Ferritic pearlitic

4 cases · 8 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Capture method: Transverse Section Aspect clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Throught wall cracking of the waterwall tube at the leakage position, thick edged, The external surface of the tube was grounded to remove the membrane and the cracking is associated to the tube attachement.
242
VIEW
ML00163 / Jun.2020
Corrosion Fatigue of a Boiler Waterwall Tube
M - Low Carbon SteelP - Seamless tubeAp - BoilerCd - Corrosion Fatigue
Cm - Transverse Section AspectDf - Thick-edged rupture
Aspect of the 3/8" thickness plate, 50 mm x 50 mm, of the low carbon steel, in a section transverse to the impact position that is to the top of the figure. The perforated hole expulsed the material to the top and bottom directions. The hole is larger in the exit of the bullet.
53
VIEW
ML00143 / Aug.2018
Impact of a .308 Winchester on A36 Plate
M - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Cm - Transverse Section AspectDf - Transverse Section
Detail of the transverse section of the 4" pipe at the longitudinal seam weld evidencing the leakage position. The damage appears as a through wall opening. The pipe thickness is 8 mm and there are no evidences of general corrosion (the SCH 80 corresponds to 8.6 mm) or pitting at the internal surface.
100
VIEW
ML00140 / May.2019
Preferential Corrosion of Pipe Seam Weld
M - Low Carbon SteelP - Longitudinal Seam Welded PipeAp - ShipCd - Preferential Dissolution
Cm - Transverse Section AspectDf - Leakage
The macrography of a longitudinal section of the shell plate (sample removed from the boiler), at the position of the fillet weld (sealing weld) with a tube, where surface welding repairs created conditions for cracking the base material in a transgranular morphology. Several cracks were identify starting from the steam drum internal surface.
448
VIEW
ML00019 / Apr.2017
Transgranular SCC in Boiler Steam Drum
M - CMn SteelP - Rolled PlateAp - BoilerCd - Stress Corrosion
Cm - Transverse Section AspectDf - Cracks

More from these cases

ML00140 — Preferential Corrosion of Pipe Seam WeldM - Low Carbon SteelP - Longitudinal Seam Welded PipeAp - ShipCd - Preferential Dissolution
Detail of the transverse section of the 4" pipe 90° from the seam weld. The thickness of the pipe is 8 mm. No evidences of general corrosion or pitting were identified.
77
VIEW
ML00140 / May.2019
Preferential Corrosion of Pipe Seam Weld
M - Low Carbon SteelP - Longitudinal Seam Welded PipeAp - ShipCd - Preferential Dissolution
Cm - Transverse Section AspectDf - Transverse Section
Detail of the transverse section of the 4" pipe 90° from the seam weld. The thickness of the pipe is 8 mm. No evidences of general corrosion or pitting were identified.
70
VIEW
ML00140 / May.2019
Preferential Corrosion of Pipe Seam Weld
M - Low Carbon SteelP - Longitudinal Seam Welded PipeAp - ShipCd - Preferential Dissolution
Cm - Transverse Section AspectDf - Transverse Section
Detail of the transverse section of the 4" pipe 180° from the seam weld. The thickness of the pipe is 8 mm. No evidences of general corrosion or pitting were identified.
64
VIEW
ML00140 / May.2019
Preferential Corrosion of Pipe Seam Weld
M - Low Carbon SteelP - Longitudinal Seam Welded PipeAp - ShipCd - Preferential Dissolution
Cm - Transverse Section AspectDf - Transverse Section
Detail of the transverse section of the 4" pipe at the longitudinal seam weld where it is not leaking yet, showing that the damage is not a crack but a localized dissolution, or localized corrosion or preferential dissolution at the autogenous seam weld. The thickness of the pipe is 8 mm and there are no evidences of general corrosion or pitting.
63
VIEW
ML00140 / May.2019
Preferential Corrosion of Pipe Seam Weld
M - Low Carbon SteelP - Longitudinal Seam Welded PipeAp - ShipCd - Preferential Dissolution
Cm - Transverse Section AspectDf - Localized Corrosion