Fractured position of the casting cylinder of 10.5 mm thickness (minimum measured thickness) showing a brittle behavior (lack of plastic deformation), typical of overloading a material with 1% ductility (measured in the tensile test). This is the view of the internal surface of the cylinder, presenting regions of localized thinning in this surface that was in contact with (treated) cooling water. The external side of the cylinder was painted.
918
VIEW
ML00141 / Jul.2018
Brittle Fracture of a Corroded Gray Cast Iron
M - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Cm - Fracture Surface AspectDf - General View
Aspect of the cracked valve body, after disassembling and removing the internal parts. The valve is part of a lot that was manufactured by forging a cubic 170mm from a forged bar in SDSS UNS S32760, and heat treated (solution annealed) by the forging company. The fabrication using these bodies included the machining, fillet weld two inserts in Alloy 625, machining again, assembling the internals, and pressure test at 15,000 psi. The cracking occurred during test, only for this valve body.
676
VIEW
ML00134 / Aug.2020
Brittle Fracture of a Superduplex Valve Body
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Cm - Aspect Before AnalysisDf - Cracking
The hose connector fracture surface presented different fracture micromechanisms associated to the microstructure: inclusion decohesion, small regions of intergranular fractures (probably due to cementite at grain boundaries), and cleavage of the ferritic structure. All these mechanisms are brittle.
560
VIEW
ML00103 / Nov.2017
Brittle Fracture of a Free-Cutting Connector
M - Low Carbon SteelP - Machined PartAp - ShipCd - Brittle Fracture
Cm - Fractography by SEMDf - Brittle Fracture
Micrography of a transverse section of the lifting part, showing interdendritic voids close to the surface at the inner diameter of the padeye. The microstructure is tempered martensite.
450
VIEW
ML00098 / Nov.2017
Brittle Fracture of a Casting Lifting Device
M - Low Alloy Medium Carbon QTP - CastingAp - LiftingCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Casting defects
Detail of the pin fracture surface, presenting both a flat aspect and a rough aspect in a shearing section of 2.5 mm width.
727
VIEW
ML00046 / Jan.2018
Brittle Fracture of SS Shear Pin
M - Martensitic Stainless SteelP - Machined PartAp - EnergyCd - Intergranular Cracking
Cm - Fractography by SEMDf - Fracture
The camshaft broke in a brittle way in a region where the shaft changed the geometry, close to a chilled lobe.
551
VIEW
ML00060 / Apr.2017
Brittle Fracture of a Chilled Cast Iron Camshaft
M - Chilled Cast IronP - ShaftAp - AutomotiveCd - Brittle Fracture
Cm - Aspect Before AnalysisDf - Fracture
The fracture surface is flat, shows the graphite nodules and cleavage of the ferritic microstructure, indicating that the material have exceeded the capacity to acomodate the stress.
945
VIEW
ML00040 / Apr.2017
Brittle Fracture of a Valve Stem
M - Nodular Cast IronP - Valve StemAp - ShipCd - Brittle Fracture
Cm - Fractography by SEMDf - Cleavage Facets
Margin of the perforated hole showing regions of fracture and a smooth appearance in the hole surface (right side of the figure). This smooth aspect was generated by the film of melted material from the bullet.
44
VIEW
ML00143 / Aug.2018
Impact of a .308 Winchester on A36 Plate
M - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Cm - Fractography by SEMDf - Ductile Fracture

More from these cases

ML00141 — Brittle Fracture of a Corroded Gray Cast IronM - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Fracture aspect of the casting cylinder at the 10.5 mm thickness, showing a brittle behavior (lack of plastic deformation). The internal side of the cylinder is to the top of the figure, and the painted surface is to the bottom of the figure.
129
VIEW
ML00141 / Jul.2018
Brittle Fracture of a Corroded Gray Cast Iron
M - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Cm - Fracture Surface AspectDf - Brittle Fracture
Detailed aspect of the cylinder fracture, the internal surface to the top of the figure and the painted external surface to the bottom of the figure.
103
VIEW
ML00141 / Jul.2018
Brittle Fracture of a Corroded Gray Cast Iron
M - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Cm - Fracture Surface AspectDf - Brittle Fracture
Macrographic aspect of a section of the cast cylinder, transverse to the fracture (top). The internal diameter of the cylinder (exposed to treated water) is to the left side and the external diameter of the cylinder (painted) is to the right side.
96
VIEW
ML00141 / Jul.2018
Brittle Fracture of a Corroded Gray Cast Iron
M - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Cm - NItal Etched MacroDf - Brittle Fracture
Micrographic aspect, as polished, of the cast cylinder section at the fracture position (top of the figure), close to the internal surface (left side). It is possible to see large graphite flakes.
98
VIEW
ML00141 / Jul.2018
Brittle Fracture of a Corroded Gray Cast Iron
M - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Cm - As polished micrographyDf - Close to the Internal Surface
Micrographic aspect, as polished, of the cast cylinder section at the fracture position (top of the figure), in the center of the thickness. It is possible to see a mixture of large graphite flakes and rosette grouping flakes.
80
VIEW
ML00141 / Jul.2018
Brittle Fracture of a Corroded Gray Cast Iron
M - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Cm - As polished micrographyDf - In the Center of the Thickness

+30 more from this case →

ML00134 — Brittle Fracture of a Superduplex Valve BodyM - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Detailed aspect of the cracking, straight and presenting a brittle aspect.
122
VIEW
ML00134 / Aug.2020
Brittle Fracture of a Superduplex Valve Body
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Cm - Aspect Before AnalysisDf - Cracking
Detail of the internal bore, showing a brittle crack through the wall.
106
VIEW
ML00134 / Aug.2020
Brittle Fracture of a Superduplex Valve Body
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Cm - Aspect Before AnalysisDf - Cracking
Aspect of a section cut transverse to the center of the body. The crack is brittle, trough wall, and was arrested in the region where the valve body was welded to the insert.
105
VIEW
ML00134 / Aug.2020
Brittle Fracture of a Superduplex Valve Body
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Cm - Transverse Section AspectDf - Cracking
Microstructural analysis of the valve body structure, close to the position where the cracking has occurred. The structure is ferritic austenitic, with a large amount of detrimental phases associated to the ferritic structure, probably sigma phase.
106
VIEW
ML00134 / Aug.2020
Brittle Fracture of a Superduplex Valve Body
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Cm - NaOH Electrolytic Etched MicroDf - Sigma
Micrographic detail of the valve body structure, close to the position where the cracking has occurred. The structure is ferritic austenitic, with a large amount of detrimental phases associated to the ferritic structure, probably sigma phase.
102
VIEW
ML00134 / Aug.2020
Brittle Fracture of a Superduplex Valve Body
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Cm - NaOH Electrolytic Etched MicroDf - Sigma

+25 more from this case →

ML00103 — Brittle Fracture of a Free-Cutting ConnectorM - Low Carbon SteelP - Machined PartAp - ShipCd - Brittle Fracture
Aspect of the external side of the connector, with a longitudinally crack of a brittle aspect. It is a 5/8" connector (15.8 mm).
134
VIEW
ML00103 / Nov.2017
Brittle Fracture of a Free-Cutting Connector
M - Low Carbon SteelP - Machined PartAp - ShipCd - Brittle Fracture
Cm - Aspect Before AnalysisDf - General View
Aspect of the internal side of the connector. The fracture, in the longitudinal direction, presents a brittle aspect. The thickness of the connector is about 2 mm.
126
VIEW
ML00103 / Nov.2017
Brittle Fracture of a Free-Cutting Connector
M - Low Carbon SteelP - Machined PartAp - ShipCd - Brittle Fracture
Cm - Aspect Before AnalysisDf - Brittle Fracture
Macroscopic detail of the brittle fracture, in the longitudinal direction.
105
VIEW
ML00103 / Nov.2017
Brittle Fracture of a Free-Cutting Connector
M - Low Carbon SteelP - Machined PartAp - ShipCd - Brittle Fracture
Cm - Aspect Before AnalysisDf - Brittle Fracture
Micrography of the longitudinal section of the fitiing, in a free-cutting steel. The microstructure is predominantly ferritic and there is a large amount of sulfide inclusions, aligned perpendicular to the forming direction.
98
VIEW
ML00103 / Nov.2017
Brittle Fracture of a Free-Cutting Connector
M - Low Carbon SteelP - Machined PartAp - ShipCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Longitudinal Section
Micrographic detail of the longitudinal section of the fitiing, in a free-cutting steel. The microstructure is predominantly ferritic, with small perlitic areas and some free cementite at ferritic grain boundaries. There is a large amount of sulfide inclusions, aligned perpendicular to the forming direction.
107
VIEW
ML00103 / Nov.2017
Brittle Fracture of a Free-Cutting Connector
M - Low Carbon SteelP - Machined PartAp - ShipCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Non Metallic Inclusions

+11 more from this case →

ML00098 — Brittle Fracture of a Casting Lifting DeviceM - Low Alloy Medium Carbon QTP - CastingAp - LiftingCd - Brittle Fracture
Aspect of the broken padeye. The outer diameter is about 10" and the thickness of the casting is about 2".
22
VIEW
ML00098 / Nov.2017
Brittle Fracture of a Casting Lifting Device
M - Low Alloy Medium Carbon QTP - CastingAp - LiftingCd - Brittle Fracture
Cm - Aspect Before AnalysisDf - General View
Aspect of the fracture surface, showing a brittle morphology. Flat fracture with chevron marks from regions close to the internal diameter of the padeye, where there are secondary cracks.
22
VIEW
ML00098 / Nov.2017
Brittle Fracture of a Casting Lifting Device
M - Low Alloy Medium Carbon QTP - CastingAp - LiftingCd - Brittle Fracture
Cm - Aspect Before AnalysisDf - Fracture
Micrography of the lifting padeye showing a dendritic path of a quenched and tempered martensitic microstructure. The segregated regions (white interdendritic regions) are more clearly identified in low magnification. Voids are located in these segregated regions.
21
VIEW
ML00098 / Nov.2017
Brittle Fracture of a Casting Lifting Device
M - Low Alloy Medium Carbon QTP - CastingAp - LiftingCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Martensite
Micrography of the lifting padeye showing a quenched and tempered martensitic microstructure. Voids are located in interdendritic segregated regions.
20
VIEW
ML00098 / Nov.2017
Brittle Fracture of a Casting Lifting Device
M - Low Alloy Medium Carbon QTP - CastingAp - LiftingCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Martensite
Micrography of the lifting padeye showing a quenched and tempered martensitic microstructure. Voids are located in interdendritic segregated regions. At this magnification the segregation is not clear.
16
VIEW
ML00098 / Nov.2017
Brittle Fracture of a Casting Lifting Device
M - Low Alloy Medium Carbon QTP - CastingAp - LiftingCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Martensite

+12 more from this case →

ML00046 — Brittle Fracture of SS Shear PinM - Martensitic Stainless SteelP - Machined PartAp - EnergyCd - Intergranular Cracking
Fracture appearance in a sheared region, presenting a ductile morphology for the fracture micromechanism.
109
VIEW
ML00046 / Jan.2018
Brittle Fracture of SS Shear Pin
M - Martensitic Stainless SteelP - Machined PartAp - EnergyCd - Intergranular Cracking
Cm - Fractography by SEMDf - Ductile Fracture
Fracture appearance in a brittle region, presenting an intergranular morphology.
93
VIEW
ML00046 / Jan.2018
Brittle Fracture of SS Shear Pin
M - Martensitic Stainless SteelP - Machined PartAp - EnergyCd - Intergranular Cracking
Cm - Fractography by SEMDf - Intergranular Cracking
Micrography of a longitudinal section of the pin, presenting a tempered martensitic structure with aligned delta ferrite and carbide phases.
80
VIEW
ML00046 / Jan.2018
Brittle Fracture of SS Shear Pin
M - Martensitic Stainless SteelP - Machined PartAp - EnergyCd - Intergranular Cracking
Cm - Kalling Etched Micrography by OMDf - Martensite, delta ferrite & carbides
Micrographic detail of the pin structure, in the longitudinal section, at the segregated band with aligned inclusions and phases, delta ferrite and carbides.
70
VIEW
ML00046 / Jan.2018
Brittle Fracture of SS Shear Pin
M - Martensitic Stainless SteelP - Machined PartAp - EnergyCd - Intergranular Cracking
Cm - Kalling Etched Micrography by OMDf - Martensite, delta ferrite & carbides
Micrographic detail of the pin structure, in the longitudinal section, presenting a martensitic matriz, aligned inclusions (grey, delta ferrite islands (poligonal white phases) and carbides (also white phases) surrounding the delta ferrite.
64
VIEW
ML00046 / Jan.2018
Brittle Fracture of SS Shear Pin
M - Martensitic Stainless SteelP - Machined PartAp - EnergyCd - Intergranular Cracking
Cm - Kalling Etched Micrography by OMDf - Martensite, delta ferrite & carbides

+1 more from this case →

ML00060 — Brittle Fracture of a Chilled Cast Iron CamshaftM - Chilled Cast IronP - ShaftAp - AutomotiveCd - Brittle Fracture
The macrography of a longitudinal section of the camshaft (tubular) in a position where there are two chilled lobes, presenting a strong microstructural change through thickness, from the hard chilled surface (500HV10) to the soft region in the middle of the thickness (187HV10).
96
VIEW
ML00060 / Apr.2017
Brittle Fracture of a Chilled Cast Iron Camshaft
M - Chilled Cast IronP - ShaftAp - AutomotiveCd - Brittle Fracture
Cm - NItal Etched MacroDf - Longitudinal Section
Close to the camshaft lobe surface, the chilled casting presents a white cast iron structure. Primary carbides and ledeburite with a hardness level about 50 HRc.
102
VIEW
ML00060 / Apr.2017
Brittle Fracture of a Chilled Cast Iron Camshaft
M - Chilled Cast IronP - ShaftAp - AutomotiveCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Close to the External Surface
Micrographic detail of the chilled structure. Primary carbides, ledeburite and perlite islands.
79
VIEW
ML00060 / Apr.2017
Brittle Fracture of a Chilled Cast Iron Camshaft
M - Chilled Cast IronP - ShaftAp - AutomotiveCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Close to the External Surface
In the center of the shaft thickness the structure is perlitic with graphite in flakes, but there are also islands of ledeburite.
62
VIEW
ML00060 / Apr.2017
Brittle Fracture of a Chilled Cast Iron Camshaft
M - Chilled Cast IronP - ShaftAp - AutomotiveCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - In the Center of the Thickness
Micrographic detail of the structure in the center of the shaft thickness. Perlitic matrix with graphite in flakes, and ledeburite islands.
53
VIEW
ML00060 / Apr.2017
Brittle Fracture of a Chilled Cast Iron Camshaft
M - Chilled Cast IronP - ShaftAp - AutomotiveCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - In the Center of the Thickness

+5 more from this case →

ML00040 — Brittle Fracture of a Valve StemM - Nodular Cast IronP - Valve StemAp - ShipCd - Brittle Fracture
Detail of the cleavage micromechanism.
195
VIEW
ML00040 / Apr.2017
Brittle Fracture of a Valve Stem
M - Nodular Cast IronP - Valve StemAp - ShipCd - Brittle Fracture
Cm - Fractography by SEMDf - Cleavage Facets
The cast iron microstructure is predominatly ferritic with graphite nodules.
169
VIEW
ML00040 / Apr.2017
Brittle Fracture of a Valve Stem
M - Nodular Cast IronP - Valve StemAp - ShipCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Graphite in Nodules
The micrography of the stem at the fracture region shows a flat fracture with transgranular clevage at the ferritic structure.
137
VIEW
ML00040 / Apr.2017
Brittle Fracture of a Valve Stem
M - Nodular Cast IronP - Valve StemAp - ShipCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Fracture
Micrography presenting a detail of the fracture surface opening to the graphite nodules.
139
VIEW
ML00040 / Apr.2017
Brittle Fracture of a Valve Stem
M - Nodular Cast IronP - Valve StemAp - ShipCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Fracture