Fracture

27 cases · 41 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Capture method: Aspect Before Analysis clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Detail of the fracture in the WHEEL 1, changing direction of propagation.
71
VIEW
ML00183 / Dec.2022
Ductile Behavior of an Aluminum Wheel
M - Aluminum Silicon MagnesiumP - CastingAp - AutomotiveCd - Ductile Behavior
Cm - Aspect Before AnalysisDf - Fracture
Brittle Fracture of a LAS Fixing Rod
2
VIEW
ML00182 / Jul.2022
Brittle Fracture of a LAS Fixing Rod
M - Low Alloy Medium Carbon QTP - StemAp - Mechanical IndustryCd - Brittle Fracture
Cm - Aspect Before AnalysisDf - Fracture
The rotor blade failed without deformation. At the rotor surface it is possible to see different colours of deposits.
53
VIEW
ML00176 / Nov.2021
Hydride Formation in a Titanium Blade
M - Unalloyed TitaniumP - BladeAp - Oil and GasCd - Hydride Formation
Cm - Aspect Before AnalysisDf - Fracture
The small wedge sample is 4 mm deep in the thickness and the circumferential weld are is about 15 mm width where it appears in the internal side of the carcass. The image shows the crack surface (fracture) where the weld aspect is evident.
32
VIEW
ML00174 / Jul.2021
Carburization of a 347 SS Welded Joint
M - Austenitic Stainless SteelP - Fabrication WeldAp - EnergyCd - Carburization
Cm - Aspect Before AnalysisDf - Fracture
Aspect of the fracture of the spring. The spring surface shows shallow pits.
49
VIEW
ML00172 / Mar.2021
Brittle Fracture of a LAS Valve Spring
M - Low Alloy Medium Carbon QTP - SpringAp - Oil and GasCd - Brittle Fracture
Cm - Aspect Before AnalysisDf - Fracture
Detailed aspect of the fractured position, in a region where the clamp was no longer coated and there is no insert in the groove (at the internal clamp diameter). The fracture is transverse to the clamp axis.
86
VIEW
ML00171 / Feb.2021
Corrosion Fatigue of U Bolt Pipe Clamp
M - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - Fracture
Fracture appearance in the side that was not damaged by the fishing, showing the two aspects of the fracture propagation, half by fatigue and half by shearing overloading.
48
VIEW
ML00169 / Nov.2020
Drill Pipe Fracture in the Pipe Body
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - Fracture
Macroscopic view of the fracture in the pipe body. In the bottom of the figure, the fracture of the pipe shows a thicker thickness, revealing that this is the pipe region that was first damaged by bending (buckling). In the top of the figure, the fracture shows a (ductile) shearing mechanism and the thickness is thinner, as will be better observed in the macrography.
39
VIEW
ML00159 / Mar.2020
Collapse of a Drill Pipe
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Ductile Behavior
Cm - Aspect Before AnalysisDf - Fracture

More from these cases

ML00182 — Brittle Fracture of a LAS Fixing RodM - Low Alloy Medium Carbon QTP - StemAp - Mechanical IndustryCd - Brittle Fracture
Brittle Fracture of a LAS Fixing Rod
5
VIEW
ML00182 / Jul.2022
Brittle Fracture of a LAS Fixing Rod
M - Low Alloy Medium Carbon QTP - StemAp - Mechanical IndustryCd - Brittle Fracture
Cm - Aspect Before AnalysisDf - Fracture
Brittle Fracture of a LAS Fixing Rod
0
VIEW
ML00182 / Jul.2022
Brittle Fracture of a LAS Fixing Rod
M - Low Alloy Medium Carbon QTP - StemAp - Mechanical IndustryCd - Brittle Fracture
Cm - Aspect Before AnalysisDf - Fracture
ML00176 — Hydride Formation in a Titanium BladeM - Unalloyed TitaniumP - BladeAp - Oil and GasCd - Hydride Formation
Detail of the fracture surface, dark in the root of the blade, presenting a brittle aspect and indication that it started from this position.
39
VIEW
ML00176 / Nov.2021
Hydride Formation in a Titanium Blade
M - Unalloyed TitaniumP - BladeAp - Oil and GasCd - Hydride Formation
Cm - Aspect Before AnalysisDf - Fracture
View of the rotor body smashed in the internal shaft, the fracture and deposits of different colours. The fracture presented a dark aspect where the failure has started.
18
VIEW
ML00176 / Nov.2021
Hydride Formation in a Titanium Blade
M - Unalloyed TitaniumP - BladeAp - Oil and GasCd - Hydride Formation
Cm - Aspect Before AnalysisDf - Fracture
ML00171 — Corrosion Fatigue of U Bolt Pipe ClampM - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Same aspect of the previous image after cleaning, showing a subcritical propagation aspect (fatigue), starting at the groove (ID) and also at the clamp surface in the OD.
75
VIEW
ML00171 / Feb.2021
Corrosion Fatigue of U Bolt Pipe Clamp
M - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - Fracture
Aspect of the clamp fracture, before cleaning, looking from the outer diameter (OD). The fracture is in a position where there is no coating anymore.
48
VIEW
ML00171 / Feb.2021
Corrosion Fatigue of U Bolt Pipe Clamp
M - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - Fracture
ML00169 — Drill Pipe Fracture in the Pipe BodyM - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Corrosion Fatigue
Fracture appearance showing the two aspects of the fracture propagation, flat by fatigue and at 45 degrees by overloading.
35
VIEW
ML00169 / Nov.2020
Drill Pipe Fracture in the Pipe Body
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - Fracture
Region of the pipe fracture, where there is a transition from the flat fatigue to the rough overloading.
27
VIEW
ML00169 / Nov.2020
Drill Pipe Fracture in the Pipe Body
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - Fracture