Welded Joint

30 cases · 340 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Capture method: Optical Microscope clear all

Welded Joint — sub-branches

Cladding 4Fabrication Weld 15In Field Weld 3Remanufacture by Welding 1Repair Weld 2Welded Testpiece for Qualification 4

Results

SortNewestOldestTitle A-ZTitle Z-A
Low magnification micrography transverse to the fillet weld in the pipe. The pipe base metal is to the bottom of the figure and the weld metal is to the top. The heat affected zone in the middle, shows a coarse grain size structure.
59
VIEW
ML00179 / Feb.2022
Hydrides in Titanium Weld
M - Unalloyed TitaniumP - In Field WeldAp - Chemical IndustryCd - Hydride Formation
Cm - Kroll Etched Micrography by OMDf - Welded Joint
Sample surface. Microstructure of the plate base metal, exposed to high temperature exhausting gases. Refined austenite and some cracks.
24
VIEW
ML00174 / Jul.2021
Carburization of a 347 SS Welded Joint
M - Austenitic Stainless SteelP - Fabrication WeldAp - EnergyCd - Carburization
Cm - Oxalic Acid Electrolytic EtchDf - Base Metal
Micrography of the pipe base metal, in a longitudinal section, presenting a slight banding and a refined structure.
147
VIEW
ML00153 / Jan.2019
X52 in a Tubular Structure
M - CMn SteelP - Seamless PipeAp - StructureCd - Qualified
Cm - Nital Etched Micrography by OMDf - Base Metal
Microstructural analysis of the valve body structure, close to the position where the cracking has occurred. The structure is ferritic austenitic, with a large amount of detrimental phases associated to the ferritic structure, probably sigma phase.
106
VIEW
ML00134 / Aug.2020
Brittle Fracture of a Superduplex Valve Body
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Cm - NaOH Electrolytic Etched MicroDf - Sigma
Image by scanning electron microscopy of the metallurgically bonded interface of the internally cladded pipe. It is a longitudinal seam welded pipe, with substrate in low alloy steel X65 and clad plate in Alloy 625 (welded by a solid state process). The region is a detail in the side of the Ni alloy clad plate where a grain refinement has occurred probably due to recrystallization of a strain hardened region during later heat treatment. The microhardness of this region is a lot higher than the value obtained out of this region, in the clad plate.
904
VIEW
ML00133 / May.2018
Seam Welded Pipe Cladded with Alloy 625
M - LAS / Ni AlloyP - Longitudinal Seam Welded PipeAp - Oil and GasCd - Welding
Cm - Oxalic Acid Electrolytic EtchDf - Clad Interface
Micrography of a longitudinal section of the pipe substrate, in low magnification, showing a uniform microstructure,
79
VIEW
ML00132 / May.2018
Seamless Pipe Overlaid with Alloy 625
M - LAS / Ni AlloyP - Seamless PipeAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Base Metal
Micrographic detail of the weld metal with islands of a coarse ferritic structure, degradated (recristalized) from an acicular morphology during to the long heat treatment cycle in high temperature. The post welding heat treatment (PWHT) was conducted during 12 hours at 640°C.
700
VIEW
ML00129 / Apr.2018
Non qualified WPS for High Strength Steel
M - Low Alloy Medium Carbon QTP - Welded Testpiece for QualificationAp - Oil and GasCd - Non qualified
Cm - Nital Etched Micrography by OMDf - Coarse Structure
Micrography of the plate in a longitudinal section, presenting a typical ferritic pearlitic structure, banded. The plate is 22 mm thick.
182
VIEW
ML00119 / Feb.2018
Thermal Fatigue of a Marine Boiler
M - Low Carbon SteelP - Fabrication WeldAp - ShipCd - Thermal Fatigue
Cm - Nital Etched Micrography by OMDf - Banded Structure

More from these cases

ML00179 — Hydrides in Titanium WeldM - Unalloyed TitaniumP - In Field WeldAp - Chemical IndustryCd - Hydride Formation
Low magnification micrography showing the weld metal, full of pores, indicating that the field welding was not properly shileded.
50
VIEW
ML00179 / Feb.2022
Hydrides in Titanium Weld
M - Unalloyed TitaniumP - In Field WeldAp - Chemical IndustryCd - Hydride Formation
Cm - Kroll Etched Micrography by OMDf - Weld Metal
Granular alpha structure of the pipe base metal.
49
VIEW
ML00179 / Feb.2022
Hydrides in Titanium Weld
M - Unalloyed TitaniumP - In Field WeldAp - Chemical IndustryCd - Hydride Formation
Cm - Kroll Etched Micrography by OMDf - Alpha
Coarse grains in the heat affected zone.
46
VIEW
ML00179 / Feb.2022
Hydrides in Titanium Weld
M - Unalloyed TitaniumP - In Field WeldAp - Chemical IndustryCd - Hydride Formation
Cm - Kroll Etched Micrography by OMDf - Heat Affected Zone
Micrography of the weld metal at the fillet weld where the cracking started, showing several brittle microcracks that corresponds to the regions where the fractography showed secondary crackis.
35
VIEW
ML00179 / Feb.2022
Hydrides in Titanium Weld
M - Unalloyed TitaniumP - In Field WeldAp - Chemical IndustryCd - Hydride Formation
Cm - Kroll Etched Micrography by OMDf - Weld Metal
Micrographic detail of the weld metal brittle microcracks, in regions with hydrides formation.
32
VIEW
ML00179 / Feb.2022
Hydrides in Titanium Weld
M - Unalloyed TitaniumP - In Field WeldAp - Chemical IndustryCd - Hydride Formation
Cm - Kroll Etched Micrography by OMDf - Weld Metal

+10 more from this case →

ML00174 — Carburization of a 347 SS Welded JointM - Austenitic Stainless SteelP - Fabrication WeldAp - EnergyCd - Carburization
Detailed microstructure of the plate base metal, exposed to high temperature exhausting gases. Refined austenite, precipitation of carbides in the grain boumdaries and some cracks.
23
VIEW
ML00174 / Jul.2021
Carburization of a 347 SS Welded Joint
M - Austenitic Stainless SteelP - Fabrication WeldAp - EnergyCd - Carburization
Cm - Oxalic Acid Electrolytic EtchDf - Austenite
Detailed microstructure of the plate base metal, exposed to high temperature exhausting gases. Refined austenite, precipitation of carbides in the grain boumdaries and some cracks.
24
VIEW
ML00174 / Jul.2021
Carburization of a 347 SS Welded Joint
M - Austenitic Stainless SteelP - Fabrication WeldAp - EnergyCd - Carburization
Cm - Oxalic Acid Electrolytic EtchDf - Crack
Sample surface. Microstructure of the weld metal, exposed to high temperature exhausting gases. Austeno-ferritic structure and some cracks.
20
VIEW
ML00174 / Jul.2021
Carburization of a 347 SS Welded Joint
M - Austenitic Stainless SteelP - Fabrication WeldAp - EnergyCd - Carburization
Cm - Oxalic Acid Electrolytic EtchDf - Weld Metal
Detailed microstructure of the weld metal, exposed to high temperature exhausting gases. Austeno-ferritic structure and some cracks.
21
VIEW
ML00174 / Jul.2021
Carburization of a 347 SS Welded Joint
M - Austenitic Stainless SteelP - Fabrication WeldAp - EnergyCd - Carburization
Cm - Oxalic Acid Electrolytic EtchDf - Ferrite and Austenite
Detailed microstructure of the weld metal, exposed to high temperature exhausting gases. Austeno-ferritic structure, strong carbide precipitation integranular and transgranular, and some cracks.
23
VIEW
ML00174 / Jul.2021
Carburization of a 347 SS Welded Joint
M - Austenitic Stainless SteelP - Fabrication WeldAp - EnergyCd - Carburization
Cm - Oxalic Acid Electrolytic EtchDf - Cracks

+3 more from this case →

ML00153 — X52 in a Tubular StructureM - CMn SteelP - Seamless PipeAp - StructureCd - Qualified
Micrography of the pipe base metal, in a longitudinal section. The ferritic structure is refined and it is possible to identify a small variation in the ferritic grain size, that is promoting the slight banding effect.
119
VIEW
ML00153 / Jan.2019
X52 in a Tubular Structure
M - CMn SteelP - Seamless PipeAp - StructureCd - Qualified
Cm - Nital Etched Micrography by OMDf - Base Metal
Micrographic detail of the very refined ferritic structure of the base metal, in the longitudinal section, indicating that the material was heat treated, since no banding is not detectable at this magnification.
101
VIEW
ML00153 / Jan.2019
X52 in a Tubular Structure
M - CMn SteelP - Seamless PipeAp - StructureCd - Qualified
Cm - Nital Etched Micrography by OMDf - Grain refined structure
Micrography of the weded joint at the cap pass fusion line. The columnar structure of the weld metal is to the top of the figure; and it is possible to see the coarse grains at the heat affected zone. Both columnar structure and coarse grains are related to the previous austenite grain boundaries. From the fusion line to the base metal (in the bottom of the figure) the grain sizes are refined.
86
VIEW
ML00153 / Jan.2019
X52 in a Tubular Structure
M - CMn SteelP - Seamless PipeAp - StructureCd - Qualified
Cm - Nital Etched Micrography by OMDf - Welded Joint
Micrography presenting the coarse grain heat affected zone of the welded joint, at the cap pass. The microstructure is bainitic.
82
VIEW
ML00153 / Jan.2019
X52 in a Tubular Structure
M - CMn SteelP - Seamless PipeAp - StructureCd - Qualified
Cm - Nital Etched Micrography by OMDf - Heat Affected Zone
Micrographic detail of the bainitic structure of the coarse grain heat affected zone, close to the fusion line (to the top of the figure).
76
VIEW
ML00153 / Jan.2019
X52 in a Tubular Structure
M - CMn SteelP - Seamless PipeAp - StructureCd - Qualified
Cm - Nital Etched Micrography by OMDf - Bainitic HAZ

+5 more from this case →

ML00134 — Brittle Fracture of a Superduplex Valve BodyM - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Micrographic detail of the valve body structure, close to the position where the cracking has occurred. The structure is ferritic austenitic, with a large amount of detrimental phases associated to the ferritic structure, probably sigma phase.
102
VIEW
ML00134 / Aug.2020
Brittle Fracture of a Superduplex Valve Body
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Cm - NaOH Electrolytic Etched MicroDf - Sigma
Metallographic detail of the large amount of sigma phase, associated to the ferritic structure.
105
VIEW
ML00134 / Aug.2020
Brittle Fracture of a Superduplex Valve Body
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Cm - NaOH Electrolytic Etched MicroDf - Sigma
Microstructural analysis of the valve body structure, far from the position where the cracking has occurred, in the bottom of the body. The structure is ferritic austenitic, with some sigma phase, not in a large amount, indicating the valve structure was not uniform.
67
VIEW
ML00134 / Aug.2020
Brittle Fracture of a Superduplex Valve Body
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Cm - NaOH Electrolytic Etched MicroDf - Ferrite and Austenite
Micrographic detail of the valve body structure, far from the position where the cracking has occurred, in the bottom of the body. The structure is ferritic austenitic, with some sigma phase, not in a large amount, indicating the valve structure was not uniform.
63
VIEW
ML00134 / Aug.2020
Brittle Fracture of a Superduplex Valve Body
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Cm - NaOH Electrolytic Etched MicroDf - Ferrite and Austenite
Micrographic detail of the valve body structure, far from the position where the cracking has occurred, in the bottom of the body. The structure is ferritic austenitic, with some sigma phase, not in a large amount, indicating the valve structure was not uniform.
61
VIEW
ML00134 / Aug.2020
Brittle Fracture of a Superduplex Valve Body
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Cm - NaOH Electrolytic Etched MicroDf - Ferrite and Austenite

+8 more from this case →

ML00133 — Seam Welded Pipe Cladded with Alloy 625M - LAS / Ni AlloyP - Longitudinal Seam Welded PipeAp - Oil and GasCd - Welding
Micrography of a longitudinal section of the pipe substrate, in low magnification, showing a uniform microstructure,
51
VIEW
ML00133 / May.2018
Seam Welded Pipe Cladded with Alloy 625
M - LAS / Ni AlloyP - Longitudinal Seam Welded PipeAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Base Metal
Micrography of a longitudinal section of the pipe substrate showing a uniform bainitic microstructure obtained by the pipe quenching and tempering,
48
VIEW
ML00133 / May.2018
Seam Welded Pipe Cladded with Alloy 625
M - LAS / Ni AlloyP - Longitudinal Seam Welded PipeAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Longitudinal Section
Micrographic detail of a longitudinal section of the pipe substrate showing a uniform bainitic microstructure,
50
VIEW
ML00133 / May.2018
Seam Welded Pipe Cladded with Alloy 625
M - LAS / Ni AlloyP - Longitudinal Seam Welded PipeAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Bainite
Micrography of a longitudinal section of the pipe at the interface with the clad plate, with Nital etch that reveals only the low alloy steel structure, to the left side of the image.
54
VIEW
ML00133 / May.2018
Seam Welded Pipe Cladded with Alloy 625
M - LAS / Ni AlloyP - Longitudinal Seam Welded PipeAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Clad Interface
Micrography of a longitudinal section of the pipe at the interface with the clad plate, with Nital etch that reveals only the low alloy steel structure, to the left side of the image.
51
VIEW
ML00133 / May.2018
Seam Welded Pipe Cladded with Alloy 625
M - LAS / Ni AlloyP - Longitudinal Seam Welded PipeAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Clad Interface

+10 more from this case →

ML00132 — Seamless Pipe Overlaid with Alloy 625M - LAS / Ni AlloyP - Seamless PipeAp - Oil and GasCd - Welding
Micrography of a longitudinal section of the pipe substrate showing a uniform bainitic microstructure obtained by the pipe quenching and tempering,
72
VIEW
ML00132 / May.2018
Seamless Pipe Overlaid with Alloy 625
M - LAS / Ni AlloyP - Seamless PipeAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Longitudinal Section
Micrographic detail of a longitudinal section of the pipe substrate showing a uniform bainitic microstructure.
68
VIEW
ML00132 / May.2018
Seamless Pipe Overlaid with Alloy 625
M - LAS / Ni AlloyP - Seamless PipeAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Bainite
Micrography of a longitudinal section of the pipe at the overlay fusion line, with Nital etch that reveals only the low alloy steel structure, to the left side of the image.
66
VIEW
ML00132 / May.2018
Seamless Pipe Overlaid with Alloy 625
M - LAS / Ni AlloyP - Seamless PipeAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Clad Interface
Micrography of a longitudinal section of the pipe at the overlay fusion line, with Nital etch that reveals only the low alloy steel structure, to the left side of the image. Some decarburization of the low alloy steel substrate is evident since the microstructure is slightly different a little far from the interface.
66
VIEW
ML00132 / May.2018
Seamless Pipe Overlaid with Alloy 625
M - LAS / Ni AlloyP - Seamless PipeAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Clad Interface
Micrographic detail of a longitudinal section of the pipe at the interface with the clad plate, with Nital etch that reveals only the low alloy steel structure, to the left side of the image.
59
VIEW
ML00132 / May.2018
Seamless Pipe Overlaid with Alloy 625
M - LAS / Ni AlloyP - Seamless PipeAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Clad Interface

+7 more from this case →

ML00129 — Non qualified WPS for High Strength SteelM - Low Alloy Medium Carbon QTP - Welded Testpiece for QualificationAp - Oil and GasCd - Non qualified
Micrography of the weld metal, at the face, presenting regions of large ferritic grains. The acicular ferrite structure in the columnar (previous austenitic) grains has suffered degradation due to the long heat treatment cycle (12 hours) in high temperature.
96
VIEW
ML00129 / Apr.2018
Non qualified WPS for High Strength Steel
M - Low Alloy Medium Carbon QTP - Welded Testpiece for QualificationAp - Oil and GasCd - Non qualified
Cm - Nital Etched Micrography by OMDf - Weld Metal
Micrography of the weld metal, at the face, presenting regions of large ferritic grains. The acicular ferrite has suffered degradation due to the long heat treatment cycle (12 hours) in a temperature of 640°C, that is higher than the recommended for the D2 filler metal.
78
VIEW
ML00129 / Apr.2018
Non qualified WPS for High Strength Steel
M - Low Alloy Medium Carbon QTP - Welded Testpiece for QualificationAp - Oil and GasCd - Non qualified
Cm - Nital Etched Micrography by OMDf - Weld Metal
Micrography of the base metal, in low magnification, showing regions of segregations in a quenched and tempered martensitic structure.
52
VIEW
ML00129 / Apr.2018
Non qualified WPS for High Strength Steel
M - Low Alloy Medium Carbon QTP - Welded Testpiece for QualificationAp - Oil and GasCd - Non qualified
Cm - Nital Etched Micrography by OMDf - Base Metal
Micrography of the base metal showing a quenched and tempered martensitic structure. The base metal adopted in the test coupon presented a hardness level of 217HB (Brinell hardness of the certificate) and after the PWHT cycle the measured base metal hardness is 224 HV10.
59
VIEW
ML00129 / Apr.2018
Non qualified WPS for High Strength Steel
M - Low Alloy Medium Carbon QTP - Welded Testpiece for QualificationAp - Oil and GasCd - Non qualified
Cm - Nital Etched Micrography by OMDf - Base Metal
Micrographic detail of the base metal structure, quenched and tempered martensite. The base metal adopted in the test coupon presented a hardness level of 217HB (Brinell hardness of the certificate) and after the PWHT cycle the measured base metal hardness is 224 HV10.
51
VIEW
ML00129 / Apr.2018
Non qualified WPS for High Strength Steel
M - Low Alloy Medium Carbon QTP - Welded Testpiece for QualificationAp - Oil and GasCd - Non qualified
Cm - Nital Etched Micrography by OMDf - Martensite

+12 more from this case →

ML00119 — Thermal Fatigue of a Marine BoilerM - Low Carbon SteelP - Fabrication WeldAp - ShipCd - Thermal Fatigue
Micrography of the plate in a longitudinal section, presenting a typical ferritic pearlitic structure, banded.
165
VIEW
ML00119 / Feb.2018
Thermal Fatigue of a Marine Boiler
M - Low Carbon SteelP - Fabrication WeldAp - ShipCd - Thermal Fatigue
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Micrographic detail of the ferritic pearlitic structure of the plate in the longitudinal section.
147
VIEW
ML00119 / Feb.2018
Thermal Fatigue of a Marine Boiler
M - Low Carbon SteelP - Fabrication WeldAp - ShipCd - Thermal Fatigue
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Micrography of the weld metal in the center os the weld. Columnar grains (of the previous austenite) with primary ferrite in the grain boundaries; ferrite with aligned second phases and acicular ferrite, intragranular.
136
VIEW
ML00119 / Feb.2018
Thermal Fatigue of a Marine Boiler
M - Low Carbon SteelP - Fabrication WeldAp - ShipCd - Thermal Fatigue
Cm - Nital Etched Micrography by OMDf - Weld Metal
Micrography of the weld metal in the center os the weld. Columnar grains (of the previous austenite) with primary ferrite in the grain boundaries and acicular ferrite intragranular.
125
VIEW
ML00119 / Feb.2018
Thermal Fatigue of a Marine Boiler
M - Low Carbon SteelP - Fabrication WeldAp - ShipCd - Thermal Fatigue
Cm - Nital Etched Micrography by OMDf - Ferritic Weld Metal
Micrographic detail of the weld metal in the center os the weld. Columnar grains (of the previous austenite) with primary ferrite in the grain boundaries; and details of the ferrite with aligned second phases and acicular ferrite, intragranular.
112
VIEW
ML00119 / Feb.2018
Thermal Fatigue of a Marine Boiler
M - Low Carbon SteelP - Fabrication WeldAp - ShipCd - Thermal Fatigue
Cm - Nital Etched Micrography by OMDf - Ferritic Weld Metal

+12 more from this case →