Welded Joint

6 cases · 25 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Standard: A Capture method: Optical Microscope Detail focus: Microstructure clear all

Welded Joint — sub-branches

Cladding 1Fabrication Weld 6In Field Weld 2Remanufacture by Welding 1Repair Weld 2Welded Testpiece for Qualification 1

Results

SortNewestOldestTitle A-ZTitle Z-A
Microstructural analysis of the valve body structure, close to the position where the cracking has occurred. The structure is ferritic austenitic, with a large amount of detrimental phases associated to the ferritic structure, probably sigma phase.
106
VIEW
ML00134 / Aug.2020
Brittle Fracture of a Superduplex Valve Body
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Cm - NaOH Electrolytic Etched MicroDf - Sigma
Micrography of a longitudinal section of the pipe showing the carbon steel pipe , internal.
123
VIEW
ML00056 / May.2018
Seamless Tube Externally Cladded with SS
M - Carbon Steel / Stainless SteelP - CladdingAp - Pulp and PaperCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
The shell plate micrography showed an austenitic structure.
101
VIEW
ML00050 / Nov.2017
Fatigue Failure of a 316SS Pressure Stabilizer
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Mechanical Fatigue
Cm - Micrography by OM using A262 Method ADf - Austenite
Micrography of a longitudinal section of the shell plate base metal, presenting a typical ferritic-perlitic microstructure.
149
VIEW
ML00008 / Nov.2017
Cold Cracks in CMn Steel Pressure Vessel
M - CMn SteelP - In Field WeldAp - BoilerCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Equiaxial grains of a ferritic structure, in a longitudinal section of the tube.
68
VIEW
ML00026 / Feb.2017
Autogenous Seam Welded Tube in Ferritic SS
M - Ferritic Stainless SteelP - Fabrication WeldAp - AutomotiveCd - Typical manufacturing
Cm - Kalling Etched Micrography by OMDf - Equiaxial Grains
Micrography of the flange in the longitudinal section. The flange microstructure is ferritic austenitic, presenting a coarse structure.
102
VIEW
ML00002 / Jan.2018
Preferential Dissolution and Cracks in SDSS
M - Super Duplex Stainless SteelP - Fabrication WeldAp - PipingCd - Preferential Dissolution
Cm - NaOH Electrolytic Etched MicroDf - Coarse Structure

More from these cases

ML00134 — Brittle Fracture of a Superduplex Valve BodyM - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Micrographic detail of the valve body structure, close to the position where the cracking has occurred. The structure is ferritic austenitic, with a large amount of detrimental phases associated to the ferritic structure, probably sigma phase.
102
VIEW
ML00134 / Aug.2020
Brittle Fracture of a Superduplex Valve Body
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Cm - NaOH Electrolytic Etched MicroDf - Sigma
Metallographic detail of the large amount of sigma phase, associated to the ferritic structure.
105
VIEW
ML00134 / Aug.2020
Brittle Fracture of a Superduplex Valve Body
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Cm - NaOH Electrolytic Etched MicroDf - Sigma
Microstructural analysis of the valve body structure, far from the position where the cracking has occurred, in the bottom of the body. The structure is ferritic austenitic, with some sigma phase, not in a large amount, indicating the valve structure was not uniform.
67
VIEW
ML00134 / Aug.2020
Brittle Fracture of a Superduplex Valve Body
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Cm - NaOH Electrolytic Etched MicroDf - Ferrite and Austenite
Micrographic detail of the valve body structure, far from the position where the cracking has occurred, in the bottom of the body. The structure is ferritic austenitic, with some sigma phase, not in a large amount, indicating the valve structure was not uniform.
63
VIEW
ML00134 / Aug.2020
Brittle Fracture of a Superduplex Valve Body
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Cm - NaOH Electrolytic Etched MicroDf - Ferrite and Austenite
Micrographic detail of the valve body structure, far from the position where the cracking has occurred, in the bottom of the body. The structure is ferritic austenitic, with some sigma phase, not in a large amount, indicating the valve structure was not uniform.
61
VIEW
ML00134 / Aug.2020
Brittle Fracture of a Superduplex Valve Body
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Cm - NaOH Electrolytic Etched MicroDf - Ferrite and Austenite
ML00056 — Seamless Tube Externally Cladded with SSM - Carbon Steel / Stainless SteelP - CladdingAp - Pulp and PaperCd - Removed From Service
Micrography of a longitudinal section of the pipe showing the stainless steel pipe , external.
100
VIEW
ML00056 / May.2018
Seamless Tube Externally Cladded with SS
M - Carbon Steel / Stainless SteelP - CladdingAp - Pulp and PaperCd - Removed From Service
Cm - Micrography by OM using A262 Method ADf - Austenite
Micrographic detail of the interface in the longitudinal section of the pipe showing the decarburized layer at the solid solution welded interface. The stainless steel structure (in the right side of the figure) is not revealed using the Nital etch.
80
VIEW
ML00056 / May.2018
Seamless Tube Externally Cladded with SS
M - Carbon Steel / Stainless SteelP - CladdingAp - Pulp and PaperCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Clad Interface
Micrographic detail of the interface in the longitudinal section of the pipe showing the decarburized layer at the solid solution welded interface. The stainless steel structure (in the right side of the figure) is not revealed using the Nital etch.
70
VIEW
ML00056 / May.2018
Seamless Tube Externally Cladded with SS
M - Carbon Steel / Stainless SteelP - CladdingAp - Pulp and PaperCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Clad Interface
Micrographic detail of the interface showing the strain hardened layer at the stainless steel side (in the right of the figure), revealed using the Electrolytic etch.
76
VIEW
ML00056 / May.2018
Seamless Tube Externally Cladded with SS
M - Carbon Steel / Stainless SteelP - CladdingAp - Pulp and PaperCd - Removed From Service
Cm - Micrography by OM using A262 Method ADf - Clad Interface
ML00008 — Cold Cracks in CMn Steel Pressure VesselM - CMn SteelP - In Field WeldAp - BoilerCd - Welding Defect
Higher magnification of the ferritic-perlitic microstructure of the shell plate in the longitudinal section.
129
VIEW
ML00008 / Nov.2017
Cold Cracks in CMn Steel Pressure Vessel
M - CMn SteelP - In Field WeldAp - BoilerCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
ML00026 — Autogenous Seam Welded Tube in Ferritic SSM - Ferritic Stainless SteelP - Fabrication WeldAp - AutomotiveCd - Typical manufacturing
Equiaxial grains of a ferritic structure, in a longitudinal section of the tube.
49
VIEW
ML00026 / Feb.2017
Autogenous Seam Welded Tube in Ferritic SS
M - Ferritic Stainless SteelP - Fabrication WeldAp - AutomotiveCd - Typical manufacturing
Cm - Kalling Etched Micrography by OMDf - Ferrite
Equiaxial grains of a ferritic structure, in a transverse section of the tube.
36
VIEW
ML00026 / Feb.2017
Autogenous Seam Welded Tube in Ferritic SS
M - Ferritic Stainless SteelP - Fabrication WeldAp - AutomotiveCd - Typical manufacturing
Cm - Kalling Etched Micrography by OMDf - Equiaxial Grains
Equiaxial grains of a ferritic structure, in a transverse section of the tube.
37
VIEW
ML00026 / Feb.2017
Autogenous Seam Welded Tube in Ferritic SS
M - Ferritic Stainless SteelP - Fabrication WeldAp - AutomotiveCd - Typical manufacturing
Cm - Kalling Etched Micrography by OMDf - Ferrite
Micrography of the transverse section of the tube presenting the autogenous weld at the fusion line.
40
VIEW
ML00026 / Feb.2017
Autogenous Seam Welded Tube in Ferritic SS
M - Ferritic Stainless SteelP - Fabrication WeldAp - AutomotiveCd - Typical manufacturing
Cm - Kalling Etched Micrography by OMDf - Fusion Line
Micrography of the transverse section of the tube presenting the autogenous weld at the fusion line.
27
VIEW
ML00026 / Feb.2017
Autogenous Seam Welded Tube in Ferritic SS
M - Ferritic Stainless SteelP - Fabrication WeldAp - AutomotiveCd - Typical manufacturing
Cm - Kalling Etched Micrography by OMDf - Fusion Line

+2 more from this case →

ML00002 — Preferential Dissolution and Cracks in SDSSM - Super Duplex Stainless SteelP - Fabrication WeldAp - PipingCd - Preferential Dissolution
Micrographic detail of the flange microstructure in the longitudinal section. The flange is ferritic austenitic, presenting 70% of austenite. In the ferrite network there are evidences of precipitation/formation of detrimental phases.
113
VIEW
ML00002 / Jan.2018
Preferential Dissolution and Cracks in SDSS
M - Super Duplex Stainless SteelP - Fabrication WeldAp - PipingCd - Preferential Dissolution
Cm - NaOH Electrolytic Etched MicroDf - Duplex structure
Micrographic detail of the flange microstructure in the longitudinal section. The flange is ferritic austenitic, presenting 70% of austenite. In the ferrite network there are evidences of precipitation/formation of detrimental phases.
100
VIEW
ML00002 / Jan.2018
Preferential Dissolution and Cracks in SDSS
M - Super Duplex Stainless SteelP - Fabrication WeldAp - PipingCd - Preferential Dissolution
Cm - NaOH Electrolytic Etched MicroDf - Duplex structure