Microstructure

167 cases · 670 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Microstructure — sub-branches

Acicular Alpha 9Acicular Ferrite 2Aligned particles 5Alpha 4Alpha and Beta 14Austenite 47Austenitic with Primary Carbides 2Austenitic with Secondary Precipitation 7Bainite 16Bainitic Ferrite 7Bainitic HAZ 8Bainitic Martensitic 6Banded Pearlite 8Banded Structure 25Carburized Layer 6Clad Interface 25Coalesced structure 8Coarse Structure 15Coating Layer 10Columnar Grains 5Decarburized Surface 1Delta Ferrite Islands 2Delta ferrite 5Dendritic 3Dual grain sizes 2Duplex structure 21Equiaxial Grains 5Ferrite 8Ferrite and Austenite 7Ferrite and Bainite 4Ferrite and Pearlite 58Ferritic Weld Metal 2Free Carbides in Pearlite Colonies 1Fusion Line 22Grain boundary intermetallics 2Grain refined structure 13Granular structure 10Graphite Type A (ASTM A247) 2Graphite in Flakes 6Graphite in Imperfect Nodules 2Graphite in Nodules 7Hard Chromium Layer 3Hypoeutetic 1Intergranular Precipitation 4Intragranular Secondary Precipitation 6Martensite 101Martensite, delta ferrite & carbides 3Matrix of ferrite and pearlite 5Mixture of Melted Metals 3Network of Primary Carbides 2Networklike precipitates 1Ni layer 2No Coating Layer 3Non Metallic Inclusions 9Overheating 3Overtempered Structure 2Pearlite 13Pearlite Matrix 3Predominantly Ferritic 15Predominantly Pearlitic 5Prior Austenite Boundaries Decorated 1Secondary Precipitation 1Sigma 12Single phase 1Strain Hardened 26Strain hardened pearlite 4Tempered Martensite 4Tempered Structure 1Thermal Spray Layer 8Two phases 4Uniform Structure 4Zn Layer 8

Results

SortNewestOldestTitle A-ZTitle Z-A
Tempered martensite of the pipe body of this API 5D grade S135 drill pipe. The material presents, at this low magnification micrographic aspect, a slightly banded structure, usual for this type of drill pipe.
58
VIEW
ML00159 / Mar.2020
Collapse of a Drill Pipe
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Ductile Behavior
Cm - Nital Etched Micrography by OMDf - Banded Structure
Micrography of the wheel in the center of the thickness, presenting a predominantly pearlitic structure and average hardness abot 196HB.
74
VIEW
ML00158 / Feb.2020
Surface Hardened Carbon Steel Wheel
M - High Carbon SteelP - WheelAp - TransportationCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Coarse Structure
Low magnification micrography, by optical microscope, of the longitudinal section of a damaged bolt, in the center of the thickness. The microstructure is austenitic, free from carbides.
100
VIEW
ML00157 / Feb.2020
Bolts Under Chloride SCC Conditions
M - Austenitic Stainless SteelP - BoltAp - Oil and GasCd - Stress Corrosion
Cm - Oxalic Acid Electrolytic EtchDf - Austenite
Higher magnification detail of the predominantly pearlitic microstructure of the wire.
88
VIEW
ML00155 / Jan.2020
Failure of a Prestressed Concrete Steel Strand
M - High Carbon SteelP - Wire RopeAp - StructureCd - Corrosion Fatigue
Cm - Nital Etched Micrography by OMDf - Predominantly Pearlitic
Low magnification metallography of the coaster after etching, revealing a casting structure of alpha plus beta phases. Beta is the dark brown matrix phase and alpha is the dendritic yellow phase.
45
VIEW
ML00156 / Jan.2020
Antique Silver Plated Decorative Piece
M - BrassP - Decorative PieceAp - OrnamentalCd - Non Destructive Examination
Cm - NH4OH+H2O+H2O2 Etched MicroDf - Alpha and Beta
The 1" flat casting product presents a ferritic perlitic matrix and graphite nodules.
112
VIEW
ML00001 / Dec.2017
Thermal Fatigue of Cast Iron
M - Nodular Cast IronP - CastAp - SiderurgyCd - Thermal Fatigue
Cm - Nital Etched Micrography by OMDf - Graphite in Nodules
As polished micrography of the crankshaft at the shaft edge, close to the surface. Graphite in nodules.
126
VIEW
ML00154 / Jan.2019
High Strength Cast Iron Crankshaft
M - Nodular Cast IronP - CastingAp - EngineCd - Surface treatment
Cm - As polished micrographyDf - Graphite in Nodules
Micrographic detail of the very refined ferritic structure of the base metal, in the longitudinal section, indicating that the material was heat treated, since no banding is not detectable at this magnification.
101
VIEW
ML00153 / Jan.2019
X52 in a Tubular Structure
M - CMn SteelP - Seamless PipeAp - StructureCd - Qualified
Cm - Nital Etched Micrography by OMDf - Grain refined structure

More from these cases

ML00159 — Collapse of a Drill PipeM - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Ductile Behavior
Micrographic detail of the tempered martensite in the longitudinal section of the pipe body. Uniform structure.
44
VIEW
ML00159 / Mar.2020
Collapse of a Drill Pipe
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Ductile Behavior
Cm - Nital Etched Micrography by OMDf - Martensite
Micrographic detail of the tempered martensite in the longitudinal section of the pipe body.
39
VIEW
ML00159 / Mar.2020
Collapse of a Drill Pipe
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Ductile Behavior
Cm - Nital Etched Micrography by OMDf - Martensite
Micrographic detail of sheared pipe, showing strong plastic deformation at the fracture. The structure shows the shear effect at the fracture.
15
VIEW
ML00159 / Mar.2020
Collapse of a Drill Pipe
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Ductile Behavior
Cm - Nital Etched Micrography by OMDf - Martensite
ML00158 — Surface Hardened Carbon Steel WheelM - High Carbon SteelP - WheelAp - TransportationCd - Removed From Service
Micrographic detail of the coarse pearlitic structure in the center of the wheel thickness. The part presents a wrought structure.
73
VIEW
ML00158 / Feb.2020
Surface Hardened Carbon Steel Wheel
M - High Carbon SteelP - WheelAp - TransportationCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Pearlite
Micrographic detail of the tempered martensitic structure.
50
VIEW
ML00158 / Feb.2020
Surface Hardened Carbon Steel Wheel
M - High Carbon SteelP - WheelAp - TransportationCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Martensite
Micrographic aspect of the pearlitic structure at the surface not heat treated, showing a lower grain size than in the center of the thickness.
35
VIEW
ML00158 / Feb.2020
Surface Hardened Carbon Steel Wheel
M - High Carbon SteelP - WheelAp - TransportationCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Pearlite
Micrographic detail of the pearlitic microstructure in a region where the structure is not so coarse than in the center of the thickness.
30
VIEW
ML00158 / Feb.2020
Surface Hardened Carbon Steel Wheel
M - High Carbon SteelP - WheelAp - TransportationCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Pearlite
ML00157 — Bolts Under Chloride SCC ConditionsM - Austenitic Stainless SteelP - BoltAp - Oil and GasCd - Stress Corrosion
Micrography, by optical microscope, of the longitudinal section of a damaged bolt, in the center of the thickness. The microstructure is austenitic, free from carbides, strain hardened. The hardness values of the material are from 200HV1 to 300HV1, that meets the class 2 of strenght (ASTM A193 B8M class 2).
79
VIEW
ML00157 / Feb.2020
Bolts Under Chloride SCC Conditions
M - Austenitic Stainless SteelP - BoltAp - Oil and GasCd - Stress Corrosion
Cm - Nital Etched Micrography by OMDf - Strain Hardened
Detail of the strain hardened austenitic microstructure. Micrography by optical microscope, of the longitudinal section of a bolt, in the center of the thickness.
76
VIEW
ML00157 / Feb.2020
Bolts Under Chloride SCC Conditions
M - Austenitic Stainless SteelP - BoltAp - Oil and GasCd - Stress Corrosion
Cm - Oxalic Acid Electrolytic EtchDf - Strain Hardened
ML00155 — Failure of a Prestressed Concrete Steel StrandM - High Carbon SteelP - Wire RopeAp - StructureCd - Corrosion Fatigue
Test
3
VIEW
ML00155 / Jan.2020
Failure of a Prestressed Concrete Steel Strand
M - High Carbon SteelP - Wire RopeAp - StructureCd - Corrosion Fatigue
Cm - As polishedDf - Acicular Alpha
ushushushs ushush s shus
3
VIEW
ML00155 / Jan.2020
Failure of a Prestressed Concrete Steel Strand
M - High Carbon SteelP - Wire RopeAp - StructureCd - Corrosion Fatigue
Cm - Chromic Acid Electrolytic EtchedDf - Acicular Alpha
fadf asdf asdf
4
VIEW
ML00155 / Jan.2020
Failure of a Prestressed Concrete Steel Strand
M - High Carbon SteelP - Wire RopeAp - StructureCd - Corrosion Fatigue
Cm - As polishedDf - Aligned particles
fasdf asfa sd
5
VIEW
ML00155 / Jan.2020
Failure of a Prestressed Concrete Steel Strand
M - High Carbon SteelP - Wire RopeAp - StructureCd - Corrosion Fatigue
Cm - Nital etched, OMDf - Austenite
fad asdf a
3
VIEW
ML00155 / Jan.2020
Failure of a Prestressed Concrete Steel Strand
M - High Carbon SteelP - Wire RopeAp - StructureCd - Corrosion Fatigue
Cm - Kalling etched, OMDf - Aligned particles

+11 more from this case →

ML00156 — Antique Silver Plated Decorative PieceM - BrassP - Decorative PieceAp - OrnamentalCd - Non Destructive Examination
Metallography of the coaster after etching, revealing a casting structure of alpha plus beta phases. Beta is the dark brown matrix phase and alpha is the dendritic yellow phase.
48
VIEW
ML00156 / Jan.2020
Antique Silver Plated Decorative Piece
M - BrassP - Decorative PieceAp - OrnamentalCd - Non Destructive Examination
Cm - NH4OH+H2O+H2O2 Etched MicroDf - Alpha and Beta
High magnification metallography of the coaster after etching, revealing a casting structure of alpha plus beta phases. Beta is the dark brown matrix phase and alpha is the dendritic yellow phase. The non destructive preparation created a metallographic surface not well polished (full of grinding scratches).
48
VIEW
ML00156 / Jan.2020
Antique Silver Plated Decorative Piece
M - BrassP - Decorative PieceAp - OrnamentalCd - Non Destructive Examination
Cm - NH4OH+H2O+H2O2 Etched MicroDf - Alpha and Beta
ML00001 — Thermal Fatigue of Cast IronM - Nodular Cast IronP - CastAp - SiderurgyCd - Thermal Fatigue
Center of the flat casting product, presenting nodular graphite and ferritic perlitic matrix.
113
VIEW
ML00001 / Dec.2017
Thermal Fatigue of Cast Iron
M - Nodular Cast IronP - CastAp - SiderurgyCd - Thermal Fatigue
Cm - Nital Etched Micrography by OMDf - Predominantly Ferritic Matrix
Nodular cast iron presenting a ferritic perlitic matrix.
109
VIEW
ML00001 / Dec.2017
Thermal Fatigue of Cast Iron
M - Nodular Cast IronP - CastAp - SiderurgyCd - Thermal Fatigue
Cm - Nital Etched Micrography by OMDf - Matrix of ferrite and pearlite
Nodular cast iron. Ferritic perlitic matrix. White regions in the pearlite colonies are free carbides.
129
VIEW
ML00001 / Dec.2017
Thermal Fatigue of Cast Iron
M - Nodular Cast IronP - CastAp - SiderurgyCd - Thermal Fatigue
Cm - Nital Etched Micrography by OMDf - Free Carbides in Pearlite Colonies
Oriundos
59
VIEW
ML00001 / Dec.2017
Thermal Fatigue of Cast Iron
M - Nodular Cast IronP - CastAp - SiderurgyCd - Thermal Fatigue
Cm - Transverse Section AspectDf - Acicular Alpha
ML00154 — High Strength Cast Iron CrankshaftM - Nodular Cast IronP - CastingAp - EngineCd - Surface treatment
As polished micrographic detail of the graphite in nodules, close to the surface of the shaft edge, in a longitudinal section.
114
VIEW
ML00154 / Jan.2019
High Strength Cast Iron Crankshaft
M - Nodular Cast IronP - CastingAp - EngineCd - Surface treatment
Cm - As polished micrographyDf - Graphite in Nodules
Micrography of the crankshaft close to the radio that is not heat treated. Graphite in nodules and a ferritic and pearlitic matrix, predominantly pearlitic.
81
VIEW
ML00154 / Jan.2019
High Strength Cast Iron Crankshaft
M - Nodular Cast IronP - CastingAp - EngineCd - Surface treatment
Cm - Nital Etched Micrography by OMDf - Matrix of ferrite and pearlite
Micrographic detail of the graphite nodules and a ferritic and pearlitic matrix, predominantly pearlitic.
82
VIEW
ML00154 / Jan.2019
High Strength Cast Iron Crankshaft
M - Nodular Cast IronP - CastingAp - EngineCd - Surface treatment
Cm - Nital Etched Micrography by OMDf - Matrix of ferrite and pearlite
Micrography of the shaft very close to the surface, in a heat treated position. Graphite in nodules. Dark blue martensitic microstructure around the nodules, brown yellow martensite and white islands of martensitic with retained austenite microstructure.
65
VIEW
ML00154 / Jan.2019
High Strength Cast Iron Crankshaft
M - Nodular Cast IronP - CastingAp - EngineCd - Surface treatment
Cm - Nital Etched Micrography by OMDf - Martensite
Micrographic detail of the graphite in nodules, dark blue martensitic microstructure around the nodules, brown yellow martensite and white yellow islands of martensitic with retained austenite microstructure.
61
VIEW
ML00154 / Jan.2019
High Strength Cast Iron Crankshaft
M - Nodular Cast IronP - CastingAp - EngineCd - Surface treatment
Cm - Nital Etched Micrography by OMDf - Martensite

+13 more from this case →

ML00153 — X52 in a Tubular StructureM - CMn SteelP - Seamless PipeAp - StructureCd - Qualified
Micrographic detail of the bainitic structure of the coarse grain heat affected zone, close to the fusion line (to the top of the figure).
76
VIEW
ML00153 / Jan.2019
X52 in a Tubular Structure
M - CMn SteelP - Seamless PipeAp - StructureCd - Qualified
Cm - Nital Etched Micrography by OMDf - Bainitic HAZ
Micrographic detail of the weld metal in the last bead. The microstructure shows primary ferrite in the (previous austenite) grain boundaries, some regions of ferrite with aligned second phases and acicular ferrite in the center of the columnar grains.
51
VIEW
ML00153 / Jan.2019
X52 in a Tubular Structure
M - CMn SteelP - Seamless PipeAp - StructureCd - Qualified
Cm - Nital Etched Micrography by OMDf - Columnar Grains
Micrographic detail of the refined ferritic microstructure, with equiaxial grains, of the weld metal in the root, reheated by the fill pass. At this magnification it is possible to see that the agglomerated carbides ar located in ferritic grain boundaries.
67
VIEW
ML00153 / Jan.2019
X52 in a Tubular Structure
M - CMn SteelP - Seamless PipeAp - StructureCd - Qualified
Cm - Nital Etched Micrography by OMDf - Equiaxial Grains