Optical Microscope

183 cases · 1637 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Optical Microscope — sub-branches

As polished micrography 128Chromic Acid Electrolytic Etched 7Eletrolytically Etched Micrography by OM 11FeCl3+HCl+Ethanol Etched Micro 15FeCl3+HCl+H2O Etched Micro 28Glyceregia Etched Micrography by OM 7H2SO4+HNO3+H3PO4 Etched Micro 4Kalling Etched Micrography by OM 202Keller Etched Micrography by OM 58Kroll Etched Micrography by OM 15Micro by OM, HCl + Ethanol + Picric Acid 12Micro by OM, picric acid+FeCl3+H2O etch 4Micrography by OM 73Micrography by OM using A262 Method A 80Micrography by OM, HF + HNO3 + H2O etch 8NH4OH+H2O+H2O2 Etched Micro 8NaOH Electrolytic Etched Micro 108Nital Etched Micrography by OM 801Oxalic Acid Electrolytic Etch 68

Results

SortNewestOldestTitle A-ZTitle Z-A
Longitudinal section micrography in a position of the thread, far from the failure. The stud presented a quenching and tempering structure and the thread was machined.
84
VIEW
ML00136 / Jun.2018
Hydrogen Cracks of Subsea Studs
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Machined Thread
Optical micrography of the transverse section of the drill collar, in the center of the thickness, presenting an uniform, granular, fully austenitic microstructure.
76
VIEW
ML00135 / May.2018
MIC of a Non Magnetic Drilling Tool
M - High Mn Austenitic SteelP - Tubular ForgingAp - O&G Well DrillingCd - Pitting Corrosion
Cm - Oxalic Acid Electrolytic EtchDf - Transverse Section
Microstructural analysis of the valve body structure, close to the position where the cracking has occurred. The structure is ferritic austenitic, with a large amount of detrimental phases associated to the ferritic structure, probably sigma phase.
106
VIEW
ML00134 / Aug.2020
Brittle Fracture of a Superduplex Valve Body
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Cm - NaOH Electrolytic Etched MicroDf - Sigma
Image by scanning electron microscopy of the metallurgically bonded interface of the internally cladded pipe. It is a longitudinal seam welded pipe, with substrate in low alloy steel X65 and clad plate in Alloy 625 (welded by a solid state process). The region is a detail in the side of the Ni alloy clad plate where a grain refinement has occurred probably due to recrystallization of a strain hardened region during later heat treatment. The microhardness of this region is a lot higher than the value obtained out of this region, in the clad plate.
904
VIEW
ML00133 / May.2018
Seam Welded Pipe Cladded with Alloy 625
M - LAS / Ni AlloyP - Longitudinal Seam Welded PipeAp - Oil and GasCd - Welding
Cm - Oxalic Acid Electrolytic EtchDf - Clad Interface
Micrography of a longitudinal section of the pipe substrate, in low magnification, showing a uniform microstructure,
79
VIEW
ML00132 / May.2018
Seamless Pipe Overlaid with Alloy 625
M - LAS / Ni AlloyP - Seamless PipeAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Base Metal
Micrography of an axial section of the roller bearing, at the external surface, where the hardness level was about 64 HRc (higher than the limit of 58HRc to 62 HRc).
86
VIEW
ML00131 / Apr.2018
Brittle Failure of a Soft Roller Bearing
M - Wear Resistant SteelP - Roller BearingAp - Mechanical IndustryCd - Heat Treatment Defect
Cm - Nital Etched Micrography by OMDf - Close to the External Surface
Micrographic aspect of the rolled thread that was heat treated later. Longitudinal section.
134
VIEW
ML00130 / Jun.2018
Fatigue Fracture of Overloaded Bolts
M - Low Alloy Medium Carbon QTP - FastenerAp - O&G Well DrillingCd - Mechanical Fatigue
Cm - Nital Etched Micrography by OMDf - At the Surface
Micrographic detail of the weld metal with islands of a coarse ferritic structure, degradated (recristalized) from an acicular morphology during to the long heat treatment cycle in high temperature. The post welding heat treatment (PWHT) was conducted during 12 hours at 640°C.
700
VIEW
ML00129 / Apr.2018
Non qualified WPS for High Strength Steel
M - Low Alloy Medium Carbon QTP - Welded Testpiece for QualificationAp - Oil and GasCd - Non qualified
Cm - Nital Etched Micrography by OMDf - Coarse Structure

More from these cases

ML00136 — Hydrogen Cracks of Subsea StudsM - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Microstructure of the stud in the longitudinal section, presenting segregated bands, not uniformly distributed in the section. The bands are associated to elongated and aligned inclusions, and a refined microstructure, probably due to carbon and alloying elements concentration.
69
VIEW
ML00136 / Jun.2018
Hydrogen Cracks of Subsea Studs
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Banded Structure
Microstructure of the stud in the longitudinal section, out of a region of segregation, where the tempered martensitic microstructure appears more uniform.
72
VIEW
ML00136 / Jun.2018
Hydrogen Cracks of Subsea Studs
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Martensite
Micrographic detail of the segregated bands, not uniformly distributed in the section. The bands are associated to elongated and aligned inclusions, and a refined microstructure, probably due to carbon and alloying elements concentration. The localized microhardness (50g) in the band showed levels about 540HV, and out of the band, in the same localtion, presented an average hardness of 321 HV, indicating that the material is non uniform in the regions where there are bands.
66
VIEW
ML00136 / Jun.2018
Hydrogen Cracks of Subsea Studs
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Banded Structure
Micrographic detail of the martensitic structure of the stud in the longitudinal section, out of a region of segregation, where the microstructure appears more uniform and the microhardness is about 370HV (50g).
62
VIEW
ML00136 / Jun.2018
Hydrogen Cracks of Subsea Studs
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Martensite
Low magnification micrography of a stud longitudinal section in the first thread fillet adjacent to the fracture, presenting a large secondary crack without any deformation evidence. This reveals a brittle material behavior, although the hardness measured at the stud end revealed 33HRc, as should be expected by the material specification.
47
VIEW
ML00136 / Jun.2018
Hydrogen Cracks of Subsea Studs
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Secondary Cracks

+17 more from this case →

ML00135 — MIC of a Non Magnetic Drilling ToolM - High Mn Austenitic SteelP - Tubular ForgingAp - O&G Well DrillingCd - Pitting Corrosion
Optical micrography of the transverse section of the drill collar, in the center of the thickness, presenting an uniform, granular, fully austenitic microstructure.
64
VIEW
ML00135 / May.2018
MIC of a Non Magnetic Drilling Tool
M - High Mn Austenitic SteelP - Tubular ForgingAp - O&G Well DrillingCd - Pitting Corrosion
Cm - Oxalic Acid Electrolytic EtchDf - Transverse Section
Micrographic detail of the transverse section of the drill collar, in the center of the thickness, presenting an uniform, granular, fully austenitic microstructure.
61
VIEW
ML00135 / May.2018
MIC of a Non Magnetic Drilling Tool
M - High Mn Austenitic SteelP - Tubular ForgingAp - O&G Well DrillingCd - Pitting Corrosion
Cm - Oxalic Acid Electrolytic EtchDf - Austenite
Optical micrography of the longitudinal section of the drill collar, in the center of the thickness, presenting slightly elongated grains of fully austenitic microstructure, cold worked. The material presented 38HRc hardness.
58
VIEW
ML00135 / May.2018
MIC of a Non Magnetic Drilling Tool
M - High Mn Austenitic SteelP - Tubular ForgingAp - O&G Well DrillingCd - Pitting Corrosion
Cm - Oxalic Acid Electrolytic EtchDf - Longitudinal Section
Optical micrography of the longitudinal section of the drill collar, in the center of the thickness, presenting slightly elongated grains of fully austenitic microstructure, cold worked.
62
VIEW
ML00135 / May.2018
MIC of a Non Magnetic Drilling Tool
M - High Mn Austenitic SteelP - Tubular ForgingAp - O&G Well DrillingCd - Pitting Corrosion
Cm - Oxalic Acid Electrolytic EtchDf - Longitudinal Section
Micrographic detail of the longitudinal section of the drill collar, in the center of the thickness, presenting slightly elongated grains of fully austenitic microstructure, cold worked.
59
VIEW
ML00135 / May.2018
MIC of a Non Magnetic Drilling Tool
M - High Mn Austenitic SteelP - Tubular ForgingAp - O&G Well DrillingCd - Pitting Corrosion
Cm - Oxalic Acid Electrolytic EtchDf - Austenite

+6 more from this case →

ML00134 — Brittle Fracture of a Superduplex Valve BodyM - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Micrographic detail of the valve body structure, close to the position where the cracking has occurred. The structure is ferritic austenitic, with a large amount of detrimental phases associated to the ferritic structure, probably sigma phase.
102
VIEW
ML00134 / Aug.2020
Brittle Fracture of a Superduplex Valve Body
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Cm - NaOH Electrolytic Etched MicroDf - Sigma
Metallographic detail of the large amount of sigma phase, associated to the ferritic structure.
105
VIEW
ML00134 / Aug.2020
Brittle Fracture of a Superduplex Valve Body
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Cm - NaOH Electrolytic Etched MicroDf - Sigma
Microstructural analysis of the valve body structure, far from the position where the cracking has occurred, in the bottom of the body. The structure is ferritic austenitic, with some sigma phase, not in a large amount, indicating the valve structure was not uniform.
67
VIEW
ML00134 / Aug.2020
Brittle Fracture of a Superduplex Valve Body
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Cm - NaOH Electrolytic Etched MicroDf - Ferrite and Austenite
Micrographic detail of the valve body structure, far from the position where the cracking has occurred, in the bottom of the body. The structure is ferritic austenitic, with some sigma phase, not in a large amount, indicating the valve structure was not uniform.
63
VIEW
ML00134 / Aug.2020
Brittle Fracture of a Superduplex Valve Body
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Cm - NaOH Electrolytic Etched MicroDf - Ferrite and Austenite
Micrographic detail of the valve body structure, far from the position where the cracking has occurred, in the bottom of the body. The structure is ferritic austenitic, with some sigma phase, not in a large amount, indicating the valve structure was not uniform.
61
VIEW
ML00134 / Aug.2020
Brittle Fracture of a Superduplex Valve Body
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Cm - NaOH Electrolytic Etched MicroDf - Ferrite and Austenite

+8 more from this case →

ML00133 — Seam Welded Pipe Cladded with Alloy 625M - LAS / Ni AlloyP - Longitudinal Seam Welded PipeAp - Oil and GasCd - Welding
Micrography of a longitudinal section of the pipe substrate, in low magnification, showing a uniform microstructure,
51
VIEW
ML00133 / May.2018
Seam Welded Pipe Cladded with Alloy 625
M - LAS / Ni AlloyP - Longitudinal Seam Welded PipeAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Base Metal
Micrography of a longitudinal section of the pipe substrate showing a uniform bainitic microstructure obtained by the pipe quenching and tempering,
48
VIEW
ML00133 / May.2018
Seam Welded Pipe Cladded with Alloy 625
M - LAS / Ni AlloyP - Longitudinal Seam Welded PipeAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Longitudinal Section
Micrographic detail of a longitudinal section of the pipe substrate showing a uniform bainitic microstructure,
50
VIEW
ML00133 / May.2018
Seam Welded Pipe Cladded with Alloy 625
M - LAS / Ni AlloyP - Longitudinal Seam Welded PipeAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Bainite
Micrography of a longitudinal section of the pipe at the interface with the clad plate, with Nital etch that reveals only the low alloy steel structure, to the left side of the image.
55
VIEW
ML00133 / May.2018
Seam Welded Pipe Cladded with Alloy 625
M - LAS / Ni AlloyP - Longitudinal Seam Welded PipeAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Clad Interface
Micrography of a longitudinal section of the pipe at the interface with the clad plate, with Nital etch that reveals only the low alloy steel structure, to the left side of the image.
51
VIEW
ML00133 / May.2018
Seam Welded Pipe Cladded with Alloy 625
M - LAS / Ni AlloyP - Longitudinal Seam Welded PipeAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Clad Interface

+10 more from this case →

ML00132 — Seamless Pipe Overlaid with Alloy 625M - LAS / Ni AlloyP - Seamless PipeAp - Oil and GasCd - Welding
Micrography of a longitudinal section of the pipe substrate showing a uniform bainitic microstructure obtained by the pipe quenching and tempering,
72
VIEW
ML00132 / May.2018
Seamless Pipe Overlaid with Alloy 625
M - LAS / Ni AlloyP - Seamless PipeAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Longitudinal Section
Micrographic detail of a longitudinal section of the pipe substrate showing a uniform bainitic microstructure.
68
VIEW
ML00132 / May.2018
Seamless Pipe Overlaid with Alloy 625
M - LAS / Ni AlloyP - Seamless PipeAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Bainite
Micrography of a longitudinal section of the pipe at the overlay fusion line, with Nital etch that reveals only the low alloy steel structure, to the left side of the image.
67
VIEW
ML00132 / May.2018
Seamless Pipe Overlaid with Alloy 625
M - LAS / Ni AlloyP - Seamless PipeAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Clad Interface
Micrography of a longitudinal section of the pipe at the overlay fusion line, with Nital etch that reveals only the low alloy steel structure, to the left side of the image. Some decarburization of the low alloy steel substrate is evident since the microstructure is slightly different a little far from the interface.
66
VIEW
ML00132 / May.2018
Seamless Pipe Overlaid with Alloy 625
M - LAS / Ni AlloyP - Seamless PipeAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Clad Interface
Micrographic detail of a longitudinal section of the pipe at the interface with the clad plate, with Nital etch that reveals only the low alloy steel structure, to the left side of the image.
59
VIEW
ML00132 / May.2018
Seamless Pipe Overlaid with Alloy 625
M - LAS / Ni AlloyP - Seamless PipeAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Clad Interface

+7 more from this case →

ML00131 — Brittle Failure of a Soft Roller BearingM - Wear Resistant SteelP - Roller BearingAp - Mechanical IndustryCd - Heat Treatment Defect
Micrographic detail of the roller bearing microstructure, close to the external surface, presenting 64 HRc and a microstructure that is martensitic with large carbides.
86
VIEW
ML00131 / Apr.2018
Brittle Failure of a Soft Roller Bearing
M - Wear Resistant SteelP - Roller BearingAp - Mechanical IndustryCd - Heat Treatment Defect
Cm - Nital Etched Micrography by OMDf - Martensite
Micrographic detail of the roller bearing microstructure, close to the external surface, presenting 64 HRc and a microstructure that is martensitic with large carbides, several presenting internal cracks.
82
VIEW
ML00131 / Apr.2018
Brittle Failure of a Soft Roller Bearing
M - Wear Resistant SteelP - Roller BearingAp - Mechanical IndustryCd - Heat Treatment Defect
Cm - Nital Etched Micrography by OMDf - Cracks
Micrography of an axial section of the roller bearing, at the internal surface, where the hardness level was about 21 HRc, indicating that in this region the material was not properly quenched and tempered.
75
VIEW
ML00131 / Apr.2018
Brittle Failure of a Soft Roller Bearing
M - Wear Resistant SteelP - Roller BearingAp - Mechanical IndustryCd - Heat Treatment Defect
Cm - Nital Etched Micrography by OMDf - Close to the Internal Surface
Micrographic detail of the roller bearing microstructure, close to the internal surface, presenting 21 HRc that reveals that the matrix is not martensitic. It is ferritic with large aligned carbides (cracked).
72
VIEW
ML00131 / Apr.2018
Brittle Failure of a Soft Roller Bearing
M - Wear Resistant SteelP - Roller BearingAp - Mechanical IndustryCd - Heat Treatment Defect
Cm - Nital Etched Micrography by OMDf - Ferrite
Micrographic detail of the roller bearing microstructure, close to the internal surface, presenting 21 HRc and a microstructure that is ferritic with large carbides (cracked) and small round carbides.
63
VIEW
ML00131 / Apr.2018
Brittle Failure of a Soft Roller Bearing
M - Wear Resistant SteelP - Roller BearingAp - Mechanical IndustryCd - Heat Treatment Defect
Cm - Nital Etched Micrography by OMDf - Cracks

+5 more from this case →

ML00130 — Fatigue Fracture of Overloaded BoltsM - Low Alloy Medium Carbon QTP - FastenerAp - O&G Well DrillingCd - Mechanical Fatigue
Micrographic aspect of the rolled thread that was heat treated later. Longitudinal section. The bolt was quenched and tempered to 30HRc and presented a martensitic structure.
124
VIEW
ML00130 / Jun.2018
Fatigue Fracture of Overloaded Bolts
M - Low Alloy Medium Carbon QTP - FastenerAp - O&G Well DrillingCd - Mechanical Fatigue
Cm - Nital Etched Micrography by OMDf - At the Surface
Micrographic detail of the rolled thread that was heat treated later. The bolt was quenched and tempered to 30 HRc and presented a martensitic structure.
110
VIEW
ML00130 / Jun.2018
Fatigue Fracture of Overloaded Bolts
M - Low Alloy Medium Carbon QTP - FastenerAp - O&G Well DrillingCd - Mechanical Fatigue
Cm - Nital Etched Micrography by OMDf - Martensite
The microstructure of the bolt is martensitic in the center of the thickness. Longitudinal section.
110
VIEW
ML00130 / Jun.2018
Fatigue Fracture of Overloaded Bolts
M - Low Alloy Medium Carbon QTP - FastenerAp - O&G Well DrillingCd - Mechanical Fatigue
Cm - Nital Etched Micrography by OMDf - In the Center of the Thickness
The microstructure of the bolt is martensitic in the center of the thickness. Longitudinal section.
103
VIEW
ML00130 / Jun.2018
Fatigue Fracture of Overloaded Bolts
M - Low Alloy Medium Carbon QTP - FastenerAp - O&G Well DrillingCd - Mechanical Fatigue
Cm - Nital Etched Micrography by OMDf - Martensite
Micrographic aspect of the rolled thread that was heat treated later. Longitudinal section.
115
VIEW
ML00130 / Jun.2018
Fatigue Fracture of Overloaded Bolts
M - Low Alloy Medium Carbon QTP - FastenerAp - O&G Well DrillingCd - Mechanical Fatigue
Cm - Nital Etched Micrography by OMDf - At the Surface

+3 more from this case →

ML00129 — Non qualified WPS for High Strength SteelM - Low Alloy Medium Carbon QTP - Welded Testpiece for QualificationAp - Oil and GasCd - Non qualified
Micrography of the weld metal, at the face, presenting regions of large ferritic grains. The acicular ferrite structure in the columnar (previous austenitic) grains has suffered degradation due to the long heat treatment cycle (12 hours) in high temperature.
97
VIEW
ML00129 / Apr.2018
Non qualified WPS for High Strength Steel
M - Low Alloy Medium Carbon QTP - Welded Testpiece for QualificationAp - Oil and GasCd - Non qualified
Cm - Nital Etched Micrography by OMDf - Weld Metal
Micrography of the weld metal, at the face, presenting regions of large ferritic grains. The acicular ferrite has suffered degradation due to the long heat treatment cycle (12 hours) in a temperature of 640°C, that is higher than the recommended for the D2 filler metal.
78
VIEW
ML00129 / Apr.2018
Non qualified WPS for High Strength Steel
M - Low Alloy Medium Carbon QTP - Welded Testpiece for QualificationAp - Oil and GasCd - Non qualified
Cm - Nital Etched Micrography by OMDf - Weld Metal
Micrography of the base metal, in low magnification, showing regions of segregations in a quenched and tempered martensitic structure.
52
VIEW
ML00129 / Apr.2018
Non qualified WPS for High Strength Steel
M - Low Alloy Medium Carbon QTP - Welded Testpiece for QualificationAp - Oil and GasCd - Non qualified
Cm - Nital Etched Micrography by OMDf - Base Metal
Micrography of the base metal showing a quenched and tempered martensitic structure. The base metal adopted in the test coupon presented a hardness level of 217HB (Brinell hardness of the certificate) and after the PWHT cycle the measured base metal hardness is 224 HV10.
59
VIEW
ML00129 / Apr.2018
Non qualified WPS for High Strength Steel
M - Low Alloy Medium Carbon QTP - Welded Testpiece for QualificationAp - Oil and GasCd - Non qualified
Cm - Nital Etched Micrography by OMDf - Base Metal
Micrographic detail of the base metal structure, quenched and tempered martensite. The base metal adopted in the test coupon presented a hardness level of 217HB (Brinell hardness of the certificate) and after the PWHT cycle the measured base metal hardness is 224 HV10.
51
VIEW
ML00129 / Apr.2018
Non qualified WPS for High Strength Steel
M - Low Alloy Medium Carbon QTP - Welded Testpiece for QualificationAp - Oil and GasCd - Non qualified
Cm - Nital Etched Micrography by OMDf - Martensite

+12 more from this case →