Crevice Corrosion in a Subsea System — Aspect Before Analysis

25 images for "fracture"

TryShipML00156corrosionLiftingML00105brittle fractureTempered Martensiteductile behaviorAustenitefatigueFerrous AlloyshydrogenHigh Alloy Steelfractureembrittlementstress corrosion
Standard: ASTM Capture method: Aspect Before Analysis clear all
M

Material

79 classified

Browse all Material →
P

Product

96 classified

Browse all Product →
Ap

Application

37 classified

Browse all Application →
C

Condition

84 classified

Browse all Condition →
Cm

Capture method

52 classified

Browse all Capture method →
Df

Detail focus

208 classified

Browse all Detail focus →

Sharpest next filters

Browse by category (1)
Microstructure16
+8 more

The Materials
Image Database

25 images for "fracture"
Aspect of the barrel nut that is broken in a brittle way (without plastic deformation). The Nut diameter is 1", the nut length is 2" and the bolt thread is 1/2" (nominal diameter).
753
VIEW
ML00148 / Sep.2018
Brittle Fracture of a 420 SS Barrel Nut
M - Martensitic Stainless SteelP - Barrel NutAp - LiftingCd - Heat Treatment Defect
Cm - Aspect Before AnalysisDf - General View
General aspect of the 5/8" allen bolt that was found fractured in an instrument connected to a subsea BOP. The fracture presented a brittle aspect and occurred at the bolt head to threaded body transition.
1495
VIEW
ML00139 / Jun.2018
Hydrogen Fracture of a 17-4 PH Allen Bolt
M - Precipitation Hardened Stainless SteelP - Allen BoltAp - SubseaCd - Hydrogen Embrittlement
Cm - Aspect Before AnalysisDf - Fracture
Aspect of the cracked valve body, after disassembling and removing the internal parts. The valve is part of a lot that was manufactured by forging a cubic 170mm from a forged bar in SDSS UNS S32760, and heat treated (solution annealed) by the forging company. The fabrication using these bodies included the machining, fillet weld two inserts in Alloy 625, machining again, assembling the internals, and pressure test at 15,000 psi. The cracking occurred during test, only for this valve body.
676
VIEW
ML00134 / Aug.2020
Brittle Fracture of a Superduplex Valve Body
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Cm - Aspect Before AnalysisDf - Cracking
The four bolts have fractured in the same position, close to the end, and the corrosion marks in the thread suggest that they have been tightened only a few fillets in a tapped hole. This condition could be responsible for overloading the fillets, relaxing the applied bolt preload, and intensifying cyclic stresses.
192
VIEW
ML00130 / Jun.2018
Fatigue Fracture of Overloaded Bolts
M - Low Alloy Medium Carbon QTP - FastenerAp - O&G Well DrillingCd - Mechanical Fatigue
Cm - Aspect Before AnalysisDf - General View
Aspect of the external side of the connector, with a longitudinally crack of a brittle aspect. It is a 5/8" connector (15.8 mm).
134
VIEW
ML00103 / Nov.2017
Brittle Fracture of a Free-Cutting Connector
M - Low Carbon SteelP - Machined PartAp - ShipCd - Brittle Fracture
Cm - Aspect Before AnalysisDf - General View
Aspect of the broken padeye. The outer diameter is about 10" and the thickness of the casting is about 2".
22
VIEW
ML00098 / Nov.2017
Brittle Fracture of a Casting Lifting Device
M - Low Alloy Medium Carbon QTP - CastingAp - LiftingCd - Brittle Fracture
Cm - Aspect Before AnalysisDf - General View
Macroscopic aspect of the 1" shaft fracture surface, revealing beach marks at the surface typical of fatigue, initiated from the surface of the spline shaft at the gear position.
498
VIEW
ML00041 / Jun.2017
Fatigue Fracture of Inconel 718 Spline Shaft
M - NiCrFe AlloyP - ShaftAp - Oil and GasCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - Fatigue Fracture
Aspect of a broken 5/16" bolt that was operating inside the pressure vessel in a condition that exceeds the limits of use of the AISI 316 steel. The fracture is located close to the position where there was the bolt head and the threads were "removed" close to the fracture surface.
75
VIEW
ML00157 / Feb.2020
Bolts Under Chloride SCC Conditions
M - Austenitic Stainless SteelP - BoltAp - Oil and GasCd - Stress Corrosion
Cm - Aspect Before AnalysisDf - Fracture

More from these cases

ML00148 — Brittle Fracture of a 420 SS Barrel NutM - Martensitic Stainless SteelP - Barrel NutAp - LiftingCd - Heat Treatment Defect
Visual aspect of both sides of the fractures. They present a macroscopically brittle aspect, with chevron marks indicating the starting point at the thinner edge of the thread.
81
VIEW
ML00148 / Sep.2018
Brittle Fracture of a 420 SS Barrel Nut
M - Martensitic Stainless SteelP - Barrel NutAp - LiftingCd - Heat Treatment Defect
Cm - Aspect Before AnalysisDf - Fracture
ML00134 — Brittle Fracture of a Superduplex Valve BodyM - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Detailed aspect of the cracking, straight and presenting a brittle aspect.
122
VIEW
ML00134 / Aug.2020
Brittle Fracture of a Superduplex Valve Body
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Cm - Aspect Before AnalysisDf - Cracking
Detail of the internal bore, showing a brittle crack through the wall.
106
VIEW
ML00134 / Aug.2020
Brittle Fracture of a Superduplex Valve Body
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Cm - Aspect Before AnalysisDf - Cracking
Image of the external surface of the valve body at the region where the Alloy 625 insert was fillet weld to the SDSS valve body. The surface was later machined, so it is possible to see only a mark indicating where the weld is. The brittle crack is arrested at the margin of the weld. It is possible to see strong deformation at the crack tip when it arrives the weld.
41
VIEW
ML00134 / Aug.2020
Brittle Fracture of a Superduplex Valve Body
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Cm - Aspect Before AnalysisDf - External Surface
ML00130 — Fatigue Fracture of Overloaded BoltsM - Low Alloy Medium Carbon QTP - FastenerAp - O&G Well DrillingCd - Mechanical Fatigue
The corrosion marks in the thread surface indicate that the bolt was not properly tightened in the tapped hole. The length of thread engagement should be at least 1x of the bolt diameter, in this case 3/8".
170
VIEW
ML00130 / Jun.2018
Fatigue Fracture of Overloaded Bolts
M - Low Alloy Medium Carbon QTP - FastenerAp - O&G Well DrillingCd - Mechanical Fatigue
Cm - Aspect Before AnalysisDf - General View
Macroscopic aspect of the bolt fracture. Part of it is flat from the bottom of the thread.
166
VIEW
ML00130 / Jun.2018
Fatigue Fracture of Overloaded Bolts
M - Low Alloy Medium Carbon QTP - FastenerAp - O&G Well DrillingCd - Mechanical Fatigue
Cm - Aspect Before AnalysisDf - Fracture
The head of the bolts presented the marks that indicated they were manufactured to meet ASTM A449 type 1 bolt, that is a medium strength low alloy steel, quenched and tempered.
148
VIEW
ML00130 / Jun.2018
Fatigue Fracture of Overloaded Bolts
M - Low Alloy Medium Carbon QTP - FastenerAp - O&G Well DrillingCd - Mechanical Fatigue
Cm - Aspect Before AnalysisDf - At the Surface
ML00103 — Brittle Fracture of a Free-Cutting ConnectorM - Low Carbon SteelP - Machined PartAp - ShipCd - Brittle Fracture
Aspect of the internal side of the connector. The fracture, in the longitudinal direction, presents a brittle aspect. The thickness of the connector is about 2 mm.
126
VIEW
ML00103 / Nov.2017
Brittle Fracture of a Free-Cutting Connector
M - Low Carbon SteelP - Machined PartAp - ShipCd - Brittle Fracture
Cm - Aspect Before AnalysisDf - Brittle Fracture
Macroscopic detail of the brittle fracture, in the longitudinal direction.
105
VIEW
ML00103 / Nov.2017
Brittle Fracture of a Free-Cutting Connector
M - Low Carbon SteelP - Machined PartAp - ShipCd - Brittle Fracture
Cm - Aspect Before AnalysisDf - Brittle Fracture
ML00098 — Brittle Fracture of a Casting Lifting DeviceM - Low Alloy Medium Carbon QTP - CastingAp - LiftingCd - Brittle Fracture
Aspect of the fracture surface, showing a brittle morphology. Flat fracture with chevron marks from regions close to the internal diameter of the padeye, where there are secondary cracks.
22
VIEW
ML00098 / Nov.2017
Brittle Fracture of a Casting Lifting Device
M - Low Alloy Medium Carbon QTP - CastingAp - LiftingCd - Brittle Fracture
Cm - Aspect Before AnalysisDf - Fracture
ML00041 — Fatigue Fracture of Inconel 718 Spline ShaftM - NiCrFe AlloyP - ShaftAp - Oil and GasCd - Vibration Induced Fatigue
xx
117
VIEW
ML00041 / Jun.2017
Fatigue Fracture of Inconel 718 Spline Shaft
M - NiCrFe AlloyP - ShaftAp - Oil and GasCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - At the Surface
Macroscopic aspect of the 1" shaft fracture surface, revealing beach marks at the surface typical of fatigue, initiated from the surface of the spline shaft at the gear position.
121
VIEW
ML00041 / Jun.2017
Fatigue Fracture of Inconel 718 Spline Shaft
M - NiCrFe AlloyP - ShaftAp - Oil and GasCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - Fatigue Fracture

View all 25 images in the Atlas →

most recent

The location of the threaded fitting started leaking after less than five years in service. Although the corrosion rate was not high, the localized material loss in the threaded surface of the carbon steel flange allowed the connection leakage.
769
VIEW
ML00184 / Apr.2023
Dissimilar Steels in a Threaded Connection
M - Low Carbon SteelP - ForgingAp - OffshoreCd - Localized Dissolution
Cm - Aspect Before AnalysisDf - General View
Front wheel 17 x 7J of a passenger vehicle (identified as WHEEL 1) that broke during a car accident on a road.
1644
VIEW
ML00183 / Dec.2022
Ductile Behavior of an Aluminum Wheel
M - Aluminum Silicon MagnesiumP - CastingAp - AutomotiveCd - Ductile Behavior
Cm - Aspect Before AnalysisDf - General View
Tool fixture 5" long, nominal diameter 2", presenting a recess 1/2" deep from two sides. The rupture occurred about 2" from the end of the rod. Scale in milimeters.
523
VIEW
ML00182 / Jul.2022
Brittle Fracture of a LAS Fixing Rod
M - Low Alloy Medium Carbon QTP - StemAp - Mechanical IndustryCd - Brittle Fracture
Cm - Aspect Before AnalysisDf - General View
Pinion of hypoid gearbox, assembled in a 1560-mm long shaft that operated during more than 60,000 hours, and removed from service due to unacceptable wear damage.
1028
VIEW
ML00181 / Apr.2022
Wear of a Carburized Hypoid Gear
M - Low Alloy for Thermochemical TreatmentP - Pinion-crown assemblyAp - ShipCd - Wear
Cm - Aspect Before AnalysisDf - General View
Aspect of the 3 1/2" diameter tube after the water leakage in high temperature.
963
VIEW
ML00180 / Mar.2022
Local Melting of Copper Cooling Tubes
M - Pure CopperP - Cooling TubeAp - SiderurgyCd - Overheating
Cm - Aspect Before AnalysisDf - General View
2" drain line from the main 10" line. The leakage occurred at the margin of the weld, a short time after the introduction of the reinforced ribs to reduce vibration.
641
VIEW
ML00179 / Feb.2022
Hydrides in Titanium Weld
M - Unalloyed TitaniumP - In Field WeldAp - Chemical IndustryCd - Hydride Formation
Cm - Field photoDf - General View
The drilling connector, 21" diameter, presented a crack at the margin of the weld in the forging side (left side of the weld in the figure).
745
VIEW
ML00178 / Jan.2022
Cold cracks in Cr-Mo Welded Forging
M - CrMo SteelP - ForgingAp - O&G Well DrillingCd - Welding Defect
Cm - Aspect Before AnalysisDf - General View
Macrography of the longitudinally seam weld of the 24" diameter tube, showing that it was welded from both sides and there is a segregation line in the center of the tube thickness.
737
VIEW
ML00177 / Dec.2021
Cr-Mo Seam Welded Tube
M - CrMo SteelP - Longitudinally Seam WeldedAp - Fired HeaterCd - Not according to spec
Cm - NItal Etched MacroDf - Seam
The titanium rotor blade of a flowmeter broke after two years in service in an acid environment, containing H2S.
339
VIEW
ML00176 / Nov.2021
Hydride Formation in a Titanium Blade
M - Unalloyed TitaniumP - BladeAp - Oil and GasCd - Hydride Formation
Cm - Aspect Before AnalysisDf - General View
Aspect of the wire rope, 1 1/2" diameter, presenting regions of flattened areas at the surface of the outer wires. It is a 6 x 19 Seale construction, right regular lay.
553
VIEW
ML00175 / Aug.2021
Localized External Wear of a Wire Rope
M - High Carbon SteelP - Wire RopeAp - Oil and GasCd - Wear
Cm - Aspect Before AnalysisDf - General View
The carcass was manufactured using niobium stabilized plates, grade AISI 347, with circumferential welds, where the through wall cracks were detected.
302
VIEW
ML00174 / Jul.2021
Carburization of a 347 SS Welded Joint
M - Austenitic Stainless SteelP - Fabrication WeldAp - EnergyCd - Carburization
Cm - Field photoDf - General View
Aged microstructure of the HP stainless steel, modified with 1%Nb, cast fitting, tubular, operating for 6 years in a furnace which design temperature is 1100°C. The material presented a network of primary carbides, white and grey, and an austenitic matrix with coalescing secondary precipitation. Some voids. The Vickers identation indicates a hardness value about 260HV 100g in the aged austenitic matrix.
492
VIEW
ML00173 / May.2021
Welding Cracks in an Aged HP Cast Fitting
M - Heat Resistant SteelP - Cast FtittingAp - PetrochemicalCd - Welding
Cm - Kalling Etched Micrography by OMDf - Microhardness identations