Atlas

13 cases · 134 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Product: Rolled Plate Microstructure: Ferritic pearlitic clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Red painted device where the 50 mm x 50 mm carbon steel plate was positioned (in the circle). The image presents the target, positioned 100 meters far from the gun, after the shot and the projectile perforated the plate, as will be presented in the other figures.
602
VIEW
ML00143 / Aug.2018
Impact of a .308 Winchester on A36 Plate
M - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Cm - Aspect Before AnalysisDf - General View
Bimetallic engine bearing, removed from service at the end of its life.
356
VIEW
ML00083 / Oct.2017
Steel Back of a Bimetallic Engine Bearing
M - Low Carbon SteelP - Cold FormedAp - ShipCd - Removed From Service
Cm - Aspect Before AnalysisDf - General View
Macrography showing the different regions of a pipe-to-plate fillet weld. See the schematic drawing in the next image
954
VIEW
ML00052 / Apr.2017
Cold Cracks in API 5CT L80 Tube Welded to a Structural Part
M - Low Alloy SteelP - Seamless tubeAp - OffshoreCd - Welding Defect
Cm - NItal Etched MacroDf - Fracture
The macrography of a longitudinal section of the shell plate (sample removed from the boiler), at the position of the fillet weld (sealing weld) with a tube, where surface welding repairs created conditions for cracking the base material in a transgranular morphology. Several cracks were identify starting from the steam drum internal surface.
448
VIEW
ML00019 / Apr.2017
Transgranular SCC in Boiler Steam Drum
M - CMn SteelP - Rolled PlateAp - BoilerCd - Stress Corrosion
Cm - Transverse Section AspectDf - Cracks
Micrography of a longitudinal section of the 1" plate, in the center of the thickness, presenting a refined ferritic perlitic microstructure. Banded.
310
VIEW
ML00063 / Apr.2017
EH36 1" Plate for Structure
M - CMn SteelP - Rolled PlateAp - ShipCd - Typical manufacturing
Cm - Nital Etched Micrography by OMDf - Grain refined structure
Typical branched stress corrosion cracks in a low carbon steel, ferritic-pertlitic structure. The cracks are filled with corrosion products.
771
VIEW
ML00018 / Apr.2017
SCC in Boiler Steam Drum
M - Low Carbon SteelP - Rolled PlateAp - BoilerCd - Stress Corrosion
Cm - Nital Etched Micrography by OMDf - Branched Cracks
Micrography of a section transverse to the Oxygen Plasma Cut surface, showing the zone affected by the heat generated in the cutting. The extension of the HAZ is about 0.5 mm. The cut was conducted in the 1 1/4" thickness of the plate.
358
VIEW
ML00033 / Jan.2017
Plasma Cut of 1 1/4" Steel Plate
M - High Strength Low AlloyP - Rolled PlateAp - StructureCd - Cutting
Cm - Nital Etched Micrography by OMDf - Heat Affected Zone
Ferritic-perlitic microstructure of a longitudinal section of the plate that was qualified to be adopted in a tubesheet boiler. Hot formed plate presenting perlite banding.
659
VIEW
ML00031 / Jan.2017
Carbon Steel Tubesheet for Boiler
M - Low Carbon SteelP - Rolled PlateAp - ShipCd - Typical manufacturing
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite

More from these cases

ML00143 — Impact of a .308 Winchester on A36 PlateM - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Aspect of a typical .308 Winchester projectile, similar to the one adopted to shot the plate, cut in a longitudinal section. It is a Cu alloy case filled with Pb-Sb.
92
VIEW
ML00143 / Aug.2018
Impact of a .308 Winchester on A36 Plate
M - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Cm - Longitudinal Section AspectDf - Longitudinal Section
Aspect of the 3/8" thickness plate, 50 mm x 50 mm, of the low carbon steel steel, in the face of impact with the projectile. The plate was perforated by the bullet.
88
VIEW
ML00143 / Aug.2018
Impact of a .308 Winchester on A36 Plate
M - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Cm - Aspect Before AnalysisDf - General View
Micrography of the plate in a section, showing a ferritic-pearlitic microstructure in the middle of the thickness.
84
VIEW
ML00143 / Aug.2018
Impact of a .308 Winchester on A36 Plate
M - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Micrography of the plate in a section, showing a ferritic-pearlitic microstructure in the middle of the thickness, in a position where the plate was not affected by the shot.
65
VIEW
ML00143 / Aug.2018
Impact of a .308 Winchester on A36 Plate
M - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Micrographic detail of the plate in a section, showing a ferritic-pearlitic microstructure in the middle of the thickness.
66
VIEW
ML00143 / Aug.2018
Impact of a .308 Winchester on A36 Plate
M - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite

+51 more from this case →

ML00083 — Steel Back of a Bimetallic Engine BearingM - Low Carbon SteelP - Cold FormedAp - ShipCd - Removed From Service
Micrography of a transverse section of the engine bearing, close to the internal surface, showing two layers of bearing alloys that presents a total thickness of 600 microns.
29
VIEW
ML00083 / Oct.2017
Steel Back of a Bimetallic Engine Bearing
M - Low Carbon SteelP - Cold FormedAp - ShipCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Surface Layer
Micrographic detail of a transverse section of the back steel of an engine bearing, presenting a predominantly ferritic structure, strain hardened.
26
VIEW
ML00083 / Oct.2017
Steel Back of a Bimetallic Engine Bearing
M - Low Carbon SteelP - Cold FormedAp - ShipCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Predominantly Ferritic
Micrography of a transverse section of the back steel of an engine bearing, presenting a predominantly ferritic structure, strain hardened.
24
VIEW
ML00083 / Oct.2017
Steel Back of a Bimetallic Engine Bearing
M - Low Carbon SteelP - Cold FormedAp - ShipCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Strain Hardened
Micrography of a transverse section of the back steel of an engine bearing, presenting a predominantly ferritic structure, strain hardened.
24
VIEW
ML00083 / Oct.2017
Steel Back of a Bimetallic Engine Bearing
M - Low Carbon SteelP - Cold FormedAp - ShipCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Strain Hardened
ML00052 — Cold Cracks in API 5CT L80 Tube Welded to a Structural PartM - Low Alloy SteelP - Seamless tubeAp - OffshoreCd - Welding Defect
Schematic drawing presenting the different regions of a pipe-to-plate fillet weld.
71
VIEW
ML00052 / Apr.2017
Cold Cracks in API 5CT L80 Tube Welded to a Structural Part
M - Low Alloy SteelP - Seamless tubeAp - OffshoreCd - Welding Defect
Cm - Identification drawingDf - Fracture
Macrography of the fillet welded joint between the 3" ND tube and the 3/4" thick plate. See the schematic drawing in the next figure
56
VIEW
ML00052 / Apr.2017
Cold Cracks in API 5CT L80 Tube Welded to a Structural Part
M - Low Alloy SteelP - Seamless tubeAp - OffshoreCd - Welding Defect
Cm - NItal Etched MacroDf - Welded Joint
Schematic drawing presenting the position of the cracking, at the margin of the weld in the tube and underbead.
47
VIEW
ML00052 / Apr.2017
Cold Cracks in API 5CT L80 Tube Welded to a Structural Part
M - Low Alloy SteelP - Seamless tubeAp - OffshoreCd - Welding Defect
Cm - Identification drawingDf - Welded Joint
The micrography shows the region underbead, of the tube HAZ, responsible for the hydrogen cracking (fracture in the right side of the photo - black). The hardness of the HAZ is about 600 HV.
55
VIEW
ML00052 / Apr.2017
Cold Cracks in API 5CT L80 Tube Welded to a Structural Part
M - Low Alloy SteelP - Seamless tubeAp - OffshoreCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Cracking
Low carbon plate base metal presenting the ferritic perlitic structure.
55
VIEW
ML00052 / Apr.2017
Cold Cracks in API 5CT L80 Tube Welded to a Structural Part
M - Low Alloy SteelP - Seamless tubeAp - OffshoreCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Base Metal

+13 more from this case →

ML00019 — Transgranular SCC in Boiler Steam DrumM - CMn SteelP - Rolled PlateAp - BoilerCd - Stress Corrosion
Schematic drawing presenting the longitudinal section of the shell plate (sample removed from the boiler), at the position of the fillet weld (sealing weld) with a tube, where surface welding repairs created conditions for cracking the base material in a transgranular morphology. Several cracks were identify starting from the steam drum internal surface.
120
VIEW
ML00019 / Apr.2017
Transgranular SCC in Boiler Steam Drum
M - CMn SteelP - Rolled PlateAp - BoilerCd - Stress Corrosion
Cm - Identification drawingDf - Cracks
Micrography of a transverse section of the shell plate in a cracked position showing the transgranular morphology of the stress corrosion cracks.
167
VIEW
ML00019 / Apr.2017
Transgranular SCC in Boiler Steam Drum
M - CMn SteelP - Rolled PlateAp - BoilerCd - Stress Corrosion
Cm - Nital Etched Micrography by SEMDf - Transgranular Cracking
Micrography of the shell plate in the longitudinal section. Ferritic-perlitic microstructure.
96
VIEW
ML00019 / Apr.2017
Transgranular SCC in Boiler Steam Drum
M - CMn SteelP - Rolled PlateAp - BoilerCd - Stress Corrosion
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Micrographic detail of the shell plate in the longitudinal section. Ferritic-perlitic microstructure.
89
VIEW
ML00019 / Apr.2017
Transgranular SCC in Boiler Steam Drum
M - CMn SteelP - Rolled PlateAp - BoilerCd - Stress Corrosion
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Micrography of the cracking showing the branched nature, typical of a stress corrosion cracking. The cracks started from the internal surface of the steam drum.
94
VIEW
ML00019 / Apr.2017
Transgranular SCC in Boiler Steam Drum
M - CMn SteelP - Rolled PlateAp - BoilerCd - Stress Corrosion
Cm - Nital Etched Micrography by OMDf - Branched Cracks

+4 more from this case →

ML00063 — EH36 1" Plate for StructureM - CMn SteelP - Rolled PlateAp - ShipCd - Typical manufacturing
Micrography of a longitudinal section of the 1" plate, in the center of the thickness, presenting a refined ferritic perlitic microstructure. Banded.
12
VIEW
ML00063 / Apr.2017
EH36 1" Plate for Structure
M - CMn SteelP - Rolled PlateAp - ShipCd - Typical manufacturing
Cm - Nital Etched Micrography by OMDf - Banded Pearlite
Micrography of a longitudinal section of the 1" plate, in the center of the thickness, presenting a refined ferritic perlitic microstructure. Banded.
10
VIEW
ML00063 / Apr.2017
EH36 1" Plate for Structure
M - CMn SteelP - Rolled PlateAp - ShipCd - Typical manufacturing
Cm - Nital Etched Micrography by OMDf - Longitudinal Section
ML00018 — SCC in Boiler Steam DrumM - Low Carbon SteelP - Rolled PlateAp - BoilerCd - Stress Corrosion
Ferritic perlitic structure of the shell plate.
207
VIEW
ML00018 / Apr.2017
SCC in Boiler Steam Drum
M - Low Carbon SteelP - Rolled PlateAp - BoilerCd - Stress Corrosion
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Macrography of a transverse section of the steam drum sample that was removed after the inspection had detected multiple cracks propagating into the thickness, more than 50% deep in the thickness.
190
VIEW
ML00018 / Apr.2017
SCC in Boiler Steam Drum
M - Low Carbon SteelP - Rolled PlateAp - BoilerCd - Stress Corrosion
Cm - NItal Etched MacroDf - Transverse Section
Micrography of the crack at the internal surface of the steam drum. The shell plate presents a ferritic perlitic structure.
162
VIEW
ML00018 / Apr.2017
SCC in Boiler Steam Drum
M - Low Carbon SteelP - Rolled PlateAp - BoilerCd - Stress Corrosion
Cm - Nital Etched Micrography by OMDf - Branched Cracks
Micrography of a crack, in a sample as polished, presenting the opened crack.
144
VIEW
ML00018 / Apr.2017
SCC in Boiler Steam Drum
M - Low Carbon SteelP - Rolled PlateAp - BoilerCd - Stress Corrosion
Cm - Micrography by OMDf - Branched Cracks
Stress corrosion cracks propagating in the ferritic-perlitic structure.
120
VIEW
ML00018 / Apr.2017
SCC in Boiler Steam Drum
M - Low Carbon SteelP - Rolled PlateAp - BoilerCd - Stress Corrosion
Cm - Nital Etched Micrography by OMDf - Branched Cracks

+3 more from this case →

ML00033 — Plasma Cut of 1 1/4" Steel PlateM - High Strength Low AlloyP - Rolled PlateAp - StructureCd - Cutting
Macroscopic aspect of the cutting surface, slightly irregular. The structural plate is 1 1/4" thick.
48
VIEW
ML00033 / Jan.2017
Plasma Cut of 1 1/4" Steel Plate
M - High Strength Low AlloyP - Rolled PlateAp - StructureCd - Cutting
Cm - Aspect Before AnalysisDf - At the Surface
Aspect of the 1 1/4" thickness plate cutting surface.
30
VIEW
ML00033 / Jan.2017
Plasma Cut of 1 1/4" Steel Plate
M - High Strength Low AlloyP - Rolled PlateAp - StructureCd - Cutting
Cm - Aspect Before AnalysisDf - At the Surface
Macrography of a transverse section of the cut surface showing the heat affected zone region.
29
VIEW
ML00033 / Jan.2017
Plasma Cut of 1 1/4" Steel Plate
M - High Strength Low AlloyP - Rolled PlateAp - StructureCd - Cutting
Cm - NItal Etched MacroDf - Heat Affected Zone
Ferritic perlitic structure of the plate. Longitudinal section.
28
VIEW
ML00033 / Jan.2017
Plasma Cut of 1 1/4" Steel Plate
M - High Strength Low AlloyP - Rolled PlateAp - StructureCd - Cutting
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Ferritic perlitic structure of the plate. Longitudinal section.
29
VIEW
ML00033 / Jan.2017
Plasma Cut of 1 1/4" Steel Plate
M - High Strength Low AlloyP - Rolled PlateAp - StructureCd - Cutting
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite

+7 more from this case →

ML00031 — Carbon Steel Tubesheet for BoilerM - Low Carbon SteelP - Rolled PlateAp - ShipCd - Typical manufacturing
Ferritic-perlitic microstructure of a longitudinal section of the plate that was qualified to be adopted in a tubesheet boiler. Hot formed plate presenting perlite banding.
213
VIEW
ML00031 / Jan.2017
Carbon Steel Tubesheet for Boiler
M - Low Carbon SteelP - Rolled PlateAp - ShipCd - Typical manufacturing
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Ferritic-perlitic microstructure of a longitudinal section of the plate that was qualified to be adopted in a tubesheet boiler. Hot formed plate presenting perlite banding.
173
VIEW
ML00031 / Jan.2017
Carbon Steel Tubesheet for Boiler
M - Low Carbon SteelP - Rolled PlateAp - ShipCd - Typical manufacturing
Cm - Nital Etched Micrography by OMDf - Banded Pearlite