Optical Microscope

7 cases · 10 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Detail focus: Brittle Cracks clear all

Optical Microscope — sub-branches

As polished micrography 1Kalling Etched Micrography by OM 1Micrography by OM 2NaOH Electrolytic Etched Micro 3Nital Etched Micrography by OM 3

Results

SortNewestOldestTitle A-ZTitle Z-A
In a cut perpendicular to the macroscopic secondary crack it is possible to see several brittle microcracks (branched), indicating that an embrittlement has occurred.
22
VIEW
ML00176 / Nov.2021
Hydride Formation in a Titanium Blade
M - Unalloyed TitaniumP - BladeAp - Oil and GasCd - Hydride Formation
Cm - As polished micrographyDf - Brittle Cracks
Micrographic detail of a secondary crack transverse to the fracture (in the top), showing its appearance as multiple openings, straight and with intergranular and transgranular characteristics .
35
VIEW
ML00161 / Mar.2020
Brittle Fracture of a High Strength Socket
M - Medium Carbon Tool SteelP - ToolAp - Oil and GasCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Brittle Cracks
Low magnification micrographic aspect of the cracking. It is brittle, transgranular and associated to the ferritic/sigma phase interfaces.
54
VIEW
ML00134 / Aug.2020
Brittle Fracture of a Superduplex Valve Body
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Cm - NaOH Electrolytic Etched MicroDf - Brittle Cracks
Micrographic detail of a longitudinal section of the pin, at the fracture position, showing secondary cracks with intergranular and transgranular morphology.
59
VIEW
ML00009 / Sep.2017
Hydrogen Cracking of a 5" Drill Pipe S135
M - Low Alloy Medium Carbon QTP - Drill PipeAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Brittle Cracks
Multiple intergranular cracks transverse to the bolt axis. Hydrogen assisted cracking due to cathodic protection of a high strenght steel. Micrography in the "as polished" condition.
104
VIEW
ML00077 / Jun.2018
Hydrogen Cracking of LAS Subsea Bolts
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Micrography by OMDf - Brittle Cracks
Micrographic detail of the longitudinal section of the stud, at the secondary cracking.
26
VIEW
ML00075 / Jun.2018
Hydrogen Cracking of IN 718 Subsea Fasteners
M - NiCrFe AlloyP - StudAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Brittle Cracks
Detail, as polished, of brittle cracks in the weld metal, from the internal side of the pipe.
67
VIEW
ML00005 / Apr.2017
Environmental Hydrogen Damage in Ti Pipe
M - Unalloyed TitaniumP - Longitudinal Seam Welded PipeAp - PipingCd - Hydride Formation
Cm - Micrography by OMDf - Brittle Cracks

More from these cases

ML00161 — Brittle Fracture of a High Strength SocketM - Medium Carbon Tool SteelP - ToolAp - Oil and GasCd - Brittle Fracture
Micrographic detail of a secondary crack transverse to the fracture (in the top), showing its transgranular appearance at this position.
34
VIEW
ML00161 / Mar.2020
Brittle Fracture of a High Strength Socket
M - Medium Carbon Tool SteelP - ToolAp - Oil and GasCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Brittle Cracks
ML00134 — Brittle Fracture of a Superduplex Valve BodyM - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Micrographic details of the cracking. It is brittle, transgranular and associated to the ferritic/sigma phase interfaces.
50
VIEW
ML00134 / Aug.2020
Brittle Fracture of a Superduplex Valve Body
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Cm - NaOH Electrolytic Etched MicroDf - Brittle Cracks
Micrographic aspect of the cracking. It is brittle, transgranular and associated to the ferritic/sigma phase interfaces.
49
VIEW
ML00134 / Aug.2020
Brittle Fracture of a Superduplex Valve Body
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Cm - NaOH Electrolytic Etched MicroDf - Brittle Cracks