Ferrous Alloys

19 cases · 32 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Capture method: Surface Aspect clear all

Ferrous Alloys — sub-branches

Carbon Steel 31Cast Iron 9High Alloy Steel 52Low Alloy Steel 56Tool Steel 2

Results

SortNewestOldestTitle A-ZTitle Z-A
The threads of the carbon steel valve body is corroded. The offshore ambient is wet and chloride rich, creating an aggressive environment for the carbon steel threads.
99
VIEW
ML00184 / Apr.2023
Dissimilar Steels in a Threaded Connection
M - Low Carbon SteelP - ForgingAp - OffshoreCd - Localized Dissolution
Cm - Surface AspectDf - Corrosion
Detail of a sound teeth, showing marks of plastic deformation across the tooth surface.
53
VIEW
ML00181 / Apr.2022
Wear of a Carburized Hypoid Gear
M - Low Alloy for Thermochemical TreatmentP - Pinion-crown assemblyAp - ShipCd - Wear
Cm - Surface AspectDf - Plastic Deformation
Pipe body surface, adjacent to the fracture, showing regions of corrosion and visual cracks transverse to the pipe axis.
29
VIEW
ML00169 / Nov.2020
Drill Pipe Fracture in the Pipe Body
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Surface AspectDf - Cracks
Low magnification microscope image showing the aspect of the thread close to the fracture surface. Looks like a wear or strong corrosion, but in fact the threads were removed because they were cracked, as can be seen in the next figures.
67
VIEW
ML00157 / Feb.2020
Bolts Under Chloride SCC Conditions
M - Austenitic Stainless SteelP - BoltAp - Oil and GasCd - Stress Corrosion
Cm - Surface AspectDf - Low Mag
Aspect of the cut surface of the fork tooth in the scoop. The thickness is 1 mm and the fabrication finishing of the surface is polished. The tooth in the center was cut for analysis in the longitudinal section.
33
VIEW
ML00151 / Dec.2018
Ferritic Stainless Steel of a Flatware Fork
M - Ferritic Stainless SteelP - Foodstuff ArticleAp - KitchenCd - Typical manufacturing
Cm - Surface AspectDf - Cut Surface
Detail of the external surface of the sleeve where the surface coating was detached, creating a lack of sealing condition.
67
VIEW
ML00147 / Aug.2018
WC Layer Detached from a Cast Lean Duplex
M - Lean Duplex Stainless SteelP - Centrifugal CastingAp - ShipCd - Lack of Sealing
Cm - Surface AspectDf - External Surface
Detail of the position where the projectile strike the plate. The plate suffered a localized perforation.
44
VIEW
ML00143 / Aug.2018
Impact of a .308 Winchester on A36 Plate
M - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Cm - Surface AspectDf - Low Mag
Detail of the position in the plate of impact with the projectile. No damage, only particles adhered at the surface.
36
VIEW
ML00142 / Aug.2018
Impact of a .308 Winchester on AR500 Plate
M - Low Alloy Wear ResistantP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Surface AspectDf - Low Mag

More from these cases

ML00184 — Dissimilar Steels in a Threaded ConnectionM - Low Carbon SteelP - ForgingAp - OffshoreCd - Localized Dissolution
Not only the threads were corroded but all regions under the painting that was detached from the surface.
86
VIEW
ML00184 / Apr.2023
Dissimilar Steels in a Threaded Connection
M - Low Carbon SteelP - ForgingAp - OffshoreCd - Localized Dissolution
Cm - Surface AspectDf - Corrosion
ML00181 — Wear of a Carburized Hypoid GearM - Low Alloy for Thermochemical TreatmentP - Pinion-crown assemblyAp - ShipCd - Wear
Macroscopic detail of the pitting damage and plastic deformation at the surface of non-fractured tooth.
58
VIEW
ML00181 / Apr.2022
Wear of a Carburized Hypoid Gear
M - Low Alloy for Thermochemical TreatmentP - Pinion-crown assemblyAp - ShipCd - Wear
Cm - Surface AspectDf - Pitting
Macroscopic detail of the fractured tooth, showing marks of plastic deformation at the tooth surface and several longitudinal cracks in the contact surfaces.
46
VIEW
ML00181 / Apr.2022
Wear of a Carburized Hypoid Gear
M - Low Alloy for Thermochemical TreatmentP - Pinion-crown assemblyAp - ShipCd - Wear
Cm - Surface AspectDf - Crack
Macroscopic detail of the fractured tooth, showing several longitudinal cracks in the contact surfaces, suggesting the occurrence of spalling damage.
44
VIEW
ML00181 / Apr.2022
Wear of a Carburized Hypoid Gear
M - Low Alloy for Thermochemical TreatmentP - Pinion-crown assemblyAp - ShipCd - Wear
Cm - Surface AspectDf - Fatigue Crack
ML00147 — WC Layer Detached from a Cast Lean DuplexM - Lean Duplex Stainless SteelP - Centrifugal CastingAp - ShipCd - Lack of Sealing
Macroscopic aspect of the OD surface of the sleeve (top of the figure), and a macrography of a longitudinal section (bottom of the figure). In the right side of the figure it is possible to see that the lack of sealing is associated to the detachment of the thermal spray surface layer.
26
VIEW
ML00147 / Aug.2018
WC Layer Detached from a Cast Lean Duplex
M - Lean Duplex Stainless SteelP - Centrifugal CastingAp - ShipCd - Lack of Sealing
Cm - Surface AspectDf - Longitudinal Section
ML00143 — Impact of a .308 Winchester on A36 PlateM - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Detail of the position where the projectile exited the plate. The plate suffered a localized perforation and the straight line is marked where the bullet was deviated from the painted device.
41
VIEW
ML00143 / Aug.2018
Impact of a .308 Winchester on A36 Plate
M - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Cm - Surface AspectDf - Low Mag
Detail of the margin of the perforated hole in the impact position. It is interesting to observe that the perforation caused the material to be expulsed from the hole, in the direction of the impact.
39
VIEW
ML00143 / Aug.2018
Impact of a .308 Winchester on A36 Plate
M - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Cm - Surface AspectDf - Plastic Deformation
Detail of the plate surface a little far from the perforated hole, in the side where the projectil stroke the plate. Drops of melted material from the bullet.
34
VIEW
ML00143 / Aug.2018
Impact of a .308 Winchester on A36 Plate
M - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Cm - Surface AspectDf - Melted film