Quenched and tempered structure of the F22 steel forging, presenting about 230HV10 average hardness.
133
VIEW
ML00178 / Jan.2022
Cold cracks in Cr-Mo Welded Forging
M - CrMo SteelP - ForgingAp - O&G Well DrillingCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Base Metal
BASE METAL SURFACE - Ferritic structure, grain refined.
90
VIEW
ML00177 / Dec.2021
Cr-Mo Seam Welded Tube
M - CrMo SteelP - Longitudinally Seam WeldedAp - Fired HeaterCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Base Metal
Cast fitting microstructure. Network of primary carbides and austenitic matrix with coalescing secondary precipitation.
38
VIEW
ML00173 / May.2021
Welding Cracks in an Aged HP Cast Fitting
M - Heat Resistant SteelP - Cast FtittingAp - PetrochemicalCd - Welding
Cm - Kalling Etched Micrography by OMDf - Base Metal
Micrography of the base metal presenting a banded microstructure in the longitudinal section of the pipe.
52
VIEW
ML00066 / May.2017
GMAW Welded Joint in 9%Ni Alloy Steel
M - Nickel Alloy SteelP - Welded Testpiece for QualificationAp - PipelineCd - Welding
Cm - Nital Etched Micrography by OMDf - Base Metal
Micrography of a longitudinal section of the fitting, at the base metal, presenting an austenitic structure with intergranular and transgranular precipitation as a result of microstructural evolution.
44
VIEW
ML00061 / Apr.2017
Creep in a Seam Weld of a 304H SS Fitting
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Creep
Cm - Micrography by OM using A262 Method ADf - Base Metal
Original casting base metal presenting a coarse martensitic structure with a small amount of delta ferrite.
50
VIEW
ML00055 / Apr.2017
CA6NM Blade Remanufactured by Welding
M - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Cm - Kalling Etched Micrography by OMDf - Base Metal Left Side
Base metal micrographic detail presenting a tempered martensitic microstructure.
27
VIEW
ML00045 / Aug.2017
Subsea Tubular F6NM Martensitic SS
M - Martensitic Stainless SteelP - Fabrication WeldAp - OffshoreCd - Welding
Cm - Kalling Etched Micrography by OMDf - Base Metal
Low carbon plate base metal presenting the ferritic perlitic structure.
55
VIEW
ML00052 / Apr.2017
Cold Cracks in API 5CT L80 Tube Welded to a Structural Part
M - Low Alloy SteelP - Seamless tubeAp - OffshoreCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Base Metal

More from these cases

ML00177 — Cr-Mo Seam Welded TubeM - CrMo SteelP - Longitudinally Seam WeldedAp - Fired HeaterCd - Not according to spec
BASE METAL T/2
41
VIEW
ML00177 / Dec.2021
Cr-Mo Seam Welded Tube
M - CrMo SteelP - Longitudinally Seam WeldedAp - Fired HeaterCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Base Metal
BASE METAL T/2
36
VIEW
ML00177 / Dec.2021
Cr-Mo Seam Welded Tube
M - CrMo SteelP - Longitudinally Seam WeldedAp - Fired HeaterCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Base Metal
ML00066 — GMAW Welded Joint in 9%Ni Alloy SteelM - Nickel Alloy SteelP - Welded Testpiece for QualificationAp - PipelineCd - Welding
Micrographic detail of a longitudinal section of the base metal presenting a quenched and tempered microstructure.
50
VIEW
ML00066 / May.2017
GMAW Welded Joint in 9%Ni Alloy Steel
M - Nickel Alloy SteelP - Welded Testpiece for QualificationAp - PipelineCd - Welding
Cm - Nital Etched Micrography by OMDf - Base Metal
ML00061 — Creep in a Seam Weld of a 304H SS FittingM - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Creep
Micrographic detail of the fitting base metal, presenting an austenitic structure with intergranular and transgranular precipitation as a result of microstructural evolution.
40
VIEW
ML00061 / Apr.2017
Creep in a Seam Weld of a 304H SS Fitting
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Creep
Cm - Micrography by OM using A262 Method ADf - Base Metal
ML00055 — CA6NM Blade Remanufactured by WeldingM - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Micrographic detail of the original casting blade structure. The tempered martensite is more clearly revealed by the scanning electron microscopy. The average hardness level measured in this side is 270 HV.
70
VIEW
ML00055 / Apr.2017
CA6NM Blade Remanufactured by Welding
M - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Cm - Kalling Etched Micrography by SEMDf - Base Metal Left Side
Higher magnification of the martensitic structure of the original casting blade structure, hardness level of 270HV10.
26
VIEW
ML00055 / Apr.2017
CA6NM Blade Remanufactured by Welding
M - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Cm - Kalling Etched Micrography by SEMDf - Base Metal Left Side
Inserted casting base metal presenting a coarse martensitic structure with a small amount of delta ferrite.
24
VIEW
ML00055 / Apr.2017
CA6NM Blade Remanufactured by Welding
M - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Cm - Kalling Etched Micrography by OMDf - Base Metal Right Side
Micrographic detail of the inserted casting structure. The martensite presents a less tempering aspect than the original casting revealing that it was heat treated in a different condition. The average hardness level measured in this side is 370 HV.
157
VIEW
ML00055 / Apr.2017
CA6NM Blade Remanufactured by Welding
M - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Cm - Kalling Etched Micrography by SEMDf - Base Metal Right Side
Higher magnification of the martensitic structure of the inserted casting structure, hardness level of 370HV10.
23
VIEW
ML00055 / Apr.2017
CA6NM Blade Remanufactured by Welding
M - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Cm - Kalling Etched Micrography by SEMDf - Base Metal Right Side
ML00045 — Subsea Tubular F6NM Martensitic SSM - Martensitic Stainless SteelP - Fabrication WeldAp - OffshoreCd - Welding
Micrography of the base metal showing a tempered martensitic microstructure.
30
VIEW
ML00045 / Aug.2017
Subsea Tubular F6NM Martensitic SS
M - Martensitic Stainless SteelP - Fabrication WeldAp - OffshoreCd - Welding
Cm - Kalling Etched Micrography by OMDf - Base Metal
Micrographic detail of the base metal tempered martensite.
24
VIEW
ML00045 / Aug.2017
Subsea Tubular F6NM Martensitic SS
M - Martensitic Stainless SteelP - Fabrication WeldAp - OffshoreCd - Welding
Cm - Kalling Etched Micrography by SEMDf - Base Metal
ML00052 — Cold Cracks in API 5CT L80 Tube Welded to a Structural PartM - Low Alloy SteelP - Seamless tubeAp - OffshoreCd - Welding Defect
High Strenght Low Alloy steel tube, base metal, presenting the bainitic structure.
54
VIEW
ML00052 / Apr.2017
Cold Cracks in API 5CT L80 Tube Welded to a Structural Part
M - Low Alloy SteelP - Seamless tubeAp - OffshoreCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Base Metal