Sampling and Analysis

29 cases · 147 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Microstructure: Austenite clear all

Sampling and Analysis — sub-branches

At the Surface 12Base Metal 7Close to the External Surface 15Close to the Internal Surface 8External Surface 7Fusion Line 5General View 23Heat Affected Zone 4In the Center of the Thickness 7Internal Surface 3Longitudinal Section 21Low Mag 5Transverse Section 10Weld Metal 8Welded Joint 12

Results

SortNewestOldestTitle A-ZTitle Z-A
The carcass was manufactured using niobium stabilized plates, grade AISI 347, with circumferential welds, where the through wall cracks were detected.
300
VIEW
ML00174 / Jul.2021
Carburization of a 347 SS Welded Joint
M - Austenitic Stainless SteelP - Fabrication WeldAp - EnergyCd - Carburization
Cm - Field photoDf - General View
Aspect of the stub end, that is used in combination with a lap joint flange. In this case it was prepared from a seam welded pipe, longitudinal, also with circunferential weld to the stub face (which means it was not flared). The cracking is circunferential in the non painted region, not associated to any welded area.
435
VIEW
ML00168 / Aug.2020
SCC of Austenitic SS Flange Stub End
M - Austenitic Stainless SteelP - Stub EndAp - Chemical IndustryCd - Stress Corrosion
Cm - Aspect Before AnalysisDf - General View
Aspect of a flared tubing, cold deformed at 37°, and the circumferential cracking.
483
VIEW
ML00167 / Aug.2020
Fatigue of a Flared Tubing Connection
M - Austenitic Stainless SteelP - TubingAp - EngineCd - Mechanical Fatigue
Cm - Aspect Before AnalysisDf - General View
As received aspect of the sacrificial casting, 2" internal diameter. The casting was solution annealed heat treated.
488
VIEW
ML00164 / Jun.2020
Austenitic SS Casting for Valve Body
M - Austenitic Stainless SteelP - CastingAp - ValveCd - Typical manufacturing
Cm - Aspect Before AnalysisDf - General View
Aspect as received, side A, of the part removed from the rectangular tube that was manufactured from plates, and originally presented two welded seams (not included in the sample). Close to the edges of the sample, where probably were the corners of the rectangular tube, the degradation is in a highest level. Three samples were analysed, with different thicknesses (indicated in the figure). Side A is the side that was in contact with the reaction (product side).
445
VIEW
ML00160 / Apr.2020
High Temperature Degradation of 310SS
M - Austenitic Stainless SteelP - Rectangular TubeAp - Chemical IndustryCd - Scaling
Cm - Aspect Before AnalysisDf - General View
Aspect of a 5/16" bolt manufactured in an AISI 316 austenitic stainless steel, that was also operating inside the pressure vessel, but was not yet damaged. It is a hexagonal head bolt, 1 1/2" long, fastened with a hexagonal nut and a lock washer.
118
VIEW
ML00157 / Feb.2020
Bolts Under Chloride SCC Conditions
M - Austenitic Stainless SteelP - BoltAp - Oil and GasCd - Stress Corrosion
Cm - Aspect Before AnalysisDf - General View
Aspect of the internal side of the drilling tool, after cleaning for inspection. Several regions of corrosion where detected where the drilling mud was adhered and remained uncleaned for a period a little longer than 1 month.
775
VIEW
ML00135 / May.2018
MIC of a Non Magnetic Drilling Tool
M - High Mn Austenitic SteelP - Tubular ForgingAp - O&G Well DrillingCd - Pitting Corrosion
Cm - Aspect Before AnalysisDf - Internal Surface
The 6 1/2" nominal diameter longitudinal seam welded pipe is internally cladded with Alloy 625. The pipe was manufactured by forming a cladded plate (probably welded by rolling) and welding it longitudinally. The pipe was heat treated (quenched and tempered) after the seam weld.
96
VIEW
ML00133 / May.2018
Seam Welded Pipe Cladded with Alloy 625
M - LAS / Ni AlloyP - Longitudinal Seam Welded PipeAp - Oil and GasCd - Welding
Cm - Aspect Before AnalysisDf - Welded Joint

More from these cases

ML00174 — Carburization of a 347 SS Welded JointM - Austenitic Stainless SteelP - Fabrication WeldAp - EnergyCd - Carburization
Aspect of one region where the cracks appeared, after grinding and polishing. Several branched cracks located in welded regions. It is the region where the sample was taken.
36
VIEW
ML00174 / Jul.2021
Carburization of a 347 SS Welded Joint
M - Austenitic Stainless SteelP - Fabrication WeldAp - EnergyCd - Carburization
Cm - Aspect Before AnalysisDf - At the Surface
Sample surface. Microstructure of the plate base metal, exposed to high temperature exhausting gases. Refined austenite and some cracks.
24
VIEW
ML00174 / Jul.2021
Carburization of a 347 SS Welded Joint
M - Austenitic Stainless SteelP - Fabrication WeldAp - EnergyCd - Carburization
Cm - Oxalic Acid Electrolytic EtchDf - Base Metal
Sample surface. Microstructure of the weld metal, exposed to high temperature exhausting gases. Austeno-ferritic structure and some cracks.
20
VIEW
ML00174 / Jul.2021
Carburization of a 347 SS Welded Joint
M - Austenitic Stainless SteelP - Fabrication WeldAp - EnergyCd - Carburization
Cm - Oxalic Acid Electrolytic EtchDf - Weld Metal
Sample surface. Microstructure of the heat affected zone (weld metal to the left side and base metal to the right side), exposed to high temperature exhausting gases. Large austenitic grain size and cracks fully opened and filled with oxides.
24
VIEW
ML00174 / Jul.2021
Carburization of a 347 SS Welded Joint
M - Austenitic Stainless SteelP - Fabrication WeldAp - EnergyCd - Carburization
Cm - Oxalic Acid Electrolytic EtchDf - Heat Affected Zone
ML00168 — SCC of Austenitic SS Flange Stub EndM - Austenitic Stainless SteelP - Stub EndAp - Chemical IndustryCd - Stress Corrosion
The stub end was manufactured from a plate and the microstructure in a longitudial section shows a refined granular austenitic structure.
62
VIEW
ML00168 / Aug.2020
SCC of Austenitic SS Flange Stub End
M - Austenitic Stainless SteelP - Stub EndAp - Chemical IndustryCd - Stress Corrosion
Cm - Oxalic Acid Electrolytic EtchDf - Longitudinal Section
Micrography of the stub end, external side to the top, presenting multiple cracks propagating throught wall.
48
VIEW
ML00168 / Aug.2020
SCC of Austenitic SS Flange Stub End
M - Austenitic Stainless SteelP - Stub EndAp - Chemical IndustryCd - Stress Corrosion
Cm - As polished micrographyDf - Close to the External Surface
Aspect of the stub end. The cracking is circunferential in the middle of the non-painted region, not associated to any welded area.
36
VIEW
ML00168 / Aug.2020
SCC of Austenitic SS Flange Stub End
M - Austenitic Stainless SteelP - Stub EndAp - Chemical IndustryCd - Stress Corrosion
Cm - Aspect Before AnalysisDf - General View
Macrography of the longitudinal section of the stub end, showing the external side to the top and the internal side to the bottom. The stub end was manufactured by welding, longitudinal seam (not evidenced in this image) and circunferential weld of tube to disc (partial penetration). The cracks starts from the external side of the stub end.
31
VIEW
ML00168 / Aug.2020
SCC of Austenitic SS Flange Stub End
M - Austenitic Stainless SteelP - Stub EndAp - Chemical IndustryCd - Stress Corrosion
Cm - Macro Oxalic Acid Electrolytic EtchedDf - Longitudinal Section
Micrography of the stub end close to the external surface, outer diameter in the top of the image, presenting multiple cracks starting fro the surface and propagating into the thickness, through wall.
32
VIEW
ML00168 / Aug.2020
SCC of Austenitic SS Flange Stub End
M - Austenitic Stainless SteelP - Stub EndAp - Chemical IndustryCd - Stress Corrosion
Cm - Oxalic Acid Electrolytic EtchDf - Close to the External Surface

+1 more from this case →

ML00167 — Fatigue of a Flared Tubing ConnectionM - Austenitic Stainless SteelP - TubingAp - EngineCd - Mechanical Fatigue
Same flared tubing, with a circumferential crack, with the focus at the internal side.
65
VIEW
ML00167 / Aug.2020
Fatigue of a Flared Tubing Connection
M - Austenitic Stainless SteelP - TubingAp - EngineCd - Mechanical Fatigue
Cm - Aspect Before AnalysisDf - General View
Micrography of a longitudinal section of the tubing showing a granular structure, austenitic.
52
VIEW
ML00167 / Aug.2020
Fatigue of a Flared Tubing Connection
M - Austenitic Stainless SteelP - TubingAp - EngineCd - Mechanical Fatigue
Cm - Oxalic Acid Electrolytic EtchDf - Longitudinal Section
Fracture surface of the tubing, close to the outer diameter.
47
VIEW
ML00167 / Aug.2020
Fatigue of a Flared Tubing Connection
M - Austenitic Stainless SteelP - TubingAp - EngineCd - Mechanical Fatigue
Cm - Fractography by SEMDf - Close to the External Surface
Micrography of a longitudinal section of the tubing where the fracture occurred. the left side is the outer diameter and the right side is the inner diameter.
37
VIEW
ML00167 / Aug.2020
Fatigue of a Flared Tubing Connection
M - Austenitic Stainless SteelP - TubingAp - EngineCd - Mechanical Fatigue
Cm - Oxalic Acid Electrolytic EtchDf - At the Surface
ML00164 — Austenitic SS Casting for Valve BodyM - Austenitic Stainless SteelP - CastingAp - ValveCd - Typical manufacturing
Macrography of a longitudinal section of the valve body, presenting the granular structure. The main bore diameter is 2". The casting was tested in two positions. In radial direction in the center of the body (3" solid), and in the longitudinal direction in the wall (1" thick).
78
VIEW
ML00164 / Jun.2020
Austenitic SS Casting for Valve Body
M - Austenitic Stainless SteelP - CastingAp - ValveCd - Typical manufacturing
Cm - Macro Oxalic Acid Electrolytic EtchedDf - Longitudinal Section
ML00160 — High Temperature Degradation of 310SSM - Austenitic Stainless SteelP - Rectangular TubeAp - Chemical IndustryCd - Scaling
Aspect as received, side B, of the same part. Side B is the external side of the rectangular tube, that was in contact with the electric furnace atmosphere. This surface of side B presented less degradation than the internal surface (side A).
88
VIEW
ML00160 / Apr.2020
High Temperature Degradation of 310SS
M - Austenitic Stainless SteelP - Rectangular TubeAp - Chemical IndustryCd - Scaling
Cm - Aspect Before AnalysisDf - General View
SAMPLE 1 AT THE FRACTURE - Micrography in low magnification where the thickness is reduced to zero (fracture). Side A (process side) to the bottom and side B (furnace environment side) to the top.
85
VIEW
ML00160 / Apr.2020
High Temperature Degradation of 310SS
M - Austenitic Stainless SteelP - Rectangular TubeAp - Chemical IndustryCd - Scaling
Cm - Oxalic Acid Electrolytic EtchDf - Low Mag
SAMPLE 1 AT 1 mm THICKNESS - Micrography in low magnification in the center of the thickness. The microstructure is austenitic with secondary intergranular and intragranular precipitation.
76
VIEW
ML00160 / Apr.2020
High Temperature Degradation of 310SS
M - Austenitic Stainless SteelP - Rectangular TubeAp - Chemical IndustryCd - Scaling
Cm - Oxalic Acid Electrolytic EtchDf - Low Mag
SAMPLE 2 AT 2 mm THICKNESS - Micrography in low magnification in the center of the thickness. The microstructure is austenitic with secondary intergranular and intragranular precipitation. No variation in the microstructure of the center of the plate, compared to sample 1.
52
VIEW
ML00160 / Apr.2020
High Temperature Degradation of 310SS
M - Austenitic Stainless SteelP - Rectangular TubeAp - Chemical IndustryCd - Scaling
Cm - Oxalic Acid Electrolytic EtchDf - Low Mag
SAMPLE 3 AT 4 mm THICKNESS - Micrography in low magnification in the center of the thickness. The microstructure is austenitic with secondary intergranular and intragranular precipitation, but this micrography was obtained in the longitudinal section, presenting the plate alignment and was etched with NaOH, adopted to colour the sigma phase .
40
VIEW
ML00160 / Apr.2020
High Temperature Degradation of 310SS
M - Austenitic Stainless SteelP - Rectangular TubeAp - Chemical IndustryCd - Scaling
Cm - NaOH Electrolytic Etched MicroDf - Low Mag

+6 more from this case →

ML00157 — Bolts Under Chloride SCC ConditionsM - Austenitic Stainless SteelP - BoltAp - Oil and GasCd - Stress Corrosion
Low magnification microscope image showing the aspect of the thread close to the fracture surface. Looks like a wear or strong corrosion, but in fact the threads were removed because they were cracked, as can be seen in the next figures.
67
VIEW
ML00157 / Feb.2020
Bolts Under Chloride SCC Conditions
M - Austenitic Stainless SteelP - BoltAp - Oil and GasCd - Stress Corrosion
Cm - Surface AspectDf - Low Mag
Macrography of the longitudinal section of a fractured bolt, still threaded to the nut and with the lock washer. The cracks can be seen in several positions: in the threads (removing then); in the center of the bolt (branched) and also in the washer (longitudinal branched cracks).
65
VIEW
ML00157 / Feb.2020
Bolts Under Chloride SCC Conditions
M - Austenitic Stainless SteelP - BoltAp - Oil and GasCd - Stress Corrosion
Cm - Macro Oxalic Acid Electrolytic EtchedDf - Longitudinal Section
ML00135 — MIC of a Non Magnetic Drilling ToolM - High Mn Austenitic SteelP - Tubular ForgingAp - O&G Well DrillingCd - Pitting Corrosion
Aspect of the external side of the nominal diameter 6 3/4" drilling tool, after cleaning for inspection. Several regions of corrosion where detected where the drilling mud was adhered and remained for a period a little longer than 1 month. This tool is a high strength steel, cold worked.
163
VIEW
ML00135 / May.2018
MIC of a Non Magnetic Drilling Tool
M - High Mn Austenitic SteelP - Tubular ForgingAp - O&G Well DrillingCd - Pitting Corrosion
Cm - Aspect Before AnalysisDf - General View
Optical micrography of the transverse section of the drill collar, in the center of the thickness, presenting an uniform, granular, fully austenitic microstructure.
76
VIEW
ML00135 / May.2018
MIC of a Non Magnetic Drilling Tool
M - High Mn Austenitic SteelP - Tubular ForgingAp - O&G Well DrillingCd - Pitting Corrosion
Cm - Oxalic Acid Electrolytic EtchDf - Transverse Section
Optical micrography of the transverse section of the drill collar, in the center of the thickness, presenting an uniform, granular, fully austenitic microstructure.
64
VIEW
ML00135 / May.2018
MIC of a Non Magnetic Drilling Tool
M - High Mn Austenitic SteelP - Tubular ForgingAp - O&G Well DrillingCd - Pitting Corrosion
Cm - Oxalic Acid Electrolytic EtchDf - Transverse Section
Optical micrography of the longitudinal section of the drill collar, in the center of the thickness, presenting slightly elongated grains of fully austenitic microstructure, cold worked. The material presented 38HRc hardness.
57
VIEW
ML00135 / May.2018
MIC of a Non Magnetic Drilling Tool
M - High Mn Austenitic SteelP - Tubular ForgingAp - O&G Well DrillingCd - Pitting Corrosion
Cm - Oxalic Acid Electrolytic EtchDf - Longitudinal Section
Optical micrography of the longitudinal section of the drill collar, in the center of the thickness, presenting slightly elongated grains of fully austenitic microstructure, cold worked.
62
VIEW
ML00135 / May.2018
MIC of a Non Magnetic Drilling Tool
M - High Mn Austenitic SteelP - Tubular ForgingAp - O&G Well DrillingCd - Pitting Corrosion
Cm - Oxalic Acid Electrolytic EtchDf - Longitudinal Section

+4 more from this case →

ML00133 — Seam Welded Pipe Cladded with Alloy 625M - LAS / Ni AlloyP - Longitudinal Seam Welded PipeAp - Oil and GasCd - Welding
The macrography of a longitudinal section shows the low alloy (C-Mn) steel pipe, internally cladded with Ni alloy clad plate.
72
VIEW
ML00133 / May.2018
Seam Welded Pipe Cladded with Alloy 625
M - LAS / Ni AlloyP - Longitudinal Seam Welded PipeAp - Oil and GasCd - Welding
Cm - Electrolytically Etched MacroDf - Longitudinal Section
Micrography of a longitudinal section of the pipe substrate, in low magnification, showing a uniform microstructure,
51
VIEW
ML00133 / May.2018
Seam Welded Pipe Cladded with Alloy 625
M - LAS / Ni AlloyP - Longitudinal Seam Welded PipeAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Base Metal
Micrography of a longitudinal section of the pipe substrate showing a uniform bainitic microstructure obtained by the pipe quenching and tempering,
48
VIEW
ML00133 / May.2018
Seam Welded Pipe Cladded with Alloy 625
M - LAS / Ni AlloyP - Longitudinal Seam Welded PipeAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Longitudinal Section