Crevice Corrosion in a Subsea System — Aspect Before Analysis

Capture method: Aspect by NDT clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Hydrides in Titanium Weld
2
VIEW
ML00179 / Feb.2022
Hydrides in Titanium Weld
M - Unalloyed TitaniumP - In Field WeldAp - Chemical IndustryCd - Hydride Formation
Cm - Aspect by NDTDf - Crack
The dye check image shows the detected crack, 50 mm long, at the margin of the weld in the forging side.
137
VIEW
ML00178 / Jan.2022
Cold cracks in Cr-Mo Welded Forging
M - CrMo SteelP - ForgingAp - O&G Well DrillingCd - Welding Defect
Cm - Aspect by NDTDf - Cracking
The circumferential welds presented several regions where the multiple cracks appeared, mainly revealed by dye check test.
49
VIEW
ML00174 / Jul.2021
Carburization of a 347 SS Welded Joint
M - Austenitic Stainless SteelP - Fabrication WeldAp - EnergyCd - Carburization
Cm - Aspect by NDTDf - Multiple cracks
After removal of the cracked part of the fitting, the dye check test indicated the presence of several cracks in the internal diameter (ID), out of the buttered layer, that means, in the fitting base metal.
42
VIEW
ML00173 / May.2021
Welding Cracks in an Aged HP Cast Fitting
M - Heat Resistant SteelP - Cast FtittingAp - PetrochemicalCd - Welding
Cm - Aspect by NDTDf - Cracks
Dye check at the groove in the clamp ID, showing several parallel cracks, transverse to the clamp axis.
51
VIEW
ML00171 / Feb.2021
Corrosion Fatigue of U Bolt Pipe Clamp
M - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Cm - Aspect by NDTDf - Cracks
Penetrant test (dye check) image of the cracks at the surface of the actuator hole, viewed from inside of the body after the longitudinal cut. The aspect of the cracks at the hole, close to the internal side of the valve, is not the same as the aspect of the cracks at the external side (a straigth line), suggesting that the original cracks had propagated by fatigue through wall. The penetrant did not stained too much at the cracked area, indicating that the cracks are not too deep in this position, or are not fully opened to the surface.
62
VIEW
ML00162 / Apr.2020
Valve Body Crack Growth from Weld Defects
M - Low Alloy Medium Carbon QTP - Valve BodyAp - O&G Well DrillingCd - Fatigue Induced by a Defect
Cm - Aspect by NDTDf - Crack
Aspect by dye check of the upper side of the pipe, at the margin of the weld between the main pipe and the lateral branch, presenting a fatigue cracking initiated at the external side, probably induced by vibration.
68
VIEW
ML00149 / Dec.2018
Vibration Induced Fatigue in a Gas Piping
M - Low Carbon SteelP - Piping spoolAp - FPSOCd - Vibration Induced Fatigue
Cm - Aspect by NDTDf - Cracking
Multiple thermal fatigue cracks at the welded joint between the smoke tube (vertical, internal diameter 248mm) and the tubesheet (horizontal, plate of 22 mm thickness). This is a view from the combustion chamber. The dye check tests revealed several parallel cracks.
1249
VIEW
ML00119 / Feb.2018
Thermal Fatigue of a Marine Boiler
M - Low Carbon SteelP - Fabrication WeldAp - ShipCd - Thermal Fatigue
Cm - Aspect by NDTDf - Thermal Fatigue Cracks

More from these cases

ML00162 — Valve Body Crack Growth from Weld DefectsM - Low Alloy Medium Carbon QTP - Valve BodyAp - O&G Well DrillingCd - Fatigue Induced by a Defect
Magnetic particle test of the same cracks at the edge of the actuator hole, viewed from inside of the body. The cracks appeared more clearly with this test than with the penetrant test, suggesting that the cracks are not fully opened to the surface.
60
VIEW
ML00162 / Apr.2020
Valve Body Crack Growth from Weld Defects
M - Low Alloy Medium Carbon QTP - Valve BodyAp - O&G Well DrillingCd - Fatigue Induced by a Defect
Cm - Aspect by NDTDf - Crack
ML00149 — Vibration Induced Fatigue in a Gas PipingM - Low Carbon SteelP - Piping spoolAp - FPSOCd - Vibration Induced Fatigue
Aspect by dye check of the internal side of the 8" pipe, at the hole of the 2" lateral branch line, presenting the through thickness cracking initiated by fatigue at the external side, probably induced by vibration.
57
VIEW
ML00149 / Dec.2018
Vibration Induced Fatigue in a Gas Piping
M - Low Carbon SteelP - Piping spoolAp - FPSOCd - Vibration Induced Fatigue
Cm - Aspect by NDTDf - Through Wall Cracking
Aspect by dye check of the upper side of the pipe, external, at the weld between the 8" main pipe and the 2" lateral branch, presenting a fatigue cracking initiated at the weld margin and propagating into the base metal in a longitudinal direction.
55
VIEW
ML00149 / Dec.2018
Vibration Induced Fatigue in a Gas Piping
M - Low Carbon SteelP - Piping spoolAp - FPSOCd - Vibration Induced Fatigue
Cm - Aspect by NDTDf - Cracks