Crevice Corrosion in a Subsea System — Aspect Before Analysis

Standard: API Capture method: Aspect Before Analysis clear all

Sampling and Analysis — sub-branches

At the Surface 1General View 8Internal Surface 2Welded Joint 2

Results

SortNewestOldestTitle A-ZTitle Z-A
Fracture position at the pipe body, about 1 meter from the tool joint end. The fracture presented two main aspects, a flat fracture transverse to the pipe axis, that propagated by fatigue through almost 50% of the pipe perimeter, and a final fracture by shear overloading.
560
VIEW
ML00169 / Nov.2020
Drill Pipe Fracture in the Pipe Body
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - General View
Lateral image of a collapsed API 5D grade S135 drill pipe, presenting the fractured region (bottom of the figure) at the pipe body. Although the pipe steel is of a high strenght, the fracture characteristic is ductile, evidencing strong plastic deformation.
545
VIEW
ML00159 / Mar.2020
Collapse of a Drill Pipe
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Ductile Behavior
Cm - Aspect Before AnalysisDf - General View
Aspect of the 4" pipe that was in seawater service for 8 years and leaked in a longitudinal line that corresponds to the seam weld. The internal surface presented thick deposits. Although the pipe was cut with a thermal process, the analysis was conducted after mechanical cutting.
100
VIEW
ML00140 / May.2019
Preferential Corrosion of Pipe Seam Weld
M - Low Carbon SteelP - Longitudinal Seam Welded PipeAp - ShipCd - Preferential Dissolution
Cm - Aspect Before AnalysisDf - General View
The 6 1/2" nominal diameter longitudinal seam welded pipe is internally cladded with Alloy 625. The pipe was manufactured by forming a cladded plate (probably welded by rolling) and welding it longitudinally. The pipe was heat treated (quenched and tempered) after the seam weld.
96
VIEW
ML00133 / May.2018
Seam Welded Pipe Cladded with Alloy 625
M - LAS / Ni AlloyP - Longitudinal Seam Welded PipeAp - Oil and GasCd - Welding
Cm - Aspect Before AnalysisDf - Welded Joint
The 4 1/2" nominal diameter seamless pipe internally overlaid with Alloy 625. This pipe corresponds to a 90° curve. The overlaid pipe was heat treated before and after bending. The final quenching and tempering heat treatment was conducted to meet API 5L X70 properties.
113
VIEW
ML00132 / May.2018
Seamless Pipe Overlaid with Alloy 625
M - LAS / Ni AlloyP - Seamless PipeAp - Oil and GasCd - Welding
Cm - Aspect Before AnalysisDf - Welded Joint
Aspect of the bolt analyzed to qualify the lot of fasteners to be adopted in subsea conditions, exposed to cathodic protection.
62
VIEW
ML00106 / Dec.2017
Inconel 718 Submarine Bolt
M - NiCrFe AlloyP - BoltAp - SubseaCd - Typical manufacturing
Cm - Aspect Before AnalysisDf - General View
Aspect of the bolt with a special head, to be adopted in subsea condition. M12, 1/2" 13UNC.
342
VIEW
ML00105 / Jun.2018
Inconel 718 Bolt of Special Head
M - NiCrFe AlloyP - FastenerAp - SubseaCd - Typical manufacturing
Cm - Aspect Before AnalysisDf - General View
Aspect of the fracture that occurred in the connection between the pin of one DP and the box of other DP, in the pin side. The photo presents the pin still connected in the box. The flat fracture indicates a brittle behavior.
641
VIEW
ML00009 / Sep.2017
Hydrogen Cracking of a 5" Drill Pipe S135
M - Low Alloy Medium Carbon QTP - Drill PipeAp - SubseaCd - Hydrogen Embrittlement
Cm - Aspect Before AnalysisDf - General View

More from these cases

ML00169 — Drill Pipe Fracture in the Pipe BodyM - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Corrosion Fatigue
This figure presents the location of the fracture at about 1 meter from the tool joint pin side. Close to the fracture the pipe presented several circunferential scratches created by the fishing of the broken piece after the fracture.
58
VIEW
ML00169 / Nov.2020
Drill Pipe Fracture in the Pipe Body
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - General View
Region where the internal coating was detached. The fracture at this position is flat.
28
VIEW
ML00169 / Nov.2020
Drill Pipe Fracture in the Pipe Body
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - Internal Surface
ML00140 — Preferential Corrosion of Pipe Seam WeldM - Low Carbon SteelP - Longitudinal Seam Welded PipeAp - ShipCd - Preferential Dissolution
Aspect of the internal surface of the pipe after cleaning, showing the leakage line.
67
VIEW
ML00140 / May.2019
Preferential Corrosion of Pipe Seam Weld
M - Low Carbon SteelP - Longitudinal Seam Welded PipeAp - ShipCd - Preferential Dissolution
Cm - Aspect Before AnalysisDf - Internal Surface