Crevice Corrosion in a Subsea System — Aspect Before Analysis

58 images for "fracture"

TryAged MartensiteML00156corrosionCoating LayerML00001brittle fractureFerrous Alloysductile behaviorHigh Alloy SteelfatigueDamagehydrogenHydrogenfractureembrittlementstress corrosion
Application: Subsea Capture method: Optical Microscope clear all
M

Material

79 classified

Browse all Material →
P

Product

96 classified

Browse all Product →
Ap

Application

37 classified

Browse all Application →
C

Condition

84 classified

Browse all Condition →
Cm

Capture method

52 classified

Browse all Capture method →
Df

Detail focus

208 classified

Browse all Detail focus →

Sharpest next filters

Browse by category (2)
Microstructure5
Standard16
+8 more

The Materials
Image Database

58 images for "fracture"
Micrography of a longitudinal section, in the center, of the broken 5/8" bolt, presenting an aged martensitic structure. There are vertical "lines" that correspond to segregation bands due to the forming direction. These bands are evident only using low magnification microscopy.
168
VIEW
ML00139 / Jun.2018
Hydrogen Fracture of a 17-4 PH Allen Bolt
M - Precipitation Hardened Stainless SteelP - Allen BoltAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Longitudinal Section
Microstructural analysis of the valve body structure, close to the position where the cracking has occurred. The structure is ferritic austenitic, with a large amount of detrimental phases associated to the ferritic structure, probably sigma phase.
106
VIEW
ML00134 / Aug.2020
Brittle Fracture of a Superduplex Valve Body
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Cm - NaOH Electrolytic Etched MicroDf - Sigma
Micrography of the longitudinal section of the bolt showing a martensitic structure, with segregation bands evidenced by the chemical etch.
99
VIEW
ML00126 / Mar.2018
Hydrogen Fracture of Subsea Allen Bolts
M - Low Alloy Medium Carbon QTP - Coated ProductAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Banded Structure
Micrography of the pin longitudinal section (transverse to the fracture), in low magnification, close to the external surface of the pin (right side of the figure). The fracture (in the top of the figure) is flat, also evidencing no plastic deformation.
41
VIEW
ML00088 / Dec.2017
Hydrogen Cracking of an API 5D S135 Drill Pipe
M - Low Alloy Medium Carbon QTP - Drill PipeAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Fracture
Micrography of the longitudinal section of the conector, at the fracture position, showing secondary cracks from the fracture surface.
64
VIEW
ML00078 / Jun.2017
Hydrogen Cracking of IN 718 Subsea Connector
M - NiCrFe AlloyP - ForgingAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Fracture
Micrography of a longitudinal section of the bolt, showing the (secondary) cracks, longitudinal, connected to the fracture surface (in the top).
78
VIEW
ML00077 / Jun.2018
Hydrogen Cracking of LAS Subsea Bolts
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Fracture
Micrographic detail of a longitudinal section of the wire, at the fracture surface (top of the figure) evidencing the intergranular and transgranular aspects of the hydrogen assisted cracking mechanism. The electrolytic oxalic acid etch reveals the delta ferrite phase. Compare with the Kalling etch in the other figure.
31
VIEW
ML00076 / Jun.2017
Hydrogen Cracking of a 17-7 PH Subsea Spring
M - Precipitation Hardened Stainless SteelP - WireAp - SubseaCd - Hydrogen Embrittlement
Cm - Micrography by OM using A262 Method ADf - Fracture
Micrography of a longitudinal section of the stud, at the fracture surface, in the thread.
44
VIEW
ML00075 / Jun.2018
Hydrogen Cracking of IN 718 Subsea Fasteners
M - NiCrFe AlloyP - StudAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Fracture

More from these cases

ML00139 — Hydrogen Fracture of a 17-4 PH Allen BoltM - Precipitation Hardened Stainless SteelP - Allen BoltAp - SubseaCd - Hydrogen Embrittlement
Micrography of a longitudinal section, in the center, of the broken 5/8" bolt, presenting an aged martensitic structure.
133
VIEW
ML00139 / Jun.2018
Hydrogen Fracture of a 17-4 PH Allen Bolt
M - Precipitation Hardened Stainless SteelP - Allen BoltAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Martensite
Micrographic detail of the aged martensitic structure. The bolt presented variations in the previous austenite grain boundaries from the center of the thickness to the surface. No delta ferrite or retained austenite islands are evidenced.
107
VIEW
ML00139 / Jun.2018
Hydrogen Fracture of a 17-4 PH Allen Bolt
M - Precipitation Hardened Stainless SteelP - Allen BoltAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Martensite
Micrography of a longitudinal section of the 5/8" bolt, at the bottom of the thread, presenting a refined structure compared to the center of the bolt and a mark at the thread flank that was probably created during tightening of the bolt.
95
VIEW
ML00139 / Jun.2018
Hydrogen Fracture of a 17-4 PH Allen Bolt
M - Precipitation Hardened Stainless SteelP - Allen BoltAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Longitudinal Section
Micrography of a longitudinal section of the 5/8" bolt, at the bottom of the thread, presenting a refined structure compared to the center of the bolt. The structure is aged martensite.
91
VIEW
ML00139 / Jun.2018
Hydrogen Fracture of a 17-4 PH Allen Bolt
M - Precipitation Hardened Stainless SteelP - Allen BoltAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Martensite
Micrographic detail of the aged martensite structure, refined when compared to the structure in the center of the bolt.
87
VIEW
ML00139 / Jun.2018
Hydrogen Fracture of a 17-4 PH Allen Bolt
M - Precipitation Hardened Stainless SteelP - Allen BoltAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Martensite

+19 more from this case →

ML00134 — Brittle Fracture of a Superduplex Valve BodyM - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Micrographic detail of the valve body structure, close to the position where the cracking has occurred. The structure is ferritic austenitic, with a large amount of detrimental phases associated to the ferritic structure, probably sigma phase.
102
VIEW
ML00134 / Aug.2020
Brittle Fracture of a Superduplex Valve Body
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Cm - NaOH Electrolytic Etched MicroDf - Sigma
Metallographic detail of the large amount of sigma phase, associated to the ferritic structure.
105
VIEW
ML00134 / Aug.2020
Brittle Fracture of a Superduplex Valve Body
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Cm - NaOH Electrolytic Etched MicroDf - Sigma
Microstructural analysis of the valve body structure, far from the position where the cracking has occurred, in the bottom of the body. The structure is ferritic austenitic, with some sigma phase, not in a large amount, indicating the valve structure was not uniform.
67
VIEW
ML00134 / Aug.2020
Brittle Fracture of a Superduplex Valve Body
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Cm - NaOH Electrolytic Etched MicroDf - Ferrite and Austenite
Micrographic detail of the valve body structure, far from the position where the cracking has occurred, in the bottom of the body. The structure is ferritic austenitic, with some sigma phase, not in a large amount, indicating the valve structure was not uniform.
63
VIEW
ML00134 / Aug.2020
Brittle Fracture of a Superduplex Valve Body
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Cm - NaOH Electrolytic Etched MicroDf - Ferrite and Austenite
Micrographic detail of the valve body structure, far from the position where the cracking has occurred, in the bottom of the body. The structure is ferritic austenitic, with some sigma phase, not in a large amount, indicating the valve structure was not uniform.
61
VIEW
ML00134 / Aug.2020
Brittle Fracture of a Superduplex Valve Body
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Cm - NaOH Electrolytic Etched MicroDf - Ferrite and Austenite

+8 more from this case →

ML00126 — Hydrogen Fracture of Subsea Allen BoltsM - Low Alloy Medium Carbon QTP - Coated ProductAp - SubseaCd - Hydrogen Embrittlement
Micrography of the longitudinal section of the bolt at the bottom of the thread fillet, showing the uniform martensitic structure, not strain hardened.
90
VIEW
ML00126 / Mar.2018
Hydrogen Fracture of Subsea Allen Bolts
M - Low Alloy Medium Carbon QTP - Coated ProductAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Uniform Structure
Micrography of the longitudinal section of the bolt at the top of the thread fillet, showing a small circunferential cracking typically of a rolling process to manufacture the thread. The thread presented no evidences of plastic deformation suggesting that the heat treatment was applied later. It is important to mention that this cracking presented no influence in the fracture of the bolt.
101
VIEW
ML00126 / Mar.2018
Hydrogen Fracture of Subsea Allen Bolts
M - Low Alloy Medium Carbon QTP - Coated ProductAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Rolled Thread
Micrography of the longitudinal section of the bolt at the bottom of the thread fillet, in the "as polished" condition, showing the zinc flakes coating layer, applied by a painting process that do not create metallurgical bonding with the substrate.
82
VIEW
ML00126 / Mar.2018
Hydrogen Fracture of Subsea Allen Bolts
M - Low Alloy Medium Carbon QTP - Coated ProductAp - SubseaCd - Hydrogen Embrittlement
Cm - As polished micrographyDf - Coating Layer
Micrographic detail of the zinc flakes coating layer in the "as polished" condition of a longitudinal section of the bolt.
71
VIEW
ML00126 / Mar.2018
Hydrogen Fracture of Subsea Allen Bolts
M - Low Alloy Medium Carbon QTP - Coated ProductAp - SubseaCd - Hydrogen Embrittlement
Cm - As polished micrographyDf - Coating Layer
Micrography of the longitudinal section of the bolt in the center of the thickness (ND 5/8") showing a uniform martensitic structure.
67
VIEW
ML00126 / Mar.2018
Hydrogen Fracture of Subsea Allen Bolts
M - Low Alloy Medium Carbon QTP - Coated ProductAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Martensite

+5 more from this case →

ML00077 — Hydrogen Cracking of LAS Subsea BoltsM - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Micrographic detail of the (secondary) cracks, longitudinal, connected to the fracture surface (in the top).
69
VIEW
ML00077 / Jun.2018
Hydrogen Cracking of LAS Subsea Bolts
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Fracture
Micrographic detail of the (secondary) cracks, longitudinal, connected to the fracture surface (in the top).
72
VIEW
ML00077 / Jun.2018
Hydrogen Cracking of LAS Subsea Bolts
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Fracture
ML00076 — Hydrogen Cracking of a 17-7 PH Subsea SpringM - Precipitation Hardened Stainless SteelP - WireAp - SubseaCd - Hydrogen Embrittlement
Micrographic detail of a longitudinal section of the wire, at the fracture surface (top of the figure) evidencing the intergranular and transgranular aspects of the hydrogen assisted cracking mechanism. The Kalling etch does not reveal the delta ferrite. Compare with the electrolytic oxalic acid etch in the other figure.
29
VIEW
ML00076 / Jun.2017
Hydrogen Cracking of a 17-7 PH Subsea Spring
M - Precipitation Hardened Stainless SteelP - WireAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Fracture

View all 58 images in the Atlas →

most recent

The location of the threaded fitting started leaking after less than five years in service. Although the corrosion rate was not high, the localized material loss in the threaded surface of the carbon steel flange allowed the connection leakage.
769
VIEW
ML00184 / Apr.2023
Dissimilar Steels in a Threaded Connection
M - Low Carbon SteelP - ForgingAp - OffshoreCd - Localized Dissolution
Cm - Aspect Before AnalysisDf - General View
Front wheel 17 x 7J of a passenger vehicle (identified as WHEEL 1) that broke during a car accident on a road.
1644
VIEW
ML00183 / Dec.2022
Ductile Behavior of an Aluminum Wheel
M - Aluminum Silicon MagnesiumP - CastingAp - AutomotiveCd - Ductile Behavior
Cm - Aspect Before AnalysisDf - General View
Tool fixture 5" long, nominal diameter 2", presenting a recess 1/2" deep from two sides. The rupture occurred about 2" from the end of the rod. Scale in milimeters.
523
VIEW
ML00182 / Jul.2022
Brittle Fracture of a LAS Fixing Rod
M - Low Alloy Medium Carbon QTP - StemAp - Mechanical IndustryCd - Brittle Fracture
Cm - Aspect Before AnalysisDf - General View
Pinion of hypoid gearbox, assembled in a 1560-mm long shaft that operated during more than 60,000 hours, and removed from service due to unacceptable wear damage.
1028
VIEW
ML00181 / Apr.2022
Wear of a Carburized Hypoid Gear
M - Low Alloy for Thermochemical TreatmentP - Pinion-crown assemblyAp - ShipCd - Wear
Cm - Aspect Before AnalysisDf - General View
Aspect of the 3 1/2" diameter tube after the water leakage in high temperature.
963
VIEW
ML00180 / Mar.2022
Local Melting of Copper Cooling Tubes
M - Pure CopperP - Cooling TubeAp - SiderurgyCd - Overheating
Cm - Aspect Before AnalysisDf - General View
2" drain line from the main 10" line. The leakage occurred at the margin of the weld, a short time after the introduction of the reinforced ribs to reduce vibration.
641
VIEW
ML00179 / Feb.2022
Hydrides in Titanium Weld
M - Unalloyed TitaniumP - In Field WeldAp - Chemical IndustryCd - Hydride Formation
Cm - Field photoDf - General View
The drilling connector, 21" diameter, presented a crack at the margin of the weld in the forging side (left side of the weld in the figure).
745
VIEW
ML00178 / Jan.2022
Cold cracks in Cr-Mo Welded Forging
M - CrMo SteelP - ForgingAp - O&G Well DrillingCd - Welding Defect
Cm - Aspect Before AnalysisDf - General View
Macrography of the longitudinally seam weld of the 24" diameter tube, showing that it was welded from both sides and there is a segregation line in the center of the tube thickness.
737
VIEW
ML00177 / Dec.2021
Cr-Mo Seam Welded Tube
M - CrMo SteelP - Longitudinally Seam WeldedAp - Fired HeaterCd - Not according to spec
Cm - NItal Etched MacroDf - Seam
The titanium rotor blade of a flowmeter broke after two years in service in an acid environment, containing H2S.
339
VIEW
ML00176 / Nov.2021
Hydride Formation in a Titanium Blade
M - Unalloyed TitaniumP - BladeAp - Oil and GasCd - Hydride Formation
Cm - Aspect Before AnalysisDf - General View
Aspect of the wire rope, 1 1/2" diameter, presenting regions of flattened areas at the surface of the outer wires. It is a 6 x 19 Seale construction, right regular lay.
552
VIEW
ML00175 / Aug.2021
Localized External Wear of a Wire Rope
M - High Carbon SteelP - Wire RopeAp - Oil and GasCd - Wear
Cm - Aspect Before AnalysisDf - General View
The carcass was manufactured using niobium stabilized plates, grade AISI 347, with circumferential welds, where the through wall cracks were detected.
301
VIEW
ML00174 / Jul.2021
Carburization of a 347 SS Welded Joint
M - Austenitic Stainless SteelP - Fabrication WeldAp - EnergyCd - Carburization
Cm - Field photoDf - General View
Aged microstructure of the HP stainless steel, modified with 1%Nb, cast fitting, tubular, operating for 6 years in a furnace which design temperature is 1100°C. The material presented a network of primary carbides, white and grey, and an austenitic matrix with coalescing secondary precipitation. Some voids. The Vickers identation indicates a hardness value about 260HV 100g in the aged austenitic matrix.
492
VIEW
ML00173 / May.2021
Welding Cracks in an Aged HP Cast Fitting
M - Heat Resistant SteelP - Cast FtittingAp - PetrochemicalCd - Welding
Cm - Kalling Etched Micrography by OMDf - Microhardness identations