Raw Material

9 cases · 44 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Capture method: Micrography by OM using A262 Method A clear all

Raw Material — sub-branches

Bar 5Carburized 1Casting 16Chromium Plated 2Cold Formed 2Forged T 1Forging 12Heat Treated Part 4Machined Part 10Pipe 20Plate 1Rod 1Rolled Bar 2Rolled Plate 19Rolled Shape 1Sheet 1Tube 17Tubular Forging 6Welded Part 1Wire 3Wrought Fitting 3

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrography of the 1.65 mm thickness tube, in the middle of the thickness of the longitudinal section. This part of the tube is located in the colder part of the equipment, position 1. The material presented carbide precipitation at grain boundaries (not yet fully surrounding the grains) and at this point the tube presented no internal corrosion.
338
VIEW
ML00086 / Nov.2017
Intergranular Corrosion of Sensitized 304SS
M - Austenitic Stainless SteelP - Seamless tubeAp - Heat ExchangerCd - Intergranular Corrosion
Cm - Micrography by OM using A262 Method ADf - Austenite
Micrography of a longitudinal section of the wire, at the fracture surface (top of the figure) evidencing the intergranular and transgranular aspects of the hydrogen assisted cracking mechanism.
37
VIEW
ML00076 / Jun.2017
Hydrogen Cracking of a 17-7 PH Subsea Spring
M - Precipitation Hardened Stainless SteelP - WireAp - SubseaCd - Hydrogen Embrittlement
Cm - Micrography by OM using A262 Method ADf - Secondary Cracks
Micrography of a longitudinal section of the pipe (seamless), that shows the through wall cracking, straigth and not associated to any welded region or microstructural problem.
64
VIEW
ML00012 / Aug.2017
Vibration Induced Fatigue in a 316/316L SS
M - Austenitic Stainless SteelP - Seamless PipeAp - OffshoreCd - Vibration Induced Fatigue
Cm - Micrography by OM using A262 Method ADf - Through Wall Cracking
Through wall cracking in the longitudinal seam weld of the fitting. Several cracks, longitudinal to the weld, were created by the connection of voids in the weld metal, associated to a strong microstructural evolution.
191
VIEW
ML00061 / Apr.2017
Creep in a Seam Weld of a 304H SS Fitting
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Creep
Cm - Micrography by OM using A262 Method ADf - Cracks
Micrography of a longitudinal section of the pipe showing the stainless steel pipe , external.
99
VIEW
ML00056 / May.2018
Seamless Tube Externally Cladded with SS
M - Carbon Steel / Stainless SteelP - CladdingAp - Pulp and PaperCd - Removed From Service
Cm - Micrography by OM using A262 Method ADf - Austenite
Microstructure of the plate in the center of the ¼” thickness. Equiaxed austenitic grains with delta ferrite stringers and grain boundary carbide precipitation (sensitization).
303
VIEW
ML00015 / Oct.2017
Intergranular Corrosion of 304SS Plate
M - Austenitic Stainless SteelP - Rolled PlateAp - RefineryCd - Intergranular Corrosion
Cm - Micrography by OM using A262 Method ADf - Intergranular Precipitation
The low magnification micrography of the longitudinal section of the pin shows the localized corrosion associated to the non metallic inclusions.
89
VIEW
ML00016 / Apr.2017
SCC in Free Cutting 303SS
M - Austenitic Stainless SteelP - Machined PartAp - OffshoreCd - Stress Corrosion
Cm - Micrography by OM using A262 Method ADf - Localized Corrosion
Longitudinal section of the main pipe showing as austenitic structure with small amount of delta ferrite, aligned. The white band in the center of the figure is a segregation band that was not fully etched.
133
VIEW
ML00006 / Apr.2017
Vibration Induced Fatigue in 304SS
M - Austenitic Stainless SteelP - Longitudinal Seam Welded PipeAp - PipingCd - Vibration Induced Fatigue
Cm - Micrography by OM using A262 Method ADf - Austenite

More from these cases

ML00086 — Intergranular Corrosion of Sensitized 304SSM - Austenitic Stainless SteelP - Seamless tubeAp - Heat ExchangerCd - Intergranular Corrosion
Micrography of the 1.65 mm thickness tube, in the middle of the thickness of the longitudinal section. This part of the tube is located in position 2, where the temperature was higher and the carbide precipitation increased during service.
272
VIEW
ML00086 / Nov.2017
Intergranular Corrosion of Sensitized 304SS
M - Austenitic Stainless SteelP - Seamless tubeAp - Heat ExchangerCd - Intergranular Corrosion
Cm - Micrography by OM using A262 Method ADf - Intergranular Precipitation
Micrography of the 1.65 mm thickness tube, in the middle of the thickness of the longitudinal section. This part of the tube is located in position 3, where intergranular and transgranular carbide precipitation occurred during service.
234
VIEW
ML00086 / Nov.2017
Intergranular Corrosion of Sensitized 304SS
M - Austenitic Stainless SteelP - Seamless tubeAp - Heat ExchangerCd - Intergranular Corrosion
Cm - Micrography by OM using A262 Method ADf - Intragranular Secondary Precipitation
Micrography of a longitudinal section of the tube in position 2, presenting thinning by intergranular corrosion at the internal surface.
193
VIEW
ML00086 / Nov.2017
Intergranular Corrosion of Sensitized 304SS
M - Austenitic Stainless SteelP - Seamless tubeAp - Heat ExchangerCd - Intergranular Corrosion
Cm - Micrography by OM using A262 Method ADf - Intergranular Corrosion
Micrographic detail of the intergranular corrosion at the internal surface of the tube in position 2. Several grains were already removed by the corrosion.
171
VIEW
ML00086 / Nov.2017
Intergranular Corrosion of Sensitized 304SS
M - Austenitic Stainless SteelP - Seamless tubeAp - Heat ExchangerCd - Intergranular Corrosion
Cm - Micrography by OM using A262 Method ADf - Intergranular Corrosion
Micrography of a longitudinal section of the tube in position 3, at the internal surface. Although there is a strong precipitation, both intergranular and transgranular, the tube did not corrode at this point.
144
VIEW
ML00086 / Nov.2017
Intergranular Corrosion of Sensitized 304SS
M - Austenitic Stainless SteelP - Seamless tubeAp - Heat ExchangerCd - Intergranular Corrosion
Cm - Micrography by OM using A262 Method ADf - Intragranular Secondary Precipitation

+1 more from this case →

ML00076 — Hydrogen Cracking of a 17-7 PH Subsea SpringM - Precipitation Hardened Stainless SteelP - WireAp - SubseaCd - Hydrogen Embrittlement
Micrographic detail of a longitudinal section of the wire, at the fracture surface (top of the figure) evidencing the intergranular and transgranular aspects of the hydrogen assisted cracking mechanism. The electrolytic oxalic acid etch reveals the delta ferrite phase. Compare with the Kalling etch in the other figure.
31
VIEW
ML00076 / Jun.2017
Hydrogen Cracking of a 17-7 PH Subsea Spring
M - Precipitation Hardened Stainless SteelP - WireAp - SubseaCd - Hydrogen Embrittlement
Cm - Micrography by OM using A262 Method ADf - Fracture
ML00012 — Vibration Induced Fatigue in a 316/316L SSM - Austenitic Stainless SteelP - Seamless PipeAp - OffshoreCd - Vibration Induced Fatigue
Micrography of a longitudinal section of the pipe presenting a granular austenitic structure, typical of a solid solution annealing condition. No carbide precipitation.
62
VIEW
ML00012 / Aug.2017
Vibration Induced Fatigue in a 316/316L SS
M - Austenitic Stainless SteelP - Seamless PipeAp - OffshoreCd - Vibration Induced Fatigue
Cm - Micrography by OM using A262 Method ADf - Austenite
ML00061 — Creep in a Seam Weld of a 304H SS FittingM - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Creep
Micrography of a longitudinal section of the fitting, at the base metal, presenting an austenitic structure with intergranular and transgranular precipitation as a result of microstructural evolution.
44
VIEW
ML00061 / Apr.2017
Creep in a Seam Weld of a 304H SS Fitting
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Creep
Cm - Micrography by OM using A262 Method ADf - Base Metal
Micrographic detail of the fitting base metal, presenting an austenitic structure with intergranular and transgranular precipitation as a result of microstructural evolution.
40
VIEW
ML00061 / Apr.2017
Creep in a Seam Weld of a 304H SS Fitting
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Creep
Cm - Micrography by OM using A262 Method ADf - Base Metal
Micrography of a transverse section of the seam weld, close to the internal surface, presenting several cracks perpendicular to the thickness.
37
VIEW
ML00061 / Apr.2017
Creep in a Seam Weld of a 304H SS Fitting
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Creep
Cm - Micrography by OM using A262 Method ADf - Close to the Internal Surface
Micrographic detail of the seam weld close to the internal surface, presenting the needles that are the result of microsctructural evolution and cracks filled with oxides.
36
VIEW
ML00061 / Apr.2017
Creep in a Seam Weld of a 304H SS Fitting
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Creep
Cm - Micrography by OM using A262 Method ADf - Close to the Internal Surface
Micrography of a transverse section of the seam weld, in the middle of the thickness, presenting several parallel cracks.
27
VIEW
ML00061 / Apr.2017
Creep in a Seam Weld of a 304H SS Fitting
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Creep
Cm - Micrography by OM using A262 Method ADf - In the Center of the Thickness

+7 more from this case →

ML00056 — Seamless Tube Externally Cladded with SSM - Carbon Steel / Stainless SteelP - CladdingAp - Pulp and PaperCd - Removed From Service
Micrography of the interface between the carbon steel that is strongly etched by the electrolytic oxalic acid (in the left side of the figure) and the stainless steel, in the longitudinal section of the pipe. There is a strain hardened layer very close to the interface, at the stainless steel side.
79
VIEW
ML00056 / May.2018
Seamless Tube Externally Cladded with SS
M - Carbon Steel / Stainless SteelP - CladdingAp - Pulp and PaperCd - Removed From Service
Cm - Micrography by OM using A262 Method ADf - Longitudinal Section
Micrographic detail of the interface showing the strain hardened layer at the stainless steel side (in the right of the figure), revealed using the Electrolytic etch.
76
VIEW
ML00056 / May.2018
Seamless Tube Externally Cladded with SS
M - Carbon Steel / Stainless SteelP - CladdingAp - Pulp and PaperCd - Removed From Service
Cm - Micrography by OM using A262 Method ADf - Clad Interface
ML00015 — Intergranular Corrosion of 304SS PlateM - Austenitic Stainless SteelP - Rolled PlateAp - RefineryCd - Intergranular Corrosion
Microstructure of the plate in the center of the ¼” thickness. Equiaxed austenitic grains with delta ferrite stringers and grain boundary carbide precipitation (sensitization).
201
VIEW
ML00015 / Oct.2017
Intergranular Corrosion of 304SS Plate
M - Austenitic Stainless SteelP - Rolled PlateAp - RefineryCd - Intergranular Corrosion
Cm - Micrography by OM using A262 Method ADf - Intergranular Precipitation
Micrographic aspect of a longitudinal section of the plate, close to the surface, in a region with intergranular corrosion. Several loose grains were removed, indicating that the structure was embrittled by the intergranular corrosion.
171
VIEW
ML00015 / Oct.2017
Intergranular Corrosion of 304SS Plate
M - Austenitic Stainless SteelP - Rolled PlateAp - RefineryCd - Intergranular Corrosion
Cm - Micrography by OM using A262 Method ADf - Intergranular Corrosion
Micrography of a section transverse to the repair weld showing that the macroscopic crack, detected at the surface of the plate, occurred exactly at the margin of the weld bead. It is possible to see that the bead was deposited over a region that was already corroded (intergranular corrosion) and the macroscopic crack is the opening of several corroded grains.
158
VIEW
ML00015 / Oct.2017
Intergranular Corrosion of 304SS Plate
M - Austenitic Stainless SteelP - Rolled PlateAp - RefineryCd - Intergranular Corrosion
Cm - Micrography by OM using A262 Method ADf - Intergranular Cracking
Detail of the fusion line region of the repair weld. It is possible to see that the cracks are filled with oxides indicating that the material was already corroded when the bead was deposited.
128
VIEW
ML00015 / Oct.2017
Intergranular Corrosion of 304SS Plate
M - Austenitic Stainless SteelP - Rolled PlateAp - RefineryCd - Intergranular Corrosion
Cm - Micrography by OM using A262 Method ADf - Intergranular Cracking
Detail of the fusion line region of the repair weld. It is possible to see that the cracks are filled with oxides indicating that the material was already corroded when the bead was deposited.
108
VIEW
ML00015 / Oct.2017
Intergranular Corrosion of 304SS Plate
M - Austenitic Stainless SteelP - Rolled PlateAp - RefineryCd - Intergranular Corrosion
Cm - Micrography by OM using A262 Method ADf - Intergranular Cracking

+1 more from this case →

ML00016 — SCC in Free Cutting 303SSM - Austenitic Stainless SteelP - Machined PartAp - OffshoreCd - Stress Corrosion
The pin microstructure in the longitudinal section shows austenitic structure, free from carbides, and sulfide inclusions that characterize the free cutting condition of this stainless steel.
77
VIEW
ML00016 / Apr.2017
SCC in Free Cutting 303SS
M - Austenitic Stainless SteelP - Machined PartAp - OffshoreCd - Stress Corrosion
Cm - Micrography by OM using A262 Method ADf - Non Metallic Inclusions
The micrographic detail of the longitudinal section of the pin shows the localized corrosion associated to the non metallic inclusions.
67
VIEW
ML00016 / Apr.2017
SCC in Free Cutting 303SS
M - Austenitic Stainless SteelP - Machined PartAp - OffshoreCd - Stress Corrosion
Cm - Micrography by OM using A262 Method ADf - Localized Corrosion
The micrographic detail of the longitudinal section of the pin shows the stress corrosion cracks propagating from crevice corrosion regions.
52
VIEW
ML00016 / Apr.2017
SCC in Free Cutting 303SS
M - Austenitic Stainless SteelP - Machined PartAp - OffshoreCd - Stress Corrosion
Cm - Micrography by OM using A262 Method ADf - Branched Cracks
ML00006 — Vibration Induced Fatigue in 304SSM - Austenitic Stainless SteelP - Longitudinal Seam Welded PipeAp - PipingCd - Vibration Induced Fatigue
Longitudinal section of the main pipe showing as austenitic structure with small amount of delta ferrite, aligned (black dots).
117
VIEW
ML00006 / Apr.2017
Vibration Induced Fatigue in 304SS
M - Austenitic Stainless SteelP - Longitudinal Seam Welded PipeAp - PipingCd - Vibration Induced Fatigue
Cm - Micrography by OM using A262 Method ADf - Austenite
Micrography transverse to the weld and to the fracture surface (right side of the figure).
116
VIEW
ML00006 / Apr.2017
Vibration Induced Fatigue in 304SS
M - Austenitic Stainless SteelP - Longitudinal Seam Welded PipeAp - PipingCd - Vibration Induced Fatigue
Cm - Micrography by OM using A262 Method ADf - Fracture
Micrography of the section transverse to the weld and in a region close to the fracture surface (to the right side of the figure). The secondary fatigue microcracks are associated to the stress concentration raisers of the margin of the weld, irregular.
110
VIEW
ML00006 / Apr.2017
Vibration Induced Fatigue in 304SS
M - Austenitic Stainless SteelP - Longitudinal Seam Welded PipeAp - PipingCd - Vibration Induced Fatigue
Cm - Micrography by OM using A262 Method ADf - Fatigue Crack