Raw Material

6 cases · 61 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Application: Boiler Capture method: Optical Microscope clear all

Raw Material — sub-branches

Rolled Plate 3Tube 3

Results

SortNewestOldestTitle A-ZTitle Z-A
The tube microstructure is ferritic-pearlitic, typical of this kind of material. No evidences of microstrutural changes were detected (no overheating, no decarburization).
177
VIEW
ML00163 / Jun.2020
Corrosion Fatigue of a Boiler Waterwall Tube
M - Low Carbon SteelP - Seamless tubeAp - BoilerCd - Corrosion Fatigue
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Micrographic detail of the longitudinal section of the tube, close to the external surface. The carburizing layer consists of a bainitic structure, with intergranular and intragranular carbide precipitation.
1184
VIEW
ML00107 / Dec.2017
Carburized 9Cr1MoV Superheater Tube
M - Heat Resistant SteelP - Seamless tubeAp - BoilerCd - Carburization
Cm - Nital Etched Micrography by OMDf - Carburized Layer
The micrography of the longitudinal section of the tube, close to OD, shows the paralel cracks, filled with oxides, perpendicular to the surface.
1441
VIEW
ML00104 / Dec.2017
Thermal Fatigue of a Boiler Tube
M - Low Carbon SteelP - Autogenously Welded TubeAp - BoilerCd - Thermal Fatigue
Cm - As polished micrographyDf - Close to the External Surface
Micrography of the shell plate in the longitudinal section. Ferritic-perlitic microstructure.
96
VIEW
ML00019 / Apr.2017
Transgranular SCC in Boiler Steam Drum
M - CMn SteelP - Rolled PlateAp - BoilerCd - Stress Corrosion
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Typical branched stress corrosion cracks in a low carbon steel, ferritic-pertlitic structure. The cracks are filled with corrosion products.
771
VIEW
ML00018 / Apr.2017
SCC in Boiler Steam Drum
M - Low Carbon SteelP - Rolled PlateAp - BoilerCd - Stress Corrosion
Cm - Nital Etched Micrography by OMDf - Branched Cracks
Ferritic-perlitic microstructure of a longitudinal section of the plate that was qualified to be adopted in a tubesheet boiler. Hot formed plate presenting perlite banding.
659
VIEW
ML00031 / Jan.2017
Carbon Steel Tubesheet for Boiler
M - Low Carbon SteelP - Rolled PlateAp - ShipCd - Typical manufacturing
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite

More from these cases

ML00163 — Corrosion Fatigue of a Boiler Waterwall TubeM - Low Carbon SteelP - Seamless tubeAp - BoilerCd - Corrosion Fatigue
The internal side of the tube presented multiple cracks, filled with oxides, blunt-tipped, typical of a corrosion fatigue cracking mechanism.
160
VIEW
ML00163 / Jun.2020
Corrosion Fatigue of a Boiler Waterwall Tube
M - Low Carbon SteelP - Seamless tubeAp - BoilerCd - Corrosion Fatigue
Cm - As polished micrographyDf - Parallel cracks
Micrographic detail of the corrosion cracking from internal side of the tube, in several points at the tube surface.
156
VIEW
ML00163 / Jun.2020
Corrosion Fatigue of a Boiler Waterwall Tube
M - Low Carbon SteelP - Seamless tubeAp - BoilerCd - Corrosion Fatigue
Cm - As polished micrographyDf - Corrosion Cracking
Low magnification micrography of the multiple cracks, parallel, transgranular. No evidences of microstrutural changes (heat evolution or decarburization).
127
VIEW
ML00163 / Jun.2020
Corrosion Fatigue of a Boiler Waterwall Tube
M - Low Carbon SteelP - Seamless tubeAp - BoilerCd - Corrosion Fatigue
Cm - Nital Etched Micrography by OMDf - Transgranular Cracking
Micrography presenting the internal tube surface with several parallel cracks, some still in the beginning (less than 0.1 mm deep).
115
VIEW
ML00163 / Jun.2020
Corrosion Fatigue of a Boiler Waterwall Tube
M - Low Carbon SteelP - Seamless tubeAp - BoilerCd - Corrosion Fatigue
Cm - Nital Etched Micrography by OMDf - Parallel cracks
Micrography of the crack tip, initiated from the internal tube surface. The crack is transgranular, filled with oxides and blunt-tipped.
109
VIEW
ML00163 / Jun.2020
Corrosion Fatigue of a Boiler Waterwall Tube
M - Low Carbon SteelP - Seamless tubeAp - BoilerCd - Corrosion Fatigue
Cm - Nital Etched Micrography by OMDf - Transgranular Cracking

+9 more from this case →

ML00107 — Carburized 9Cr1MoV Superheater TubeM - Heat Resistant SteelP - Seamless tubeAp - BoilerCd - Carburization
Micrography of the longitudinal section of the tube, close to the internal surface. A thick scale is evident, but no microstructural changes compared to the center of the tube.
183
VIEW
ML00107 / Dec.2017
Carburized 9Cr1MoV Superheater Tube
M - Heat Resistant SteelP - Seamless tubeAp - BoilerCd - Carburization
Cm - Nital Etched Micrography by OMDf - Bainite
Micrography of a longitudinal section of the tube in the center of the thickness, showing a ferritic-bainitic structure of this CrMoV steel.
156
VIEW
ML00107 / Dec.2017
Carburized 9Cr1MoV Superheater Tube
M - Heat Resistant SteelP - Seamless tubeAp - BoilerCd - Carburization
Cm - Nital Etched Micrography by OMDf - Bainite
Micrography of a longitudinal section of the tube in the center of the thickness, showing a ferritic-bainitic structure of this CrMoV steel.
137
VIEW
ML00107 / Dec.2017
Carburized 9Cr1MoV Superheater Tube
M - Heat Resistant SteelP - Seamless tubeAp - BoilerCd - Carburization
Cm - Nital Etched Micrography by OMDf - Bainite
Micrography of a longitudinal section of the tube in the center of the thickness, showing a ferritic-bainitic structure of this CrMoV steel.
142
VIEW
ML00107 / Dec.2017
Carburized 9Cr1MoV Superheater Tube
M - Heat Resistant SteelP - Seamless tubeAp - BoilerCd - Carburization
Cm - Nital Etched Micrography by OMDf - Bainite
Micrography of the longitudinal section of the tube, close to the external surface, presenting a thick deposit.
110
VIEW
ML00107 / Dec.2017
Carburized 9Cr1MoV Superheater Tube
M - Heat Resistant SteelP - Seamless tubeAp - BoilerCd - Carburization
Cm - As polished micrographyDf - Close to the External Surface

+7 more from this case →

ML00104 — Thermal Fatigue of a Boiler TubeM - Low Carbon SteelP - Autogenously Welded TubeAp - BoilerCd - Thermal Fatigue
The micrography of the longitudinal section of the tube, close to ID, shows the paralel cracks, filled with oxides, perpendicular to the surface.
229
VIEW
ML00104 / Dec.2017
Thermal Fatigue of a Boiler Tube
M - Low Carbon SteelP - Autogenously Welded TubeAp - BoilerCd - Thermal Fatigue
Cm - As polished micrographyDf - Close to the Internal Surface
Micrographic details of the longitudinal section of the tube, close to OD, showing paralel cracks, filled with oxides, perpendicular to the surface.
115
VIEW
ML00104 / Dec.2017
Thermal Fatigue of a Boiler Tube
M - Low Carbon SteelP - Autogenously Welded TubeAp - BoilerCd - Thermal Fatigue
Cm - As polished micrographyDf - Cracks Transverse to the Surface
Micrographic details of the longitudinal section of the tube, close to OD, showing paralel cracks, filled with oxides, perpendicular to the surface.
109
VIEW
ML00104 / Dec.2017
Thermal Fatigue of a Boiler Tube
M - Low Carbon SteelP - Autogenously Welded TubeAp - BoilerCd - Thermal Fatigue
Cm - As polished micrographyDf - Thermal Fatigue Cracks
Micrographic details of the longitudinal section of the tube, close to ID, showing paralel cracks, filled with oxides, perpendicular to the surface.
103
VIEW
ML00104 / Dec.2017
Thermal Fatigue of a Boiler Tube
M - Low Carbon SteelP - Autogenously Welded TubeAp - BoilerCd - Thermal Fatigue
Cm - As polished micrographyDf - Cracks Transverse to the Surface
Micrographic details of the longitudinal section of the tube, close to ID, showing paralel cracks, filled with oxides, perpendicular to the surface.
99
VIEW
ML00104 / Dec.2017
Thermal Fatigue of a Boiler Tube
M - Low Carbon SteelP - Autogenously Welded TubeAp - BoilerCd - Thermal Fatigue
Cm - As polished micrographyDf - Thermal Fatigue Cracks

+10 more from this case →

ML00019 — Transgranular SCC in Boiler Steam DrumM - CMn SteelP - Rolled PlateAp - BoilerCd - Stress Corrosion
Micrographic detail of the shell plate in the longitudinal section. Ferritic-perlitic microstructure.
89
VIEW
ML00019 / Apr.2017
Transgranular SCC in Boiler Steam Drum
M - CMn SteelP - Rolled PlateAp - BoilerCd - Stress Corrosion
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Micrography of the cracking showing the branched nature, typical of a stress corrosion cracking. The cracks started from the internal surface of the steam drum.
94
VIEW
ML00019 / Apr.2017
Transgranular SCC in Boiler Steam Drum
M - CMn SteelP - Rolled PlateAp - BoilerCd - Stress Corrosion
Cm - Nital Etched Micrography by OMDf - Branched Cracks
Micrographic detail of the cracking showing the branched nature, typical of a stress corrosion cracking. The cracks presented a transgranular morphology
86
VIEW
ML00019 / Apr.2017
Transgranular SCC in Boiler Steam Drum
M - CMn SteelP - Rolled PlateAp - BoilerCd - Stress Corrosion
Cm - Nital Etched Micrography by OMDf - Transgranular Crack
Micrographic detail of the transgranular stress corrosion cracking.
80
VIEW
ML00019 / Apr.2017
Transgranular SCC in Boiler Steam Drum
M - CMn SteelP - Rolled PlateAp - BoilerCd - Stress Corrosion
Cm - Nital Etched Micrography by OMDf - Transgranular Crack
Micrographic detail of the transgranular stress corrosion cracking.
157
VIEW
ML00019 / Apr.2017
Transgranular SCC in Boiler Steam Drum
M - CMn SteelP - Rolled PlateAp - BoilerCd - Stress Corrosion
Cm - Nital Etched Micrography by OMDf - Transgranular Crack
ML00018 — SCC in Boiler Steam DrumM - Low Carbon SteelP - Rolled PlateAp - BoilerCd - Stress Corrosion
Ferritic perlitic structure of the shell plate.
207
VIEW
ML00018 / Apr.2017
SCC in Boiler Steam Drum
M - Low Carbon SteelP - Rolled PlateAp - BoilerCd - Stress Corrosion
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Micrography of the crack at the internal surface of the steam drum. The shell plate presents a ferritic perlitic structure.
162
VIEW
ML00018 / Apr.2017
SCC in Boiler Steam Drum
M - Low Carbon SteelP - Rolled PlateAp - BoilerCd - Stress Corrosion
Cm - Nital Etched Micrography by OMDf - Branched Cracks
Micrography of a crack, in a sample as polished, presenting the opened crack.
144
VIEW
ML00018 / Apr.2017
SCC in Boiler Steam Drum
M - Low Carbon SteelP - Rolled PlateAp - BoilerCd - Stress Corrosion
Cm - Micrography by OMDf - Branched Cracks
Stress corrosion cracks propagating in the ferritic-perlitic structure.
120
VIEW
ML00018 / Apr.2017
SCC in Boiler Steam Drum
M - Low Carbon SteelP - Rolled PlateAp - BoilerCd - Stress Corrosion
Cm - Nital Etched Micrography by OMDf - Branched Cracks
Micrography of a crack, as polished, presenting the cracks filled with corrosion products.
100
VIEW
ML00018 / Apr.2017
SCC in Boiler Steam Drum
M - Low Carbon SteelP - Rolled PlateAp - BoilerCd - Stress Corrosion
Cm - Micrography by OMDf - Branched Cracks

+2 more from this case →

ML00031 — Carbon Steel Tubesheet for BoilerM - Low Carbon SteelP - Rolled PlateAp - ShipCd - Typical manufacturing
Ferritic-perlitic microstructure of a longitudinal section of the plate that was qualified to be adopted in a tubesheet boiler. Hot formed plate presenting perlite banding.
213
VIEW
ML00031 / Jan.2017
Carbon Steel Tubesheet for Boiler
M - Low Carbon SteelP - Rolled PlateAp - ShipCd - Typical manufacturing
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Ferritic-perlitic microstructure of a longitudinal section of the plate that was qualified to be adopted in a tubesheet boiler. Hot formed plate presenting perlite banding.
173
VIEW
ML00031 / Jan.2017
Carbon Steel Tubesheet for Boiler
M - Low Carbon SteelP - Rolled PlateAp - ShipCd - Typical manufacturing
Cm - Nital Etched Micrography by OMDf - Banded Pearlite