Crevice Corrosion in a Subsea System — Aspect Before Analysis

54 images

TrySubseaML00028corrosionFPSOML00109brittle fractureAductile behaviorASTMfatigueFerrous AlloyshydrogenHigh Alloy Steelfractureembrittlementstress corrosion
Condition: Damage Microstructure: Duplex Ferritic Austenitic Detail focus: Sampling and Analysis clear all
M

Material

79 classified

Browse all Material →
P

Product

96 classified

Browse all Product →
Ap

Application

37 classified

Browse all Application →
C

Condition

84 classified

Browse all Condition →
Cm

Capture method

52 classified

Browse all Capture method →
Df

Detail focus

208 classified

Browse all Detail focus →

Sharpest next filters

Browse by category (1)
Standard17
+9 more

The Materials
Image Database

54 images
Vertical piping in a corrosive oil producing system of a FPSO. The line is a nominal diameter 14" sch 10S (pipe thickness about 5 mm) and the flanged branch line is a 2" nominal diameter welded to the main pipe using a weldolet (forged fitting). The fatigue induced cracking occurred longitudinal to the main pipe, originated at the margem of the weld interface with the pipe.
1480
VIEW
ML00150 / Dec.2018
Vibration Induced Fatigue in a SS Oil Piping
M - Duplex Stainless SteelP - PipingAp - FPSOCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - General View
Macroscopic aspect of the outer diameter of the flanged sleeve presenting adhered products at the surface. The flanged sleeve was manufactured by centrifugal casting in a lean duplex stainless steel and it was externally coated by thermal spray (TS) in a position of sealing. After 5 years in service the system suffered leakage.
569
VIEW
ML00147 / Aug.2018
WC Layer Detached from a Cast Lean Duplex
M - Lean Duplex Stainless SteelP - Centrifugal CastingAp - ShipCd - Lack of Sealing
Cm - Aspect Before AnalysisDf - External Surface
Aspect of the valve body after cutting a slice containg the crack and the welded joint of the body to the insert (fillet weld). The cracking was arrested at the position of this welded joint.
56
VIEW
ML00134 / Aug.2020
Brittle Fracture of a Superduplex Valve Body
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Cm - NaOH Electrolytic Etched MacroDf - Welded Joint
Fractographic detail of the longitudinal Charpy V testpiece, broken at -46°C and presenting energy of 64J (the average energy of three tespieces was 70J). The Charpy V testpiece was removed from the center of the bar. The micromechanism is quasicleavage and the test in this direction presented energy values superior than the minimum requirement of 45J.
944
VIEW
ML00123 / Feb.2018
Non Qualified Superduplex for Subsea
M - Super Duplex Stainless SteelP - BarAp - Oil and GasCd - Not according to spec
Cm - Fractography by SEMDf - Broken Testpiece
Aspect of the fitting welded to a tubing, ND 5/8" in a hydraulic line. The through wall cracking is longitudinal in the fitting side.
1032
VIEW
ML00094 / Sep.2017
MIC of a Subsea Hydraulic Line
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Behavior
Cm - Aspect Before AnalysisDf - General View
Macrography of a longitudinal section of the flange to pipe weld, cracked in the flange. Pipe thickness, measured, is 5 mm. Flange thickness at the welded region is 7.5 mm. The macro was etched using NaOH solution, electrolytic.
181
VIEW
ML00002 / Jan.2018
Preferential Dissolution and Cracks in SDSS
M - Super Duplex Stainless SteelP - Fabrication WeldAp - PipingCd - Preferential Dissolution
Cm - NaOH Electrolytic Etched MacroDf - Longitudinal Section

More from these cases

ML00150 — Vibration Induced Fatigue in a SS Oil PipingM - Duplex Stainless SteelP - PipingAp - FPSOCd - Vibration Induced Fatigue
Macrography of the section transverse to the ND 14" main pipe (that is only 5mm thick) and to the ND 2" branch that is a weldolet fitting welded to the main pipe and flange. This image is interesting because it shows clearly how thin is the pipe compared with the fitting thickness and the large amount of welding required to assure a full penetration weld in the weldolet.
220
VIEW
ML00150 / Dec.2018
Vibration Induced Fatigue in a SS Oil Piping
M - Duplex Stainless SteelP - PipingAp - FPSOCd - Vibration Induced Fatigue
Cm - NaOH Electrolytic Etched MacroDf - Transverse Section
Duplex stainless steel piping, in a region where the 14" ND pipe is only 5mm thick and the branch is a weldolet (forged fitting) welded to the pipe and to the flange, a lot more thicker than the pipe.
107
VIEW
ML00150 / Dec.2018
Vibration Induced Fatigue in a SS Oil Piping
M - Duplex Stainless SteelP - PipingAp - FPSOCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - General View
Macrographic detail of the pipe to weldolet weld, and the through wall cracking in the pipe from the margin of the weld. The pipe thickness is only 5 mm (SCH 10S) but the large thickness of the fitting required several weld passes to create a full penetration weld.
84
VIEW
ML00150 / Dec.2018
Vibration Induced Fatigue in a SS Oil Piping
M - Duplex Stainless SteelP - PipingAp - FPSOCd - Vibration Induced Fatigue
Cm - NaOH Electrolytic Etched MacroDf - Welded Joint
Micrography of the heat affected zone of the pipe to the fitting, at the pipe position, where the weld is in angle to the pipe (welded at the pipe surface). Weld metal to the top.
85
VIEW
ML00150 / Dec.2018
Vibration Induced Fatigue in a SS Oil Piping
M - Duplex Stainless SteelP - PipingAp - FPSOCd - Vibration Induced Fatigue
Cm - NaOH Electrolytic Etched MicroDf - Heat Affected Zone
Micrography of the heat affected zone of the pipe to the fitting, at the pipe position. Base metal to the bottom of the figure and fusion line to the top.
87
VIEW
ML00150 / Dec.2018
Vibration Induced Fatigue in a SS Oil Piping
M - Duplex Stainless SteelP - PipingAp - FPSOCd - Vibration Induced Fatigue
Cm - NaOH Electrolytic Etched MicroDf - Heat Affected Zone

+9 more from this case →

ML00147 — WC Layer Detached from a Cast Lean DuplexM - Lean Duplex Stainless SteelP - Centrifugal CastingAp - ShipCd - Lack of Sealing
Detail of the external surface of the sleeve where the surface coating was detached, creating a lack of sealing condition.
67
VIEW
ML00147 / Aug.2018
WC Layer Detached from a Cast Lean Duplex
M - Lean Duplex Stainless SteelP - Centrifugal CastingAp - ShipCd - Lack of Sealing
Cm - Surface AspectDf - External Surface
General view of the 10" diameter flanged sleeve, 1/2" wall thickness, manufactured by centrifugal casting of lean duplex stainless steel (DSS), Alloy 2304 (without Mo), with an external coating applied by thermal spray (TS). The sleeve is assembled in a shaft. The internal environment is oil and a seal box is assembled in the external side that is wet with seawater.
56
VIEW
ML00147 / Aug.2018
WC Layer Detached from a Cast Lean Duplex
M - Lean Duplex Stainless SteelP - Centrifugal CastingAp - ShipCd - Lack of Sealing
Cm - Aspect Before AnalysisDf - General View
Longitudinal slice of the flanged sleeve, 180 mm long, in a macrography presenting the 1/2" tubular wall thickness where the sealing was applied. The external surface of the sleeve (seawater wet) is in the left side of the figure and the internal surface (oiled) is in the right side. The flange is to the top of the figure.
52
VIEW
ML00147 / Aug.2018
WC Layer Detached from a Cast Lean Duplex
M - Lean Duplex Stainless SteelP - Centrifugal CastingAp - ShipCd - Lack of Sealing
Cm - Longitudinal Section AspectDf - General View
Micrography of a longitudinal section of the sleeve, at the external surface where there are two layers of coating. The electrolytic etch evidenced the duplex stainless steel substrate (bottom of the figure) and the weave interface of the substrate and the first thermal spray layer, about 1 mm thick, in a stainless steel. The surface layer, of tugnsten carbide, about 0.2 mm thick, is black and not clearly visible in this figure.
50
VIEW
ML00147 / Aug.2018
WC Layer Detached from a Cast Lean Duplex
M - Lean Duplex Stainless SteelP - Centrifugal CastingAp - ShipCd - Lack of Sealing
Cm - NaOH Electrolytic Etched MicroDf - External Surface
Micrography of the longitudinal section of the sleeve, at the interface between the substrate and the first thermal spray layer. The substrate (bottom of the figure) shows a ferritic-austenitic microstructure and detrimental phases that look like sigma. The thermal spray layer (top of the figure) presents the non-etched stainless steel, disposed in layers, with oxides (gray) and voids (black). The substrate is deformed in a thin layer at the interface.
38
VIEW
ML00147 / Aug.2018
WC Layer Detached from a Cast Lean Duplex
M - Lean Duplex Stainless SteelP - Centrifugal CastingAp - ShipCd - Lack of Sealing
Cm - NaOH Electrolytic Etched MicroDf - Close to the External Surface

+5 more from this case →

ML00134 — Brittle Fracture of a Superduplex Valve BodyM - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Image of the external surface of the valve body at the region where the Alloy 625 insert was fillet weld to the SDSS valve body. The surface was later machined, so it is possible to see only a mark indicating where the weld is. The brittle crack is arrested at the margin of the weld. It is possible to see strong deformation at the crack tip when it arrives the weld.
41
VIEW
ML00134 / Aug.2020
Brittle Fracture of a Superduplex Valve Body
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Cm - Aspect Before AnalysisDf - External Surface
Macrographic detail of the valve at the welded joint of the SDSS body (left side of the figure) to the Alloy 625 insert (right side of the figure), by a fillet weld. The cracking was arrested at the position of this welded joint.
48
VIEW
ML00134 / Aug.2020
Brittle Fracture of a Superduplex Valve Body
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Cm - NaOH Electrolytic Etched MacroDf - Welded Joint
Low magnification micrography of the valve at the welded joint of the body to the insert (fillet weld). The cracking was arrested at the position of this welded joint because the structures of the weld metal, insert and heat affected zones are tough (austenitic in the weld metal and insert, and free from sigma in the HAZ) .
47
VIEW
ML00134 / Aug.2020
Brittle Fracture of a Superduplex Valve Body
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Cm - NaOH Electrolytic Etched MicroDf - Welded Joint
Micrography of the valve at the welded joint of the body to the insert (fillet weld). The cracking was arrested at the position of this welded joint because the structures of the weld metal, insert and heat affected zones are tough (austenitic in the weld metal and insert, and free from sigma in the HAZ) .
46
VIEW
ML00134 / Aug.2020
Brittle Fracture of a Superduplex Valve Body
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Cm - NaOH Electrolytic Etched MicroDf - Heat Affected Zone
Micrographic detail of the fusion line of the welded joint of the body to the insert (fillet weld). The cracking was arrested at the position of this welded joint because the structures of the weld metal, insert and heat affected zones are tough (austenitic in the weld metal and insert, and free from sigma in the HAZ) .
39
VIEW
ML00134 / Aug.2020
Brittle Fracture of a Superduplex Valve Body
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Cm - NaOH Electrolytic Etched MicroDf - Heat Affected Zone

+2 more from this case →

ML00123 — Non Qualified Superduplex for SubseaM - Super Duplex Stainless SteelP - BarAp - Oil and GasCd - Not according to spec
Fractography of the broken Charpy V testpiece, longitudinal, broken at -46°C and presenting energy of 64J (the average of three values was 70J). In this direction the material presented an energy value higher than the minimum requirement of 45J.
109
VIEW
ML00123 / Feb.2018
Non Qualified Superduplex for Subsea
M - Super Duplex Stainless SteelP - BarAp - Oil and GasCd - Not according to spec
Cm - Fractography by SEMDf - Broken Testpiece
Fractography of the Charpy V testpiece, transverse section, broken at -46°C and presenting energy of 20J (the average of three results was 33J). The coarse structure and the alignement created a condition for low energy results in this specific direction, and the material did not present the minimum requirement of 45J.
103
VIEW
ML00123 / Feb.2018
Non Qualified Superduplex for Subsea
M - Super Duplex Stainless SteelP - BarAp - Oil and GasCd - Not according to spec
Cm - Fractography by SEMDf - Broken Testpiece
Micrography of a transverse section of the forged bar in the center of the thickness. Ferrite and austenite. Coarse structure.
74
VIEW
ML00123 / Feb.2018
Non Qualified Superduplex for Subsea
M - Super Duplex Stainless SteelP - BarAp - Oil and GasCd - Not according to spec
Cm - NaOH Electrolytic Etched MicroDf - Transverse Section
Micrography of a longitudinal section of the forged bar in the center of the thickness. Ferrite and austenite. Coarse structure.
61
VIEW
ML00123 / Feb.2018
Non Qualified Superduplex for Subsea
M - Super Duplex Stainless SteelP - BarAp - Oil and GasCd - Not according to spec
Cm - NaOH Electrolytic Etched MicroDf - Longitudinal Section
Micrography of a transverse section of the forged bar in the center of the thickness. Ferrite and austenite. The ferrite amount, measured by metallographic method, manual counting, is 59%.
53
VIEW
ML00123 / Feb.2018
Non Qualified Superduplex for Subsea
M - Super Duplex Stainless SteelP - BarAp - Oil and GasCd - Not according to spec
Cm - NaOH Electrolytic Etched MicroDf - Transverse Section

+1 more from this case →

ML00094 — MIC of a Subsea Hydraulic LineM - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Behavior
Detail of the longitudinal through wall cracking in the fitting welded to a tubing, ND 5/8" in a hydraulic line.
87
VIEW
ML00094 / Sep.2017
MIC of a Subsea Hydraulic Line
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Behavior
Cm - Aspect Before AnalysisDf - External Surface
Macrography of a longitudinal section of the fitting to tubing weld, with the longitudinal cracking at the tubular fitting position.
69
VIEW
ML00094 / Sep.2017
MIC of a Subsea Hydraulic Line
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Behavior
Cm - Kalling Etched MacroDf - Longitudinal Section
Aspect of the internal side of the fitting to tubing welded joint, after longitudinal cut. It is possible to see that the cracking (still filled with corrosion products) is located in the fitting side (left side) far from the welded joint to the tubing (right side).
58
VIEW
ML00094 / Sep.2017
MIC of a Subsea Hydraulic Line
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Behavior
Cm - Aspect Before AnalysisDf - Internal Surface
Aspect of the internal side of the fitting, at the cracked position with corrosion products and several surface microcracks adjacent to the main crack.
52
VIEW
ML00094 / Sep.2017
MIC of a Subsea Hydraulic Line
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Behavior
Cm - Surface AspectDf - Internal Surface
Aspect by scanning electron microscopy of the cracking at the external surface of the fitting.
47
VIEW
ML00094 / Sep.2017
MIC of a Subsea Hydraulic Line
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Behavior
Cm - Surface Aspect by SEMDf - External Surface

+6 more from this case →

View all 54 images in the Atlas →

most recent

The location of the threaded fitting started leaking after less than five years in service. Although the corrosion rate was not high, the localized material loss in the threaded surface of the carbon steel flange allowed the connection leakage.
769
VIEW
ML00184 / Apr.2023
Dissimilar Steels in a Threaded Connection
M - Low Carbon SteelP - ForgingAp - OffshoreCd - Localized Dissolution
Cm - Aspect Before AnalysisDf - General View
Front wheel 17 x 7J of a passenger vehicle (identified as WHEEL 1) that broke during a car accident on a road.
1644
VIEW
ML00183 / Dec.2022
Ductile Behavior of an Aluminum Wheel
M - Aluminum Silicon MagnesiumP - CastingAp - AutomotiveCd - Ductile Behavior
Cm - Aspect Before AnalysisDf - General View
Tool fixture 5" long, nominal diameter 2", presenting a recess 1/2" deep from two sides. The rupture occurred about 2" from the end of the rod. Scale in milimeters.
523
VIEW
ML00182 / Jul.2022
Brittle Fracture of a LAS Fixing Rod
M - Low Alloy Medium Carbon QTP - StemAp - Mechanical IndustryCd - Brittle Fracture
Cm - Aspect Before AnalysisDf - General View
Pinion of hypoid gearbox, assembled in a 1560-mm long shaft that operated during more than 60,000 hours, and removed from service due to unacceptable wear damage.
1028
VIEW
ML00181 / Apr.2022
Wear of a Carburized Hypoid Gear
M - Low Alloy for Thermochemical TreatmentP - Pinion-crown assemblyAp - ShipCd - Wear
Cm - Aspect Before AnalysisDf - General View
Aspect of the 3 1/2" diameter tube after the water leakage in high temperature.
962
VIEW
ML00180 / Mar.2022
Local Melting of Copper Cooling Tubes
M - Pure CopperP - Cooling TubeAp - SiderurgyCd - Overheating
Cm - Aspect Before AnalysisDf - General View
2" drain line from the main 10" line. The leakage occurred at the margin of the weld, a short time after the introduction of the reinforced ribs to reduce vibration.
641
VIEW
ML00179 / Feb.2022
Hydrides in Titanium Weld
M - Unalloyed TitaniumP - In Field WeldAp - Chemical IndustryCd - Hydride Formation
Cm - Field photoDf - General View
The drilling connector, 21" diameter, presented a crack at the margin of the weld in the forging side (left side of the weld in the figure).
745
VIEW
ML00178 / Jan.2022
Cold cracks in Cr-Mo Welded Forging
M - CrMo SteelP - ForgingAp - O&G Well DrillingCd - Welding Defect
Cm - Aspect Before AnalysisDf - General View
Macrography of the longitudinally seam weld of the 24" diameter tube, showing that it was welded from both sides and there is a segregation line in the center of the tube thickness.
737
VIEW
ML00177 / Dec.2021
Cr-Mo Seam Welded Tube
M - CrMo SteelP - Longitudinally Seam WeldedAp - Fired HeaterCd - Not according to spec
Cm - NItal Etched MacroDf - Seam
The titanium rotor blade of a flowmeter broke after two years in service in an acid environment, containing H2S.
339
VIEW
ML00176 / Nov.2021
Hydride Formation in a Titanium Blade
M - Unalloyed TitaniumP - BladeAp - Oil and GasCd - Hydride Formation
Cm - Aspect Before AnalysisDf - General View
Aspect of the wire rope, 1 1/2" diameter, presenting regions of flattened areas at the surface of the outer wires. It is a 6 x 19 Seale construction, right regular lay.
552
VIEW
ML00175 / Aug.2021
Localized External Wear of a Wire Rope
M - High Carbon SteelP - Wire RopeAp - Oil and GasCd - Wear
Cm - Aspect Before AnalysisDf - General View
The carcass was manufactured using niobium stabilized plates, grade AISI 347, with circumferential welds, where the through wall cracks were detected.
300
VIEW
ML00174 / Jul.2021
Carburization of a 347 SS Welded Joint
M - Austenitic Stainless SteelP - Fabrication WeldAp - EnergyCd - Carburization
Cm - Field photoDf - General View
Aged microstructure of the HP stainless steel, modified with 1%Nb, cast fitting, tubular, operating for 6 years in a furnace which design temperature is 1100°C. The material presented a network of primary carbides, white and grey, and an austenitic matrix with coalescing secondary precipitation. Some voids. The Vickers identation indicates a hardness value about 260HV 100g in the aged austenitic matrix.
491
VIEW
ML00173 / May.2021
Welding Cracks in an Aged HP Cast Fitting
M - Heat Resistant SteelP - Cast FtittingAp - PetrochemicalCd - Welding
Cm - Kalling Etched Micrography by OMDf - Microhardness identations