Crevice Corrosion in a Subsea System — Aspect Before Analysis

15 images

TryChemical IndustryML00011corrosionOil and GasML00041brittle fractureDamageductile behaviorCorrosionfatigueUNShydrogenASTMfractureembrittlementstress corrosion
Microstructure: Granular Capture method: Aspect Before Analysis Detail focus: Sampling and Analysis clear all
M

Material

79 classified

Browse all Material →
P

Product

96 classified

Browse all Product →
Ap

Application

37 classified

Browse all Application →
C

Condition

84 classified

Browse all Condition →
Cm

Capture method

52 classified

Browse all Capture method →
Df

Detail focus

208 classified

Browse all Detail focus →

Sharpest next filters

Browse by category (1)
Standard32
+24 more

The Materials
Image Database

15 images
Decorative table service fork, with a non metallic handle that is broken. The metallic part is about 165 mm long and presents two shapes: the scoop and the handle. The scoop is 53mm wide and 73mm long and the handle is about 9 mm wide and 75 mm long.
731
VIEW
ML00151 / Dec.2018
Ferritic Stainless Steel of a Flatware Fork
M - Ferritic Stainless SteelP - Foodstuff ArticleAp - KitchenCd - Typical manufacturing
Cm - Aspect Before AnalysisDf - General View
Red painted device where the 50 mm x 50 mm 6061 T6 aluminum alloy plate was positioned (in the circle). The image presents the target, positioned 100 meters far from the gun, after the shot and the projectile perforated the plate.
478
VIEW
ML00145 / Sep.2018
Impact of a .380 Winchester on 6061 T6 Plate
M - Aluminum Magnesium SiliconP - Rolled PlateAp - StructureCd - Pierced
Cm - Aspect Before AnalysisDf - General View
Aspect of the internal side of the drilling tool, after cleaning for inspection. Several regions of corrosion where detected where the drilling mud was adhered and remained uncleaned for a period a little longer than 1 month.
775
VIEW
ML00135 / May.2018
MIC of a Non Magnetic Drilling Tool
M - High Mn Austenitic SteelP - Tubular ForgingAp - O&G Well DrillingCd - Pitting Corrosion
Cm - Aspect Before AnalysisDf - Internal Surface
The 6 1/2" nominal diameter longitudinal seam welded pipe is internally cladded with Alloy 625. The pipe was manufactured by forming a cladded plate (probably welded by rolling) and welding it longitudinally. The pipe was heat treated (quenched and tempered) after the seam weld.
97
VIEW
ML00133 / May.2018
Seam Welded Pipe Cladded with Alloy 625
M - LAS / Ni AlloyP - Longitudinal Seam Welded PipeAp - Oil and GasCd - Welding
Cm - Aspect Before AnalysisDf - Welded Joint
The welded joint of the flat position is shown from the root side. It is possible to see that the use of the backing generated the possibility for melting the base metal out of the groove, without detection of this condition during welding, responsible for creating defects and avoiding the WPS qualification.
102
VIEW
ML00118 / Jan.2018
Non qualified GMAW of Aluminum Plates
M - Aluminum Magnesium ManganeseP - Welded Testpiece for QualificationAp - ShipCd - Non qualified
Cm - Aspect Before AnalysisDf - General View
Brittle aspect of the failure of the conector in the male thread. Both sides of the fracture.
96
VIEW
ML00078 / Jun.2017
Hydrogen Cracking of IN 718 Subsea Connector
M - NiCrFe AlloyP - ForgingAp - SubseaCd - Hydrogen Embrittlement
Cm - Aspect Before AnalysisDf - General View
The nut was sectioned in the longitudinal direction to reveal the position of the Nylon insert.
59
VIEW
ML00062 / Apr.2017
Inconel 718 Lock Nut with Polymer Insert
M - NiCrFe AlloyP - Cold FormedAp - PipingCd - Typical manufacturing
Cm - Aspect Before AnalysisDf - Transverse Section
xx
117
VIEW
ML00041 / Jun.2017
Fatigue Fracture of Inconel 718 Spline Shaft
M - NiCrFe AlloyP - ShaftAp - Oil and GasCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - At the Surface

More from these cases

ML00151 — Ferritic Stainless Steel of a Flatware ForkM - Ferritic Stainless SteelP - Foodstuff ArticleAp - KitchenCd - Typical manufacturing
Lateral view of the fork showing the profile. The scoop convex depth is 10 mm and the handle concave depth is 3 mm. The overal thickness of the part is 1 mm.
53
VIEW
ML00151 / Dec.2018
Ferritic Stainless Steel of a Flatware Fork
M - Ferritic Stainless SteelP - Foodstuff ArticleAp - KitchenCd - Typical manufacturing
Cm - Aspect Before AnalysisDf - General View
ML00145 — Impact of a .380 Winchester on 6061 T6 PlateM - Aluminum Magnesium SiliconP - Rolled PlateAp - StructureCd - Pierced
Aspect of the 3/8" thickness plate, 50 mm x 50 mm, of the aluminum alloy plate, in the face of impact with the projectile. The plate was perforated by the bullet.
52
VIEW
ML00145 / Sep.2018
Impact of a .380 Winchester on 6061 T6 Plate
M - Aluminum Magnesium SiliconP - Rolled PlateAp - StructureCd - Pierced
Cm - Aspect Before AnalysisDf - General View
Other view of the 3/8" thickness, 50 mm x 50 mm, 6061 T6 aluminum plate, in the face of impact with the projectile. The plate suffered a localized perforation.
34
VIEW
ML00145 / Sep.2018
Impact of a .380 Winchester on 6061 T6 Plate
M - Aluminum Magnesium SiliconP - Rolled PlateAp - StructureCd - Pierced
Cm - Aspect Before AnalysisDf - General View
Other view of the 3/8" thickness, 50 mm x 50 mm, 6061 T6 aluminum plate, in the opposite face of impact. The plate suffered a localized perforation and this image shows the position of the exit of the bullet.
31
VIEW
ML00145 / Sep.2018
Impact of a .380 Winchester on 6061 T6 Plate
M - Aluminum Magnesium SiliconP - Rolled PlateAp - StructureCd - Pierced
Cm - Aspect Before AnalysisDf - General View
ML00135 — MIC of a Non Magnetic Drilling ToolM - High Mn Austenitic SteelP - Tubular ForgingAp - O&G Well DrillingCd - Pitting Corrosion
Aspect of the external side of the nominal diameter 6 3/4" drilling tool, after cleaning for inspection. Several regions of corrosion where detected where the drilling mud was adhered and remained for a period a little longer than 1 month. This tool is a high strength steel, cold worked.
163
VIEW
ML00135 / May.2018
MIC of a Non Magnetic Drilling Tool
M - High Mn Austenitic SteelP - Tubular ForgingAp - O&G Well DrillingCd - Pitting Corrosion
Cm - Aspect Before AnalysisDf - General View
ML00118 — Non qualified GMAW of Aluminum PlatesM - Aluminum Magnesium ManganeseP - Welded Testpiece for QualificationAp - ShipCd - Non qualified
The welded joint of the vertical up position is shown from the root side. It is possible to see that the use of the backing generated the possibility for melting the base metal out of the groove, without detection of this condition during welding, responsible for creating defects and avoiding the WPS qualification.
122
VIEW
ML00118 / Jan.2018
Non qualified GMAW of Aluminum Plates
M - Aluminum Magnesium ManganeseP - Welded Testpiece for QualificationAp - ShipCd - Non qualified
Cm - Aspect Before AnalysisDf - General View

View all 15 images in the Atlas →

most recent

The location of the threaded fitting started leaking after less than five years in service. Although the corrosion rate was not high, the localized material loss in the threaded surface of the carbon steel flange allowed the connection leakage.
769
VIEW
ML00184 / Apr.2023
Dissimilar Steels in a Threaded Connection
M - Low Carbon SteelP - ForgingAp - OffshoreCd - Localized Dissolution
Cm - Aspect Before AnalysisDf - General View
Front wheel 17 x 7J of a passenger vehicle (identified as WHEEL 1) that broke during a car accident on a road.
1644
VIEW
ML00183 / Dec.2022
Ductile Behavior of an Aluminum Wheel
M - Aluminum Silicon MagnesiumP - CastingAp - AutomotiveCd - Ductile Behavior
Cm - Aspect Before AnalysisDf - General View
Tool fixture 5" long, nominal diameter 2", presenting a recess 1/2" deep from two sides. The rupture occurred about 2" from the end of the rod. Scale in milimeters.
523
VIEW
ML00182 / Jul.2022
Brittle Fracture of a LAS Fixing Rod
M - Low Alloy Medium Carbon QTP - StemAp - Mechanical IndustryCd - Brittle Fracture
Cm - Aspect Before AnalysisDf - General View
Pinion of hypoid gearbox, assembled in a 1560-mm long shaft that operated during more than 60,000 hours, and removed from service due to unacceptable wear damage.
1028
VIEW
ML00181 / Apr.2022
Wear of a Carburized Hypoid Gear
M - Low Alloy for Thermochemical TreatmentP - Pinion-crown assemblyAp - ShipCd - Wear
Cm - Aspect Before AnalysisDf - General View
Aspect of the 3 1/2" diameter tube after the water leakage in high temperature.
963
VIEW
ML00180 / Mar.2022
Local Melting of Copper Cooling Tubes
M - Pure CopperP - Cooling TubeAp - SiderurgyCd - Overheating
Cm - Aspect Before AnalysisDf - General View
2" drain line from the main 10" line. The leakage occurred at the margin of the weld, a short time after the introduction of the reinforced ribs to reduce vibration.
641
VIEW
ML00179 / Feb.2022
Hydrides in Titanium Weld
M - Unalloyed TitaniumP - In Field WeldAp - Chemical IndustryCd - Hydride Formation
Cm - Field photoDf - General View
The drilling connector, 21" diameter, presented a crack at the margin of the weld in the forging side (left side of the weld in the figure).
745
VIEW
ML00178 / Jan.2022
Cold cracks in Cr-Mo Welded Forging
M - CrMo SteelP - ForgingAp - O&G Well DrillingCd - Welding Defect
Cm - Aspect Before AnalysisDf - General View
Macrography of the longitudinally seam weld of the 24" diameter tube, showing that it was welded from both sides and there is a segregation line in the center of the tube thickness.
737
VIEW
ML00177 / Dec.2021
Cr-Mo Seam Welded Tube
M - CrMo SteelP - Longitudinally Seam WeldedAp - Fired HeaterCd - Not according to spec
Cm - NItal Etched MacroDf - Seam
The titanium rotor blade of a flowmeter broke after two years in service in an acid environment, containing H2S.
339
VIEW
ML00176 / Nov.2021
Hydride Formation in a Titanium Blade
M - Unalloyed TitaniumP - BladeAp - Oil and GasCd - Hydride Formation
Cm - Aspect Before AnalysisDf - General View
Aspect of the wire rope, 1 1/2" diameter, presenting regions of flattened areas at the surface of the outer wires. It is a 6 x 19 Seale construction, right regular lay.
552
VIEW
ML00175 / Aug.2021
Localized External Wear of a Wire Rope
M - High Carbon SteelP - Wire RopeAp - Oil and GasCd - Wear
Cm - Aspect Before AnalysisDf - General View
The carcass was manufactured using niobium stabilized plates, grade AISI 347, with circumferential welds, where the through wall cracks were detected.
301
VIEW
ML00174 / Jul.2021
Carburization of a 347 SS Welded Joint
M - Austenitic Stainless SteelP - Fabrication WeldAp - EnergyCd - Carburization
Cm - Field photoDf - General View
Aged microstructure of the HP stainless steel, modified with 1%Nb, cast fitting, tubular, operating for 6 years in a furnace which design temperature is 1100°C. The material presented a network of primary carbides, white and grey, and an austenitic matrix with coalescing secondary precipitation. Some voids. The Vickers identation indicates a hardness value about 260HV 100g in the aged austenitic matrix.
492
VIEW
ML00173 / May.2021
Welding Cracks in an Aged HP Cast Fitting
M - Heat Resistant SteelP - Cast FtittingAp - PetrochemicalCd - Welding
Cm - Kalling Etched Micrography by OMDf - Microhardness identations