Atlas

7 cases · 15 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Capture method: As polished clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Etched micrograph showing a transgranular crack running across equiaxed ferrite grains with dark grain-boundary carbides.
24
VIEW
ML00171 / Feb.2021
Corrosion Fatigue of U Bolt Pipe Clamp
M - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Cm - As polishedDf - Acicular Alpha
Teste João
2
VIEW
ML00169 / Nov.2020
Drill Pipe Fracture in the Pipe Body
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - As polishedDf - Acicular Alpha
Micrographic aspect, as polished, of the secondary cracks with brittle aspect (straight cracks).
43
VIEW
ML00161 / Mar.2020
Brittle Fracture of a High Strength Socket
M - Medium Carbon Tool SteelP - ToolAp - Oil and GasCd - Brittle Fracture
Cm - As polishedDf - Brittle Cracks
Back of the coaster showing the region that was prepared for the non destructive analysis. It was ground and polished (the coating was removed), showing the yellow aspect of the substrate, in the left bottom part of the image.
64
VIEW
ML00156 / Jan.2020
Antique Silver Plated Decorative Piece
M - BrassP - Decorative PieceAp - OrnamentalCd - Non Destructive Examination
Cm - As polishedDf - General View
Micrography of a typical corroded wire, in a longitudinal section as polished, showing loss of thickness by corrosion. The loss of material is accelerated by the corrosion in "layers" associated to the strained microstructure.
43
VIEW
ML00155 / Jan.2020
Failure of a Prestressed Concrete Steel Strand
M - High Carbon SteelP - Wire RopeAp - StructureCd - Corrosion Fatigue
Cm - As polishedDf - Corrosion
Micrography of the painted external surface of the cast cylinder.
25
VIEW
ML00141 / Jul.2018
Brittle Fracture of a Corroded Gray Cast Iron
M - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Cm - As polishedDf - Close to the External Surface
The as polished micrographic aspect of the corroded surface shows pitting and several microcracks, probably associated to the biological attack and material embrittlement. Replication technique.
924
VIEW
ML00092 / Sep.2017
MIC of a Valve Body
M - Martensitic Stainless SteelP - Valve BodyAp - Oil and GasCd - Brittle Behavior
Cm - As polishedDf - Microcracks

More from these cases

ML00169 — Drill Pipe Fracture in the Pipe BodyM - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Corrosion Fatigue
Teste Joao
3
VIEW
ML00169 / Nov.2020
Drill Pipe Fracture in the Pipe Body
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - As polishedDf - Acicular Alpha
ML00155 — Failure of a Prestressed Concrete Steel StrandM - High Carbon SteelP - Wire RopeAp - StructureCd - Corrosion Fatigue
Micrography of a typical as polished corrosion-fatigue mechanism, in a longitudinal section. The loss of material is accelerated a lot by the cracks through the thickness.
43
VIEW
ML00155 / Jan.2020
Failure of a Prestressed Concrete Steel Strand
M - High Carbon SteelP - Wire RopeAp - StructureCd - Corrosion Fatigue
Cm - As polishedDf - Cracks
Test
3
VIEW
ML00155 / Jan.2020
Failure of a Prestressed Concrete Steel Strand
M - High Carbon SteelP - Wire RopeAp - StructureCd - Corrosion Fatigue
Cm - As polishedDf - Acicular Alpha
fadf asdf asdf
4
VIEW
ML00155 / Jan.2020
Failure of a Prestressed Concrete Steel Strand
M - High Carbon SteelP - Wire RopeAp - StructureCd - Corrosion Fatigue
Cm - As polishedDf - Aligned particles
fasdfa fasdfasdf
3
VIEW
ML00155 / Jan.2020
Failure of a Prestressed Concrete Steel Strand
M - High Carbon SteelP - Wire RopeAp - StructureCd - Corrosion Fatigue
Cm - As polishedDf - Acicular Ferrite
Test...
4
VIEW
ML00155 / Jan.2020
Failure of a Prestressed Concrete Steel Strand
M - High Carbon SteelP - Wire RopeAp - StructureCd - Corrosion Fatigue
Cm - As polishedDf - Acicular Alpha

+2 more from this case →