“fatigue”

6 cases · 9 images for “fatigue”

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Detail focus: Cracks clear all

Results

SortRelevanceNewestOldestTitle A-ZTitle Z-A
Close to the ID of the clamp, at the groove position, there are cracks in the coating (white brown) and also at the substrate.
63
VIEW
ML00171 / Feb.2021
Corrosion Fatigue of U Bolt Pipe Clamp
M - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - Cracks
Aspect by dye check of the upper side of the pipe, external, at the weld between the 8" main pipe and the 2" lateral branch, presenting a fatigue cracking initiated at the weld margin and propagating into the base metal in a longitudinal direction.
55
VIEW
ML00149 / Dec.2018
Vibration Induced Fatigue in a Gas Piping
M - Low Carbon SteelP - Piping spoolAp - FPSOCd - Vibration Induced Fatigue
Cm - Aspect by NDTDf - Cracks
Micrography of the section transverse to the weld, presenting one crack at the edge of the tube. This is not the best direction of analysis because the cracks are parallel to the analyzed section. It is possible to see the crack from the surface, large and filled with oxides.
78
VIEW
ML00119 / Feb.2018
Thermal Fatigue of a Marine Boiler
M - Low Carbon SteelP - Fabrication WeldAp - ShipCd - Thermal Fatigue
Cm - Nital Etched Micrography by OMDf - Cracks
The macrography of a longitudinal section of the tube in the damaged area shows the circunferential cracks, from the internal and external sides of the tube. The outer diameter of the tube is in the top of the figure and the inner diameter is in the bottom of the figure. From the outside there are several paralel cracks, as well as from the inner side.
126
VIEW
ML00104 / Dec.2017
Thermal Fatigue of a Boiler Tube
M - Low Carbon SteelP - Autogenously Welded TubeAp - BoilerCd - Thermal Fatigue
Cm - NItal Etched MacroDf - Cracks
Pipe body surface, adjacent to the fracture, showing regions of corrosion and visual cracks transverse to the pipe axis.
29
VIEW
ML00169 / Nov.2020
Drill Pipe Fracture in the Pipe Body
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Surface AspectDf - Cracks
Micrography of a typical corrosion-fatigue mechanism, in a longitudinal section. The loss of material is accelerated a lot by the cracks through the thickness.
42
VIEW
ML00155 / Jan.2020
Failure of a Prestressed Concrete Steel Strand
M - High Carbon SteelP - Wire RopeAp - StructureCd - Corrosion Fatigue
Cm - Nital Etched Micrography by OMDf - Cracks

More from these cases

ML00171 — Corrosion Fatigue of U Bolt Pipe ClampM - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Detailed aspect of the cracks at the clamp substrate and at the coating.
59
VIEW
ML00171 / Feb.2021
Corrosion Fatigue of U Bolt Pipe Clamp
M - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - Cracks
Dye check at the groove in the clamp ID, showing several parallel cracks, transverse to the clamp axis.
51
VIEW
ML00171 / Feb.2021
Corrosion Fatigue of U Bolt Pipe Clamp
M - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Cm - Aspect by NDTDf - Cracks
ML00155 — Failure of a Prestressed Concrete Steel StrandM - High Carbon SteelP - Wire RopeAp - StructureCd - Corrosion Fatigue
Micrography of a typical as polished corrosion-fatigue mechanism, in a longitudinal section. The loss of material is accelerated a lot by the cracks through the thickness.
43
VIEW
ML00155 / Jan.2020
Failure of a Prestressed Concrete Steel Strand
M - High Carbon SteelP - Wire RopeAp - StructureCd - Corrosion Fatigue
Cm - As polishedDf - Cracks