitic Valve RingM - Martensitic Stainless SteelP - ForgingAp - EnergyCd - Brittle Behavior
Micrography of a transverse section of the ring, at the pitting position, as polished, showing that there are intergranular cracks and the martensitic structure is corroded (chemical dissolution) inside the pitting.
33
VIEW
ML00124 / Feb.2018
MIC of a Martensitic Valve Ring
M - Martensitic Stainless SteelP - ForgingAp - EnergyCd - Brittle Behavior
Cm - As polished micrographyDf - Corrosion
Micrographic detail of a transverse section of the ring, showing the corroded martensitic structure (chemical dissolution) inside the pitting.
32
VIEW
ML00124 / Feb.2018
MIC of a Martensitic Valve Ring
M - Martensitic Stainless SteelP - ForgingAp - EnergyCd - Brittle Behavior
Cm - As polished micrographyDf - Corrosion
Micrographic detail of a transverse section of the ring, showing the corroded martensitic structure (chemical dissolution) inside the pitting.
33
VIEW
ML00124 / Feb.2018
MIC of a Martensitic Valve Ring
M - Martensitic Stainless SteelP - ForgingAp - EnergyCd - Brittle Behavior
Cm - As polished micrographyDf - Intergranular Cracking
Micrography of a transverse section of the ring at the cracking position. The cracks are intergranular and opened at the position close to the surface.
27
VIEW
ML00124 / Feb.2018
MIC of a Martensitic Valve Ring
M - Martensitic Stainless SteelP - ForgingAp - EnergyCd - Brittle Behavior
Cm - Kalling Etched Micrography by OMDf - Martensite
Micrography of a transverse section of the ring at the cracking position. The cracks are intergranular and opened at the position close to the surface. it is possible to identify dissolution of the structure adjacent to the grain boundaries,
25
VIEW
ML00124 / Feb.2018
MIC of a Martensitic Valve Ring
M - Martensitic Stainless SteelP - ForgingAp - EnergyCd - Brittle Behavior
Cm - Kalling Etched Micrography by OMDf - Crack

+4 more from this case →

ML00046 — Brittle Fracture of SS Shear PinM - Martensitic Stainless SteelP - Machined PartAp - EnergyCd - Intergranular Cracking
Micrographic detail of the pin structure, in the longitudinal section, at the segregated band with aligned inclusions and phases, delta ferrite and carbides.
70
VIEW
ML00046 / Jan.2018
Brittle Fracture of SS Shear Pin
M - Martensitic Stainless SteelP - Machined PartAp - EnergyCd - Intergranular Cracking
Cm - Kalling Etched Micrography by OMDf - Martensite, delta ferrite & carbides
Micrographic detail of the pin structure, in the longitudinal section, presenting a martensitic matriz, aligned inclusions (grey, delta ferrite islands (poligonal white phases) and carbides (also white phases) surrounding the delta ferrite.
64
VIEW
ML00046 / Jan.2018
Brittle Fracture of SS Shear Pin
M - Martensitic Stainless SteelP - Machined PartAp - EnergyCd - Intergranular Cracking
Cm - Kalling Etched Micrography by OMDf - Martensite, delta ferrite & carbides
ML00071 — Reheating Cracking of a CrMo Vessel WeldM - CrMo SteelP - In Field WeldAp - EnergyCd - Welding Defect
Micrographic aspect of opened cracks, filled with oxides.
63
VIEW
ML00071 / Jan.2019
Reheating Cracking of a CrMo Vessel Weld
M - CrMo SteelP - In Field WeldAp - EnergyCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Cracks
Micrographic details of opened cracks, filled with oxides.
56
VIEW
ML00071 / Jan.2019
Reheating Cracking of a CrMo Vessel Weld
M - CrMo SteelP - In Field WeldAp - EnergyCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Cracks
Micrographic aspect of thin cracks.
59
VIEW
ML00071 / Jan.2019
Reheating Cracking of a CrMo Vessel Weld
M - CrMo SteelP - In Field WeldAp - EnergyCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Cracks
Micrographic details of thin cracks.
63
VIEW
ML00071 / Jan.2019
Reheating Cracking of a CrMo Vessel Weld
M - CrMo SteelP - In Field WeldAp - EnergyCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Cracks
ML00058 — High-Pressure Piston Seal in Casting Al AlloyM - Aluminum TinP - CastingAp - EnergyCd - Removed From Service
Micrography of the cast Aluminum alloy (AlSnCuNi) typically adopted for bearing applications.
45
VIEW
ML00058 / Apr.2017
High-Pressure Piston Seal in Casting Al Alloy
M - Aluminum TinP - CastingAp - EnergyCd - Removed From Service
Cm - Keller Etched Micrography by OMDf - Casting Structure
Micrography of the cast Aluminum alloy (AlSnCuNi) typically adopted for bearing applications.
34
VIEW
ML00058 / Apr.2017
High-Pressure Piston Seal in Casting Al Alloy
M - Aluminum TinP - CastingAp - EnergyCd - Removed From Service
Cm - Keller Etched Micrography by OMDf - Casting Structure
Micrography of the cast Aluminum alloy (AlSnCuNi) typically adopted for bearing applications.
32
VIEW
ML00058 / Apr.2017
High-Pressure Piston Seal in Casting Al Alloy
M - Aluminum TinP - CastingAp - EnergyCd - Removed From Service
Cm - Keller Etched Micrography by OMDf - Casting Structure
ML00055 — CA6NM Blade Remanufactured by WeldingM - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Inserted casting base metal presenting a coarse martensitic structure with a small amount of delta ferrite.
24
VIEW
ML00055 / Apr.2017
CA6NM Blade Remanufactured by Welding
M - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Cm - Kalling Etched Micrography by OMDf - Base Metal Right Side
Micrography of the original casting blade at the fusion line of the welding with the insert casting. There is a refinement effect on the coarse base metal structure.
24
VIEW
ML00055 / Apr.2017
CA6NM Blade Remanufactured by Welding
M - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Cm - Kalling Etched Micrography by OMDf - HAZ Left Side
Micrographic detail of the fusion line of the original casting blade welded to the insert casting. There is a refinement effect on the coarse base metal structure.
21
VIEW
ML00055 / Apr.2017
CA6NM Blade Remanufactured by Welding
M - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Cm - Kalling Etched Micrography by OMDf - HAZ Left Side
Micrography of the inserted casting at the heat affected zone of the welding with the original casting. There is a refinement effect on the coarse base metal structure.
20
VIEW
ML00055 / Apr.2017
CA6NM Blade Remanufactured by Welding
M - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Cm - Kalling Etched Micrography by OMDf - HAZ Right Side
Micrographic detail of the fusion line of the inserted casting welded to the original casting. There is a refinement effect on the coarse base metal structure.
15
VIEW
ML00055 / Apr.2017
CA6NM Blade Remanufactured by Welding
M - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Cm - Kalling Etched Micrography by OMDf - HAZ Right Side

+2 more from this case →

ML00048 — Medium Carbon Steel Pins of Electrical InsulatorsM - Medium Carbon SteelP - Forged PinAp - EnergyCd - Typical manufacturing
Detail of Pin A microstructure. Ferritic-perlitic.
138
VIEW
ML00048 / Apr.2017
Medium Carbon Steel Pins of Electrical Insulators
M - Medium Carbon SteelP - Forged PinAp - EnergyCd - Typical manufacturing
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Pin B micrography presenting a ferritic-bainitic structure.
97
VIEW
ML00048 / Apr.2017
Medium Carbon Steel Pins of Electrical Insulators
M - Medium Carbon SteelP - Forged PinAp - EnergyCd - Typical manufacturing
Cm - Nital Etched Micrography by OMDf - Ferrite and Bainite
Detail of Pin B microstructure. Ferritic-bainitic.
87
VIEW
ML00048 / Apr.2017
Medium Carbon Steel Pins of Electrical Insulators
M - Medium Carbon SteelP - Forged PinAp - EnergyCd - Typical manufacturing
Cm - Nital Etched Micrography by OMDf - Ferrite and Bainite
ML00047 — Ductile Cast Iron Caps of Electrical InsulatorsM - Ductile Cast IronP - Cast iron capAp - EnergyCd - Typical manufacturing
Detail of CAP A microstructure. Graphite in imperfect nodules and ferritic matrix. Grey sulphide inclusions.
88
VIEW
ML00047 / Mar.2017
Ductile Cast Iron Caps of Electrical Insulators
M - Ductile Cast IronP - Cast iron capAp - EnergyCd - Typical manufacturing
Cm - Nital Etched Micrography by OMDf - Predominantly Ferritic
Micrography of CAP B, showing graphite in nodules and ferritic matrix.
67
VIEW
ML00047 / Mar.2017
Ductile Cast Iron Caps of Electrical Insulators
M - Ductile Cast IronP - Cast iron capAp - EnergyCd - Typical manufacturing
Cm - Nital Etched Micrography by OMDf - Graphite in Nodules
Detail of CAP B microstructure. Graphite in nodules and ferritic matrix. Small sulphide inclusions (grey).
60
VIEW
ML00047 / Mar.2017
Ductile Cast Iron Caps of Electrical Insulators
M - Ductile Cast IronP - Cast iron capAp - EnergyCd - Typical manufacturing
Cm - Nital Etched Micrography by OMDf - Predominantly Ferritic
Micrography of CAP C, showing graphite in nodules and ferritic-perlitic matrix.
52
VIEW
ML00047 / Mar.2017
Ductile Cast Iron Caps of Electrical Insulators
M - Ductile Cast IronP - Cast iron capAp - EnergyCd - Typical manufacturing
Cm - Nital Etched Micrography by OMDf - Graphite in Nodules
Detail of CAP C microstructure. Graphite in nodules and ferritic-perlitic matrix.
56
VIEW
ML00047 / Mar.2017
Ductile Cast Iron Caps of Electrical Insulators
M - Ductile Cast IronP - Cast iron capAp - EnergyCd - Typical manufacturing
Cm - Nital Etched Micrography by OMDf - Predominantly Ferritic