Crevice Corrosion in a Subsea System — Aspect Before Analysis

53 images

TryAusteniteML00072corrosionGranularML00061brittle fractureOil and Gasductile behaviorShipfatigueFerrous AlloyshydrogenHigh Alloy Steelfractureembrittlementstress corrosion
Standard: ALLOY Capture method: Optical Microscope Detail focus: Sampling and Analysis clear all
M

Material

79 classified

Browse all Material →
P

Product

96 classified

Browse all Product →
Ap

Application

37 classified

Browse all Application →
C

Condition

84 classified

Browse all Condition →
Cm

Capture method

52 classified

Browse all Capture method →
Df

Detail focus

208 classified

Browse all Detail focus →

Sharpest next filters

Browse by category (1)
Microstructure21
+13 more

The Materials
Image Database

53 images
Micrography of a longitudinal section of the sleeve, at the external surface where there are two layers of coating. The electrolytic etch evidenced the duplex stainless steel substrate (bottom of the figure) and the weave interface of the substrate and the first thermal spray layer, about 1 mm thick, in a stainless steel. The surface layer, of tugnsten carbide, about 0.2 mm thick, is black and not clearly visible in this figure.
50
VIEW
ML00147 / Aug.2018
WC Layer Detached from a Cast Lean Duplex
M - Lean Duplex Stainless SteelP - Centrifugal CastingAp - ShipCd - Lack of Sealing
Cm - NaOH Electrolytic Etched MicroDf - External Surface
Micrography of the plate section, as polished, close to the surface that suffered the impact. No evidences of damage.
26
VIEW
ML00142 / Aug.2018
Impact of a .308 Winchester on AR500 Plate
M - Low Alloy Wear ResistantP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - As polished micrographyDf - At the Surface
Optical micrography of the transverse section of the drill collar, in the center of the thickness, presenting an uniform, granular, fully austenitic microstructure.
76
VIEW
ML00135 / May.2018
MIC of a Non Magnetic Drilling Tool
M - High Mn Austenitic SteelP - Tubular ForgingAp - O&G Well DrillingCd - Pitting Corrosion
Cm - Oxalic Acid Electrolytic EtchDf - Transverse Section
Micrography of a longitudinal section of the pipe substrate, in low magnification, showing a uniform microstructure,
51
VIEW
ML00133 / May.2018
Seam Welded Pipe Cladded with Alloy 625
M - LAS / Ni AlloyP - Longitudinal Seam Welded PipeAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Base Metal
Micrography of a longitudinal section of the pipe substrate, in low magnification, showing a uniform microstructure,
79
VIEW
ML00132 / May.2018
Seamless Pipe Overlaid with Alloy 625
M - LAS / Ni AlloyP - Seamless PipeAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Base Metal
Low magnification micrography of the plate base metal, presenting granular structure not clearly identified and aligned particles.
88
VIEW
ML00118 / Jan.2018
Non qualified GMAW of Aluminum Plates
M - Aluminum Magnesium ManganeseP - Welded Testpiece for QualificationAp - ShipCd - Non qualified
Cm - Keller Etched Micrography by OMDf - Base Metal
Micrography of the 4130 steel, normalized and tempered. The structure is sligthly banded (segregated) and the average hardness level is 20 HRc.
92
VIEW
ML00102 / May.2018
AISI 4130 Forging Welded and Overlaid
M - Low Alloy SteelP - CladdingAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Base Metal
As polished micrography of the hydraulic line sample in the longitudinal section, close to the outer diameter, showing that the cracks are branched and thin, opened to the external surface.
58
VIEW
ML00095 / Sep.2017
MIC of a Riser Control Line
M - Austenitic Stainless SteelP - Fabrication WeldAp - Oil and GasCd - Brittle Behavior
Cm - Micrography by OMDf - Close to the External Surface

More from these cases

ML00147 — WC Layer Detached from a Cast Lean DuplexM - Lean Duplex Stainless SteelP - Centrifugal CastingAp - ShipCd - Lack of Sealing
Micrography of the longitudinal section of the sleeve, at the interface between the substrate and the first thermal spray layer. The substrate (bottom of the figure) shows a ferritic-austenitic microstructure and detrimental phases that look like sigma. The thermal spray layer (top of the figure) presents the non-etched stainless steel, disposed in layers, with oxides (gray) and voids (black). The substrate is deformed in a thin layer at the interface.
38
VIEW
ML00147 / Aug.2018
WC Layer Detached from a Cast Lean Duplex
M - Lean Duplex Stainless SteelP - Centrifugal CastingAp - ShipCd - Lack of Sealing
Cm - NaOH Electrolytic Etched MicroDf - Close to the External Surface
Micrography of the longitudinal section of the cast sleeve in the middle of the thickness. The microstructure is coarse, austenitic ferritic.
34
VIEW
ML00147 / Aug.2018
WC Layer Detached from a Cast Lean Duplex
M - Lean Duplex Stainless SteelP - Centrifugal CastingAp - ShipCd - Lack of Sealing
Cm - NaOH Electrolytic Etched MicroDf - In the Center of the Thickness
Micrography of the longitudinal section of the cast sleeve, close to the internal diameter (ID). The microstructure is coarse, austenitic ferritic, and presents the same microstructure, ferritic and austenitic, all through the thickness.
21
VIEW
ML00147 / Aug.2018
WC Layer Detached from a Cast Lean Duplex
M - Lean Duplex Stainless SteelP - Centrifugal CastingAp - ShipCd - Lack of Sealing
Cm - NaOH Electrolytic Etched MicroDf - Internal Surface
ML00142 — Impact of a .308 Winchester on AR500 PlateM - Low Alloy Wear ResistantP - Rolled PlateAp - StructureCd - Non-Pierced
Micrography of the plate section, as polished, close to the surface that suffered the impact. At this magnification it is possible to see a deposit over the plate surface, but no evidences of damage in the plate.
25
VIEW
ML00142 / Aug.2018
Impact of a .308 Winchester on AR500 Plate
M - Low Alloy Wear ResistantP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - As polished micrographyDf - At the Surface
Micrographic detail of the plate section, as polished, close to the surface that suffered the impact. The deposits at the surface are the melted bullet films.
23
VIEW
ML00142 / Aug.2018
Impact of a .308 Winchester on AR500 Plate
M - Low Alloy Wear ResistantP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - As polished micrographyDf - At the Surface
Micrographic detail of the plate section, as polished, close to the surface that suffered the impact. The orange is the copper alloy melted film.
20
VIEW
ML00142 / Aug.2018
Impact of a .308 Winchester on AR500 Plate
M - Low Alloy Wear ResistantP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - As polished micrographyDf - At the Surface
Micrographic detail of the plate section, as polished, close to the surface that suffered the impact. The lead alloy melted and formed this gray deposit.
19
VIEW
ML00142 / Aug.2018
Impact of a .308 Winchester on AR500 Plate
M - Low Alloy Wear ResistantP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - As polished micrographyDf - At the Surface
Micrography of the plate section, close to the surface that suffered the impact. Smooth waves but no evidences of damage.
15
VIEW
ML00142 / Aug.2018
Impact of a .308 Winchester on AR500 Plate
M - Low Alloy Wear ResistantP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Nital Etched Micrography by OMDf - At the Surface

+3 more from this case →

ML00135 — MIC of a Non Magnetic Drilling ToolM - High Mn Austenitic SteelP - Tubular ForgingAp - O&G Well DrillingCd - Pitting Corrosion
Optical micrography of the transverse section of the drill collar, in the center of the thickness, presenting an uniform, granular, fully austenitic microstructure.
64
VIEW
ML00135 / May.2018
MIC of a Non Magnetic Drilling Tool
M - High Mn Austenitic SteelP - Tubular ForgingAp - O&G Well DrillingCd - Pitting Corrosion
Cm - Oxalic Acid Electrolytic EtchDf - Transverse Section
Optical micrography of the longitudinal section of the drill collar, in the center of the thickness, presenting slightly elongated grains of fully austenitic microstructure, cold worked. The material presented 38HRc hardness.
57
VIEW
ML00135 / May.2018
MIC of a Non Magnetic Drilling Tool
M - High Mn Austenitic SteelP - Tubular ForgingAp - O&G Well DrillingCd - Pitting Corrosion
Cm - Oxalic Acid Electrolytic EtchDf - Longitudinal Section
Optical micrography of the longitudinal section of the drill collar, in the center of the thickness, presenting slightly elongated grains of fully austenitic microstructure, cold worked.
62
VIEW
ML00135 / May.2018
MIC of a Non Magnetic Drilling Tool
M - High Mn Austenitic SteelP - Tubular ForgingAp - O&G Well DrillingCd - Pitting Corrosion
Cm - Oxalic Acid Electrolytic EtchDf - Longitudinal Section
Micrography of the damaged region close to the external surface, presenting a localized dissolution/corrosion.
58
VIEW
ML00135 / May.2018
MIC of a Non Magnetic Drilling Tool
M - High Mn Austenitic SteelP - Tubular ForgingAp - O&G Well DrillingCd - Pitting Corrosion
Cm - Oxalic Acid Electrolytic EtchDf - Close to the External Surface
Micrography of the damaged region close to the external surface, presenting a localized dissolution/corrosion.
53
VIEW
ML00135 / May.2018
MIC of a Non Magnetic Drilling Tool
M - High Mn Austenitic SteelP - Tubular ForgingAp - O&G Well DrillingCd - Pitting Corrosion
Cm - Oxalic Acid Electrolytic EtchDf - Close to the External Surface

+2 more from this case →

ML00133 — Seam Welded Pipe Cladded with Alloy 625M - LAS / Ni AlloyP - Longitudinal Seam Welded PipeAp - Oil and GasCd - Welding
Micrography of a longitudinal section of the pipe substrate showing a uniform bainitic microstructure obtained by the pipe quenching and tempering,
48
VIEW
ML00133 / May.2018
Seam Welded Pipe Cladded with Alloy 625
M - LAS / Ni AlloyP - Longitudinal Seam Welded PipeAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Longitudinal Section
ML00132 — Seamless Pipe Overlaid with Alloy 625M - LAS / Ni AlloyP - Seamless PipeAp - Oil and GasCd - Welding
Micrography of a longitudinal section of the pipe substrate showing a uniform bainitic microstructure obtained by the pipe quenching and tempering,
72
VIEW
ML00132 / May.2018
Seamless Pipe Overlaid with Alloy 625
M - LAS / Ni AlloyP - Seamless PipeAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Longitudinal Section
Low magnification micrography of a longitudinal section of the pipe at the interface between overlay layers, with electrolytic etch that reveals the Ni alloy structure, large columnar grains with celular morphology.
65
VIEW
ML00132 / May.2018
Seamless Pipe Overlaid with Alloy 625
M - LAS / Ni AlloyP - Seamless PipeAp - Oil and GasCd - Welding
Cm - Chromic Acid Electrolytic EtchedDf - Weld Metal
Micrography of a longitudinal section of the pipe at the interface between overlay layers, with electrolytic etch that reveals the Ni alloy structure, large grains with celular dendritic morphology.
52
VIEW
ML00132 / May.2018
Seamless Pipe Overlaid with Alloy 625
M - LAS / Ni AlloyP - Seamless PipeAp - Oil and GasCd - Welding
Cm - Chromic Acid Electrolytic EtchedDf - Weld Metal
Micrographic detail of a longitudinal section of the pipe in the overlay weld metal, with electrolytic etch that reveals the Ni alloy structure with celular dendritic morphology and precipitates.
48
VIEW
ML00132 / May.2018
Seamless Pipe Overlaid with Alloy 625
M - LAS / Ni AlloyP - Seamless PipeAp - Oil and GasCd - Welding
Cm - Chromic Acid Electrolytic EtchedDf - Weld Metal
ML00118 — Non qualified GMAW of Aluminum PlatesM - Aluminum Magnesium ManganeseP - Welded Testpiece for QualificationAp - ShipCd - Non qualified
Micrography of the plate base metal, presenting granular structure evidenced by the different shadows in the grains.
76
VIEW
ML00118 / Jan.2018
Non qualified GMAW of Aluminum Plates
M - Aluminum Magnesium ManganeseP - Welded Testpiece for QualificationAp - ShipCd - Non qualified
Cm - Keller Etched Micrography by OMDf - Base Metal
Micrographic detail of the aligned particles in the plate base metal. The grain boundaries are not clearly identified in this higher magnification.
73
VIEW
ML00118 / Jan.2018
Non qualified GMAW of Aluminum Plates
M - Aluminum Magnesium ManganeseP - Welded Testpiece for QualificationAp - ShipCd - Non qualified
Cm - Keller Etched Micrography by OMDf - Base Metal
Low magnification micrography of the welded joint at the heat affected zone of the flat position, in the last bead (face). Longitudinal section of the plate, transverse to the welded joint.
68
VIEW
ML00118 / Jan.2018
Non qualified GMAW of Aluminum Plates
M - Aluminum Magnesium ManganeseP - Welded Testpiece for QualificationAp - ShipCd - Non qualified
Cm - Keller Etched Micrography by OMDf - Last Bead HAZ
Micrography of the welded joint at the heat affected zone of the flat position, in the last bead (face). Longitudinal section of the plate, transverse to the welded joint.
64
VIEW
ML00118 / Jan.2018
Non qualified GMAW of Aluminum Plates
M - Aluminum Magnesium ManganeseP - Welded Testpiece for QualificationAp - ShipCd - Non qualified
Cm - Keller Etched Micrography by OMDf - Last Bead HAZ
Micrographic detail of the welded joint at the heat affected zone of the flat position, in the last bead (face). Longitudinal section of the plate, transverse to the welded joint.
57
VIEW
ML00118 / Jan.2018
Non qualified GMAW of Aluminum Plates
M - Aluminum Magnesium ManganeseP - Welded Testpiece for QualificationAp - ShipCd - Non qualified
Cm - Keller Etched Micrography by OMDf - Last Bead HAZ

+3 more from this case →

ML00102 — AISI 4130 Forging Welded and OverlaidM - Low Alloy SteelP - CladdingAp - Oil and GasCd - Welding
Micrography of the 4130 steel, normalized and tempered. The microstructure is bainitic.
88
VIEW
ML00102 / May.2018
AISI 4130 Forging Welded and Overlaid
M - Low Alloy SteelP - CladdingAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Base Metal
Micrography of the tubular 4130 forging at the heat affected zone (HAZ) of the Inconel overlay (white because it was not etched with the Nital). The structure is ferritic/bainitic because the overlay was conducted in two layers, and all the HAZ was reheated during welding.
66
VIEW
ML00102 / May.2018
AISI 4130 Forging Welded and Overlaid
M - Low Alloy SteelP - CladdingAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Heat Affected Zone
Micrography of the tubular 4130 forging at the heat affected zone (HAZ) of the Inconel overlay (white because it was not etched with the Nital). The structure is ferritic/bainitic because the overlay was conducted in two layers, and all the HAZ was reheated during welding.
61
VIEW
ML00102 / May.2018
AISI 4130 Forging Welded and Overlaid
M - Low Alloy SteelP - CladdingAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Heat Affected Zone
Micrography of the tubular 4130 forging at the heat affected zone (HAZ), butt weld face. The structure is tempered martensite because the welded joint was PWHT at 630°C. The original forging was normalized and tempered at 660°C.
48
VIEW
ML00102 / May.2018
AISI 4130 Forging Welded and Overlaid
M - Low Alloy SteelP - CladdingAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Heat Affected Zone
Micrography of the tubular 4130 forging at the heat affected zone (HAZ) at the face of the butt weld. The structure is a tempered martensite because the joint was PWHT at 630°C. The original forging was normalized and tempered at 660°C.
43
VIEW
ML00102 / May.2018
AISI 4130 Forging Welded and Overlaid
M - Low Alloy SteelP - CladdingAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Heat Affected Zone

+2 more from this case →

View all 53 images in the Atlas →

most recent

The location of the threaded fitting started leaking after less than five years in service. Although the corrosion rate was not high, the localized material loss in the threaded surface of the carbon steel flange allowed the connection leakage.
769
VIEW
ML00184 / Apr.2023
Dissimilar Steels in a Threaded Connection
M - Low Carbon SteelP - ForgingAp - OffshoreCd - Localized Dissolution
Cm - Aspect Before AnalysisDf - General View
Front wheel 17 x 7J of a passenger vehicle (identified as WHEEL 1) that broke during a car accident on a road.
1644
VIEW
ML00183 / Dec.2022
Ductile Behavior of an Aluminum Wheel
M - Aluminum Silicon MagnesiumP - CastingAp - AutomotiveCd - Ductile Behavior
Cm - Aspect Before AnalysisDf - General View
Tool fixture 5" long, nominal diameter 2", presenting a recess 1/2" deep from two sides. The rupture occurred about 2" from the end of the rod. Scale in milimeters.
523
VIEW
ML00182 / Jul.2022
Brittle Fracture of a LAS Fixing Rod
M - Low Alloy Medium Carbon QTP - StemAp - Mechanical IndustryCd - Brittle Fracture
Cm - Aspect Before AnalysisDf - General View
Pinion of hypoid gearbox, assembled in a 1560-mm long shaft that operated during more than 60,000 hours, and removed from service due to unacceptable wear damage.
1028
VIEW
ML00181 / Apr.2022
Wear of a Carburized Hypoid Gear
M - Low Alloy for Thermochemical TreatmentP - Pinion-crown assemblyAp - ShipCd - Wear
Cm - Aspect Before AnalysisDf - General View
Aspect of the 3 1/2" diameter tube after the water leakage in high temperature.
962
VIEW
ML00180 / Mar.2022
Local Melting of Copper Cooling Tubes
M - Pure CopperP - Cooling TubeAp - SiderurgyCd - Overheating
Cm - Aspect Before AnalysisDf - General View
2" drain line from the main 10" line. The leakage occurred at the margin of the weld, a short time after the introduction of the reinforced ribs to reduce vibration.
641
VIEW
ML00179 / Feb.2022
Hydrides in Titanium Weld
M - Unalloyed TitaniumP - In Field WeldAp - Chemical IndustryCd - Hydride Formation
Cm - Field photoDf - General View
The drilling connector, 21" diameter, presented a crack at the margin of the weld in the forging side (left side of the weld in the figure).
745
VIEW
ML00178 / Jan.2022
Cold cracks in Cr-Mo Welded Forging
M - CrMo SteelP - ForgingAp - O&G Well DrillingCd - Welding Defect
Cm - Aspect Before AnalysisDf - General View
Macrography of the longitudinally seam weld of the 24" diameter tube, showing that it was welded from both sides and there is a segregation line in the center of the tube thickness.
737
VIEW
ML00177 / Dec.2021
Cr-Mo Seam Welded Tube
M - CrMo SteelP - Longitudinally Seam WeldedAp - Fired HeaterCd - Not according to spec
Cm - NItal Etched MacroDf - Seam
The titanium rotor blade of a flowmeter broke after two years in service in an acid environment, containing H2S.
339
VIEW
ML00176 / Nov.2021
Hydride Formation in a Titanium Blade
M - Unalloyed TitaniumP - BladeAp - Oil and GasCd - Hydride Formation
Cm - Aspect Before AnalysisDf - General View
Aspect of the wire rope, 1 1/2" diameter, presenting regions of flattened areas at the surface of the outer wires. It is a 6 x 19 Seale construction, right regular lay.
552
VIEW
ML00175 / Aug.2021
Localized External Wear of a Wire Rope
M - High Carbon SteelP - Wire RopeAp - Oil and GasCd - Wear
Cm - Aspect Before AnalysisDf - General View
The carcass was manufactured using niobium stabilized plates, grade AISI 347, with circumferential welds, where the through wall cracks were detected.
300
VIEW
ML00174 / Jul.2021
Carburization of a 347 SS Welded Joint
M - Austenitic Stainless SteelP - Fabrication WeldAp - EnergyCd - Carburization
Cm - Field photoDf - General View
Aged microstructure of the HP stainless steel, modified with 1%Nb, cast fitting, tubular, operating for 6 years in a furnace which design temperature is 1100°C. The material presented a network of primary carbides, white and grey, and an austenitic matrix with coalescing secondary precipitation. Some voids. The Vickers identation indicates a hardness value about 260HV 100g in the aged austenitic matrix.
491
VIEW
ML00173 / May.2021
Welding Cracks in an Aged HP Cast Fitting
M - Heat Resistant SteelP - Cast FtittingAp - PetrochemicalCd - Welding
Cm - Kalling Etched Micrography by OMDf - Microhardness identations

Partners

Companies involved

TECMETAL