Fracture

43 cases · 114 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Results

SortNewestOldestTitle A-ZTitle Z-A
Detailed aspect of the spring close to the fracture position. The wire surface shows a morphology that reveals the material structure.
58
VIEW
ML00076 / Jun.2017
Hydrogen Cracking of a 17-7 PH Subsea Spring
M - Precipitation Hardened Stainless SteelP - WireAp - SubseaCd - Hydrogen Embrittlement
Cm - Aspect Before AnalysisDf - Fracture
Micrography of a longitudinal section of the stud, at the fracture surface, in the thread.
44
VIEW
ML00075 / Jun.2018
Hydrogen Cracking of IN 718 Subsea Fasteners
M - NiCrFe AlloyP - StudAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Fracture
Detail of the brittle part of the bolt fracture, presenting a secondary cracking longitudinal to the bolt axis. The region of the bolt at the bottom of the thread (close to the surface) is brighter than the internal part of the bolt suggesting different fracture mechanisms.
111
VIEW
ML00074 / Jun.2018
Hydrogen Cracking of a 17-4 PH Subsea Bolt
M - Precipitation Hardened Stainless SteelP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Fracture Surface AspectDf - Fracture
After opening a crack it was possible to see the fracture appearance.
70
VIEW
ML00071 / Jan.2019
Reheating Cracking of a CrMo Vessel Weld
M - CrMo SteelP - In Field WeldAp - EnergyCd - Welding Defect
Cm - Fractography by SEMDf - Fracture
Aspect of the fracture in the middle of the fillet weld between the superior plate (Low carbon 8 mm thick no longer there) and the inferior plate (C-Mn 12 mm thick), in an overlap geometry.
77
VIEW
ML00067 / May.2017
Cold Cracks in C-Mn SAW Weld Metal
M - CMn SteelP - Fabrication WeldAp - AutomotiveCd - Welding Defect
Cm - Aspect Before AnalysisDf - Fracture
The camshaft broke in a brittle way in a region where the shaft changed the geometry, close to a chilled lobe.
551
VIEW
ML00060 / Apr.2017
Brittle Fracture of a Chilled Cast Iron Camshaft
M - Chilled Cast IronP - ShaftAp - AutomotiveCd - Brittle Fracture
Cm - Aspect Before AnalysisDf - Fracture
The micrography of the stem at the fracture region shows a flat fracture with transgranular clevage at the ferritic structure.
137
VIEW
ML00040 / Apr.2017
Brittle Fracture of a Valve Stem
M - Nodular Cast IronP - Valve StemAp - ShipCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Fracture
Detail of the pin surface showing that the material easily cracks because it presents regions of localized corrosion.
45
VIEW
ML00016 / Apr.2017
SCC in Free Cutting 303SS
M - Austenitic Stainless SteelP - Machined PartAp - OffshoreCd - Stress Corrosion
Cm - Surface Aspect by SEMDf - Fracture

More from these cases

ML00076 — Hydrogen Cracking of a 17-7 PH Subsea SpringM - Precipitation Hardened Stainless SteelP - WireAp - SubseaCd - Hydrogen Embrittlement
Micrographic detail of a longitudinal section of the wire, at the fracture surface (top of the figure) evidencing the intergranular and transgranular aspects of the hydrogen assisted cracking mechanism. The electrolytic oxalic acid etch reveals the delta ferrite phase. Compare with the Kalling etch in the other figure.
31
VIEW
ML00076 / Jun.2017
Hydrogen Cracking of a 17-7 PH Subsea Spring
M - Precipitation Hardened Stainless SteelP - WireAp - SubseaCd - Hydrogen Embrittlement
Cm - Micrography by OM using A262 Method ADf - Fracture
Micrographic detail of a longitudinal section of the wire, at the fracture surface (top of the figure) evidencing the intergranular and transgranular aspects of the hydrogen assisted cracking mechanism. The Kalling etch does not reveal the delta ferrite. Compare with the electrolytic oxalic acid etch in the other figure.
29
VIEW
ML00076 / Jun.2017
Hydrogen Cracking of a 17-7 PH Subsea Spring
M - Precipitation Hardened Stainless SteelP - WireAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Fracture
ML00067 — Cold Cracks in C-Mn SAW Weld MetalM - CMn SteelP - Fabrication WeldAp - AutomotiveCd - Welding Defect
Micrography of the fractured region in the center of the fillet weld metal, that is hard due to the increase in the Mn and Si contents.
43
VIEW
ML00067 / May.2017
Cold Cracks in C-Mn SAW Weld Metal
M - CMn SteelP - Fabrication WeldAp - AutomotiveCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Fracture
ML00060 — Brittle Fracture of a Chilled Cast Iron CamshaftM - Chilled Cast IronP - ShaftAp - AutomotiveCd - Brittle Fracture
Micrography transverse to the fracture, showing that the region that broke presented in the shaft thickness a large amount of brittle structures (ledeburite), that suggest a too large extension of the chill effect.
53
VIEW
ML00060 / Apr.2017
Brittle Fracture of a Chilled Cast Iron Camshaft
M - Chilled Cast IronP - ShaftAp - AutomotiveCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Fracture
Micrographic detail of the structure in a section transverse to the fracture, showing that the brittle region in the shaft is associated to a large amount of ledeburite.
43
VIEW
ML00060 / Apr.2017
Brittle Fracture of a Chilled Cast Iron Camshaft
M - Chilled Cast IronP - ShaftAp - AutomotiveCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Fracture
Camshaft in the broken region, close to a lobe where the cast iron was chilled.
48
VIEW
ML00060 / Apr.2017
Brittle Fracture of a Chilled Cast Iron Camshaft
M - Chilled Cast IronP - ShaftAp - AutomotiveCd - Brittle Fracture
Cm - Aspect Before AnalysisDf - Fracture
ML00040 — Brittle Fracture of a Valve StemM - Nodular Cast IronP - Valve StemAp - ShipCd - Brittle Fracture
Micrography presenting a detail of the fracture surface opening to the graphite nodules.
139
VIEW
ML00040 / Apr.2017
Brittle Fracture of a Valve Stem
M - Nodular Cast IronP - Valve StemAp - ShipCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Fracture