Ferritic pearlitic

38 cases · 499 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Results

SortNewestOldestTitle A-ZTitle Z-A
Macrography of the longitudinally seam weld of the 24" diameter tube, showing that it was welded from both sides and there is a segregation line in the center of the tube thickness.
737
VIEW
ML00177 / Dec.2021
Cr-Mo Seam Welded Tube
M - CrMo SteelP - Longitudinally Seam WeldedAp - Fired HeaterCd - Not according to spec
Cm - NItal Etched MacroDf - Seam
Aspect before cleaning of the heavy U bolt pipe clamp, 38 mm diameter wire, at the fractured position. It is possible to see that it broke in a region where the clamp was no longer coated and there is no insert in the groove (at the internal clamp diameter). The fracture is transverse to the clamp axis.
522
VIEW
ML00171 / Feb.2021
Corrosion Fatigue of U Bolt Pipe Clamp
M - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - General View
Aspect of the waterwall during removal of the leaking tube. The leakage was detected, by visual inspection, from the outside of the boiler.
1675
VIEW
ML00163 / Jun.2020
Corrosion Fatigue of a Boiler Waterwall Tube
M - Low Carbon SteelP - Seamless tubeAp - BoilerCd - Corrosion Fatigue
Cm - Field photoDf - General View
Macrography of a section longitudinal to the pipe and transverse to the weld. The thickness of the pipe is 12,7 mm (1/2") and it was welded in 6 passes, the root pass, one fill pass and four cap passes.
855
VIEW
ML00153 / Jan.2019
X52 in a Tubular Structure
M - CMn SteelP - Seamless PipeAp - StructureCd - Qualified
Cm - NItal Etched MacroDf - Welded Joint
Gas piping. Aspect of a branching line 2" ND, lateral to a horizontal main pipe ND 8", welded using a weldolet. The cracking started at the margin of the weld in the upper part of the pipe, where the weld crossed the longitudinal direction of the pipe, perpendicular to the branch.
932
VIEW
ML00149 / Dec.2018
Vibration Induced Fatigue in a Gas Piping
M - Low Carbon SteelP - Piping spoolAp - FPSOCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - Cracking
Red painted device where the 50 mm x 50 mm carbon steel plate was positioned (in the circle). The image presents the target, positioned 100 meters far from the gun, after the shot and the projectile perforated the plate, as will be presented in the other figures.
602
VIEW
ML00143 / Aug.2018
Impact of a .308 Winchester on A36 Plate
M - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Cm - Aspect Before AnalysisDf - General View
Fractured position of the casting cylinder of 10.5 mm thickness (minimum measured thickness) showing a brittle behavior (lack of plastic deformation), typical of overloading a material with 1% ductility (measured in the tensile test). This is the view of the internal surface of the cylinder, presenting regions of localized thinning in this surface that was in contact with (treated) cooling water. The external side of the cylinder was painted.
918
VIEW
ML00141 / Jul.2018
Brittle Fracture of a Corroded Gray Cast Iron
M - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Cm - Fracture Surface AspectDf - General View
Aspect of a transverse section of the 4" pipe showing the barnacles adhered to the internal pipe surface, and the leakage position (in the top of the figure). It is possible to see that the deposits are attached all throught the internal pipe perimeter but the damage is localized. The damage morphology suggests it is a crack, or a welding defect, but the microstructural analysis indicated that the damage is a galvanic effect at the autogenous seam weld.
1135
VIEW
ML00140 / May.2019
Preferential Corrosion of Pipe Seam Weld
M - Low Carbon SteelP - Longitudinal Seam Welded PipeAp - ShipCd - Preferential Dissolution
Cm - Longitudinal Section AspectDf - Localized Corrosion

More from these cases

ML00177 — Cr-Mo Seam Welded TubeM - CrMo SteelP - Longitudinally Seam WeldedAp - Fired HeaterCd - Not according to spec
Identification of the regions of metallographies of the base metal, heat affected zone (HAZ) and weld metal. Locations in the root, in the center of the thickness and close to the tube OD (external surface).
118
VIEW
ML00177 / Dec.2021
Cr-Mo Seam Welded Tube
M - CrMo SteelP - Longitudinally Seam WeldedAp - Fired HeaterCd - Not according to spec
Cm - NItal Etched MacroDf - Welded Joint
BASE METAL SURFACE - Ferritic structure, grain refined.
90
VIEW
ML00177 / Dec.2021
Cr-Mo Seam Welded Tube
M - CrMo SteelP - Longitudinally Seam WeldedAp - Fired HeaterCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Base Metal
BASE METAL SURFACE - The micrography (transverse to the tube) presents the ferritic/pearlitic/bainitic structure.
75
VIEW
ML00177 / Dec.2021
Cr-Mo Seam Welded Tube
M - CrMo SteelP - Longitudinally Seam WeldedAp - Fired HeaterCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Granular structure
BASE METAL SURFACE - The microstructure of the base metal is ferritic/pearlitic/bainitic.
74
VIEW
ML00177 / Dec.2021
Cr-Mo Seam Welded Tube
M - CrMo SteelP - Longitudinally Seam WeldedAp - Fired HeaterCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Grain refined structure
HAZ SURFACE
72
VIEW
ML00177 / Dec.2021
Cr-Mo Seam Welded Tube
M - CrMo SteelP - Longitudinally Seam WeldedAp - Fired HeaterCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Last Bead HAZ

+20 more from this case →

ML00171 — Corrosion Fatigue of U Bolt Pipe ClampM - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Aspect of the U bolt clamp with partial detachment of the coating (white brown) in a region where the polimeric insert (dirty white) is still in the wire groove at the internal clamp diameter (ID).
91
VIEW
ML00171 / Feb.2021
Corrosion Fatigue of U Bolt Pipe Clamp
M - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - General View
Detailed aspect of the fractured position, in a region where the clamp was no longer coated and there is no insert in the groove (at the internal clamp diameter). The fracture is transverse to the clamp axis.
86
VIEW
ML00171 / Feb.2021
Corrosion Fatigue of U Bolt Pipe Clamp
M - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - Fracture
Same aspect of the previous image after cleaning, showing a subcritical propagation aspect (fatigue), starting at the groove (ID) and also at the clamp surface in the OD.
75
VIEW
ML00171 / Feb.2021
Corrosion Fatigue of U Bolt Pipe Clamp
M - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - Fracture
In the region where the polimeric insert was loose, the protective coating of the clamp has suffered detachment.
69
VIEW
ML00171 / Feb.2021
Corrosion Fatigue of U Bolt Pipe Clamp
M - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - Layer Detachment
Close to the ID of the clamp, at the groove position, there are cracks in the coating (white brown) and also at the substrate.
63
VIEW
ML00171 / Feb.2021
Corrosion Fatigue of U Bolt Pipe Clamp
M - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - Cracks

+22 more from this case →

ML00163 — Corrosion Fatigue of a Boiler Waterwall TubeM - Low Carbon SteelP - Seamless tubeAp - BoilerCd - Corrosion Fatigue
Aspect of the sample removed from the waterwall, where the tube has leaked, presenting the crack in the membrane.
361
VIEW
ML00163 / Jun.2020
Corrosion Fatigue of a Boiler Waterwall Tube
M - Low Carbon SteelP - Seamless tubeAp - BoilerCd - Corrosion Fatigue
Cm - Field photoDf - Through Wall Cracking
Aspect of the tube internal surface after removal from the boiler, presenting multiple longitudinal cracks.
295
VIEW
ML00163 / Jun.2020
Corrosion Fatigue of a Boiler Waterwall Tube
M - Low Carbon SteelP - Seamless tubeAp - BoilerCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - Internal Surface
Aspect of the external surface of the leaking tube, after removal of the membrane.
262
VIEW
ML00163 / Jun.2020
Corrosion Fatigue of a Boiler Waterwall Tube
M - Low Carbon SteelP - Seamless tubeAp - BoilerCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - External Surface
Throught wall cracking of the waterwall tube at the leakage position, thick edged, The external surface of the tube was grounded to remove the membrane and the cracking is associated to the tube attachement.
242
VIEW
ML00163 / Jun.2020
Corrosion Fatigue of a Boiler Waterwall Tube
M - Low Carbon SteelP - Seamless tubeAp - BoilerCd - Corrosion Fatigue
Cm - Transverse Section AspectDf - Thick-edged rupture
Macrography of the transverse section of the tube, in a position where the cracking was not yet through wall. The internal tube surface shows multiple corrosion fatigue cracks, parallel, under the weld of the membrane, probably related to the cold side of the tube (the cracks opened to the boiler outside). The external side of the tube presenting a small crack at the margem of the weld, suggesting also the action of thermal stresses.
214
VIEW
ML00163 / Jun.2020
Corrosion Fatigue of a Boiler Waterwall Tube
M - Low Carbon SteelP - Seamless tubeAp - BoilerCd - Corrosion Fatigue
Cm - NItal Etched MacroDf - Multiple cracks

+18 more from this case →

ML00153 — X52 in a Tubular StructureM - CMn SteelP - Seamless PipeAp - StructureCd - Qualified
Micrography of the pipe base metal, in a longitudinal section, presenting a slight banding and a refined structure.
147
VIEW
ML00153 / Jan.2019
X52 in a Tubular Structure
M - CMn SteelP - Seamless PipeAp - StructureCd - Qualified
Cm - Nital Etched Micrography by OMDf - Base Metal
Micrography of the pipe base metal, in a longitudinal section. The ferritic structure is refined and it is possible to identify a small variation in the ferritic grain size, that is promoting the slight banding effect.
119
VIEW
ML00153 / Jan.2019
X52 in a Tubular Structure
M - CMn SteelP - Seamless PipeAp - StructureCd - Qualified
Cm - Nital Etched Micrography by OMDf - Base Metal
Micrographic detail of the very refined ferritic structure of the base metal, in the longitudinal section, indicating that the material was heat treated, since no banding is not detectable at this magnification.
101
VIEW
ML00153 / Jan.2019
X52 in a Tubular Structure
M - CMn SteelP - Seamless PipeAp - StructureCd - Qualified
Cm - Nital Etched Micrography by OMDf - Grain refined structure
Schematic drawing of the API 5L X52 pipe, butt welded to another pipe, showing the 4 cap passes. The pipe is nominal diameter 8" and thickness 1/2". The qualification of the WPS was conducted according to the structural code, with toughness requirements (Charpy V at 0°C), with 4 lateral bending tests, all approved, and 2 welded joint tensile tests, one with ruptured in the base metal and the other ruptured in the weld metal, both presenting strenght level higher than the minimum specified. The pipe was tensile tested.
95
VIEW
ML00153 / Jan.2019
X52 in a Tubular Structure
M - CMn SteelP - Seamless PipeAp - StructureCd - Qualified
Cm - Identification drawingDf - Welded Joint
Micrography of the weded joint at the cap pass fusion line. The columnar structure of the weld metal is to the top of the figure; and it is possible to see the coarse grains at the heat affected zone. Both columnar structure and coarse grains are related to the previous austenite grain boundaries. From the fusion line to the base metal (in the bottom of the figure) the grain sizes are refined.
86
VIEW
ML00153 / Jan.2019
X52 in a Tubular Structure
M - CMn SteelP - Seamless PipeAp - StructureCd - Qualified
Cm - Nital Etched Micrography by OMDf - Welded Joint

+8 more from this case →

ML00149 — Vibration Induced Fatigue in a Gas PipingM - Low Carbon SteelP - Piping spoolAp - FPSOCd - Vibration Induced Fatigue
Gas piping. Aspect of a branching line 2" ND with a flange, lateral to a main pipe ND 8", welded using a weldolet. The cracking is at the margin of the weld.
115
VIEW
ML00149 / Dec.2018
Vibration Induced Fatigue in a Gas Piping
M - Low Carbon SteelP - Piping spoolAp - FPSOCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - General View
Micrography of a transverse section of the seamless pipe, presenting a ferritic-pearlitic structure.
84
VIEW
ML00149 / Dec.2018
Vibration Induced Fatigue in a Gas Piping
M - Low Carbon SteelP - Piping spoolAp - FPSOCd - Vibration Induced Fatigue
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Micrography of a transverse section of the seamless pipe, presenting a ferritic-pearlitic structure.
70
VIEW
ML00149 / Dec.2018
Vibration Induced Fatigue in a Gas Piping
M - Low Carbon SteelP - Piping spoolAp - FPSOCd - Vibration Induced Fatigue
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Gas piping. Aspect of a branching line 2" ND, lateral to a horizontal main pipe ND 8", welded using a weldolet. In the lower part of the branch there are no cracks.
61
VIEW
ML00149 / Dec.2018
Vibration Induced Fatigue in a Gas Piping
M - Low Carbon SteelP - Piping spoolAp - FPSOCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - Welded Joint
Aspect of the brach line viewed from the internal side of the main pipe, after cuting. It is possible to see that the pipe was perforated by a thermal cutting (looking the finishing aspect of the edge of the hole). The weldolet was welded only from the external side of the pipe.
62
VIEW
ML00149 / Dec.2018
Vibration Induced Fatigue in a Gas Piping
M - Low Carbon SteelP - Piping spoolAp - FPSOCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - Internal Surface

+13 more from this case →

ML00143 — Impact of a .308 Winchester on A36 PlateM - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Aspect of a typical .308 Winchester projectile, similar to the one adopted to shot the plate, cut in a longitudinal section. It is a Cu alloy case filled with Pb-Sb.
92
VIEW
ML00143 / Aug.2018
Impact of a .308 Winchester on A36 Plate
M - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Cm - Longitudinal Section AspectDf - Longitudinal Section
Aspect of the 3/8" thickness plate, 50 mm x 50 mm, of the low carbon steel steel, in the face of impact with the projectile. The plate was perforated by the bullet.
88
VIEW
ML00143 / Aug.2018
Impact of a .308 Winchester on A36 Plate
M - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Cm - Aspect Before AnalysisDf - General View
Micrography of the plate in a section, showing a ferritic-pearlitic microstructure in the middle of the thickness.
84
VIEW
ML00143 / Aug.2018
Impact of a .308 Winchester on A36 Plate
M - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Micrography of the plate in a section, showing a ferritic-pearlitic microstructure in the middle of the thickness, in a position where the plate was not affected by the shot.
65
VIEW
ML00143 / Aug.2018
Impact of a .308 Winchester on A36 Plate
M - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Micrographic detail of the plate in a section, showing a ferritic-pearlitic microstructure in the middle of the thickness.
66
VIEW
ML00143 / Aug.2018
Impact of a .308 Winchester on A36 Plate
M - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite

+51 more from this case →

ML00141 — Brittle Fracture of a Corroded Gray Cast IronM - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Fracture aspect of the casting cylinder at the 10.5 mm thickness, showing a brittle behavior (lack of plastic deformation). The internal side of the cylinder is to the top of the figure, and the painted surface is to the bottom of the figure.
129
VIEW
ML00141 / Jul.2018
Brittle Fracture of a Corroded Gray Cast Iron
M - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Cm - Fracture Surface AspectDf - Brittle Fracture
Detailed aspect of the cylinder fracture, the internal surface to the top of the figure and the painted external surface to the bottom of the figure.
103
VIEW
ML00141 / Jul.2018
Brittle Fracture of a Corroded Gray Cast Iron
M - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Cm - Fracture Surface AspectDf - Brittle Fracture
Macrographic aspect of a section of the cast cylinder, transverse to the fracture (top). The internal diameter of the cylinder (exposed to treated water) is to the left side and the external diameter of the cylinder (painted) is to the right side.
96
VIEW
ML00141 / Jul.2018
Brittle Fracture of a Corroded Gray Cast Iron
M - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Cm - NItal Etched MacroDf - Brittle Fracture
Micrographic aspect, as polished, of the cast cylinder section at the fracture position (top of the figure), close to the internal surface (left side). It is possible to see large graphite flakes.
98
VIEW
ML00141 / Jul.2018
Brittle Fracture of a Corroded Gray Cast Iron
M - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Cm - As polished micrographyDf - Close to the Internal Surface
Micrographic aspect, as polished, of the cast cylinder section at the fracture position (top of the figure), in the center of the thickness. It is possible to see a mixture of large graphite flakes and rosette grouping flakes.
80
VIEW
ML00141 / Jul.2018
Brittle Fracture of a Corroded Gray Cast Iron
M - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Cm - As polished micrographyDf - In the Center of the Thickness

+30 more from this case →

ML00140 — Preferential Corrosion of Pipe Seam WeldM - Low Carbon SteelP - Longitudinal Seam Welded PipeAp - ShipCd - Preferential Dissolution
Micrography of the pipe transverse section presenting a granular microstructure.
147
VIEW
ML00140 / May.2019
Preferential Corrosion of Pipe Seam Weld
M - Low Carbon SteelP - Longitudinal Seam Welded PipeAp - ShipCd - Preferential Dissolution
Cm - Nital Etched Micrography by OMDf - Transverse Section
Micrography of the pipe transverse section presenting a predominatly ferritic-perlitic microstructure.
132
VIEW
ML00140 / May.2019
Preferential Corrosion of Pipe Seam Weld
M - Low Carbon SteelP - Longitudinal Seam Welded PipeAp - ShipCd - Preferential Dissolution
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Micrographic detail of the predominatly ferritic-perlitic microstructure. Pipe transverse section.
95
VIEW
ML00140 / May.2019
Preferential Corrosion of Pipe Seam Weld
M - Low Carbon SteelP - Longitudinal Seam Welded PipeAp - ShipCd - Preferential Dissolution
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Aspect of the 4" pipe that was in seawater service for 8 years and leaked in a longitudinal line that corresponds to the seam weld. The internal surface presented thick deposits. Although the pipe was cut with a thermal process, the analysis was conducted after mechanical cutting.
100
VIEW
ML00140 / May.2019
Preferential Corrosion of Pipe Seam Weld
M - Low Carbon SteelP - Longitudinal Seam Welded PipeAp - ShipCd - Preferential Dissolution
Cm - Aspect Before AnalysisDf - General View
Detail of the transverse section of the 4" pipe at the longitudinal seam weld evidencing the leakage position. The damage appears as a through wall opening. The pipe thickness is 8 mm and there are no evidences of general corrosion (the SCH 80 corresponds to 8.6 mm) or pitting at the internal surface.
100
VIEW
ML00140 / May.2019
Preferential Corrosion of Pipe Seam Weld
M - Low Carbon SteelP - Longitudinal Seam Welded PipeAp - ShipCd - Preferential Dissolution
Cm - Transverse Section AspectDf - Leakage

+19 more from this case →