Optical Microscope

2 cases · 36 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Product: Allen Bolt clear all

Optical Microscope — sub-branches

As polished micrography 6Kalling Etched Micrography by OM 22Nital Etched Micrography by OM 8

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrography of a longitudinal section, in the center, of the broken 5/8" bolt, presenting an aged martensitic structure. There are vertical "lines" that correspond to segregation bands due to the forming direction. These bands are evident only using low magnification microscopy.
168
VIEW
ML00139 / Jun.2018
Hydrogen Fracture of a 17-4 PH Allen Bolt
M - Precipitation Hardened Stainless SteelP - Allen BoltAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Longitudinal Section
Micrography of the longitudinal section of the bolt showing a martensitic structure, with segregation bands evidenced by the chemical etch.
99
VIEW
ML00126 / Mar.2018
Hydrogen Fracture of Subsea Allen Bolts
M - Low Alloy Medium Carbon QTP - Coated ProductAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Banded Structure

More from these cases

ML00139 — Hydrogen Fracture of a 17-4 PH Allen BoltM - Precipitation Hardened Stainless SteelP - Allen BoltAp - SubseaCd - Hydrogen Embrittlement
Micrography of a longitudinal section, in the center, of the broken 5/8" bolt, presenting an aged martensitic structure.
133
VIEW
ML00139 / Jun.2018
Hydrogen Fracture of a 17-4 PH Allen Bolt
M - Precipitation Hardened Stainless SteelP - Allen BoltAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Martensite
Micrographic detail of the aged martensitic structure. The bolt presented variations in the previous austenite grain boundaries from the center of the thickness to the surface. No delta ferrite or retained austenite islands are evidenced.
107
VIEW
ML00139 / Jun.2018
Hydrogen Fracture of a 17-4 PH Allen Bolt
M - Precipitation Hardened Stainless SteelP - Allen BoltAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Martensite
Micrography of a longitudinal section of the 5/8" bolt, at the bottom of the thread, presenting a refined structure compared to the center of the bolt and a mark at the thread flank that was probably created during tightening of the bolt.
95
VIEW
ML00139 / Jun.2018
Hydrogen Fracture of a 17-4 PH Allen Bolt
M - Precipitation Hardened Stainless SteelP - Allen BoltAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Longitudinal Section
Micrography of a longitudinal section of the 5/8" bolt, at the bottom of the thread, presenting a refined structure compared to the center of the bolt. The structure is aged martensite.
91
VIEW
ML00139 / Jun.2018
Hydrogen Fracture of a 17-4 PH Allen Bolt
M - Precipitation Hardened Stainless SteelP - Allen BoltAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Martensite
Micrographic detail of the aged martensite structure, refined when compared to the structure in the center of the bolt.
87
VIEW
ML00139 / Jun.2018
Hydrogen Fracture of a 17-4 PH Allen Bolt
M - Precipitation Hardened Stainless SteelP - Allen BoltAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Martensite

+19 more from this case →

ML00126 — Hydrogen Fracture of Subsea Allen BoltsM - Low Alloy Medium Carbon QTP - Coated ProductAp - SubseaCd - Hydrogen Embrittlement
Micrography of the longitudinal section of the bolt at the bottom of the thread fillet, showing the uniform martensitic structure, not strain hardened.
90
VIEW
ML00126 / Mar.2018
Hydrogen Fracture of Subsea Allen Bolts
M - Low Alloy Medium Carbon QTP - Coated ProductAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Uniform Structure
Micrography of the longitudinal section of the bolt at the top of the thread fillet, showing a small circunferential cracking typically of a rolling process to manufacture the thread. The thread presented no evidences of plastic deformation suggesting that the heat treatment was applied later. It is important to mention that this cracking presented no influence in the fracture of the bolt.
101
VIEW
ML00126 / Mar.2018
Hydrogen Fracture of Subsea Allen Bolts
M - Low Alloy Medium Carbon QTP - Coated ProductAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Rolled Thread
Micrography of the longitudinal section of the bolt at the bottom of the thread fillet, in the "as polished" condition, showing the zinc flakes coating layer, applied by a painting process that do not create metallurgical bonding with the substrate.
82
VIEW
ML00126 / Mar.2018
Hydrogen Fracture of Subsea Allen Bolts
M - Low Alloy Medium Carbon QTP - Coated ProductAp - SubseaCd - Hydrogen Embrittlement
Cm - As polished micrographyDf - Coating Layer
Micrographic detail of the zinc flakes coating layer in the "as polished" condition of a longitudinal section of the bolt.
71
VIEW
ML00126 / Mar.2018
Hydrogen Fracture of Subsea Allen Bolts
M - Low Alloy Medium Carbon QTP - Coated ProductAp - SubseaCd - Hydrogen Embrittlement
Cm - As polished micrographyDf - Coating Layer
Micrography of the longitudinal section of the bolt in the center of the thickness (ND 5/8") showing a uniform martensitic structure.
67
VIEW
ML00126 / Mar.2018
Hydrogen Fracture of Subsea Allen Bolts
M - Low Alloy Medium Carbon QTP - Coated ProductAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Martensite

+5 more from this case →