Ferritic pearlitic

8 cases · 70 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Application: Structure Capture method: Optical Microscope clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrography of the pipe base metal, in a longitudinal section, presenting a slight banding and a refined structure.
147
VIEW
ML00153 / Jan.2019
X52 in a Tubular Structure
M - CMn SteelP - Seamless PipeAp - StructureCd - Qualified
Cm - Nital Etched Micrography by OMDf - Base Metal
Micrography of the plate in a section, showing a ferritic-pearlitic microstructure in the middle of the thickness.
84
VIEW
ML00143 / Aug.2018
Impact of a .308 Winchester on A36 Plate
M - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Micrographic detail of a transverse section of the tubing, in the center of the thickness. Ferritic-pearlitic structure. Pearlite colonies in bands.
401
VIEW
ML00116 / Jan.2018
CMn Steel Structural Tubing 6 mm thick
M - CMn SteelP - Seamless Round ShapeAp - StructureCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Micrographic detail of a transverse section of the 5 mm thick tubing, in the center of the thickness. Ferritic-pearlitic structure, with the pearlite presenting a coalesced aspect. The tubing was in service at ambient temperature, painted, and the coalesced aspect was generated before service, perhaps during the tubing manufacturing.
393
VIEW
ML00115 / Jan.2018
CMn Steel Structural Tubing 5 mm thick
M - CMn SteelP - Seamless Round ShapeAp - StructureCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Micrographic detail of a transverse section of the tubing, in the center of the thickness. Ferritic-pearlitic structure. Pearlite colonies in bands.
346
VIEW
ML00114 / Jan.2018
CMn Steel Structural Tubing 8 mm thick
M - CMn SteelP - Seamless Round ShapeAp - StructureCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Micrographic detail of the ferritic-pearlitic structure of the angle L shape, equal legs, in the transverse section.
468
VIEW
ML00035 / Dec.2017
Carbon Steel L Shape
M - Low Carbon SteelP - Rolled ShapeAp - StructureCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Micrographic detail of the slightly banded perlitic structure, in the center of the thickness. ND 3". 7.6 mm thick.
530
VIEW
ML00090 / Sep.2017
Carbon Steel Tubing for Structural Application
M - Low Carbon SteelP - TubeAp - StructureCd - Typical manufacturing
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Micrography of a section transverse to the Oxygen Plasma Cut surface, showing the zone affected by the heat generated in the cutting. The extension of the HAZ is about 0.5 mm. The cut was conducted in the 1 1/4" thickness of the plate.
359
VIEW
ML00033 / Jan.2017
Plasma Cut of 1 1/4" Steel Plate
M - High Strength Low AlloyP - Rolled PlateAp - StructureCd - Cutting
Cm - Nital Etched Micrography by OMDf - Heat Affected Zone

More from these cases

ML00153 — X52 in a Tubular StructureM - CMn SteelP - Seamless PipeAp - StructureCd - Qualified
Micrography of the pipe base metal, in a longitudinal section. The ferritic structure is refined and it is possible to identify a small variation in the ferritic grain size, that is promoting the slight banding effect.
119
VIEW
ML00153 / Jan.2019
X52 in a Tubular Structure
M - CMn SteelP - Seamless PipeAp - StructureCd - Qualified
Cm - Nital Etched Micrography by OMDf - Base Metal
Micrographic detail of the very refined ferritic structure of the base metal, in the longitudinal section, indicating that the material was heat treated, since no banding is not detectable at this magnification.
101
VIEW
ML00153 / Jan.2019
X52 in a Tubular Structure
M - CMn SteelP - Seamless PipeAp - StructureCd - Qualified
Cm - Nital Etched Micrography by OMDf - Grain refined structure
Micrography of the weded joint at the cap pass fusion line. The columnar structure of the weld metal is to the top of the figure; and it is possible to see the coarse grains at the heat affected zone. Both columnar structure and coarse grains are related to the previous austenite grain boundaries. From the fusion line to the base metal (in the bottom of the figure) the grain sizes are refined.
86
VIEW
ML00153 / Jan.2019
X52 in a Tubular Structure
M - CMn SteelP - Seamless PipeAp - StructureCd - Qualified
Cm - Nital Etched Micrography by OMDf - Welded Joint
Micrography presenting the coarse grain heat affected zone of the welded joint, at the cap pass. The microstructure is bainitic.
82
VIEW
ML00153 / Jan.2019
X52 in a Tubular Structure
M - CMn SteelP - Seamless PipeAp - StructureCd - Qualified
Cm - Nital Etched Micrography by OMDf - Heat Affected Zone
Micrographic detail of the bainitic structure of the coarse grain heat affected zone, close to the fusion line (to the top of the figure).
76
VIEW
ML00153 / Jan.2019
X52 in a Tubular Structure
M - CMn SteelP - Seamless PipeAp - StructureCd - Qualified
Cm - Nital Etched Micrography by OMDf - Bainitic HAZ

+5 more from this case →

ML00143 — Impact of a .308 Winchester on A36 PlateM - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Micrography of the plate in a section, showing a ferritic-pearlitic microstructure in the middle of the thickness, in a position where the plate was not affected by the shot.
65
VIEW
ML00143 / Aug.2018
Impact of a .308 Winchester on A36 Plate
M - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Micrographic detail of the plate in a section, showing a ferritic-pearlitic microstructure in the middle of the thickness.
66
VIEW
ML00143 / Aug.2018
Impact of a .308 Winchester on A36 Plate
M - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Micrographic detail of the ferritic-pearlitic microstructure.
53
VIEW
ML00143 / Aug.2018
Impact of a .308 Winchester on A36 Plate
M - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Micrographic detail of the plate section, as polished, close to the surface that suffered the impact. The plate material deformed during the perforation,
31
VIEW
ML00143 / Aug.2018
Impact of a .308 Winchester on A36 Plate
M - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Cm - As polished micrographyDf - Transverse Section
Micrographic detail of the plate section, as polished, close to the surface that suffered the impact. The copper alloy melted and created a yellow-orange deposit.
25
VIEW
ML00143 / Aug.2018
Impact of a .308 Winchester on A36 Plate
M - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Cm - As polished micrographyDf - Melted film

+22 more from this case →

ML00116 — CMn Steel Structural Tubing 6 mm thickM - CMn SteelP - Seamless Round ShapeAp - StructureCd - Removed From Service
Low magnification micrography of a transverse section of the tubing, in the center of the thickness. Ferritic-pearlitic banded structure.
30
VIEW
ML00116 / Jan.2018
CMn Steel Structural Tubing 6 mm thick
M - CMn SteelP - Seamless Round ShapeAp - StructureCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Banded Structure
Micrography of a transverse section of the tubing, in the center of the thickness. Ferritic-pearlitic structure. Bands of pearlite colonies. Refined grains.
26
VIEW
ML00116 / Jan.2018
CMn Steel Structural Tubing 6 mm thick
M - CMn SteelP - Seamless Round ShapeAp - StructureCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - In the Center of the Thickness
Micrography of a transverse section of the tubing in the center of the thickness. Ferritic-pearlitic structure. The structure is fully ferritic in a small extension at the surface, due to a decarburization effect during manufacturing.
26
VIEW
ML00116 / Jan.2018
CMn Steel Structural Tubing 6 mm thick
M - CMn SteelP - Seamless Round ShapeAp - StructureCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Close to the External Surface
Micrographic detail of a transverse section of the tubing, close to the internal surface. Ferritic-pearlitic structure, refined.
20
VIEW
ML00116 / Jan.2018
CMn Steel Structural Tubing 6 mm thick
M - CMn SteelP - Seamless Round ShapeAp - StructureCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Close to the Internal Surface
ML00115 — CMn Steel Structural Tubing 5 mm thickM - CMn SteelP - Seamless Round ShapeAp - StructureCd - Removed From Service
Low magnification micrography of a transverse section of the tubing, in the center of the thickness. Banded structure, ferritic-pearlitic.
16
VIEW
ML00115 / Jan.2018
CMn Steel Structural Tubing 5 mm thick
M - CMn SteelP - Seamless Round ShapeAp - StructureCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Banded Structure
Micrography of a transverse section of the tubing, in the center of the thickness. Ferritic-pearlitic structure. The pearlite is banded and presented a coalesced aspect.
12
VIEW
ML00115 / Jan.2018
CMn Steel Structural Tubing 5 mm thick
M - CMn SteelP - Seamless Round ShapeAp - StructureCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - In the Center of the Thickness
Micrographic detail of a transverse section of the tubing, at the external surface. Ferritic-pearlitic structure. The roughness of the surface is high because the structure was painted and a blasting treatment was probably applied to the surface to improve adherence.
15
VIEW
ML00115 / Jan.2018
CMn Steel Structural Tubing 5 mm thick
M - CMn SteelP - Seamless Round ShapeAp - StructureCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Close to the External Surface
Micrographic detail of a transverse section of the tubing, close to the internal surface. Ferritic-pearlitic structure. Very close to the surface the amount of ferrite is higher than in the center and the grain is coarser, due to a decarburization effect probably occurred when the surface was exposed to high temperature during manufacturing.
13
VIEW
ML00115 / Jan.2018
CMn Steel Structural Tubing 5 mm thick
M - CMn SteelP - Seamless Round ShapeAp - StructureCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Close to the Internal Surface
ML00114 — CMn Steel Structural Tubing 8 mm thickM - CMn SteelP - Seamless Round ShapeAp - StructureCd - Removed From Service
Low magnification micrography of a transverse section of the tubing, in the center of the thickness. Ferritic-pearlitic banded structure.
29
VIEW
ML00114 / Jan.2018
CMn Steel Structural Tubing 8 mm thick
M - CMn SteelP - Seamless Round ShapeAp - StructureCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Banded Structure
Micrography of a transverse section of the tubing, in the center of the thickness. Ferritic-pearlitic structure. Bands of pearlite colonies. Refined grains.
30
VIEW
ML00114 / Jan.2018
CMn Steel Structural Tubing 8 mm thick
M - CMn SteelP - Seamless Round ShapeAp - StructureCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - In the Center of the Thickness
Micrography of a transverse section of the tubing, at the external surface. Ferritic-pearlitic structure. The roughness of the surface is high because the structure was painted and a blasting treatment was probably applied to the surface to improve adherence.
20
VIEW
ML00114 / Jan.2018
CMn Steel Structural Tubing 8 mm thick
M - CMn SteelP - Seamless Round ShapeAp - StructureCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Close to the External Surface
Micrography of a transverse section of the tubing, close to the internal surface. Ferritic-pearlitic structure, refined.
16
VIEW
ML00114 / Jan.2018
CMn Steel Structural Tubing 8 mm thick
M - CMn SteelP - Seamless Round ShapeAp - StructureCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Close to the Internal Surface
ML00035 — Carbon Steel L ShapeM - Low Carbon SteelP - Rolled ShapeAp - StructureCd - Removed From Service
Micrography of the transverse section of the rolled shape presenting an aligned structure, ferritic-pearlitic. Transverse section.
97
VIEW
ML00035 / Dec.2017
Carbon Steel L Shape
M - Low Carbon SteelP - Rolled ShapeAp - StructureCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - In the Center of the Thickness
Micrography of the transverse section of the rolled shape presenting a ferritic-pearlitic microstructure. Transverse section, close to the surface.
80
VIEW
ML00035 / Dec.2017
Carbon Steel L Shape
M - Low Carbon SteelP - Rolled ShapeAp - StructureCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - At the Surface
Micrography of the transverse section of the rolled shape presenting an aligned structure, ferritic-pearlitic.
62
VIEW
ML00035 / Dec.2017
Carbon Steel L Shape
M - Low Carbon SteelP - Rolled ShapeAp - StructureCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Transverse Section
Micrography of the transverse section of the rolled shape presenting an aligned structure, ferritic-pearlitic, and long sulfide inclusions. Center of the leg of 12 mm thickness.
58
VIEW
ML00035 / Dec.2017
Carbon Steel L Shape
M - Low Carbon SteelP - Rolled ShapeAp - StructureCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Non Metallic Inclusions
ML00090 — Carbon Steel Tubing for Structural ApplicationM - Low Carbon SteelP - TubeAp - StructureCd - Typical manufacturing
Micrography of a longitudinal section of the tube, in the center of the thickness. ND 3". 7.6 mm thick.
55
VIEW
ML00090 / Sep.2017
Carbon Steel Tubing for Structural Application
M - Low Carbon SteelP - TubeAp - StructureCd - Typical manufacturing
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Micrography of a longitudinal section of the tube, in the center of the thickness. ND 3". 7.6 mm thick.
43
VIEW
ML00090 / Sep.2017
Carbon Steel Tubing for Structural Application
M - Low Carbon SteelP - TubeAp - StructureCd - Typical manufacturing
Cm - Nital Etched Micrography by OMDf - Longitudinal Section
ML00033 — Plasma Cut of 1 1/4" Steel PlateM - High Strength Low AlloyP - Rolled PlateAp - StructureCd - Cutting
Ferritic perlitic structure of the plate. Longitudinal section.
28
VIEW
ML00033 / Jan.2017
Plasma Cut of 1 1/4" Steel Plate
M - High Strength Low AlloyP - Rolled PlateAp - StructureCd - Cutting
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Ferritic perlitic structure of the plate. Longitudinal section.
29
VIEW
ML00033 / Jan.2017
Plasma Cut of 1 1/4" Steel Plate
M - High Strength Low AlloyP - Rolled PlateAp - StructureCd - Cutting
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Martensitic structure at the cutting HAZ. Longitudinal section.
29
VIEW
ML00033 / Jan.2017
Plasma Cut of 1 1/4" Steel Plate
M - High Strength Low AlloyP - Rolled PlateAp - StructureCd - Cutting
Cm - Nital Etched Micrography by OMDf - Martensite
Martensitic structure at the cutting HAZ. Longitudinal section.
29
VIEW
ML00033 / Jan.2017
Plasma Cut of 1 1/4" Steel Plate
M - High Strength Low AlloyP - Rolled PlateAp - StructureCd - Cutting
Cm - Nital Etched Micrography by OMDf - Martensite
Intercritical heating at 0.5 mm from the cut surface, showing martensitic islands.
32
VIEW
ML00033 / Jan.2017
Plasma Cut of 1 1/4" Steel Plate
M - High Strength Low AlloyP - Rolled PlateAp - StructureCd - Cutting
Cm - Nital Etched Micrography by OMDf - Heat Affected Zone

+2 more from this case →